CN100391632C - 一种废弃混凝土再生利用的方法 - Google Patents

一种废弃混凝土再生利用的方法 Download PDF

Info

Publication number
CN100391632C
CN100391632C CNB200510019051XA CN200510019051A CN100391632C CN 100391632 C CN100391632 C CN 100391632C CN B200510019051X A CNB200510019051X A CN B200510019051XA CN 200510019051 A CN200510019051 A CN 200510019051A CN 100391632 C CN100391632 C CN 100391632C
Authority
CN
China
Prior art keywords
powder
mortar
sand
waste concrete
discarded concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB200510019051XA
Other languages
English (en)
Other versions
CN1709594A (zh
Inventor
胡曙光
何永佳
丁庆军
吕林女
吴静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhan University of Technology WUT
Original Assignee
Wuhan University of Technology WUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhan University of Technology WUT filed Critical Wuhan University of Technology WUT
Priority to CNB200510019051XA priority Critical patent/CN100391632C/zh
Publication of CN1709594A publication Critical patent/CN1709594A/zh
Application granted granted Critical
Publication of CN100391632C publication Critical patent/CN100391632C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种废弃混凝土再生利用的方法。一种废弃混凝土再生利用的方法，其特征在于包括如下步骤：1)将废弃混凝土破碎，把粗集料和砂浆分离开来；2)将砂浆破碎成≤1cm粒径的颗粒，然后用磨机磨细至比表面积≥300m2/kg的粉体；3)将磨细后的砂浆粉体与比表面积≥300m2/kg的Ca(OH)2细粉混合均匀，再与水拌合均匀成型，各组份所占重量百分比为砂浆粉体40-70、Ca(OH)2细粉20-50、水10-20；4)脱模后放入高压釜内在1-1.5MPa压力下压蒸4-8小时制得灰砂产品。该方法可使废弃混凝土得到有效利用，制得强度达到45Mpa以上的灰砂产品。

Description

一种废弃混凝土再生利用的方法
技术领域
本发明属于建筑材料领域，具体涉及一种废弃混凝土再生利用的方法。
背景技术
随着建设规模的扩大，大量新建筑拨地而起，同时大量旧建筑物和工程结构被拆除，产生数量惊人的建筑废弃物，其中废弃混凝土占了相当大的一部分。大量废弃混凝土作为垃圾被填埋，这种粗放的处理方式不仅占用大量宝贵土地建设堆场，同时也是对资源的巨大浪费。在资源和能源日益紧张的情况下，将废弃混凝土再生资源化进行有效利用具有重大的意义。目前对废弃混凝土的再生利用主要集中在粗集料方面，而占废弃混凝土组分相当比重的砂浆却没有得到有效利用。
发明内容
针对上述问题，本发明的目的在于提供一种废弃混凝土再生利用的方法，该方法可使废弃混凝土得到有效利用，可制得强度高的灰砂产品。
为了实现上述目的，本发明的技术方案是：一种废弃混凝土再生利用的方法，其特征在于包括如下步骤：1)、将废弃混凝土破碎，把粗集料和砂浆分离开来；2)、将砂浆破碎成≤1cm粒径的颗粒，然后用磨机磨细至比表面积≥300m2/kg的粉体；3)、将磨细后的砂浆粉体与比表面积≥300m2/kg的Ca(OH)2细粉混合均匀，再与水拌合均匀成型，各组份所占重量百分比为砂浆粉体40-70％、Ca(OH)2细粉20-50％、水10-20％；4)、脱模后放入高压釜内在1-1.5MPa压力下压蒸4-8小时制得灰砂产品。
将废弃混凝土中的粗集料除去后，剩余的大部分是砂浆，砂浆中含有水泥等胶凝材料的水化产物、未水化胶凝材料颗粒和石英砂。普通石英砂未经粉磨活性很低，但粉磨至比表面积300m2/kg以上之后的石英砂在压蒸条件下与Ca(OH)2反应可以得到具有相当高强度的制品。砂浆中的未水化胶凝材料颗粒在此条件下可以参与反应，形成水化产物，提高制品的强度和密实性；而砂浆中的水化产物磨细至比表面积300m2/kg以上之后可以起到晶核的作用，降低成核势垒，诱导水热反应体系中产物晶体析出，加速反应进程。
本发明的方法可使废弃混凝土得到有效利用，制得强度达到45Mpa以上的灰砂产品。
具体实施方式
实施例1：
一种废弃混凝土再生利用的方法，包括如下步骤：1)、收集建筑物拆除后的废弃混凝土，将废弃混凝土破碎，把粗集料和砂浆分离开来；2)、将砂浆破碎成1cm粒径的颗粒，然后用磨机磨细至比表面积300m2/kg的粉体；3)、将磨细后的砂浆粉体与Ca(OH)2细粉(比表面积300m2/kg)混合均匀，再与水拌合均匀成型，各组份的重量比为砂浆粉体∶Ca(OH)2细粉∶水＝1∶0.3∶0.15；4)、脱模后放入高压釜内在1MPa压力下压蒸4小时制得灰砂产品。经检测，灰砂产品28d强度达到50MPa。
实施例2：
一种废弃混凝土再生利用的方法，包括如下步骤：1)、收集道路翻修后废弃的路面混凝土，将废弃混凝土破碎，把粗集料和砂浆分离开来；2)、将砂浆破碎成8mm粒径的颗粒，然后用磨机磨细至比表面积350m2/kg的粉体；3)、将磨细后的砂浆粉体与Ca(OH)2细粉(比表面积350m2/kg)混合均匀，再与水拌合均匀成型，各组份的重量比为砂浆粉体∶Ca(OH)2细粉∶水＝1∶0.5∶0.20；4)、脱模后放入高压釜内在1.2MPa压力下压蒸6小时制得灰砂产品。经检测，灰砂产品28d强度达到45MPa。
实施例3：
一种废弃混凝土再生利用的方法，包括如下步骤：1)、收集道路翻修后废弃的路面混凝土，将废弃混凝土破碎，把粗集料和砂浆分离开来；2)、将砂浆破碎成5mm粒径的颗粒，然后用磨机磨细至比表面积350m2/kg的粉体；3)、将磨细后的砂浆粉体与Ca(OH)2细粉(比表面积350m2/kg)混合均匀，再与水拌合均匀成型，各组份的重量比为砂浆粉体∶Ca(OH)2细粉∶水＝1∶0.5∶0.20；4)、脱模后放入高压釜内在1.5MPa压力下压蒸8小时制得灰砂产品。经检测，灰砂产品28d强度达到50MPa。

Claims (1)

1.一种废弃混凝土再生利用的方法，其特征在于包括如下步骤：1)、将废弃混凝土破碎，把粗集料和砂浆分离开来；2)、将砂浆破碎成≤1cm粒径的颗粒，然后用磨机磨细至比表面积≥300m2/kg的粉体；3)、将磨细后的砂浆粉体与比表面积≥300m2/kg的Ca(OH)2细粉混合均匀，再与水拌合均匀成型，各组份所占重量百分比为砂浆粉体40-70％、Ca(OH)2细粉20-50％、水10-20％；4)、脱模后放入高压釜内在1-1.5MPa压力下压蒸4-8小时制得灰砂产品。
CNB200510019051XA 2005-07-05 2005-07-05 一种废弃混凝土再生利用的方法 Expired - Fee Related CN100391632C (zh)