CN102505404B - A kind of trimming process of double-mercerized cotton knitted silk-like fabric - Google Patents
A kind of trimming process of double-mercerized cotton knitted silk-like fabric Download PDFInfo
- Publication number
- CN102505404B CN102505404B CN201110279918.0A CN201110279918A CN102505404B CN 102505404 B CN102505404 B CN 102505404B CN 201110279918 A CN201110279918 A CN 201110279918A CN 102505404 B CN102505404 B CN 102505404B
- Authority
- CN
- China
- Prior art keywords
- mercerized cotton
- temperature
- fabric
- adopt
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of trimming process of double-mercerized cotton knitted silk-like fabric, singes mercerized cotton knitted cloth through a, grey cloth; B, grey cloth mercerising; C, boil drift; D, cellulase treatment; E, in advance softness; F, mercerized cotton Final finishing; The mercerized cotton knitted cloth with silk like fabric effect is obtained above after a few procedure.Adopt this technical matters can make to expect after arrangement feel super smooth well-pressed, drapability good and resilience excellent, particularly it has glossiness as real silk and sense of touch.
Description
Technical field:
The present invention relates to a kind of textile finishing technique, be specifically related to a kind of trimming process of double-mercerized cotton knitted silk-like fabric.
Background technology:
Cotton fiber goods, because of the advantage such as theory of its softness next to the skin, good hygroscopicity and people's back to nature, enjoy liking of consumption always.Along with the continuous ripe of textile dyeing and finishing process technology develops in recent years, exploitation has more the cotton fiber new product trend of the times of high added value.Two mercerized cotton silk like fabric fabric is the expensive goods developed under this theory thought.
Utility model content:
The object of the invention is to provide a kind of trimming process of double-mercerized cotton knitted silk-like fabric, singeing, two mercerization, cellulase treatment technique and postfinishing process are organically combined, make after arrangement, to expect that feel is smooth as pearl, well-pressed, drapability is good and resilience is excellent, particularly it has silkiness glossiness and sense of touch, improves product specification and the added value of mariages light cotton products further.
In order to achieve the above object, the present invention adopts following technical scheme:
A kind of trimming process of double-mercerized cotton knitted silk-like fabric, is characterized in that:
A, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame, and burner adopts a positive and a negative, and thermal source is natural gas or gasification gasoline, burner temperature 1100 DEG C ~ 1200 DEG C, and the speed of a motor vehicle 75 ~ 95m/min, singes quality control more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240 ~ 280g/L, silkete penetrating agent DM-1205G3 ~ 5g/L, alkali liquid temperature 18 DEG C ~ 22 DEG C, leaching caustic lye of soda time 40 ~ 45s, adopts glacial acetic acid to neutralize after mercerising;
C, boil drift: equipment adopts high temperature overflow machine, boiling drift formula is: high-efficiency refining agent DM-13640.3 ~ 0.5g/L, NaOH1 ~ 2g/L, 30%H
2o
24 ~ 6g/L; Bath raio is 1: 8 ~ 10, boils drift 45 ~ 50min under the temperature conditions of 98 DEG C;
D, cellulase treatment: equipment adopts high temperature overflow machine, acidic cellulase DM-86271.0% ~ 1.5% (owf), adopt glacial acetic acid regulator solution pH=4 ~ 5; bath raio 1: 10 ~ 15; process 60 ~ 70min under the temperature conditions of 45 DEG C ~ 60 DEG C; then carry out enzyme-deactivating, adopt 85 DEG C of hot water treatment 10min;
E, in advance softness: equipment adopts high temperature overflow machine, first clean once with the hot water of 60 DEG C ~ 80 DEG C, then add hydrophilically modified silicone softening agent R1.0% ~ 2.5% (owf) and 98% glacial acetic acid 0.3 ~ 0.4ml/L carries out preliminary treatment; bath raio 1: 10 ~ 15, under 45 DEG C ~ 55 DEG C temperature conditions, process 30 ~ 45min;
F, mercerized cotton Final finishing:
Adopt high-temperature forming machine, adopt padding process, dressing liquid formula is:
Superlastic finishing agent DM-354150g/L
Catalyst DM-35425g/L
Flexible silicon breast SILYOUSOFTT8056100g/L
One leaching one is rolled, and dries under 100 DEG C of temperature conditions, and then shape 20 ~ 40s under 160 DEG C of temperature conditions.
The beneficial effect of present invention process is:
Soft to two mercerization, cellulase treatment technique and organosilicon Final finishing technique organically combines, to obtain a kind of fabric style of uniqueness by this technology.Fabric lines after two mercerization and cellulase treatment technique is clear, any surface finish, drapability are got well and produce gloss as lasting and similar real silk, but smooth degree and resilience are still short of; Postfinishing process adopts reactive amino silicon breast and soluble polyurethane to combine to improve further fabric feeling.Amino silicone breast and polyurethane reaction active strong, intermolecular cross-linking film forming after drying sizing, forms network structure, fibre-fibre friction resistance significantly reduces, resilience improves, thus the sense of touch of super smooth, pro-skin as acquisition pearl and silkiness gloss.
Detailed description of the invention:
Embodiment: a kind of trimming process of double-mercerized cotton knitted silk-like fabric, a, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame, burner adopts a positive and a negative, thermal source is natural gas or gasification gasoline, burner temperature 1100 DEG C ~ 1200 DEG C, the speed of a motor vehicle 75 ~ 95m/min, singes quality control more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240 ~ 280g/L, silkete penetrating agent DM-1205G3 ~ 5g/L, alkali liquid temperature 18 DEG C ~ 22 DEG C, leaching caustic lye of soda time 40 ~ 45s, adopts glacial acetic acid to neutralize after mercerising;
C, boil drift: equipment adopts high temperature overflow machine, boiling drift formula is: high-efficiency refining agent DM-13640.3 ~ 0.5g/L, NaOH1 ~ 2g/L, 30%H
2o
24 ~ 6g/L; Bath raio is 1: 8 ~ 10, boils drift 45 ~ 50min under the temperature conditions of 98 DEG C;
D, cellulase treatment: equipment adopts high temperature overflow machine, acidic cellulase DM-86271.0% ~ 1.5% (owf), adopt glacial acetic acid regulator solution pH=4 ~ 5; bath raio 1: 10 ~ 15; process 60 ~ 70min under the temperature conditions of 45 DEG C ~ 60 DEG C; then carry out enzyme-deactivating, adopt 85 DEG C of hot water treatment 10min;
E, in advance softness: equipment adopts high temperature overflow machine, first clean once with the hot water of 60 DEG C ~ 80 DEG C, then add hydrophilically modified silicone softening agent R1.0% ~ 2.5% (owf) and 98% glacial acetic acid 0.3 ~ 0.4ml/L carries out preliminary treatment; bath raio 1: 10 ~ 15, under 45 DEG C ~ 55 DEG C temperature conditions, process 30 ~ 45min;
F, mercerized cotton Final finishing:
Adopt high-temperature forming machine, adopt padding process, dressing liquid formula is:
Superlastic finishing agent DM-354150g/L
Catalyst DM-35425g/L
Flexible silicon breast SILYOUSOFTT8056100g/L
One leaching one is rolled, and dries under 100 DEG C of temperature conditions, and then shape 20 ~ 40s under 160 DEG C of temperature conditions.
Claims (1)
1. a trimming process of double-mercerized cotton knitted silk-like fabric, is characterized in that:
A, grey cloth are singed: equipment adopts open-width knitted fabric gassing frame, and burner adopts a positive and a negative, and thermal source is natural gas or gasification gasoline, burner temperature 1100 DEG C ~ 1200 DEG C, and the speed of a motor vehicle 75 ~ 95m/min, singes quality control more than 3 grades;
B, grey cloth mercerising: equipment adopts knitting open width mercerizing range, NaOH concentration 240 ~ 280g/L, silkete penetrating agent DM-1205G3 ~ 5g/L, alkali liquid temperature 18 DEG C ~ 22 DEG C, leaching caustic lye of soda time 40 ~ 45s, adopts glacial acetic acid to neutralize after mercerising;
C, boil drift: equipment adopts high temperature overflow machine, boiling drift formula is: high-efficiency refining agent DM-13640.3 ~ 0.5g/L, NaOH1 ~ 2g/L, 30%H
2o
24 ~ 6g/L; Bath raio is 1: 8 ~ 10, boils drift 45 ~ 50min under the temperature conditions of 98 DEG C;
D, cellulase treatment: equipment adopts high temperature overflow machine, acidic cellulase DM-86271.0% ~ 1.5% (owf), adopt glacial acetic acid regulator solution pH=4 ~ 5; bath raio 1: 10 ~ 15; process 60 ~ 70min under the temperature conditions of 45 DEG C ~ 60 DEG C; then carry out enzyme-deactivating, adopt 85 DEG C of hot water treatment 10min;
E, in advance softness: equipment adopts high temperature overflow machine, first clean once with the hot water of 60 DEG C ~ 80 DEG C, then add hydrophilically modified silicone softening agent R1.0% ~ 2.5% (owf) and 98% glacial acetic acid 0.3 ~ 0.4ml/L carries out preliminary treatment; bath raio 1: 10 ~ 15, under 45 DEG C ~ 55 DEG C temperature conditions, process 30 ~ 45min;
F, mercerized cotton Final finishing:
Adopt high-temperature forming machine, adopt padding process, dressing liquid formula is:
Superlastic finishing agent DM-354150g/L
Catalyst DM-35425g/L
Flexible silicon breast SILYOUSOFTT8056100g/L
One leaching one is rolled, and dries under 100 DEG C of temperature conditions, and then shape 20 ~ 40s under 160 DEG C of temperature conditions.