CN102505404A - Trimming process of double-mercerized cotton knitted silk-like fabric - Google Patents
Trimming process of double-mercerized cotton knitted silk-like fabric Download PDFInfo
- Publication number
- CN102505404A CN102505404A CN2011102799180A CN201110279918A CN102505404A CN 102505404 A CN102505404 A CN 102505404A CN 2011102799180 A CN2011102799180 A CN 2011102799180A CN 201110279918 A CN201110279918 A CN 201110279918A CN 102505404 A CN102505404 A CN 102505404A
- Authority
- CN
- China
- Prior art keywords
- adopt
- fabric
- mercerized cotton
- equipment adopts
- temperature conditions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a trimming process of a double-mercerized cotton knitted silk-like fabric. The mercerized cotton knitted fabric is processed with the following procedures: a, gray fabric singeing; b, gray fabric mercerizing; c, scouring and bleaching; d, processing through bio-enzyme; e, pre-softening; and f, trimming the mercerized cotton. Through the process, the mercerized cotton knitted fabric with silk-like effect can be obtained. The fabric trimmed through the technique disclosed by the invention is of ultra-smooth and stiff hand sense, good drapability, excellent rebound resilience and particularly the lustrousness and tactility of real silk.
Description
Technical field:
The present invention relates to a kind of textile finishing technology, be specifically related to the imitative silk finishing technique of a kind of pair of mercerized cotton knitted cloth.
Background technology:
The cotton fiber goods enjoy liking of consumption because of its softness next to the shin, good hygroscopicity and the advantages such as theory of people's back to nature always.Along with the continuous ripe development of textile dyeing and finishing process technology in recent years, exploitation has more the cotton fiber new product trend of the times of high added value.The imitative silk fabric of two mercerized cottons is the expensive goods of under this theory thought, developing.
The utility model content:
The object of the invention provides the imitative silk finishing technique of a kind of pair of mercerized cotton knitted cloth; Singeing, mariages light technology, biology enzyme treatment process and postfinishing process are organically combined; Make smooth, well-pressed as arrangement back lining feel such as the pearl, drapability is good and resilience is excellent; Particularly it has silkiness glossiness and sense of touch, further improves the product specification and the added value of mariages light cotton products.
In order to achieve the above object, the present invention adopts following technical scheme:
A kind of pair of imitative silk finishing technique of mercerized cotton knitted cloth is characterized in that:
A, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame, and it is one positive one anti-that burner adopts, and thermal source is natural gas or gasification gasoline, 1100 ℃～1200 ℃ of burner temperature, and the speed of a motor vehicle 75～95m/min, the quality control of singing is more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240～280g/L, and silkete penetrating agent DM-1205G 3～5g/L, 18 ℃～22 ℃ of alkali liquid temperatures soak caustic lye of soda time 40～45s, adopt the glacial acetic acid neutralization behind the mercerising;
C, boil and float: equipment adopts the high temperature overflow machine, boils floating prescription and be: high-efficiency refining agent DM-1364 0.3～0.5g/L, NaOH 1～2g/L, 30%H
2O
24～6g/L; Bath raio is 1: 8～10, under 98 ℃ temperature conditions, boils and floats 45～50min;
D, biology enzyme are handled: equipment adopts the high temperature overflow machine; Acidic cellulase DM-8627 1.0%～1.5% (owf); Adopt glacial acetic acid regulator solution pH=4～5, the temperature conditions that bath raio is 1: 10～15,45 ℃～60 ℃ is handled 60～70min down; Carry out enzyme-deactivating then, adopt 85 ℃ of hot water treatment 10min to get final product;
E, soft in advance: equipment adopts the high temperature overflow machine; Elder generation is cleaned once with 60 ℃～80 ℃ hot water; Add hydrophilically modified silicone softening agent R 1.0%～2.5% (owf) then and 98% glacial acetic acid, 0.3～0.4ml/L carries out preliminary treatment; bath raio 1: 10～15, under 45 ℃～55 ℃ temperature conditions, handle 30～45min;
Put in order after f, the mercerized cotton:
Adopt the high-temperature shaping machine, adopt and pad technology, the dressing liquid prescription is:
The ultra finishing agent DM-3541 50g/L that plays
Catalyst DM-3542 5g/L
Flexible silicon breast SILYOUSOFT T8056 100g/L
One soaks one rolls, oven dry under 100 ℃ of temperature conditions, and typing 20～40s gets final product under 160 ℃ of temperature conditions then.
The beneficial effect of technology of the present invention is:
This technology with mariages light technology, biology enzyme treatment process and organosilicon after the soft technology of arrangement organically combine, to obtain a kind of fabric style of uniqueness.Fabric lines behind mariages light technology and biology enzyme treatment process is clear, any surface finish, drapability is good and produce gloss as the lasting and similar real silk, but smooth degree and resilience still are short of; Postfinishing process employing reactive amino silicon breast and soluble polyurethane combine fabric feeling are further improved.Amino silicon is newborn and polyurethane reaction is active strong, and intermolecular cross-linking film forming after drying and shaping forms network structure, and the fibre-fibre friction resistance significantly reduces, resilience improves, thereby super along sense of touch and silkiness gloss sliding, close skin as the acquisition pearl.
The specific embodiment:
Embodiment: a kind of pair of imitative silk finishing technique of mercerized cotton knitted cloth; A, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame; It is one positive one anti-that burner adopts, and thermal source is natural gas or gasification gasoline, 1100 ℃～1200 ℃ of burner temperature; The speed of a motor vehicle 75～95m/min, the quality control of singing is more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240～280g/L, and silkete penetrating agent DM-1205G 3～5g/L, 18 ℃～22 ℃ of alkali liquid temperatures soak caustic lye of soda time 40～45s, adopt the glacial acetic acid neutralization behind the mercerising;
C, boil and float: equipment adopts the high temperature overflow machine, boils floating prescription and be: high-efficiency refining agent DM-1364 0.3～0.5g/L, NaOH 1～2g/L, 30%H
2O
24～6g/L; Bath raio is 1: 8～10, under 98 ℃ temperature conditions, boils and floats 45～50min;
D, biology enzyme are handled: equipment adopts the high temperature overflow machine; Acidic cellulase DM-8627 1.0%～1.5% (owf); Adopt glacial acetic acid regulator solution pH=4～5, the temperature conditions that bath raio is 1: 10～15,45 ℃～60 ℃ is handled 60～70min down; Carry out enzyme-deactivating then, adopt 85 ℃ of hot water treatment 10min to get final product;
E, soft in advance: equipment adopts the high temperature overflow machine; Elder generation is cleaned once with 60 ℃～80 ℃ hot water; Add hydrophilically modified silicone softening agent R 1.0%～2.5% (owf) then and 98% glacial acetic acid, 0.3～0.4ml/L carries out preliminary treatment; bath raio 1: 10～15, under 45 ℃～55 ℃ temperature conditions, handle 30～45min;
Put in order after f, the mercerized cotton:
Adopt the high-temperature shaping machine, adopt and pad technology, the dressing liquid prescription is:
The ultra finishing agent DM-3541 50g/L that plays
Catalyst DM-3542 5g/L
Flexible silicon breast SILYOUSOFT T8056 100g/L
One soaks one rolls, oven dry under 100 ℃ of temperature conditions, and typing 20～40s gets final product under 160 ℃ of temperature conditions then.
Claims (1)
1. two mercerized cotton knitted cloths are imitated the silk finishing technique, it is characterized in that:
A, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame, and it is one positive one anti-that burner adopts, and thermal source is natural gas or gasification gasoline, 1100 ℃～1200 ℃ of burner temperature, and the speed of a motor vehicle 75～95m/min, the quality control of singing is more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240～280g/L, and silkete penetrating agent DM-1205G 3～5g/L, 18 ℃～22 ℃ of alkali liquid temperatures soak caustic lye of soda time 40～45s, adopt the glacial acetic acid neutralization behind the mercerising;
C, boil and float: equipment adopts the high temperature overflow machine, boils floating prescription and be: high-efficiency refining agent DM-1364 0.3～0.5g/L, NaOH 1～2g/L, 30%H
2O
24～6g/L; Bath raio is 1: 8～10, under 98 ℃ temperature conditions, boils and floats 45～50min;
D, biology enzyme are handled: equipment adopts the high temperature overflow machine; Acidic cellulase DM-8627 1.0%～1.5% (owf); Adopt glacial acetic acid regulator solution pH=4～5, the temperature conditions that bath raio is 1: 10～15,45 ℃～60 ℃ is handled 60～70min down; Carry out enzyme-deactivating then, adopt 85 ℃ of hot water treatment 10min to get final product;
E, soft in advance: equipment adopts the high temperature overflow machine; Elder generation is cleaned once with 60 ℃～80 ℃ hot water; Add hydrophilically modified silicone softening agent R 1.0%～2.5% (owf) then and 98% glacial acetic acid, 0.3～0.4ml/L carries out preliminary treatment; bath raio 1: 10～15, under 45 ℃～55 ℃ temperature conditions, handle 30～45min;
Put in order after f, the mercerized cotton:
Adopt the high-temperature shaping machine, adopt and pad technology, the dressing liquid prescription is:
The ultra finishing agent DM-3541 50g/L that plays
Catalyst DM-3542 5g/L
Flexible silicon breast SILYOUSOFT T8056 100g/L
One soaks one rolls, oven dry under 100 ℃ of temperature conditions, and typing 20～40s gets final product under 160 ℃ of temperature conditions then.