CN102605529A - 高仿真小羊皮及其制造工艺 - Google Patents

高仿真小羊皮及其制造工艺 Download PDF

Info

Publication number
CN102605529A
CN102605529A CN2012100792887A CN201210079288A CN102605529A CN 102605529 A CN102605529 A CN 102605529A CN 2012100792887 A CN2012100792887 A CN 2012100792887A CN 201210079288 A CN201210079288 A CN 201210079288A CN 102605529 A CN102605529 A CN 102605529A
Authority
CN
China
Prior art keywords
carry out
high emulation
manufacturing technique
impregnation
cape skin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100792887A
Other languages
English (en)
Other versions
CN102605529B (zh
Inventor
钱国春
庞天恩
赵映科
沈水琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Meisheng New Materials Co ltd
Original Assignee
ZHEJIANG MEISHENG INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHEJIANG MEISHENG INDUSTRY Co Ltd filed Critical ZHEJIANG MEISHENG INDUSTRY Co Ltd
Priority to CN 201210079288 priority Critical patent/CN102605529B/zh
Publication of CN102605529A publication Critical patent/CN102605529A/zh
Application granted granted Critical
Publication of CN102605529B publication Critical patent/CN102605529B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高仿真小羊皮及其制造工艺，属于纺织面料技术领域，由涤纶收缩丝和海岛长丝复合而成的复合丝为原料，并通过以下步骤制得：（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色；（12）烘干；（13）检验、成品。本发明高仿真小羊皮，手感与羊皮十分相似，回弹力性能好，垂感好，挺括，防尘，拒水，抗皱性强，透气性好，手感丰满、柔软，容易清洗干净。

Description

高仿真小羊皮及其制造工艺
技术领域
本发明涉及一种高仿真小羊皮及其制造工艺，属于纺织面料技术领域。
背景技术
羊皮由于具有轻、薄、手感柔软等性能，是皮革服装的理想面料，制成的服装光泽柔和自然，轻薄柔软，富有弹性。但羊皮生产过程中的环境污染很严重，一直不能很好的得到解决。其中，最大的污染就是废水，羊皮剥下来以后要进行清洗，而清洗羊皮要用大量的酸、碱等化学品。
发明内容
为解决上述问题，本发明提供一种高仿真小羊皮及其制造工艺。
为实现上述目的，本发明所采用的技术方案为：
一种高仿真小羊皮，由涤纶收缩丝和海岛长丝复合而成的复合丝为原料。
作为上述方案的进一步设置，所述涤纶收缩丝的规格为75D、130 D、160D中的任意一种。
所述海岛长丝的规格为105D、130D中的任意一种。
一种高仿真小羊皮的制造工艺，包括以下步骤：
（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色（同普通麂皮绒的染色工艺相同）；（12）烘干；（13）检验、成品。
所述步骤（1）中，经28~36针/英寸的大圆机织造得到坯布。
所述步骤（2），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为5~10%，并在100±5℃的温度条件下进行，用时140~180min，浴比1:15，以实现20~25%的减量目的。
所述步骤（3）的烘干温度为120~150℃，车速为8~15m/min；所述步骤（10）的烘干温度为120~150℃，车速为8~15m/min；所述步骤（12）的烘干温度为120~150℃，车速为8~15m/min。
所述步骤（5），含浸后PU树脂所占的重量百分比为8~15%，且含浸时间为1~2分钟。PU树脂的模量可以为30、60、100中的任意一种，同时含浸时在PU树脂内添加适量的助剂DMF（二甲基甲酰胺），且添加量为常规情况下PU树脂与DMF之间的配制量。
所述步骤（6），放入常温的水中进行15分钟的水凝固。
所述步骤（8），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为3~5%，并在100±5℃的温度条件下进行，用时160~180min，浴比1:15，以实现15%的减量目的。两次的碱减量开纤，可以进一步提高透气性。
本发明高仿真小羊皮，手感与羊皮十分相似，回弹力性能好，垂感好，挺括，防尘，拒水，抗皱性强，透气性好，手感丰满、柔软，容易清洗干净。同时，本发明高仿真小羊皮的制造工艺，用水量少，尤其体现在染色工序上（相对传统的印染布）。
本发明高仿真小羊皮，主要应用于服装、箱包、手套、靴子等方面。
本发明高仿真小羊皮的具体性能参数如下：门幅140~160cm,克重250~350g/㎡，横向伸长率130%，横向断裂强力350N。
 
具体实施方式
下面通过具体实施例对本发明作进一步说明，但本发明并不受以下实施例所限定。
实施例1
一种高仿真小羊皮，由涤纶收缩丝和海岛长丝复合而成的复合丝为原料。
其中，涤纶收缩丝的规格为75D，海岛长丝的规格为130D。
本发明高仿真小羊皮的制造工艺，包括以下步骤：
（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色；（12）烘干；（13）检验、成品。
步骤（1）中，在28英寸大圆机上织成坯布。
步骤（2），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为5%，并在100℃的温度条件下进行，用时160min，浴比1:15。
步骤（3）的烘干温度为140℃，车速为11m/min；所述步骤（10）的烘干温度为140℃，车速为11m/min；所述步骤（12）的烘干温度为140℃，车速为11m/min。
步骤（5），含浸后PU树脂所占的重量百分比为12%，且含浸时间为1.5分钟。
步骤（6），放入常温的水中进行15分钟的水凝固。
步骤（8），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为4%，并在100℃的温度条件下进行，用时170min，浴比1:15。
 
实施例2
一种高仿真小羊皮，由涤纶收缩丝和海岛长丝复合而成的复合丝为原料。
其中，涤纶收缩丝的规格为130D，海岛长丝的规格为105D。
本发明高仿真小羊皮的制造工艺，包括以下步骤：
（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色；（12）烘干；（13）检验、成品。
步骤（1）中，在32英寸大圆机上织成坯布。
步骤（2），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为10%，并在95℃的温度条件下进行，用时180min，浴比1:15。
步骤（3）的烘干温度为120℃，车速为8m/min；所述步骤（10）的烘干温度为120℃，车速为8m/min；所述步骤（12）的烘干温度为120℃，车速为8m/min。
步骤（5），含浸后PU树脂所占的重量百分比为15%，且含浸时间为1分钟。
步骤（6），放入常温的水中进行15分钟的水凝固。
步骤（8），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为5%，并在95℃的温度条件下进行，用时180min，浴比1:15。
 
实施例3
一种高仿真小羊皮，由涤纶收缩丝和海岛长丝复合而成的复合丝为原料。
其中，涤纶收缩丝的规格为160D，海岛长丝的规格为105D。
本发明高仿真小羊皮的制造工艺，包括以下步骤：
（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色；（12）烘干；（13）检验、成品。
步骤（1）中，在36英寸大圆机上织成坯布。
步骤（2），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为8%，并在105℃的温度条件下进行，用时140min，浴比1:15。
步骤（3）的烘干温度为150℃，车速为15m/min；所述步骤（10）的烘干温度为150℃，车速为15m/min；所述步骤（12）的烘干温度为150℃，车速为15m/min。
步骤（5），含浸后PU树脂所占的重量百分比为8%，且含浸时间为2分钟。
步骤（6），放入常温的水中进行15分钟的水凝固。
步骤（8），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为3%，并在105℃的温度条件下进行，用时160min，浴比1:15。
 
上述实施例仅用于解释说明本发明的发明构思，而非对本发明权利保护的限定，凡利用此构思对本发明进行非实质性的改动，均应落入本发明的保护范围。

Claims (10)

1.一种高仿真小羊皮，其特征在于：由涤纶收缩丝和海岛长丝复合而成的复合丝为原料。
2.如权利要求1所述的高仿真小羊皮，其特征在于：所述涤纶收缩丝的规格为75D、130D、160D中的任意一种。
3.如权利要求1所述的高仿真小羊皮，其特征在于：所述海岛长丝的规格为105D、130D中的任意一种。
4.一种如权利要求1所述高仿真小羊皮的制造工艺，其特征在于包括以下步骤：
（1）以复合丝为原料，针织得到坯布；（2）进行第一次碱减量开纤；（3）烘干；（4）进行双面磨毛；（5）含浸：选用PU树脂进行含浸；（6）水凝固；（7）水洗；（8）进行第二次碱减量开纤；（9）水洗；（10）烘干；（11）染色；（12）烘干；（13）检验、成品。
5.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（1）中，经28~36针/英寸的大圆机织造得到坯布。
6.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（2），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为5~10%，并在100±5℃的温度条件下进行，用时140~180min，浴比1:15。
7.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（3）的烘干温度为120~150℃，车速为8~15m/min；所述步骤（10）的烘干温度为120~150℃，车速为8~15m/min；所述步骤（12）的烘干温度为120~150℃，车速为8~15m/min。
8.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（5），含浸后PU树脂所占的重量百分比为8~15%，且含浸时间为1~2分钟。
9.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（6），放入常温的水中进行15分钟的水凝固。
10.如权利要求4所述高仿真小羊皮的制造工艺，其特征在于：所述步骤（8），选用NaOH溶液进行碱减量开纤，且NaOH溶液的浓度为3~5%，并在100±5℃的温度条件下进行，用时160~180min，浴比1:15。
CN 201210079288 2012-03-23 2012-03-23 高仿真小羊皮及其制造工艺 Active CN102605529B (zh)