CN102621202B - 丙酮酸-3-吡啶甲酰腙镍(ⅱ)配合物/多壁碳纳米管修饰玻碳电极的制备方法 - Google Patents

丙酮酸-3-吡啶甲酰腙镍(ⅱ)配合物/多壁碳纳米管修饰玻碳电极的制备方法 Download PDF

Info

Publication number
CN102621202B
CN102621202B CN 201210080978 CN201210080978A CN102621202B CN 102621202 B CN102621202 B CN 102621202B CN 201210080978 CN201210080978 CN 201210080978 CN 201210080978 A CN201210080978 A CN 201210080978A CN 102621202 B CN102621202 B CN 102621202B
Authority
CN
China
Prior art keywords
carbon electrode
preparation
glassy carbon
complex
electrode
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201210080978
Other languages
English (en)
Other versions
CN102621202A (zh
Inventor
张小鸽
刘峥
袁帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin University of Technology
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN 201210080978 priority Critical patent/CN102621202B/zh
Publication of CN102621202A publication Critical patent/CN102621202A/zh
Application granted granted Critical
Publication of CN102621202B publication Critical patent/CN102621202B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了丙酮酸-3-吡啶甲酰腙镍(Ⅱ)配合物和多壁碳纳米管修饰玻碳电极的制备方法。(1)把玻碳电极在金相砂纸上抛光至镜面，接着依次置于二次蒸馏水和无水乙醇中超声振荡3分钟，然后于红外干燥箱中干燥；(2)称取43.000～46.000mg丙酮酸-3-吡啶甲酰腙镍(Ⅱ)配合物和0.500～3.500mg多壁碳纳米管(先用质量百分比浓度为98％硝酸加热回流4小时处理)于25mL烧杯中，再用移液管准确量取10.0mL二甲基亚砜加入其中，然后超声振荡6分钟，获得悬浮溶液；(3)用微量取样器抽取10μL步骤(2)所得溶液，滴涂于步骤(1)干燥好的玻碳电极表面，在红外干燥箱中干燥。本发明制作方法简单，制备的电极对
Figure DSA00000690025900011
有较高的电催化氧化活性，可应用于食品中

Description

丙酮酸-3-吡啶甲酰腙镍(Ⅱ)配合物/多壁碳纳米管修饰玻碳电极的制备方法
技术领域
本发明属电化学技术领域，特别涉及丙酮酸-3-吡啶甲酰腙镍(II)配合物/多壁碳纳米管修饰玻碳电极的制备方法。 
背景技术
目前，席夫碱及其配合物种类繁多，结构多样，有许多独特的性能，在分析化学、医药领域、催化领域、腐蚀领域、光致变色等许多方面应用非常广泛。电化学分析法因其操作简便，方便随时随地测量而引起人们广泛关注，其中配合物修饰电极在分析测试方面的应用，因其配合物中过渡金属氧化还原电对可作为小分子及离子(如 
Figure BSA00000690026100011
)和电极之间的电子交换媒介，优势明显。碳纳米管具有的独特的物理化学性质，用作电极材料，能很好地促进电活性物质的电子传递，是一种良好的电子传递媒介。将配合物和多壁碳纳米管制备成一种复合电极材料，利用其协同增效作用，有望获得高灵敏度、高选择性的修饰电极，应用于分析测试领域。亚硝酸盐是致癌物-亚硝酸胺的重要前体，其作为肉类加工中的防腐剂和发色剂已有悠久的历史，可保持肉制品的色、香、味，同时对肉毒梭状芽抱杆菌有抑制作用，具有一定的防腐性，迄今尚未发现理想的替代品。然而在适宜的条件下，亚硝酸盐可与肉中的氨基酸发生反应，也可在人体的胃肠道内和蛋白质的消化物二级胺和四级胺反应，生成致癌的亚硝胺。因此，对 
Figure BSA00000690026100012
的测定方法与技术的研究一直引起广泛的关注，研究新型化学修饰剂的制备、其与多壁碳纳米管的协同作用及相关电极的制作方法至关重要。 
发明内容
本发明的目的是提供一种能分析检测 
Figure BSA00000690026100013
的丙酮酸-3-吡啶甲酰腙镍(II)配合物/多壁碳纳米管修饰玻碳电极的制备方法。 
具体步骤为： 
(1)把玻碳电极在金相砂纸上抛光至镜面，接着依次置于二次蒸馏水和无水乙醇中超声振荡3分钟，然后于红外干燥箱中干燥； 
(2)将多壁碳纳米管用质量百分比浓度为98％的硝酸加热回流4小时； 
(3)称取43.000～46.000mg丙酮酸-3-吡啶甲酰腙镍(II)配合物和步骤(2)所得的多壁碳纳米管0.500～3.500mg于25mL烧杯中，再用移液管准确量取10.0mL二甲基亚砜加入其中，然后超声振荡6分钟，获得悬浮溶液； 
(4)用微量取样器抽取10μL步骤(3)所得悬浮溶液，滴涂于步骤(1)干燥好 的玻碳电极表面，在红外干燥箱中干燥，即制得丙酮酸-3-吡啶甲酰腙镍(II)配合物/碳纳米管修饰玻碳电极。 
本发明制得的丙酮酸-3-吡啶甲酰腙镍(II)配合物/碳纳米管修饰玻碳电极，对 
Figure BSA00000690026100021
有较好的电催化氧化活性。在 
Figure BSA00000690026100022
浓度为4×10-3～1.2×10-2mol/L范围内， 
Figure BSA00000690026100023
的浓度与氧化峰电流成线性关系，这表明可利用这一修饰玻碳电极对 
Figure BSA00000690026100024
作定量分析。 
本发明制备了丙酮酸-3-吡啶甲酰腙镍(II)配合物修饰剂，用循环伏安法测定表明丙酮酸-3-吡啶甲酰腙镍(II)配合物对 
Figure BSA00000690026100025
的电催化氧化活性较高，是一种理想的电活性物质。 
本发明制作方法简单，制备的修饰电极对 有较高的电催化氧化活性，可应用于食品样品中 
Figure BSA00000690026100027
的分析测定。 
具体实施方式
实施例： 
(1)把玻碳电极在金相砂纸上抛光至镜面，接着依次置于二次蒸馏水和无水乙醇中超声振荡3分钟，然后于红外干燥箱中干燥； 
(2)称取45.000mg丙酮酸-3-吡啶甲酰腙镍(II)配合物和1.000mg多壁碳纳米管(先用质量百分比浓度为98％的硝酸加热回流4小时处理)于25mL烧杯中，再用移液管准确量取10.0mL二甲基亚砜加入其中，然后超声振荡6分钟； 
(3)用微量取样器抽取10μL步骤(2)所得溶液，滴涂于步骤(1)干燥好的玻碳电极表面，在红外干燥箱中干燥，即制得了3-吡啶甲酰腙席夫碱镍(II)配合物/碳纳米管修饰玻碳电极。 
将市售火腿肠制成泥状物，准确称取25.0g于100mL烧杯中，加入20mL热的pH7-8的磷酸盐溶液缓冲溶液，饱和硼砂10mL，搅拌均匀后，移入250mL容量瓶中，加缓冲溶液至220mL左右，以NaOH溶液调节pH＝9，然后将容量瓶放入水浴加热4小时，温度在60-80℃，取出后趁热滴加ZnSO4溶液沉淀蛋白质，使溶液澄清，若不产生沉淀可在滴加几滴NaOH。待蛋白质澄清后，加pH7-8的磷酸盐缓冲溶液稀释至刻度。以吸管吸取上层油脂，最后过滤除去肉渣及蛋白质沉淀，得清澈透明溶液备用。 
将修饰电极活化后，放入所制得的火腿肠澄清液中，用循环伏安法进行扫描1圈，扫描速度0.1V/s，电位-1V-1.6V。由于火腿肠样品中 
Figure BSA00000690026100028
浓度很低，循环伏安图上基本没有出现氧化峰电流值。为了考察修饰电极的实际应用可能性， 做了加标回收实验：用微量取样器准确量取50.0μL4mol/L的 
Figure BSA00000690026100031
标准溶液，加入含50.0mL火腿肠澄清液的烧杯中，采用碳纳米管镍配合物修饰电极进行循环伏安测定，所得氧化峰电流值带入公式：Ip＝1.078e-4+0.0419×C，计算出所测得的 
Figure BSA00000690026100032
浓度，计算回收率和相对偏差，结果见表1。 
表1：回收率的测定 
Figure BSA00000690026100033

Claims (1)

1.一种丙酮酸-3-吡啶甲酰腙镍（Ⅱ）配合物/多壁碳纳米管修饰玻碳电极的制备方法，其特征在于具体步骤为：
(1)把玻碳电极在金相砂纸上抛光至镜面，接着依次置于二次蒸馏水和无水乙醇中超声振荡3分钟，然后于红外干燥箱中干燥;
(2)将多壁碳纳米管用质量百分比浓度为98%的硝酸加热回流4小时;
(3)称取43.000～46.000mg 丙酮酸-3-吡啶甲酰腙镍（Ⅱ）配合物和步骤(2)所得的多壁碳纳米管0.500～3.500mg于25mL烧杯中，再用移液管准确量取10.0mL二甲基亚砜加入其中，然后超声振荡6分钟，获得悬浮溶液;
(4)用微量取样器抽取10μL步骤(3)所得悬浮溶液，滴涂于步骤(1)干燥好的玻碳电极表面，在红外干燥箱中干燥，即制得丙酮酸-3-吡啶甲酰腙镍（Ⅱ）配合物/多壁碳纳米管修饰玻碳电极。
CN 201210080978 2012-03-22 2012-03-22 丙酮酸-3-吡啶甲酰腙镍(ⅱ)配合物/多壁碳纳米管修饰玻碳电极的制备方法 Expired - Fee Related CN102621202B (zh)