CN104312507A - 一种耐高温胶粘剂及其制备方法 - Google Patents

一种耐高温胶粘剂及其制备方法 Download PDF

Info

Publication number
CN104312507A
CN104312507A CN201410582310.9A CN201410582310A CN104312507A CN 104312507 A CN104312507 A CN 104312507A CN 201410582310 A CN201410582310 A CN 201410582310A CN 104312507 A CN104312507 A CN 104312507A
Authority
CN
China
Prior art keywords
temperature
preparation
benzoxazine
temperature resistance
resistance adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410582310.9A
Other languages
English (en)
Other versions
CN104312507B (zh
Inventor
权栋栋
王丽丽
魏书同
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Nanhai Nan Xing Resin Co., Ltd.
Original Assignee
Shandong Zhongda Pharmaceutical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Zhongda Pharmaceutical Co Ltd filed Critical Shandong Zhongda Pharmaceutical Co Ltd
Priority to CN201410582310.9A priority Critical patent/CN104312507B/zh
Publication of CN104312507A publication Critical patent/CN104312507A/zh
Application granted granted Critical
Publication of CN104312507B publication Critical patent/CN104312507B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种耐高温胶粘剂及其制备方法，属于高温胶粘剂技术领域。本发明的耐高温胶粘剂，以苯并噁嗪为主要原料，多组分协同作用，使得本发明耐高温胶粘剂产品具有高温稳定性好、易于使用等优点；苯并噁嗪树脂是一种耐高温树脂，玻璃化转变温度Tg为在180℃以上，比环氧乙烷高约30℃左右，因此本发明胶粘剂耐热指数较高，比环氧乙烷胶粘剂有更好的耐热性和热稳定性；制备方法工艺流程简便，提高了生产效率，操作方便。

Description

一种耐高温胶粘剂及其制备方法
技术领域
    本发明涉及一种胶粘剂的制备方法，具体地，涉及一种耐高温胶粘剂及其制备方法。
背景技术
近年来，胶粘剂的应用越来越广泛，胶接技术已经成为包含胶接、焊接和机械连接在内的当代三大连接技术之一。其中，耐高温胶粘剂在航空航天、汽车、电子、军工和机械制造业等技术领域应用较为广泛。
其中，由于环氧树脂含有多种极性基团和活性很大的环氧基，因而与金属、玻璃、水泥、木材、塑料等多种极性材料具有很强的粘结力，同时环氧固化物的内聚强度也很大，所以胶结强度很高，在工业和生活领域得到了广泛的应用。现代科学技术的发展对胶粘剂的耐温性提出了更高的要求。例如，大型发电机组核电站的一些重要部位要使用耐温180-200℃的绝缘胶粘剂，车辆离合器摩擦片、制动带的胶结需要能在250-300℃工作的结构胶粘剂。因此研究耐高温胶粘剂十分重要。
发明内容
    本发明为解决上述问题，本发明提供了一种耐高温胶粘剂及其制备方法，本发明实现上述目的所采用的技术如下：
一种耐高温胶粘剂，由以下重量份的组分组成：
环氧树脂            50-60份；
苯并噁嗪树脂        20-30份；
滑石粉              5-12份；
氧化铝粉            10-30份；
二乙烯三胺          40-50份。
其中所述的环氧树脂由以下份数的组份组成，所述份数均为重量份：
E44                 25-30份；
E21                 25-30份。
其中所述的苯并噁嗪树脂可以为市售，或者按照以下方法进行合成：
将25.6-30.3g苯酚和100-150ml二氧六环加入三口烧瓶中，以50-80r/min的搅拌速度进行搅拌，温度升至80-90℃，逐滴加入多聚甲醛50.6-65.3g，滴加完毕后继续反应4-6h，反应结束后，开始真空脱水，在60-80℃、-95kPa脱除多余的溶剂及水，直至无气泡产生，得到金黄色液体，即为苯并噁嗪树脂。
其中所述的滑石粉为200-300目。
其中所述的氧化铝粉为200-300目。
制备工艺如下：
（1）将环氧树脂、苯并噁嗪树脂、滑石粉和氧化铝粉依次加入JJ-5行星式水泥胶砂搅拌机，搅拌均匀；
（2）使用时，加入二乙烯三胺，熟化10-20min即可使用。
 本发明所具有的有益效果是：
1、以苯并噁嗪为原料，多组分协同；苯并噁嗪树脂是一种耐高温树脂，玻璃化转变温度Tg为在180℃以上，比环氧乙烷高约30℃左右，因此本发明胶粘剂耐热指数较高，比环氧乙烷胶粘剂有更好的耐热性和热稳定性。
2、制备方法工艺流程简便，提高了生产效率，操作方便。
具体实施方式
下面将结合具体实施例对本发明做进一步说明，具体实施例不限制本发明。
实施例1 ：本发明提供了一种耐高温胶粘剂，由以下重量份的组分组成：
E44                 25份；
E21                 25份；
苯并噁嗪树脂        20份；
滑石粉              5份；
氧化铝粉            10份；
二乙烯三胺          40份。
本发明耐高温胶粘剂制备工艺如下：
（1）将25.6g苯酚和100ml二氧六环加入三口烧瓶中，以50r/min的搅拌速度进行搅拌，温度升至80℃，逐滴加入多聚甲醛50.6g，滴加完毕后继续反应4h，反应结束后，开始真空脱水，在60℃、-95kPa脱除多余的溶剂及水，直至无气泡产生，得到金黄色液体，即为苯并噁嗪树脂。
（2）将环氧树脂、苯并噁嗪树脂、滑石粉和氧化铝粉依次加入JJ-5行星式水泥胶砂搅拌机，搅拌均匀；
（3）使用时，加入二乙烯三胺，熟化10min即可使用。
实施例2 ：本发明提供了一种耐高温胶粘剂，由以下重量份的组分组成：
E44                 28份；
E21                 28份；
苯并噁嗪树脂        25份；
滑石粉              8份；
氧化铝粉            20份；
二乙烯三胺          45份。
本发明耐高温胶粘剂制备工艺如下：
（1）将26.5g苯酚和120ml二氧六环加入三口烧瓶中，以60r/min的搅拌速度进行搅拌，温度升至85℃，逐滴加入多聚甲醛55.6g，滴加完毕后继续反应5h，反应结束后，开始真空脱水，在70℃、-95kPa脱除多余的溶剂及水，直至无气泡产生，得到金黄色液体，即为苯并噁嗪树脂。 
（2）将环氧树脂、苯并噁嗪树脂、滑石粉和氧化铝粉依次加入JJ-5行星式水泥胶砂搅拌机，搅拌均匀；
（3）使用时，加入二乙烯三胺，熟化15min即可使用。
实施例3 ：本发明提供了一种耐高温胶粘剂，由以下重量份的组分组成：
E44                 30份；
E21                 30份；
苯并噁嗪树脂        30份；
滑石粉              12份；
氧化铝粉            30份；
二乙烯三胺          50份。
本发明耐高温胶粘剂制备工艺如下：
（1）将30.3g苯酚和150ml二氧六环加入三口烧瓶中，以80r/min的搅拌速度进行搅拌，温度升至90℃，逐滴加入多聚甲醛65.3g，滴加完毕后继续反应6h，反应结束后，开始真空脱水，在80℃、-95kPa脱除多余的溶剂及水，直至无气泡产生，得到金黄色液体，即为苯并噁嗪树脂。
（2）将环氧树脂、苯并噁嗪树脂、滑石粉和氧化铝粉依次加入JJ-5行星式水泥胶砂搅拌机，搅拌均匀；
（3）使用时，加入二乙烯三胺，熟化20min即可使用。

Claims (8)

1.一种耐高温胶粘剂，由下述原料构成，所述份数均为重量份:
环氧树脂            50-60份 
苯并噁嗪树脂        20-30份 
滑石粉              5-12份 
氧化铝粉            10-30份 
二乙烯三胺          40-50份。
2.权利要求1的一种耐高温胶粘剂，其特征在于：所述的环氧树脂由以下份数的组份组成，所述份数均为重量份：
E44                 25-30份
E21                 25-30份。
3.权利要求1的一种耐高温胶粘剂，其特征在于：所述的滑石粉为200-300目。
4.权利要求1的一种耐高温胶粘剂，其特征在于：所述的氧化铝粉为200-300目。
5.如权利要求1所述的所述的苯并噁嗪的制备方法为：将25.6-30.3g苯酚和100-150ml二氧六环加入三口烧瓶中，进行搅拌，温度升至80-90℃，逐滴加入多聚甲醛50.6-65.3g，滴加完毕后继续反应4-6h，反应结束后，开始真空脱水，直至无气泡产生，得到金黄色液体，即为苯并噁嗪树脂。
6.如权利要求5所述的苯并噁嗪的制备方法，其特征在于：将苯酚和二氧六环加入三口烧瓶中，以50-80r/min的搅拌速度进行搅拌。
7.如权利要求5所述的苯并噁嗪的制备方法，其特征在于：真空脱水在60-80℃、-95kPa脱除多余的溶剂及水。
8.如权利要求1所述的一种耐高温胶粘剂的制备方法，其特征在于：
1）将环氧树脂、苯并噁嗪树脂、滑石粉和氧化铝粉依次加入JJ-5行星式水泥胶砂搅拌机，搅拌均匀；
2）使用时，加入二乙烯三胺，熟化10-20min使用。
CN201410582310.9A 2014-10-28 2014-10-28 一种耐高温胶粘剂及其制备方法 Expired - Fee Related CN104312507B (zh)