CN106120352A - The cotton smooth comfortable type fabric of a kind of Semen Phaseoli - Google Patents
The cotton smooth comfortable type fabric of a kind of Semen Phaseoli Download PDFInfo
- Publication number
- CN106120352A CN106120352A CN201610764772.1A CN201610764772A CN106120352A CN 106120352 A CN106120352 A CN 106120352A CN 201610764772 A CN201610764772 A CN 201610764772A CN 106120352 A CN106120352 A CN 106120352A
- Authority
- CN
- China
- Prior art keywords
- semen phaseoli
- cotton
- fabric
- smooth comfortable
- cellulase
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the cotton smooth comfortable type fabric of a kind of Semen Phaseoli, the Semen Phaseoli cotton face fabric become initially with material knitting, Semen Phaseoli cotton face fabric is carried out refine, bleach, dye after immerse to cellulase compounding finish solution, each component of cellulase compounding finish solution is cellulase: 1.5 ~ 5%o.w.f, penetrating agent: 0.5 ~ 5%o.w.f, dispersant: 1 ~ 1.5%o.w.f, glacial acetic acid 0.1 ~ 1%o.w.f, finally carries out high-temperature shaping and obtains the cotton smooth comfortable type fabric of Semen Phaseoli.The Semen Phaseoli cotton face fabric smooth comfortable type fabric texture that the present invention prepares is frivolous, smooth comfortable, washes excellent in stability, and the cellulase compounding finishing agent energy-conserving and environment-protective of employing, handling process is short, has a extensive future.Fabric indices all reaches country's textile standard requirement.
Description
Technical field
The present invention relates to the cotton smooth comfortable type fabric of a kind of Semen Phaseoli, belong to fabric preparing technical field.
Background technology
Along with people's living standard improves, people become spring and summer to frivolous smooth comfortable requirement and wear mainly telling of fabric
Ask, and tradition is textile and the knitting fabric of blended fibre knitwears is difficult to reach requirement.
Improve the most concrete effective method of smooth comfortableness aspect of the knitting fabrics such as cotton textiles, and the interpolation used at present
Method many washings poor stability, environmental pollution that finishing agent processes are big, process the defects such as feel difference and be difficult to spread.
Summary of the invention
The problem that the invention aims to solve pure-cotton fabric smooth comfortableness difference, it is provided that a kind of Semen Phaseoli cotton is smooth
Comfortable type fabric, uses cellulose treatment Semen Phaseoli cotton face fabric, and the fabric texture obtained is frivolous, smooth comfortable.
The present invention adopts the following technical scheme that the cotton smooth comfortable type fabric of a kind of Semen Phaseoli, and preparation method comprises the steps:
(1) raw material is woven on the single or double weft-knitting machine that plane No. is 24 pins/inch or 28 pins/inch form, adopt
Carry out braiding by one side flat needle structure or two-sided double thread structure and make Semen Phaseoli cotton face fabric;
(2) being joined by Semen Phaseoli cotton face fabric and carry out refine in refining liquid, refine bath raio is 15~20:1, and the temperature of refining liquid is 60
~100 DEG C, refining time is 35~50min;
(3) the Semen Phaseoli cotton face fabric after refine joined in bleaching liquid bleach, bleaching liquid be mass concentration be 1~10%
Hydrogen peroxide, bleaching bath ratio is 5~20:1, and the temperature of bleaching liquid is 10~55 DEG C, takes out fabric, enter after bleaching 5~25min
Row clear water washs, and dries stand-by;
(4), after the Semen Phaseoli cotton face fabric after bleaching being carried out dyeing, it is immersed in cellulase compounding finish solution, wherein
Each constituent content is: cellulase: 1.5 ~ 5%o.w.f, penetrating agent: 0.5 ~ 5%o.w.f, dispersant: 1 ~ 1.5 %o.w.f, ice vinegar
Acid 0.1 ~ 1%o.w.f, finally enters Semen Phaseoli cotton face fabric in forming machine and carries out high-temperature shaping.
Further, in described step (4) Semen Phaseoli cotton face fabric in cellulase compounding finish solution in normal temperature condition
Lower stirring 5 ~ 45min, mixing speed is 35 ~ 150 revs/min.
Further, described penetrating agent is fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene or the two mixture.
Further, described dispersant is glycerol monostearate, glyceryl tristearate or the two mixture.
Further, described cellulase is acidic cellulase.
The Semen Phaseoli cotton face fabric smooth comfortable type fabric texture that the present invention prepares is frivolous, smooth comfortable, washes stability
Excellence, the cellulase compounding finishing agent energy-conserving and environment-protective of employing, handling process is short, has a extensive future.Fabric indices is equal
Reach country's textile standard requirement.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is further illustrated.
Embodiment one:
The cotton smooth comfortable type fabric of a kind of Semen Phaseoli, preparation method comprises the steps:
(1) it is to weave on 24 pins/inch single weft knitting machine to form by raw material in plane No., uses one side flat needle structure to compile
Knit and make Semen Phaseoli cotton face fabric;
(2) being joined by Semen Phaseoli cotton face fabric and carry out refine in refining liquid, refine bath raio is 15:1, and the temperature of refining liquid is 100 DEG C,
Refining time is 35min;
(3) the Semen Phaseoli cotton face fabric after refine joined in bleaching liquid bleach, bleaching liquid be mass concentration be the dioxygen of 10%
Water, bleaching bath ratio is for 5:1, and the temperature of bleaching liquid is 55 DEG C, takes out fabric, carries out clear water washing, dry after bleaching 5min
Stand-by;
(4), after the Semen Phaseoli cotton face fabric after bleaching being carried out dyeing, it is immersed in cellulase compounding finish solution, wherein
Each constituent content is: acidic cellulase: 1.5%o.w.f, penetrating agent: 0.5%o.w.f, dispersant: 1 %o.w.f, glacial acetic acid
0.1%o.w.f, Semen Phaseoli cotton face fabric stirs 5min in cellulase compounding finish solution under normal temperature condition, and mixing speed is
150 revs/min, finally Semen Phaseoli cotton face fabric is entered in forming machine and carry out high-temperature shaping.
Penetrating agent is fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene or the two mixture;
Dispersant is glycerol monostearate, glyceryl tristearate or the two mixture.
Embodiment two:
The cotton smooth comfortable type fabric of a kind of Semen Phaseoli, preparation method comprises the steps:
(1) it is to weave on 24 pins/inch single weft knitting machine to form by raw material in plane No., uses one side flat needle structure to compile
Knit and make Semen Phaseoli cotton face fabric;
(2) being joined by Semen Phaseoli cotton face fabric and carry out refine in refining liquid, refine bath raio is 18:1, and the temperature of refining liquid is 80 DEG C,
Refining time is 40min;
(3) the Semen Phaseoli cotton face fabric after refine joined in bleaching liquid bleach, bleaching liquid be mass concentration be the dioxygen of 5%
Water, bleaching bath ratio is for 15:1, and the temperature of bleaching liquid is 45 DEG C, takes out fabric, carry out clear water washing, get rid of after bleaching 20min
Dry stand-by;
(4), after the Semen Phaseoli cotton face fabric after bleaching being carried out dyeing, it is immersed in cellulase compounding finish solution, wherein
Each constituent content is: acidic cellulase: 3%o.w.f, penetrating agent: 2%o.w.f, dispersant: 1 %o.w.f, glacial acetic acid 0.5%
O.w.f, Semen Phaseoli cotton face fabric stirs 40min in cellulase compounding finish solution under normal temperature condition, and mixing speed is 100
Rev/min, finally Semen Phaseoli cotton face fabric is entered in forming machine and carry out high-temperature shaping.
Penetrating agent is fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene or the two mixture;
Dispersant is glycerol monostearate, glyceryl tristearate or the two mixture.
Embodiment three:
The cotton smooth comfortable type fabric of a kind of Semen Phaseoli, preparation method comprises the steps:
(1) raw material is woven on the double side weft knitting knitting machine that plane No. is 28 pins/inch form, use two-sided double thread structure to enter
Semen Phaseoli cotton face fabric is made in row braiding;
(2) being joined by Semen Phaseoli cotton face fabric and carry out refine in refining liquid, refine bath raio is 20:1, and the temperature of refining liquid is 60 DEG C,
Refining time is 50min;
(3) the Semen Phaseoli cotton face fabric after refine joined in bleaching liquid bleach, bleaching liquid be mass concentration be the dioxygen of 1%
Water, bleaching bath ratio is for 20:1, and the temperature of bleaching liquid is 10 DEG C, takes out fabric, carry out clear water washing, get rid of after bleaching 25min
Dry stand-by;
(4), after the Semen Phaseoli cotton face fabric after bleaching being carried out dyeing, it is immersed in cellulase compounding finish solution, wherein
Each constituent content is: acidic cellulase: 5%o.w.f, penetrating agent: 5%o.w.f, dispersant: 1.5 %o.w.f, glacial acetic acid 1%
O.w.f, Semen Phaseoli cotton face fabric stirs 45min in cellulase compounding finish solution under normal temperature condition, and mixing speed is 35
Rev/min, finally Semen Phaseoli cotton face fabric is entered in forming machine and carry out high-temperature shaping.
Penetrating agent is fatty alcohol-polyoxyethylene ether, alkylphenol polyoxyethylene or the two mixture;
Dispersant is glycerol monostearate, glyceryl tristearate or the two mixture.
Claims (5)
1. the cotton smooth comfortable type fabric of Semen Phaseoli, it is characterised in that: preparation method comprises the steps:
(1) raw material is woven on the single or double weft-knitting machine that plane No. is 24 pins/inch or 28 pins/inch form, adopt
Carry out braiding by one side flat needle structure or two-sided double thread structure and make Semen Phaseoli cotton face fabric;
(2) being joined by Semen Phaseoli cotton face fabric and carry out refine in refining liquid, refine bath raio is 15~20:1, and the temperature of refining liquid is 60
~100 DEG C, refining time is 35~50min;
(3) the Semen Phaseoli cotton face fabric after refine joined in bleaching liquid bleach, bleaching liquid be mass concentration be 1~10%
Hydrogen peroxide, bleaching bath ratio is 5~20:1, and the temperature of bleaching liquid is 10~55 DEG C, takes out fabric, enter after bleaching 5~25min
Row clear water washs, and dries stand-by;
(4), after the Semen Phaseoli cotton face fabric after bleaching being carried out dyeing, it is immersed in cellulase compounding finish solution, wherein
Each constituent content is: cellulase: 1.5 ~ 5%o.w.f, penetrating agent: 0.5 ~ 5%o.w.f, dispersant: 1 ~ 1.5 %o.w.f, ice vinegar
Acid 0.1 ~ 1%o.w.f, finally enters Semen Phaseoli cotton face fabric in forming machine and carries out high-temperature shaping.
2. the cotton smooth comfortable type fabric of Semen Phaseoli as claimed in claim 1, it is characterised in that: Semen Phaseoli cotton face in described step (4)
Material stirs 5 ~ 45min in cellulase compounding finish solution under normal temperature condition, and mixing speed is 35 ~ 150 revs/min.
3. the cotton smooth comfortable type fabric of Semen Phaseoli as claimed in claim 1, it is characterised in that: described penetrating agent is fatty alcohol polyoxy
Vinyl Ether, alkylphenol polyoxyethylene or the two mixture.
4. the cotton smooth comfortable type fabric of Semen Phaseoli as claimed in claim 1, it is characterised in that: described dispersant is that stearic acid list is sweet
Grease, glyceryl tristearate or the two mixture.
5. the cotton smooth comfortable type fabric of Semen Phaseoli as claimed in claim 1, it is characterised in that: described cellulase is acid fiber
Element enzyme.