CN102867603A - 一种钕铁硼永磁材料及生产工艺 - Google Patents
一种钕铁硼永磁材料及生产工艺 Download PDFInfo
- Publication number
- CN102867603A CN102867603A CN 201210369877 CN201210369877A CN102867603A CN 102867603 A CN102867603 A CN 102867603A CN 201210369877 CN201210369877 CN 201210369877 CN 201210369877 A CN201210369877 A CN 201210369877A CN 102867603 A CN102867603 A CN 102867603A
- Authority
- CN
- China
- Prior art keywords
- permanent magnet
- magnet material
- iron boron
- neodymium iron
- boron permanent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种钕铁硼永磁材料及生产工艺，属于稀土材料领域。特点是一种钕铁硼永磁材料添加镓属于Nd15Fe78-xB7Gax(x=0.30-1.0)系永磁材料，在x=0.55时，采用的生产工艺是粉末冶金烧结和两级回火工艺即烧结温度1105℃、烧结时间80min，一级回火温度900℃、回火时间70min,二级回火温度610℃、回火时间110min。其性能最佳。有益效果是工艺操作简单，添加一些金属镓提高了钕铁硼系永磁材料的综合性能，成本低廉。
Description
技术领域
本发明涉及一种钕铁硼永磁材料，特别是一种钕铁硼永磁材料及生产工艺，属于稀土材料技术领域。
背景技术
Nd15Fe78B7系永磁材料（简称Nd-Fe-B系）在现代科学技术与信息产业中得到了广泛的应用，烧结Nd-Fe-B永磁体是目前为止磁性最强的永磁材料。现在实验室样品的(BH)已达到444KJ/m3,工艺品（BH）已达到398 KJ/m3（理论值为525KJ/m3），但在实际应用中其抗退磁能力却较差，原因就是内禀矫顽力只达到理论矫顽力的1/3左右。所以提高烧结钕铁硼的内禀矫顽力是提高其磁性能和扩展其使用范围的关键技术之一。
发明内容
针对上述现有技术存在的问题，现在有两种方法可以提高其矫顽力，一种是优化生产工艺，降低氧的含量，一种是添加一些金属元素改善组织结构。本发明提供一种钕铁硼永磁材料及生产工艺，通过优化生产工艺和添加一定量金属镓改善其组织结构，提高内禀矫顽力。
为了实现上述目的，本发明采用的技术方案是：一种钕铁硼永磁材料及生产工艺，所述的钕铁硼永磁材料添加金属镓属于Nd15Fe78-xB7Gax(x=0.30-1.0)系永磁材料，制造工艺采用粉末冶金烧结和两级回火工艺。
进一步，钕铁硼永磁材料Nd15Fe78-xB7Gax在x=0.55为最佳的Ga添加量。
进一步，生产工艺是烧结温度1050℃-1150℃，烧结时间80min,一级回火温度870℃-920℃，回火时间70min,二级回火温度580℃-640℃，回火时间110min。
进一步，生产工艺是烧结温度1105℃，烧结时间80min，一级回火温度900℃，回火时间70min,二级回火温度610℃，回火时间110min。
本发明的有益效果是：工艺操作简单，且添加一定量金属镓，能在最大磁能积基本不变的条件下，提高Nd-Fe-B系永磁体的内禀矫顽力和居里温度，扩大了其应用范围且成本低廉。
附图说明
图1是本发明的烧结曲线图；
图2是本发明的实施1烧结曲线图。
具体实施方式
下面将结合附图对本发明作进一步说明。
实施例1：一种添加镓的钕铁硼永磁材料
配料：
| 组分 | Nd | Fe | B | Ga |
| 含量wt％ | 15 | 74.45 | 7 | 0.55 |
采用传统的粉末冶金方法制备Nd-Fe-B+Ga永磁材料，其工艺流程为：原材料→熔炼→铸锭→粗破碎→细破碎→磁场取向与成形→烧结→回火→机械加工与表面处理→性能检测。其中的工艺参数为：球磨球料比15:1、球磨时间60min，垂直模压+冷等静压（300Mpa），烧结温度1105℃、烧结时间80min,900℃一级热处理70min、610℃二级热处理110min。把烧结完的磁体加工成Φ10×10的柱状样品，在磁性测量仪上进行性能检测。
磁性能如下：最大磁能积BH(max): 250KJ/m3， 内禀矫顽力Hcj:1005KA/m 。
Claims (4)
1. 一种钕铁硼永磁材料及生产工艺，其特征在于， 所述的钕铁硼永磁材料添加金属镓属于Nd15Fe78-xB7Gax(x=0.30-1.0)系永磁材料，制造工艺采用粉末冶金烧结和两级回火工艺。
2. 根据权利要求1 所述的一种钕铁硼永磁材料及生产工艺，其特征在于，所述的钕铁硼永磁材料Nd15Fe78-xB7Gax在x=0.55为最佳的Ga添加量。
3. 根据权利要求1 所述的一种钕铁硼永磁材料及生产工艺，其特征在于，所述的生产工艺是烧结温度1050℃-1150℃，烧结时间80min,一级回火温度870℃-920℃，回火时间70min,二级回火温度580℃-640℃，回火时间110min。
4. 根据权利要求1 所述的一种钕铁硼永磁材料及生产工艺，其特征在于，所述的生产工艺是烧结温度1105℃，烧结时间80min，一级回火温度900℃、回火时间70min,二级回火温度610℃、回火时间110min。