CN102876271A - 观光电梯用玻璃粘合剂及其制备方法 - Google Patents

观光电梯用玻璃粘合剂及其制备方法 Download PDF

Info

Publication number
CN102876271A
CN102876271A CN2012103625157A CN201210362515A CN102876271A CN 102876271 A CN102876271 A CN 102876271A CN 2012103625157 A CN2012103625157 A CN 2012103625157A CN 201210362515 A CN201210362515 A CN 201210362515A CN 102876271 A CN102876271 A CN 102876271A
Authority
CN
China
Prior art keywords
parts
glass adhesive
sightseeing elevator
glass
tetraethoxysilane
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103625157A
Other languages
English (en)
Inventor
徐再忠
双华
屠永其
芦伟荣
顾军
吴春荣
计小红
徐洪生
徐晨宇
陈晓东
朱雪林
吕凤娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Fen Lake Elevator Co Ltd
Original Assignee
Suzhou Fen Lake Elevator Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Fen Lake Elevator Co Ltd filed Critical Suzhou Fen Lake Elevator Co Ltd
Priority to CN2012103625157A priority Critical patent/CN102876271A/zh
Publication of CN102876271A publication Critical patent/CN102876271A/zh
Pending legal-status Critical Current

Abstract

本发明涉及观光电梯用玻璃粘合剂，其特包括以重量份计的以下组分：环氧树脂100、四乙氧基硅烷 40-60、甲基三乙氧基硅烷25-35、多聚异氰酸酯 1-5、邻苯二甲酸二甲酯 0.5-1.5、炭黑 10-20、乙醇1-10、氧化镁10-20、云母粉0.1-1.0、硬脂酸钙1-10。按比例称取环氧树脂、邻苯二甲酸二甲酯、四乙氧基硅烷、甲基三乙氧基硅烷、多聚异氰酸酯，混合后加热到50-60摄氏度，搅拌10-15min，然后加入其他组份，混合均匀即可。本发明所得的胶可用于玻璃与金属、陶瓷之间的粘接密封，且耐酸碱、耐老化、耐高温。

Description

观光电梯用玻璃粘合剂及其制备方法
技术领域
    本发明涉及一种粘合剂，具体应用于观光电梯的玻璃。
背景技术
观光电梯的井道和轿厢至少有一侧透明，乘客可观看轿厢外景物。一般在轿厢的该透明侧安装钢化夹胶玻璃，该玻璃与电梯其他部件连接的部位需要用合适的胶来粘合，因为工作环境可能处于日照下，因此需要耐高温。
发明内容
    本发明所要解决的技术问题是提供一种观光电梯用玻璃粘合剂。
为解决上述技术问题，本发明是这样实现的 ：
观光电梯用玻璃粘合剂，包括以重量份计的以下组分：环氧树脂100、四乙氧基硅烷  40-60、甲基三乙氧基硅烷    25-35、多聚异氰酸酯  1-5、邻苯二甲酸二甲酯  0.5-1.5、炭黑  10-20、乙醇 1-10、氧化镁10-20、云母粉  0.1-1.0、硬脂酸钙1-10。
云母粉具有良好的耐热性能，白云母的熔点为1260-1290摄氏度，金云母的熔点为1270-1330摄氏度。
制备方法如下：将环氧树脂、邻苯二甲酸二甲酯、四乙氧基硅烷、甲基三乙氧基硅烷、多聚异氰酸酯、混合后加热到50-60摄氏度，搅拌10-15min，然后加入其他组份，混合均匀即可。
本发明无需使用有机溶剂，对人体无损害，环保，制备所得的观光电梯用玻璃粘合剂是无色的黏稠液，易于涂布、成膜性好、可用于玻璃与金属、陶瓷之间的粘接密封，且耐酸碱、耐老化可达10年之久。 
具体实施方式
下面结合具体实施方式对本发明做进一步的详细说明。
实施例1-4制观光电梯用玻璃粘合剂采用的组分的含量如下（单位：g）
表1
组份 实施例1 实施例2 实施例3 实施例4
环氧树脂 100 100 100 100
四乙氧基硅烷 40 50 60 45
甲基三乙氧基硅烷 25 30 35 28
多聚异氰酸酯 1 2 3 5
邻苯二甲酸二甲酯 0.5 1.0 1.5 0.8
炭黑 10 12 15 20
乙醇 1 5 10 3
氧化镁 10 14 16 20
云母粉 0.1 1.0 0.5 0.8
硬脂酸钙 10 2 6 1
制备方法如下：将环氧树脂、邻苯二甲酸二甲酯、四乙氧基硅烷、甲基三乙氧基硅烷、多聚异氰酸酯、混合后加热到50-60摄氏度，搅拌10-15min，然后加入其他组份，混合均匀即可。
实施例1所得胶，固化温度25℃、2h或者60℃、20min，使用温度-40℃-150℃。
上述具体实施方式不以任何形式限制本发明的技术方案，凡是采用等同替换或等效变换的方式所获得的技术方案均落在本发明的保护范围。   

Claims (2)

1.观光电梯用玻璃粘合剂，其特包括以重量份计的以下组分：环氧树脂100、四乙氧基硅烷  40-60、甲基三乙氧基硅烷25-35、多聚异氰酸酯  1-5、邻苯二甲酸二甲酯  0.5-1.5、炭黑  10-20、乙醇 1-10、氧化镁10-20、云母粉0.1-1.0、硬脂酸钙1-10。
2.基于权利要求1所述的观光电梯用玻璃粘合剂的制备方法，其特征在于按比例称取环氧树脂、邻苯二甲酸二甲酯、四乙氧基硅烷、甲基三乙氧基硅烷、多聚异氰酸酯，混合后加热到50-60摄氏度，搅拌10-15min，然后加入其他组份，混合均匀即可。
CN2012103625157A 2012-09-26 2012-09-26 观光电梯用玻璃粘合剂及其制备方法 Pending CN102876271A (zh)