CN102839559A - 一种涂布字典纸的生产方法 - Google Patents

一种涂布字典纸的生产方法 Download PDF

Info

Publication number
CN102839559A
CN102839559A CN2012103417756A CN201210341775A CN102839559A CN 102839559 A CN102839559 A CN 102839559A CN 2012103417756 A CN2012103417756 A CN 2012103417756A CN 201210341775 A CN201210341775 A CN 201210341775A CN 102839559 A CN102839559 A CN 102839559A
Authority
CN
China
Prior art keywords
paper
page
coated
coating
production method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103417756A
Other languages
English (en)
Other versions
CN102839559B (zh
Inventor
王巨波
张�诚
张美娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CRANE CO., LTD.
Original Assignee
ZHEJIANG XIANHE SPECIAL PAPER CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG XIANHE SPECIAL PAPER CO Ltd filed Critical ZHEJIANG XIANHE SPECIAL PAPER CO Ltd
Priority to CN201210341775.6A priority Critical patent/CN102839559B/zh
Publication of CN102839559A publication Critical patent/CN102839559A/zh
Application granted granted Critical
Publication of CN102839559B publication Critical patent/CN102839559B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种涂布字典纸的生产方法，属造纸行业，该方法包括如下步骤：制备磨浆后进行配浆；加入烷基烯酮二聚体、阳离子淀粉；浆料进行上网抄造；纸页进入压榨部；纸页进入前干燥部；纸页进入机内双面薄膜涂布，其中，控制涂料的浓度、粘度使两面的涂布量均达到3-5g/m2；纸页经过非接触的热风干燥箱预干燥；纸页进入后干燥部；纸页进入双压区软压光进行表面整饰；卷纸机卷取。本发明在纸页抄造时不加填料，纸页内部结合力提高，使纸面紧度提高，同时涂布层把纸页表面毛细孔填满，本发明生产的涂布字典纸具有纸页薄，不透明度、平滑度和紧度高的有益效果。

Description

一种涂布字典纸的生产方法
技术领域
本发明涉及一种字典纸的生产方法。
背景技术
现有技术中，生产字典纸最低定量只能到28g/m2,随着定量降低，纸的厚度相应下降，纸页的不透明度和紧度随之下降，通常，不透明度低于70%，紧度小于0.764g/cm3，不透明度降低后，由于纸页表面密布毛细孔，在印刷时油墨有一定渗透，纸页背面印刷内容会透过纸面，造成印刷质量不良，影响阅读，如果定量增加，将会增加纸浆的用量，增加成本，同时也增加了字典的重量和体积，不方便携带。
发明内容
本发明为了克服现有技术的不足，提供了一种涂布字典纸的生产方法，该生产方法采用双面涂布，纸页由涂层、植物纤物、涂层组成三层结构，由于三层的折光率不同，分别为1.98、1.57、1.98，光在透过纸时，其光的折射加强，使不透明度加强；由于涂布颜料白度较高，同时通过涂布，纸面的平滑度提高，光的反射增加，不透明度增加，印刷时油墨不易渗透。
本发明的技术方案是：
一种涂布字典纸的生产方法，包括如下步骤：
A、制备磨浆后进行配浆；
B、加入烷基烯酮二聚体、阳离子淀粉；
C、浆料进行上网抄造；
D、纸页进入压榨部；
E、纸页进入前干燥部；
F、纸页进入机内双面薄膜涂布，其中，控制涂料的浓度、粘度使两面的涂布量均达到3-5g/m2；
G、纸页经过非接触的热风干燥箱预干燥；
H、纸页进入后干燥部；
I、纸页进入双压区软压光进行表面整饰；
J、卷纸机卷取。
所述步骤F中，涂料的配方按：80份重质超细碳酸钙，20份金红石型钛白粉，10-15份丁苯乳胶，15-20份季胺型阳离子淀粉，0.3-0.5份保水剂，0.01-0.03份分散剂， 0.5-0.7份润滑剂，0.01-0.03消泡剂，涂料的固含量35-40%，涂料的粘度1800厘泊。
所述步骤A中磨浆后阔叶木浆浆度20-40○SR，针叶木浆浆度50-70○SR，并按阔叶木浆40-60%，针叶木浆40-60%进行配浆。
所述步骤C中，抄造时的上网浓度为0.5-0.6%，车速为500-600m/min，纸页在进入饰面辊前脱水量为70-80%，出网部湿纸页的干度为20-21%。
所述步骤D中，压榨部由四辊三压区组成，三道压区的压力分别是：60kN/m2、80kN/m2、120kN/m2，出压榨后的湿纸页的干度为40-43%。
所述步骤E中，出前干燥部的水分为4-7%。
所述步骤Ｈ中，出后干燥部的水分为3-5%。
所述步骤I中，双压区软压光的压力为120-180kN/m2，热辊表面温度为110-160℃。
本发明一种涂布字典纸的生产方法在纸页抄造时不加填料，纸页内部结合力提高，使纸面紧度提高，同时涂布层把纸页表面毛细孔填满，用本方法生产的字典纸，平滑度大于150s，不透明度大于82%，紧度可达0.82-0.84 g/cm3，表面强度用蜡拔检测大于16级，表面光泽为亚光，本发明生产的涂布字典纸具有纸页薄，不透明度、平滑度和紧度高的有益效果。
具体实施方式
下面通过实施例，具体说明本发明一种涂布字典纸的生产方法。
实施例：制备磨浆后进行配浆，磨浆后阔叶木浆浆度20-40○SR，针叶木浆浆度50-70○SR，并按阔叶木浆40-60%，针叶木浆40-60%进行配浆；加入烷基烯酮二聚体 0.5kg/T浆、阳离子淀粉 0.1-0.2 kg/T浆；浆料进行上网抄造，抄造时的上网浓度为0.5-0.6%，车速为500-600m/min，纸页在进入饰面辊前脱水量为70-80%，出网部湿纸页的干度为20-21%；纸页进入压榨部，压榨部由四辊三压区组成，三道压区的压力分别是：60kN/m2、80kN/m2、120kN/m2，出压榨后的湿纸页的干度为40-43%；纸页进入前干燥部，水分为4-7%；纸页进入机内双面薄膜涂布，其中，控制涂料的浓度、粘度使两面的涂布量均达到3-5g/m2，涂料的配方按：80份重质超细碳酸钙，20份金红石型钛白粉，10-15份丁苯乳胶，15-20份季胺型阳离子淀粉，0.3-0.5份保水剂，0.01-0.03份分散剂，0.5-0.7份润滑剂，0.01-0.03消泡剂，涂料的固含量35-40%，涂料的粘度1800厘泊。纸页经过非接触的热风干燥箱预干燥，热风温度为100-130℃；纸页进入后干燥部，出后干燥部的水分为3-5%；纸页进入双压区软压光进行表面整饰，双压区软压光的压力为120-150kN/m2，热辊表面温度为120-150℃。
在上述步骤、条件相同的情况下，选取不同的定量和两面涂量时可以得到不同的不透明度、平滑度和紧度，如表1所示，项目0为现有技术生产的字典纸，项目1-3为涂布字典纸，从表1中可以看出，用本发明方法生产的字典纸，不透明度、平滑度和紧度要明显高于现有技术生产的字典纸。
表1
Figure BDA0000213938941
以上所述仅为本发明的较佳实施例而已，并不以此限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。

Claims (8)

1.一种涂布字典纸的生产方法，其特征是，包括如下步骤：
A、制备磨浆后进行配浆；
B、加入烷基烯酮二聚体、阳离子淀粉；
C、浆料进行上网抄造；
D、纸页进入压榨部；
E、纸页进入前干燥部；
F、纸页进入机内双面薄膜涂布，其中，控制涂料的浓度、粘度使两面的涂布量均达到3-5g/m2；
G、纸页经过非接触的热风干燥箱预干燥；
H、纸页进入后干燥部；
I、纸页进入双压区软压光进行表面整饰；
J、卷纸机卷取。
2.如权利要求1所述的一种涂布字典纸的生产方法，其特征是：所述步骤F中，涂料的配方按：80份重质超细碳酸钙，20份金红石型钛白粉，10-15份丁苯乳胶，15-20份季胺型阳离子淀粉，0.3-0.5份保水剂，0.01-0.03份分散剂， 0.5-0.7份润滑剂，0.01-0.03消泡剂，涂料的固含量35-40%，涂料的粘度1800厘泊。
3.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤A中磨浆后阔叶木浆浆度20-40○SR，针叶木浆浆度50-70○SR，并按阔叶木浆40-60%，针叶木浆40-60%进行配浆。
4.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤C中，抄造时的上网浓度为0.5-0.6%，车速为500-600m/min，纸页在进入饰面辊前脱水量为70-80%，出网部湿纸页的干度为20-21%。
5.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤D中，压榨部由四辊三压区组成，三道压区的压力分别是：60kN/m2、80kN/m2、120kN/m2，出压榨后的湿纸页的干度为40-43%。
6.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤E中，出前干燥部的水分为4-7%。
7.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤Ｈ中，出后干燥部的水分为3-5%。
8.如权利要求1或2所述的一种涂布字典纸的生产方法，其特征是：所述步骤I中，双压区软压光的压力为120-180kN/m2，热辊表面温度为110-160℃。
CN201210341775.6A 2012-09-14 2012-09-14 一种涂布字典纸的生产方法 Active CN102839559B (zh)