CN102674446A - 一种片状结构钛酸铅粉体的制备方法 - Google Patents

一种片状结构钛酸铅粉体的制备方法 Download PDF

Info

Publication number
CN102674446A
CN102674446A CN2012101430972A CN201210143097A CN102674446A CN 102674446 A CN102674446 A CN 102674446A CN 2012101430972 A CN2012101430972 A CN 2012101430972A CN 201210143097 A CN201210143097 A CN 201210143097A CN 102674446 A CN102674446 A CN 102674446A
Authority
CN
China
Prior art keywords
reaction kettle
preparation
lead
titanium
titanate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101430972A
Other languages
English (en)
Other versions
CN102674446B (zh
Inventor
徐刚
何俊浩
任召辉
韩高荣
沈鸽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang University ZJU
Original Assignee
Zhejiang University ZJU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University ZJU filed Critical Zhejiang University ZJU
Priority to CN201210143097.2A priority Critical patent/CN102674446B/zh
Publication of CN102674446A publication Critical patent/CN102674446A/zh
Application granted granted Critical
Publication of CN102674446B publication Critical patent/CN102674446B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种片状结构钛酸铅的制备方法，包括制备钛的羟基氧化物沉淀和铅的去离子水溶液作为反应物料，加入适宜浓度的四甲基氢氧化铵促进晶化并控制形貌，于150~200℃下，水热反应得到单分散的片状结构钛酸铅。本发明工艺过程简单，易于控制，无污染，成本低，易于规模化生产。在微电子器件、催化剂、发光材料等领域具有广阔的应用前景。

Description

一种片状结构钛酸铅粉体的制备方法
技术领域
本发明涉及一种片状结构钛酸铅粉体的制备方法，属于无机非金属材料领域。
背景技术
传统钙钛矿结构钛酸铅是一种典型的铁电材料，其铁电相变的居里温度为490℃。由于具有优异的铁电、压电、介电性能，这使得钛酸铅在非挥发性铁电存储器、压电传感器、热释电敏感器和高介电电容器等微电子器件的制备上有着广泛的应用。
片状结构钛酸铅由于其在一维方向上的大表面积使其在高介电电容器等微电子器件上将会有巨大的应用前景，但是，目前报道的合成出的钛酸铅粉体形貌主要是块状结构、一维的柱状结构，对于二维的片状结构的报道很少。
发明内容
本发明的目的在于提供一种工艺简单的片状结构钛酸铅的制备方法。
本发明的片状结构钛酸铅的制备方法，包括以下步骤：
1） 将钛酸四丁酯溶于乙二醇甲醚，调节溶液中的Ti4+离子浓度为0.1~2mol/L；
2） 搅拌状态下，向步骤1）制得的钛酸四丁酯的乙二醇甲醚溶液中加入质量浓度30%的氨水溶液，氨水溶液体积为钛酸四丁酯的乙二醇甲醚溶液体积的1/4~1/5， 沉淀，过滤，洗涤，得到钛的羟基氧化物沉淀；
3） 将硝酸铅溶于去离子水中，形成硝酸铅水溶液，调节溶液中铅离子的浓度为0.1~2.5mol/L；
4） 将步骤2）中得到的钛的羟基氧化物沉淀、步骤3）中得到的硝酸铅水溶液和质量分数为98%的四甲基氢氧化铵晶体加入到反应釜内胆中，并用去离子水调节物料体积为反应釜容积的1/3~4/5，搅拌1小时，其中钛的摩尔浓度为0.05~1mol/L，铅和钛的摩尔比为0.5~5，四甲基氢氧化铵的摩尔浓度为0.15~0.25mol/L，摩尔浓度的体积基数为前躯体浆料的总体积；
5） 将装有前驱体浆料的反应釜内胆置于反应釜中，密封，在150~200℃下保温6~100小时进行水热处理，然后让反应釜自然冷却到室温，取出反应物，过滤，依次用去离子水、乙醇清洗，烘干，得到片状结构钛酸铅。
本发明所使用的反应釜为聚四氟乙烯内胆，不锈钢套件密闭的反应釜。
本发明所使用的钛酸四丁酯、硝酸铅、四甲基氢氧化铵的纯度都不低于化学纯。
本发明利用四甲基氢氧化铵制备的片状结构钛酸铅，是一种含有碳酸根、硝酸根、氢氧根的片状结构钛酸铅，其分子式为PbTiO2(CO3)0.3(NO3)0.35(OH)。制备工艺简单，易于控制，无污染，成本低。该片状钛酸铅在微电子器件、催化剂、发光材料等领域具有广阔的应用前景。
附图说明
图1是片状结构钛酸铅的XRD图谱；
图2是片状结构钛酸铅的扫描电镜照片。
具体实施方式
以下结合实施例进一步说明本发明。
实例1
1） 将钛酸四丁酯溶于10ml乙二醇甲醚中，磁力搅拌溶解，得到Ti4+浓度为0.1mol/L；
2） 搅拌状态下，向步骤1）制得的钛酸四丁酯的乙二醇甲醚溶液中加入质量浓度30%的氨水溶液，加入的氨水溶液体积为钛酸四丁酯的乙二醇甲醚溶液体积的1/5， 沉淀，过滤，洗涤，得到钛的羟基氧化物沉淀；
3） 将硝酸铅溶于去离子水中，形成硝酸铅水溶液，使得Pb2+浓度为0.1mol/L；
4） 将步骤2）中得到的钛的羟基氧化物沉淀、步骤3）中得到的硝酸铅水溶液和质量分数为98%的四甲基氢氧化铵晶体一起加入到反应釜内胆中，并用去离子水调节物料体积为反应釜容积的4/5，搅拌1小时。其中钛的摩尔浓度为1mol/L，铅和钛的摩尔比为0.5，四甲基氢氧化铵的摩尔浓度为0.15mol/L，摩尔浓度的体积基数为前躯体浆料的总体积；
5） 将装有前驱体浆料的反应釜内胆置于反应釜中，密封，在150℃下保温100个小时进行水热处理，然后让反应釜自然冷却到室温，取出反应物，过滤，依次用去离子水、乙醇清洗，烘干，得到片状结构的钛酸铅粉体。其XRD图谱见图1，扫描电镜照片见图2。
实例2
1） 将钛酸四丁酯溶于10ml乙二醇甲醚中，磁力搅拌溶解，得到Ti4+浓度为0.5mol/L；
2） 搅拌状态下，向步骤1）制得的钛酸四丁酯的乙二醇甲醚溶液中加入质量浓度30%的氨水溶液，加入的氨水溶液体积为钛酸四丁酯的乙二醇甲醚溶液体积的1/5， 沉淀，过滤，洗涤，得到钛的羟基氧化物沉淀；
3） 将硝酸铅溶于去离子水中，形成硝酸铅水溶液，使得Pb2+浓度为0.55mol/L；
4） 将步骤2）中得到的钛的羟基氧化物沉淀、步骤3）中得到的硝酸铅水溶液和质量分数为98%的四甲基氢氧化铵晶体一起加入到反应釜内胆中，并用去离子水调节物料体积为反应釜容积的4/5，搅拌1小时。其中钛的摩尔浓度为1mol/L，铅和钛的摩尔比为1.1，四甲基氢氧化铵的摩尔浓度为0.2mol/L，摩尔浓度的体积基数为前躯体浆料的总体积；
5） 将装有前驱体浆料的反应釜内胆置于反应釜中，密封，在180℃下保温24个小时进行水热处理，然后让反应釜自然冷却到室温，取出反应物，过滤，依次用去离子水、乙醇清洗，烘干，得到片状结构的钛酸铅粉体。
实例3
1） 将钛酸四丁酯溶于10ml乙二醇甲醚中，磁力搅拌溶解，得到Ti4+浓度为2mol/L；
2） 搅拌状态下，向步骤1）制得的钛酸四丁酯的乙二醇甲醚溶液中加入质量浓度30%的氨水溶液，加入的氨水溶液体积为钛酸四丁酯的乙二醇甲醚溶液体积的1/4， 沉淀，过滤，洗涤，得到钛的羟基氧化物沉淀；
3） 将硝酸铅溶于去离子水中，形成硝酸铅水溶液，使得Pb2+浓度为2.5mol/L；
4） 将步骤2）中得到的钛的羟基氧化物沉淀、步骤3）中得到的硝酸铅水溶液和质量分数为98%的四甲基氢氧化铵晶体一起加入到反应釜内胆中，并用去离子水调节物料体积为反应釜容积的4/5，搅拌1小时。其中钛的摩尔浓度为0.05mol/L，铅和钛的摩尔比为5，四甲基氢氧化铵的摩尔浓度为0.25mol/L，摩尔浓度的体积基数为前躯体浆料的总体积；
5） 将装有前驱体浆料的反应釜内胆置于反应釜中，密封，在200℃下保温6个小时进行水热处理，然后让反应釜自然冷却到室温，取出反应物，过滤，依次用去离子水、乙醇清洗，烘干，得到片状结构的钛酸铅粉体。

Claims (3)

1. 一种片状结构钛酸铅的制备方法，其特征在于包括以下步骤：
1） 将钛酸四丁酯溶于乙二醇甲醚，调节溶液中的Ti4+离子浓度为0.1~2mol/L；
2） 搅拌状态下，向步骤1）制得的钛酸四丁酯的乙二醇甲醚溶液中加入质量浓度30%的氨水溶液，氨水溶液体积为钛酸四丁酯的乙二醇甲醚溶液体积的1/4~1/5， 沉淀，过滤，洗涤，得到钛的羟基氧化物沉淀；
3） 将硝酸铅溶于去离子水中，形成硝酸铅水溶液，调节溶液中铅离子的浓度为0.1~2.5mol/L；
4） 将步骤2）中得到的钛的羟基氧化物沉淀、步骤3）中得到的硝酸铅水溶液和质量分数为98%的四甲基氢氧化铵晶体加入到反应釜内胆中，并用去离子水调节物料体积为反应釜容积的1/3~4/5，搅拌1小时，其中钛的摩尔浓度为0.05~1mol/L，铅和钛的摩尔比为0.5~5，四甲基氢氧化铵的摩尔浓度为0.15~0.25mol/L，摩尔浓度的体积基数为前躯体浆料的总体积；
5） 将装有前驱体浆料的反应釜内胆置于反应釜中，密封，在150~200℃下保温6~100小时进行水热处理，然后让反应釜自然冷却到室温，取出反应物，过滤，依次用去离子水、乙醇清洗，烘干，得到片状结构钛酸铅。
2. 根据权利要求1所述的片状结构钛酸铅的制备方法，其特征是所说的反应釜为聚四氟乙烯内胆，不锈钢套件密闭的反应釜。
3. 根据权利要求1所述的片状结构钛酸铅的制备方法，其特征是所说的钛酸四丁酯、硝酸铅、四甲基氢氧化铵的纯度都不低于化学纯。
CN201210143097.2A 2012-05-10 2012-05-10 一种片状结构钛酸铅粉体的制备方法 Expired - Fee Related CN102674446B (zh)