CN101591846A - A kind of preparation method of moisture-absorption and perspiration finish fabric - Google Patents
A kind of preparation method of moisture-absorption and perspiration finish fabric Download PDFInfo
- Publication number
- CN101591846A CN101591846A CNA2009103037789A CN200910303778A CN101591846A CN 101591846 A CN101591846 A CN 101591846A CN A2009103037789 A CNA2009103037789 A CN A2009103037789A CN 200910303778 A CN200910303778 A CN 200910303778A CN 101591846 A CN101591846 A CN 101591846A
- Authority
- CN
- China
- Prior art keywords
- fabric
- temperature
- agent
- moisture
- under
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of moisture-absorption and perspiration finish fabric, comprise the A fabric selection, B fabric boil float, the moisture absorbing and sweat releasing of the middle inspection of the soft finish of the mercerising of C fabric, D coloration of textile materials, E fabric, F fabric, G fabric is handled, the training baking setting of H fabric.The present invention can be applicable to natural fabric or regenerated fiber fabrics such as cotton, fiber crops, hair, silk, the finish fabric that adopts the present invention to produce has lasting washable moisture absorbing and sweat releasing effect, the class and the grade of clothes can be promoted significantly, dacron can be replaced to a great extent.
Description
Technical field
The present invention relates to a kind of processing method of cloth.Particularly relate to a kind of preparation method with finish fabric of moisture absorption sweat discharging functions.
Background technology
As everyone knows, polyester textile has good intensity and stability, but, its hygroscopicity is poor, fabric sees through the ability of the high hot sweat gas of skin drainage, on fiber, accumulate static easily, thereby influenced people's wearing comfortableness, prior art has solved the hydrophily problem of polyester fiber at present, as different in nature cross section polyster fibre spinning process technology and terylene hydrophilic finiss technology, realize the moisture absorption sweat discharging functions of terylene clothes by the hydrophilicity that improves dacron, but this moisture absorbing and sweat releasing technology mainly is to be used for synthetic fabrics, and is not suitable for the face fiber.Cotton fiber itself is with regard to possess hydrophilic property, but the water-retaining property of cotton fiber also is very strong, and cotton fiber is after having sucked sweat, in case saturated by sweat, rate of drying is slow, and is very long to the water balance required time from moisture state.In addition, the COTTON FABRIC weight of soaking into moisture content increases the weight of, and human body skin is had sticking slimy bad odour, when garment fabric is attached to skin surface, often hinders the activity of health.
Summary of the invention
The objective of the invention is to provide a kind of preparation method of moisture-absorption and perspiration finish fabric at natural fabric or regenerated fiber fabric.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of preparation method of moisture-absorption and perspiration finish fabric comprises the step of following order:
The selection of A fabric: select cotton or fiber crops or natural fabric or regenerated fiber fabrics such as hair or silk;
Boiling of B fabric floated: fabric is put into be made up of the caustic soda of the hydrogen peroxide of the refining agent of 1g/l, 5g/l and 2g/l that working solution is 1: 8～12 in bath raio, temperature is to boil 40～50 minutes under 90～100 ℃ of conditions, washing together then;
The mercerising of C fabric: is that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 18～25m/min in 15～22 ℃ the caustic soda with fabric in concentration, and washing together then;
The D coloration of textile materials: with fabric form by the soda ash of the unknown powder of the dye leveller of 1g/l, 50～100g/l, 15～25g/l that dyeing liquor is 1: 8～12 in bath raio, temperature is to dye 40～50 minutes under 55～65 ℃ the condition, washing together, then under 90～100 ℃, soaped 10～20 minutes, washed 10～20 minutes 50～60 ℃ of following fixation with color-fixing agent then with soaping agent;
The soft finish of E fabric: the silicone softening agent with 3～5% is 1: 8～12 in bath raio, temperature is to carry out hand feel finishing processing 10～20 minutes under 45～50 ℃ the condition, dewaters then, dries;
The middle inspection of F fabric: the feel, hydrophily and the resistance to water that detect fabric;
The moisture absorbing and sweat releasing of G fabric is handled: with viscosity is the reverse side that the moisture absorbing and sweat releasing agent of 30000～50000mPa.s is printed on fabric, makes the water area of refusing of the reverse side of fabric reach 30～60%, dries under 100～150 ℃ temperature then;
The training baking setting of H fabric: fabric is trained baking 1～2 minute under 150～170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.
As improvement of the technical scheme: a kind of preparation method of moisture-absorption and perspiration finish fabric, its best sequential steps is as follows:
The selection of A fabric: select cotton or fiber crops or natural fabric or regenerated fiber fabrics such as hair or silk;
Boiling of B fabric floated: fabric is put into to form working solution by the caustic soda of the hydrogen peroxide of the refining agent of 1g/l, 5g/l and 2g/l be that 1: 10, temperature are to boil 45 minutes under 95 ℃ of conditions in bath raio, washing together then;
The mercerising of C fabric: is that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 18～25m/min in 20 ℃ the caustic soda with fabric in concentration, and washing together then;
The D coloration of textile materials: is that 1: 10, temperature be 60 ℃ condition under dye 45 minute be made of dyeing liquor the soda ash of the unknown powder of the dye leveller of 1g/l, 50～100g/l, 15～25g/l in bath raio with fabric, washing together, then under 95 ℃, soaped 15 minutes, washed 15 minutes 60 ℃ of following fixation with color-fixing agent then with soaping agent;
The soft finish of E fabric: the silicone softening agent with 3～5% is that 1: 10, temperature are to carry out hand feel finishing processing 15 minutes under 50 ℃ the condition in bath raio, dewaters then, dries;
The middle inspection of F fabric: the feel, hydrophily and the resistance to water that detect fabric;
The moisture absorbing and sweat releasing of G fabric is handled: with viscosity is the reverse side that the moisture absorbing and sweat releasing agent of 30000～50000mPa.s is printed on fabric, makes the water area of refusing of the reverse side of fabric reach 30～60%, dries under 120 ℃ temperature then;
The training baking setting of H fabric: fabric is trained baking 1 minute under 170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.
As further improvement in the technical proposal: in the step of described D coloration of textile materials, in dyeing liquor, add the vital staining agent.In the moisture absorbing and sweat releasing of described G fabric is handled, utilize ROTARY SCREAM PRINTING the moisture absorbing and sweat releasing agent to be printed on the reverse side of fabric.
The invention has the beneficial effects as follows: the moisture-absorption and perspiration finish fabric that adopts preparation method of the present invention to make can absorb also transporting rapidly to the outer surface of fabric with sweat, and skin surface still can keep relative dry and comfortable, go out many again sweat, clothes also is unlikely to be bonded on the skin, keeps a dry and comfortable relatively comfortable microcosmic to wear environment.Moisture-absorption and perspiration finish fabric can be widely used in tights, shirt, woman style coat, sportswear, Western-style trousers, lining, etc. make clothes that the characteristic of meeting " breathing " arranged.
The specific embodiment
The present invention is further described below in conjunction with embodiment.
Embodiment one:
Selecting the COTTON FABRIC 10kg of grammes per square metre between 150～220, form working solution with what fabric was put into 80kg by the hydrogen peroxide of refining agent DMG-1361, the 5g/l of 1g/l and the caustic soda of 2g/l, is to boil 50 minutes under 90 ℃ of conditions in temperature, and washing together then.
Be that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 18m/min in 15 ℃ the caustic soda with fabric in concentration then, washing together then.
Then get the unknown powder that fabric 10kg after the above-mentioned processing puts into 80kg by dye leveller DMG-3, the 50～100g/l of 1g/l, the soda ash of 15～25g/l is formed dyeing liquor, be to dye 50 minutes under 55 ℃ the condition in temperature, washing together, then under 90 ℃, soaped 20 minutes, washed 20 minutes 50 ℃ of following fixation with color-fixing agent DMG-5233 then with soaping agent DMG-5232.In dyeing course, be well in order to dye, in dyeing liquor, add the vital staining agent of any concentration.
Fabric 10kg after getting then that previous step is rapid and handling puts into 3～5% the silicone softening agent DMG-6302 of 80kg, is to carry out hand feel finishing processing 20 minutes under 45 ℃ the condition in temperature, dewaters then, dries.
Then carry out the middle inspection of fabric, detect feel, hydrophily and the resistance to water of fabric.Hydrophily requires 30 minutes capillary effects to be not less than 12cm, and family's washing still keeps good hydrophilicity 20 times.
Then be the reverse side that the moisture absorbing and sweat releasing agent DMG-3419 of 30000～50000mPa.s is printed on fabric, make the water area of refusing of the reverse side of fabric reach 30～60%, under 100 ℃ temperature, dry then viscosity.For the moisture absorbing and sweat releasing agent being printed on well the reverse side of fabric, the mode of employing ROTARY SCREAM PRINTING is printed on the moisture absorbing and sweat releasing agent reverse side of fabric.
Then fabric is trained baking 2 minutes under 150 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.Carry out the check of finished product at last, detect the washable hydrophily of fabric face and the washable waterproof and moisture permeability of reverse side.
Embodiment two:
Select the COTTON FABRIC 10kg of grammes per square metre between 150～220, that puts into 120kg forms working solution by the hydrogen peroxide of refining agent DMG-1361, the 5g/l of 1g/l and the caustic soda of 2g/l, is to boil 40 minutes under 100 ℃ of conditions in temperature, and washing together then.
Be that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 25m/min in 22 ℃ the caustic soda with fabric in concentration then, washing together then.
Then getting fabric 10kg after the above-mentioned processing puts into 120kg and forms dyeing liquor by the unknown powder of dye leveller DMG-3, the 50～100g/l of 1g/l, the soda ash of 15～25g/l, be to dye 40 minutes under 65 ℃ the condition in temperature, washing together, then under 100 ℃, soaped 10 minutes, washed 10 minutes 60 ℃ of following fixation with color-fixing agent DMG-5233 then with soaping agent DMG-5232.In dyeing course, be well in order to dye, in dyeing liquor, add the vital staining agent of any concentration.
Fabric 10kg after getting then that previous step is rapid and handling puts into 3～5% the silicone softening agent DMG-6302 of 120kg, in temperature is to carry out hand feel finishing processing 10 minutes under 50 ℃ the condition, dewaters then, dries.
Then carry out the middle inspection of fabric, detect feel, hydrophily and the resistance to water of fabric, hydrophily requires 30 minutes capillary effects to be not less than 12cm, and family's washing still keeps good hydrophilicity 20 times.
Then be the reverse side that the moisture absorbing and sweat releasing agent DMG-3419 of 30000～50000mPa.s is printed on fabric, make the water area of refusing of the reverse side of fabric reach 30～60%, under 150 ℃ temperature, dry then viscosity.For the moisture absorbing and sweat releasing agent being printed on well the reverse side of fabric, the mode of employing ROTARY SCREAM PRINTING is printed on the moisture absorbing and sweat releasing agent reverse side of fabric.
Then fabric is trained baking 1 minute under 170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.Carry out the check of finished product at last, detect the washable hydrophily of fabric face and the washable waterproof and moisture permeability of reverse side.
Embodiment three:
Selecting the COTTON FABRIC 10kg of grammes per square metre between 150～220, put into 100kg and put into by the hydrogen peroxide of refining agent DMG-1361, the 5g/l of 1g/l and the caustic soda of 2g/l and form working solution, is to boil 45 minutes under 95 ℃ of conditions in temperature, and washing together then.
Be that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 20m/min in 20 ℃ the caustic soda with fabric in concentration then, washing together then.
Then get the unknown powder that fabric 10kg after the above-mentioned processing puts into 100kg by dye leveller DMG-3, the 50～100g/l of 1g/l, the soda ash of 15～25g/l is formed dyeing liquor, be to dye 45 minutes under 60 ℃ the condition in temperature, washing together, then under 95 ℃, soaped 15 minutes, washed 15 minutes 60 ℃ of following fixation with color-fixing agent DMG-5233 then with soaping agent DMG-5232.In dyeing course, be well in order to dye, in dyeing liquor, add the vital staining agent of any concentration.
Fabric 10kg after getting then that previous step is rapid and handling puts into 3～5% the silicone softening agent DMG-6302 of 100kg, in temperature is to carry out hand feel finishing processing 15 minutes under 50 ℃ the condition, dewaters then, dries.
Then carry out the middle inspection of fabric, detect feel, hydrophily and the resistance to water of fabric, hydrophily requires 30 minutes capillary effects to be not less than 12cm, and family's washing still keeps good hydrophilicity 20 times.
Then be the reverse side that the moisture absorbing and sweat releasing agent DMG-3419 of 30000～50000mPa.s is printed on fabric, make the water area of refusing of the reverse side of fabric reach 30～60%, under 120 ℃ temperature, dry then viscosity.For the moisture absorbing and sweat releasing agent being printed on well the reverse side of fabric, the mode of employing ROTARY SCREAM PRINTING is printed on the moisture absorbing and sweat releasing agent reverse side of fabric.
Then fabric is trained baking 1 minute under 170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.Carry out the check of finished product at last, detect the washable hydrophily of fabric face and the washable waterproof and moisture permeability of reverse side.
The fabric face that adopts the present invention to handle has good hydrophilicity, and reverse side has good washable waterproof and moisture permeability, is particularly suitable for being applied to sportswear next to the shin, can promote the class and the grade of clothes significantly, can replace dacron to a great extent.For having the natural fabric or the regenerated fiber fabric such as fiber crops, hair, silk, bamboo fibre of similar performance with cotton, the present invention is suitable equally.
The refining agent of using in above-mentioned three embodiment, dye leveller, soaping agent, color-fixing agent, silicone softening agent, moisture absorbing and sweat releasing agent etc. can replace with the like product of other models, and these all products are all bought from the market and obtained.
Claims (4)
1. the preparation method of a moisture-absorption and perspiration finish fabric is characterized in that comprising the step of following order:
The selection of A fabric: select cotton or fiber crops or natural fabric or regenerated fiber fabrics such as hair or silk;
Boiling of B fabric floated: fabric is put into be made up of the caustic soda of the hydrogen peroxide of the refining agent of 1g/l, 5g/l and 2g/l that working solution is 1: 8～12 in bath raio, temperature is to boil 40～50 minutes under 90～100 ℃ of conditions, washing together then;
The mercerising of C fabric: is that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 18～25m/min in 15～22 ℃ the caustic soda with fabric in concentration, and washing together then;
The D coloration of textile materials: with fabric form by the soda ash of the unknown powder of the dye leveller of 1g/l, 50～100g/l, 15～25g/l that dyeing liquor is 1: 8～12 in bath raio, temperature is to dye 40～50 minutes under 55～65 ℃ the condition, washing together, then under 90～100 ℃, soaped 10～20 minutes, washed 10～20 minutes 50～60 ℃ of following fixation with color-fixing agent then with soaping agent;
The soft finish of E fabric: the silicone softening agent with 3～5% is 1: 8～12 in bath raio, temperature is to carry out hand feel finishing processing 10～20 minutes under 45～50 ℃ the condition, dewaters then, dries;
The middle inspection of F fabric: the feel, hydrophily and the resistance to water that detect fabric;
The moisture absorbing and sweat releasing of G fabric is handled: with viscosity is the reverse side that the moisture absorbing and sweat releasing agent of 30000～50000mPa.s is printed on fabric, makes the water area of refusing of the reverse side of fabric reach 30～60%, dries under 100～150 ℃ temperature then;
The training baking setting of H fabric: fabric is trained baking 1～2 minute under 150～170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.
2. the preparation method of a kind of moisture-absorption and perspiration finish fabric according to claim 1 is characterized in that comprising the sequential steps of following the best:
The selection of A fabric: select cotton or fiber crops or natural fabric or regenerated fiber fabrics such as hair or silk;
Boiling of B fabric floated: fabric is put into to form working solution by the caustic soda of the hydrogen peroxide of the refining agent of 1g/l, 5g/l and 2g/l be that 1: 10, temperature are to boil 45 minutes under 95 ℃ of conditions in bath raio, washing together then;
The mercerising of C fabric: is that 13～31Be ', temperature are to carry out mercerising with open-width or cylinder type mercerizing range with 18～25m/min in 20 ℃ the caustic soda with fabric in concentration, and washing together then;
The D coloration of textile materials: is that 1: 10, temperature be 60 ℃ condition under dye 45 minute be made of dyeing liquor the soda ash of the unknown powder of the dye leveller of 1g/l, 50～100g/l, 15～25g/l in bath raio with fabric, washing together, then under 95 ℃, soaped 15 minutes, washed 15 minutes 60 ℃ of following fixation with color-fixing agent then with soaping agent;
The soft finish of E fabric: the silicone softening agent with 3～5% is that 1: 10, temperature are to carry out hand feel finishing processing 15 minutes under 50 ℃ the condition in bath raio, dewaters then, dries;
The middle inspection of F fabric: the feel, hydrophily and the resistance to water that detect fabric;
The moisture absorbing and sweat releasing of G fabric is handled: with viscosity is the reverse side that the moisture absorbing and sweat releasing agent of 30000～50000mPa.s is printed on fabric, makes the water area of refusing of the reverse side of fabric reach 30～60%, dries under 120 ℃ temperature then;
The training baking setting of H fabric: fabric is trained baking 1 minute under 170 ℃ temperature, with the washability of consolidating the fabric waterproof effect, the planarization and the size stability of fabric.
3. the preparation method of a kind of moisture-absorption and perspiration finish fabric according to claim 1 and 2 is characterized in that in the step of described D coloration of textile materials, adds the vital staining agent in dyeing liquor.
4. the preparation method of a kind of moisture-absorption and perspiration finish fabric according to claim 1 and 2 is characterized in that utilizing ROTARY SCREAM PRINTING the moisture absorbing and sweat releasing agent to be printed on the reverse side of fabric in the moisture absorbing and sweat releasing of described G fabric is handled.