CN102728777A - 一种多组分混合铸造型砂及其制备方法 - Google Patents
一种多组分混合铸造型砂及其制备方法 Download PDFInfo
- Publication number
- CN102728777A CN102728777A CN2012101870120A CN201210187012A CN102728777A CN 102728777 A CN102728777 A CN 102728777A CN 2012101870120 A CN2012101870120 A CN 2012101870120A CN 201210187012 A CN201210187012 A CN 201210187012A CN 102728777 A CN102728777 A CN 102728777A
- Authority
- CN
- China
- Prior art keywords
- sand
- preparation
- parts
- acrylic resin
- resin modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种多组分混合铸造型砂及其制备方法,其按组成原料的重量份称取石英砂80-90、回用砂30-40、海泡石5-15、香菇栽培料出菇后废料3-8、水泥1-3、改性丙烯酸树脂1-3和水适量,混合均匀,干混3-5分钟,再加入水,湿混5-8分钟,放入储砂斗中,造型,分离得到成品。本发明制备方法简单,配方合理、成本低廉、生产效率高,利用香菇栽培袋料出菇后废料,烘干后粉碎,作为型砂原料,变废为宝。
Description
技术领域
本发明涉及铸造技术领域,具体涉及一种多组分混合铸造型砂及其制备方法。
背景技术
型砂在铸造生产中的作用极为重要,因型砂的质量不好而造成的铸件废品约占铸件总废品的30~50%,通常对型砂的要求有强度和热稳定性、流动性、可塑性、透气性和溃散性,即在铸件凝固后型砂是否容易破坏,是否容易从铸件上清除的性能。
目前,在型砂的制备过程中,一般由新砂、旧砂、粘结剂和辅料按一定比例混合制成。
发明内容
为了缓解现有技术的不足和缺陷,本发明的目的在于提供一种多组分混合铸造型砂及其制备方法。
为了实现上述目的本发明采用如下技术方案:
多组分混合铸造型砂,其组成原料重量份为:石英砂80-90、回用砂30-40、海泡石5-15、香菇栽培料出菇后废料3-8、水泥1-3、改性丙烯酸树脂1-3和水适量。
多组分混合铸造型砂,其组成原料重量份为:石英砂85、回用砂35、海泡石10、香菇栽培料出菇后废料5、水泥2、改性丙烯酸树脂2和水适量。
多组分混合铸造型砂的制作方法,按组成原料的重量份称取石英砂、回用砂、海泡石、香菇栽培料出菇后废料、水泥和改性丙烯酸树脂,混合均匀,干混3-5分钟,再加入水,湿混5-8分钟,放入储砂斗中,造型,分离得到成品。
香菇栽培料出菇后废料烘干后粉碎使用。
所述的改性丙烯酸树脂由组成原料叔碳酸乙烯酯10-12、苯乙烯10-12、丙烯酸丁酯8-10、丙三醇4-6、异十二烷基硫醇0.1-0.2、过硫酸钠0.3-0.5和溶剂醋酸丁酯40-45,制备方法:将溶剂醋酸丁酯加入反应釜中,充氮气保护,再将过硫酸钠以外的其它反应原料加入反应釜中,搅拌,加热到140-150℃,将过硫酸钠加入反应釜中,搅拌,保温反应3-4小时,降温至90℃以上,过滤,得到。
本发明的优点:
本发明制备方法简单,配方合理、成本低廉、生产效率高,利用香菇栽培袋料出菇后废料,烘干后粉碎,作为型砂原料,变废为宝。
具体实施方式
实施例1:多组分混合铸造型砂,其组成原料重量份为:石英砂80、回用砂30、海泡石5、香菇栽培料出菇后废料3、水泥1、改性丙烯酸树脂1和水适量。
多组分混合铸造型砂的制作方法,按组成原料的重量份称取石英砂、回用砂、海泡石、香菇栽培料出菇后废料、水泥和改性丙烯酸树脂,混合均匀,干混3-5分钟,再加入水,湿混5-8分钟,放入储砂斗中,造型,分离得到成品。
所述的改性丙烯酸树脂由组成原料叔碳酸乙烯酯10-12、苯乙烯10-12、丙烯酸丁酯8-10、丙三醇4-6、异十二烷基硫醇0.1-0.2、过硫酸钠0.3-0.5和溶剂醋酸丁酯40-45,制备方法:将溶剂醋酸丁酯加入反应釜中,充氮气保护,再将过硫酸钠以外的其它反应原料加入反应釜中,搅拌,加热到140-150℃,将过硫酸钠加入反应釜中,搅拌,保温反应3-4小时,降温至90℃以上,过滤,得到。
实施例2:多组分混合铸造型砂,其组成原料重量份为:石英砂85、回用砂35、海泡石10、香菇栽培料出菇后废料5、水泥2、改性丙烯酸树脂2和水适量。
多组分混合铸造型砂的制作方法,如同实施例1。
所述的改性丙烯酸树脂配方及制备方法如同实施例1。
实施例3:多组分混合铸造型砂,其组成原料重量份为:石英砂90、回用砂40、海泡石15、香菇栽培料出菇后废料8、水泥3、改性丙烯酸树脂3和水适量。
多组分混合铸造型砂的制作方法,如同实施例1。
所述的改性丙烯酸树脂配方及制备方法如同实施例1。
本发明制得的型砂性能:湿压强度≥0.15Mpa,透气性≥83,水分3.2-3.5,紧实率48-58,破碎指数(j:)85-88%。
Claims (4)
1.一种多组分混合铸造型砂,其特征在于其组成原料重量份为:石英砂80-90、回用砂30-40、海泡石5-15、香菇栽培料出菇后废料3-8、水泥1-3、改性丙烯酸树脂1-3和水适量。
2.根据权利要求1所述的多组分混合铸造型砂,其特征在于其组成原料重量份为:石英砂85、回用砂35、海泡石10、香菇栽培料出菇后废料5、水泥2、改性丙烯酸树脂2和水适量。
3.一种如权利要求1所述的多组分混合铸造型砂的制作方法,其特征在于:按组成原料的重量份称取石英砂、回用砂、海泡石、香菇栽培料出菇后废料、水泥和改性丙烯酸树脂,混合均匀,干混3-5分钟,再加入水,湿混5-8分钟,放入储砂斗中,造型,分离得到成品。
4.根据权利要求1所述的利用废锯末的型砂,其特征在于:所述的改性丙烯酸树脂由组成原料叔碳酸乙烯酯10-12、苯乙烯10-12、丙烯酸丁酯8-10、丙三醇4-6、异十二烷基硫醇0.1-0.2、过硫酸钠0.3-0.5和溶剂醋酸丁酯40-45,制备方法:将溶剂醋酸丁酯加入反应釜中,充氮气保护,再将过硫酸钠以外的其它反应原料加入反应釜中,搅拌,加热到140-150℃,将过硫酸钠加入反应釜中,搅拌,保温反应3-4小时,降温至90℃以上,过滤,得到。