CN102585665A - 一种耐甲醇汽油导静电防腐涂料 - Google Patents

一种耐甲醇汽油导静电防腐涂料 Download PDF

Info

Publication number
CN102585665A
CN102585665A CN2012100418047A CN201210041804A CN102585665A CN 102585665 A CN102585665 A CN 102585665A CN 2012100418047 A CN2012100418047 A CN 2012100418047A CN 201210041804 A CN201210041804 A CN 201210041804A CN 102585665 A CN102585665 A CN 102585665A
Authority
CN
China
Prior art keywords
component
parts
epoxy resin
gasoline
methanol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012100418047A
Other languages
English (en)
Other versions
CN102585665B (zh
Inventor
金晓岚
刘再康
李继凯
高晓静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHIJIAZHUANG KINGDAR SPECIAL COATING CO Ltd
Original Assignee
SHIJIAZHUANG KINGDAR SPECIAL COATING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHIJIAZHUANG KINGDAR SPECIAL COATING CO Ltd filed Critical SHIJIAZHUANG KINGDAR SPECIAL COATING CO Ltd
Priority to CN201210041804.7A priority Critical patent/CN102585665B/zh
Publication of CN102585665A publication Critical patent/CN102585665A/zh
Application granted granted Critical
Publication of CN102585665B publication Critical patent/CN102585665B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种耐甲醇汽油导静电防腐涂料，由以下原料按重量份数组成：A组分：环氧树脂 25~39；颜填料5~20；导静电填料15~28；碳纳米管0.2~2；肉桂醛0.3~1；助剂 2~6；稀释剂5~16；B组分：改性芳脂胺固化剂7~11。本发明中，环氧树脂由环氧酚醛树脂和双酚F型环氧树脂按重量比3:1~3的比例组成，改性芳脂胺固化剂为D9050、D9340中的一种或两种的混合物。本发明先分别制得A组分、B组分。使用时将B组分缓慢加入到A组分中搅拌均匀即可得最终产品。本发明所制得的防腐涂料可耐强溶剂渗透腐蚀，长期储存甲醇汽油不会有游离颗粒析出，从而保证成品油品质不会因储存而受到影响。

Description

一种耐甲醇汽油导静电防腐涂料
技术领域
本发明涉及一种涂料，具体地说是一种耐甲醇汽油导静电防腐涂料。
背景技术
车用甲醇汽油国家标准的发布，为甲醇汽油的大规模推广应用创造了良好条件。但甲醇汽油在储藏和运输过程中因水分的存在而激活金属的酸腐蚀和电化学腐蚀问题，目前单独用于汽油储罐或单独用于甲醇储罐的内防腐涂料无法满足甲醇汽油储罐的防腐要求。因此，早日提供既能耐甲醇的强溶胀、又能耐汽油腐蚀，同时保证油品不受涂料的二次污染的导静电涂料，从而满足甲醇汽油生产、储藏和运输过程中的腐蚀控制要求，成为全新的亟待解决的重要课题。
发明内容
本发明旨在提供一种涂层致密、耐甲醇溶胀、耐油品腐蚀且能导静电的耐甲醇汽油导静电防腐涂料。
本发明的耐甲醇汽油导静电防腐涂料，由以下原料按重量份数组成：
A组分
Figure BDA0000137692870000011
B组分
改性芳脂胺固化剂      7～11
本发明中，环氧树脂由环氧酚醛树脂和双酚F型环氧树脂按重量比3∶1～3的比例组成，改性芳脂胺固化剂为D9050、D9340中的一种或两种的混合物。
本发明中，A组分中的环氧树脂选择环氧酚醛树脂和双酚F型环氧树脂按3∶1～3比例组成，本设计既可保证固化后的高分子网络结构交联密度大，结构致密，又可避免漆膜较脆的问题发生。而且，该A组分与所选择的B组分混合后，发热量不高，形成的涂膜内应力小，因而空间结构稳定。本发明中，肉桂醛可在涂膜与钢质储罐基材接触时形成一层薄膜，为防止甲醇汽油对基材的腐蚀增加一层防线。综上，本发明所制得的防腐涂料可耐强溶剂渗透腐蚀。
本发明的导静电填料、颜填料、助剂和稀释剂均可按现有技术中常规的用料和用量。导静电填料由导电云母粉、导电氧化锌中一种或两种的混合。颜填料选择钛白粉、铁红粉、磷酸锌、氧化锌、三聚磷酸铝、云母粉、高岭土中的一种或几种的混合。助剂为防沉剂、分散剂、消泡剂及流平剂的混合。其中防沉剂为聚乙烯蜡、聚酰胺蜡、气相二氧化硅中的一种。分散剂为BYK-104S、BYK-104、Borchi Gen 0755、AFCONA-5210中的一种。消泡剂为氟改性有机硅类消泡聚合物、二甲基硅油中的一种或几种的混合。流平剂为BYK-306、DIGO-1484中的一种。稀释剂为二甲苯、正丁醇、环己酮中的一种或几种混合物。
本发明在添加导静电填料方面不仅有常用的导电云母粉和导电氧化锌，还添加有小比例的碳纳米管。碳纳米管的导静电性能较好且稳定，但价格昂贵；导电云母粉和导电氧化锌价格适宜，但添加量较大，影响涂料其他防腐功能填料的添加量。为得到导静电、防腐蚀性能兼备，同时价格适宜的导静电填料，采用混合添加并严格控制比例的方式实现。
本发明中，碳纳米管为TimesfillerTM CF-0、TimesfillerTM CF-1、TimesfillerTM CF-2中的一种。
本发明的耐甲醇汽油导静电防腐涂料的制备方法简单，具体步骤是：先按比例称量各种原料待用。将经大约1/2混合稀释剂量稀释的混合环氧树脂搅拌均匀，加入配方量的颜填料和分散助剂搅拌均匀后上砂磨机研磨至细度为30μm，再加入其他助剂和导静电填料，并补足剩余稀释剂搅拌均匀，制得A组分。B组分由D9050和D9340按配方量混合均匀得到。使用时将B组分缓慢加入到A组分中搅拌均匀即可得最终产品。
具体实施方式
所有实施例所用的原材料均为市售产品。环氧酚醛树脂型号为DEN431，双酚F环氧树脂型号为YDF-170，改性芳脂胺固化剂D9340、D9050、D 6150、D6250购自上海君江公司。Ancamine2143为美国空气产品公司产改性脂环族胺固化剂。
实施例1：
按比例称量下列原料：
A组分
Figure BDA0000137692870000021
Figure BDA0000137692870000031
B组分
固化剂D9050                  5.5kg
固化剂D9340                  5.5kg
取配方量一半的正丁醇加入到双酚F环氧树脂和环氧酚醛树脂的混合液中，搅拌均匀。加入配方量的分散剂、消泡剂及流平剂后，再加入配方量的颜填料钛白粉、磷酸锌混合好后，上砂磨机研磨至细度30μm，细度合格后加入防沉剂聚酰胺蜡，缓慢投入配方量的导静电填料。最后加入剩余的正丁醇，搅拌均匀制得A组分。B组分由D9050和D9340按配方量混合均匀得到。使用时将B组分缓慢加入到A组分中搅拌均匀即可得最终产品。
实施例2：
按比例称量下列原料：
A组分
B组分
固化剂D9050                11kg
制备方法与实施例1相同。
实施例3：
按比例称量下列原料：
A组分
Figure BDA0000137692870000033
Figure BDA0000137692870000041
B组分
固化剂D9050                 5.5kg
固化剂D9340                 3.5kg
制备方法与实施例1相同。
实施例4：
按比例称量下列原料：
A组分
Figure BDA0000137692870000042
B组分
固化剂D9340                 11.0kg
制备方法与实施例1相同。
实施例5：
按比例称量下列原料：
A组分
Figure BDA0000137692870000043
Figure BDA0000137692870000051
B组分
固化剂D9340                    7.0kg
制备方法与实施例1相同。
实施例6：
按比例称量下列原料：
A组分
Figure BDA0000137692870000052
B组分
固化剂D9050                    7.0kg
制备方法与实施例1相同。
对比实施例1
按比例称量下列原料：
A组分
Figure BDA0000137692870000053
Figure BDA0000137692870000061
B组分
固化剂D9050                    7kg
制备方法与实施例1相同。
对比实施例2
按比例称量下列原料：
A组分
Figure BDA0000137692870000062
B组分
固化剂D9050                    7kg
制备方法与实施例1相同。
对比实施例3
按比例称量下列原料：
A组分
Figure BDA0000137692870000063
Figure BDA0000137692870000071
B组分
固化剂D6150               7.0kg
制备方法与实施例1相同。
对比实施例4
按比例称量下列原料：
A组分
Figure BDA0000137692870000072
B组分
固化剂D6250                11.0kg
制备方法与实施例1相同。
对比实施例5
按比例称量下列原料：
A组分
Figure BDA0000137692870000073
Figure BDA0000137692870000081
B组分
Ancamine2143                  10.0kg
制备方法与实施例1相同。
实施例1-6及对比实施例1-5的检测指标如下：
本发明所制最终产品，具有良好的导静电性能，涂膜的表面电阻率在108～1011Ω，符合国家标准要求，且导静电性能稳定。在防腐蚀性方面有优异的耐盐雾性、耐酸、耐碱、耐盐、耐水、耐汽油、耐M15和M85甲醇汽油性；长期储存甲醇汽油不会有游离颗粒析出，可有效防止油品受到二次污染，从而保证成品油品质不会因储存而受到影响。

Claims (2)

1.一种耐甲醇汽油导静电防腐涂料，其特征在于由以下原料按重量比组成：
A组分
环氧树脂             25~39
颜填料               5~20
导静电填料           15~28
碳纳米管             0.2~2
肉桂醛      　　　　 0.3~1
助剂                 2~ 6
稀释剂               5~16
B组分
改性芳脂胺固化剂     7~11
其中，环氧树脂由环氧酚醛树脂和双酚F型环氧树脂按重量比3:1~3的比例组成；改性芳脂胺固化剂为D9050、D9340中的一种或两种的混合物。
2.权利要求1所述的耐甲醇汽油导静电防腐涂料，其特征在于由以下原料按重量比组成：
A组分
环氧树脂             30~35
颜填料               13~20
导静电填料           20~25
碳纳米管             0.2~2
肉桂醛      　　　 　0.4~0.8
助剂                 2~ 6
稀释剂               5~16
B组分
改性芳脂胺固化剂     7~11。
CN201210041804.7A 2012-02-23 2012-02-23 一种耐甲醇汽油导静电防腐涂料 Expired - Fee Related CN102585665B (zh)