CN102532783B - 一种流动性良好的abs/pbt合金材料及其制备方法 - Google Patents
一种流动性良好的abs/pbt合金材料及其制备方法 Download PDFInfo
- Publication number
- CN102532783B CN102532783B CN201010596755.4A CN201010596755A CN102532783B CN 102532783 B CN102532783 B CN 102532783B CN 201010596755 A CN201010596755 A CN 201010596755A CN 102532783 B CN102532783 B CN 102532783B
- Authority
- CN
- China
- Prior art keywords
- abs
- pbt
- alloy material
- styrene
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种流动性良好的ABS/PBT合金材料及其制备方法,包括以下组分和重量份数:ABS类树脂200-600,PBT树脂100-400,相容剂10-100,增韧剂10-200,光热稳定剂1-10,加工助剂1-10。本发明的流动性良好的ABS/PBT合金材料,采用双螺杆挤出工艺制备,具有流程简单、连续、生产效率高、产品质量稳定的优点。同时材料具有冲击强度高、外观良好、流动性高、耐化学性好、加工成型好等特点,可用于注塑成型各种汽车零部件、保险杠骨架、家用电器外壳、打印机和复印机等办公用品外壳。
Description
技术领域
本发明涉及一种ABS/PBT合金材料,尤其涉及一种流动性良好的ABS/PBT合金材料及其制备方法。
背景技术
ABS是一种性能优良的热塑性树脂,有着优良的物理力学性能、表面硬度、较高的强度,且有一定的耐热性,但其缺点是耐侯性差,且易受有机溶剂腐蚀,所以要在ABS中加入各种改性剂改善其性能。聚对苯二甲酸丁二醇酯(PBT)是一类结晶型聚酯,有优良的综合性能,如机械强度高、耐疲劳性和尺寸稳定性好,蠕变也小,具有优良的耐有机溶剂和耐化学药品性,且有优异的自润滑性能和成型加工性能,成型周期短。ABS/PBT合金在找到合适的相容剂与增韧剂之后可获得良好的冲击性能,但往往流动性会受到一定的影响,这样会影响材料的加工过程,如果可以在保持材料良好的力学性能的同时,增大体系的流动性,将会更加利于加工。
发明内容
本发明就是为了解决上述现有技术存在的问题而提供一种流动性良好的ABS/PBT合金材料及其制备方法。
本发明的目的通过以下技术方案来实现:
一种流动性良好的ABS/PBT合金材料,包括以下组分和重量份数:
ABS类树脂 200-600,
PBT树脂 100-400,
相容剂 10-100,
增韧剂 10-200,
光热稳定剂 1-10,
加工助剂 1-10。
所述ABS类树脂选自丙烯腈-丁二烯-苯乙烯三元接枝共聚物、丙烯腈-苯乙烯二元共聚物、丙烯腈-乙烯丙烯弹性体-苯乙烯接枝共聚物、丙烯腈-苯乙烯-丙烯酸三元共聚物、苯乙烯-丁二烯-苯乙烯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯接枝共聚物或氢化的苯乙烯-丁二烯-苯乙烯共聚物中的一种或几种,其胶含量为20%-70%。
所述PBT树脂为聚对苯二甲酸丁二醇酯,相对密度为1.25-1.35g/cm3,熔点为220-225℃。
所述相容剂为ABS-g-MAH、丙烯腈-苯乙烯-马来酸酐共聚物、SEBS-g-MAH、AS-g-GMA、ABS-g-GMA、丙烯酸酯类中的一种或几种。
所述增韧剂为MBS、ACR、SBS及硅橡胶类中的一种或几种。
所述光热稳定剂为烷基化单酚、烷基化多酚、亚磷酸二苯酯、亚磷酸三苯酯、碱金属或碱土金属的硅酸盐、位阻酚或羟基苯并三唑中的一种或几种。
所述加工助剂为润滑剂,具体选自固体石蜡、液体石蜡、低分子量聚乙烯、硬脂酸钙、硬脂酸锌、硬脂酸酰胺、甲撑双硬脂酸酰胺和N,N-乙撑双硬脂酸酰胺EBS中的一种或几种。
一种流动性良好的ABS/PBT合金材料的制备方法,包括如下步骤:
将ABS类树脂、PBT树脂、相容剂、增韧剂、光热稳定剂和加工助剂按配比称重,混合均匀后送入双螺杆挤出机中,经混炼、挤出、拉条、冷却、切粒后获得成品;双螺杆挤出机各段螺杆温度为210-250℃之间,螺杆转速为100-500转/分钟之间。
与现有技术相比,本发明具有以下有益效果:
本发明提供了一种流动性良好的ABS/PBT合金材料,采用双螺杆挤出工艺制备,具有流程简单、连续、生产效率高、产品质量稳定的优点。同时材料具有冲击强度高、外观良好、流动性高、耐化学性好、加工成型好等特点,可用于注塑成型各种汽车零部件、保险杠骨架、家用电器外壳、打印机和复印机等办公用品外壳。
具体实施方式
下面结合各实施例详细描述本发明。
实施例1-3中组分及配比(重量份数)如表1所示。将ABS类树脂、PBT树脂、相容剂、增韧剂、光热稳定剂及加工助剂按配比称量,经高速搅拌机混合均匀后将上述混合物送入挤出机中,在螺杆的输送和剪切作用下,充分熔合、混炼,再经机头挤出、拉条、冷却、切粒后进行包装;双螺杆挤出机各段螺杆温度控制在210-240℃之间,螺杆转速为400转/分钟。
其中,ABS树脂为大庆石化的的750,其为丙烯腈-丁二烯-苯乙烯接枝共聚物;PBT树脂为德国巴斯夫的B4500,其为聚对苯二甲酸丁二酯;相容剂为杰事杰新材料有限公司的ABS-G,为ABS-g-MAH共聚物;增韧剂为罗门哈斯的MBS类核壳结构增韧剂;光热稳定剂为CIBA的β-(3,5-二叔丁基-4-羟基苯基)丙酸正十八碳醇酯Irganox1076和三(2,4-二叔丁基苯基)亚磷酸酯Irganox168;加工助剂为国产乙撑双硬脂酰胺EBS。
将实施例1-3制备得到的复合物注塑成测试用的标准样条,按照ASTM标准和美国UL标准进行性能测试,结果如表2所示。
表1
表2
实施例4
一种流动性良好的ABS/PBT合金材料的制备方法,包括如下步骤:
将ABS类树脂丙烯腈-苯乙烯二元共聚物300重量份、丙烯腈-乙烯丙烯弹性体-苯乙烯接枝共聚物300重量份、PBT400重量份、相容剂丙烯腈-苯乙烯-马来酸酐共聚物10重量份、增韧剂ACR 10重量份、光热稳定剂亚磷酸三苯酯1重量份和加工助剂液体石蜡1重量份按配比称重,混合均匀后送入双螺杆挤出机中,经混炼、挤出、拉条、冷却、切粒后获得成品;双螺杆挤出机各段螺杆温度为210-230℃之间,螺杆转速为100转/分钟。
实施例5
一种流动性良好的ABS/PBT合金材料的制备方法,包括如下步骤:
将ABS类树脂甲基丙烯酸甲酯-丁二烯-苯乙烯接枝共聚物100重量份(胶含量为30%)、苯乙烯-丁二烯-苯乙烯共聚物100重量份(胶含量为50%)、PBT100重量份、相容剂SEBS-g-MAH 100重量份、增韧剂SBS 200重量份、光热稳定剂羟基苯并三唑10重量份和加工助剂低分子量聚乙烯10重量份按配比称重,混合均匀后送入双螺杆挤出机中,经混炼、挤出、拉条、冷却、切粒后获得成品;双螺杆挤出机各段螺杆温度为220-250℃之间,螺杆转速为500转/分钟。
实施例6
一种流动性良好的ABS/PBT合金材料的制备方法,包括如下步骤:
将ABS类树脂丙烯腈-苯乙烯-丙烯酸三元共聚物150重量份(胶含量为20%)、氢化的苯乙烯-丁二烯-苯乙烯共聚物200重量份(胶含量为70%)、PBT300重量份、相容剂AS-g-GMA30重量份、ABS-g-GMA50重量份、增韧剂MBS60重量份、硅橡胶20重量份、光热稳定剂亚磷酸二苯酯2重量份、位阻酚3重量份和加工助剂硬脂酸酰胺4重量份、甲撑双硬脂酸酰胺4重量份按配比称重,混合均匀后送入双螺杆挤出机中,经混炼、挤出、拉条、冷却、切粒后获得成品;双螺杆挤出机各段螺杆温度为225-235℃之间,螺杆转速为300转/分钟。
以上公开的仅为本申请的几个具体实施例,但本申请并非局限于此,任何本领域的技术人员能思之的变化,都应落在本申请的保护范围内。
Claims (5)
1.一种流动性良好的ABS/PBT合金材料,其特征在于,包括以下组分和重量份数:
所述增韧剂为MBS;
所述加工助剂为EBS;
所述相容剂为ABS-G。
2.如权利要求1所述的一种流动性良好的ABS/PBT合金材料,其特征在于,所述ABS类树脂选自丙烯腈-丁二烯-苯乙烯三元接枝共聚物、丙烯腈-苯乙烯二元共聚物、丙烯腈-乙烯丙烯弹性体-苯乙烯接枝共聚物、丙烯腈-苯乙烯-丙烯酸三元共聚物、苯乙烯-丁二烯-苯乙烯共聚物、甲基丙烯酸甲酯-丁二烯-苯乙烯接枝共聚物或氢化的苯乙烯-丁二烯-苯乙烯共聚物中的一种或几种,其胶含量为20%-70%。
3.如权利要求1所述的一种流动性良好的ABS/PBT合金材料,其特征在于,所述PBT树脂为聚对苯二甲酸丁二醇酯,相对密度为1.25-1.35g/cm3,熔点为220-225℃。
4.如权利要求1所述的一种流动性良好的ABS/PBT合金材料,其特征在于,所述光热稳定剂为烷基化单酚、烷基化多酚、亚磷酸二苯酯、亚磷酸三苯酯、碱金属或碱土金属的硅酸盐、位阻酚或羟基苯并三唑中的一种或几种。
5.一种如权利要求1所述的流动性良好的ABS/PBT合金材料的制备方法,其特征在于,包括如下步骤:
将ABS类树脂、PBT树脂、相容剂、增韧剂、光热稳定剂和加工助剂按配比称重,混合均匀后送入双螺杆挤出机中,经混炼、挤出、拉条、冷却、切粒后获得成品;双螺杆挤出机各段螺杆温度为210-250℃之间,螺杆转速为100-500转/分钟之间。