CN108914315A - A kind of spring sweat absorption antibacterial underwear fabric - Google Patents
A kind of spring sweat absorption antibacterial underwear fabric Download PDFInfo
- Publication number
- CN108914315A CN108914315A CN201810772966.5A CN201810772966A CN108914315A CN 108914315 A CN108914315 A CN 108914315A CN 201810772966 A CN201810772966 A CN 201810772966A CN 108914315 A CN108914315 A CN 108914315A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- graphene
- fibre
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of spring sweat absorption antibacterial underwear fabric, which is made of following raw materials according：Ultra-fine polyester fiber, bamboo fibre, tencel fiber, chitin and graphene regenerated celulose fibre；By each material component of scientific matching, under mutually acting synergistically between each component, the elasticity, intensity, water imbibition of fabric are improved；Fabric properties are excellent, have good feel, drapability, gas permeability, elasticity etc., and antibacterial effect is significant, is ideal personal health-care undervest fabric.
Description
Technical field
The invention belongs to textile technology fields, and in particular to a kind of spring sweat absorption antibacterial underwear fabric.
Background technique
It is cotton spinning underwear fabric soft touch, comfortable, it is usually used in making the fabrics such as underwear, bedding.Terylene is that synthesis is fine
An important species in dimension, but be not easy to perspire, feel the feeling of spinosity drawing, it is easy to electrostatic is played, biggest advantage is
Wrinkle resistance and conformality are fine.Terylene underwear is one important kind of Underwear market, it is largely applied to market, Hen Duoren
The clothes worn is also this kind.Terylene intensity is high, wearability is good, in doing the higher work of intensity should not by clothing wear,
Its rotproofness and it is sun protection be all it is good, as bleaching agent, oxidant these the unsuitable damaging laundry of use.But terylene
Have the shortcomings that very important, absorption of perspiration is poor, and dyeability is poor, and the fadedness after dyeing in other words is bad, and anti-Sai function
Poor, absorbing sweat, is not easy to make one to feel that skin is sultry, as being easy product electrostatic in a dry environment.It is obtained as this field
A kind of technical staff's divination by means of the milfoil spring sweat absorption antibacterial underwear fabric of excellent combination property to be developed.
Summary of the invention
The purpose of the present invention is being directed to existing problem, a kind of spring sweat absorption antibacterial underwear fabric is provided.
The invention is realized by the following technical scheme：
A kind of spring sweat absorption antibacterial underwear fabric, again by ultra-fine polyester fiber, bamboo fibre, tencel fiber, chitin and graphene
Raw cellulosic fibre blend is weaved, and wherein the parts by weight of ultra-fine polyester fiber are 55 ~ 65 parts, the parts by weight of bamboo fibre
It is 10 ~ 15 parts, the parts by weight of tencel fiber are 10 ~ 20 parts, and the parts by weight of chitin are 5 ~ 10 parts, graphene regenerated fiber
The parts by weight of cellulose fiber are 5 ~ 10 parts.
A kind of preparation method of spring sweat absorption antibacterial underwear fabric, includes the following steps：The first step, pre-treatment：Using tea
Leaf extract antimicrobial coating inorganic agent respectively regenerates ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and graphene
Cellulose fibre carries out coating treatment；Second step, weaving：Using ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and
The blended silk thread of graphene regenerated celulose fibre is weaved, and Dobby Weave Design uses satin weave, using appropriate
Twisting, is made fabric using water-jet loom；Third step, oils at starching：The fabric of second step preparation is subjected to starching and the place that oils
Reason；4th step, desizing refining：Desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under：：PH value 6 ~ 7, refining agent are bathed in desizing：0.3 ~ 1g/L, NaOH：0.3 ~ 1g/L, bath raio：1：8 ~ 12, temperature：60 ~ 70 DEG C, when
Between：3~5min；5th step, alkali process：After the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions are NaOH5 ~ 10g/
L, temperature：60 ~ 75 DEG C, the time：1~5min；6th step, sizing：It after the completion of Alkali reduction, carries out shaping, temperature：100 ~ 120 DEG C,
Time：10~20s；7th step, rear shaping and drying：Shaping and drying is handled after carrying out after stamp, is first carried out clear water and is padded, then 130
Drying and shaping under the conditions of ~ 150 DEG C.
Further, the graphene regenerated celulose fibre is to carry out biomass graphene and rayon spinning liquid uniformly
Doping mixing, through wet spinning, graphene modification regeneration cellulose fibre obtained.
Beneficial effects of the present invention：
Spring sweat absorption antibacterial fabric provided by the invention is free of antibacterial agent, but the surface structure of fabric has lotus leaf effect, i.e., logical
Processing assigns its water repellent, refuses oil, refuses dirty anti-sticking effect, can have a negative impact to the living condition of microorganism, thus
Show the effect for inhibiting harmful microorganism to grow.Nontoxic, health environment-friendly reduces cost.
Using being blended, the methods of copolymerization, function modified are compound by graphene and viscose glue stoste, to construct graphene and viscose glue
Uniform and stable dispersion.Analysis is it is found that the excellent performance of graphene assigns regenerated celulose fibre excellent physics after tested
The multiple functions such as mechanical performance and far infrared, antibacterial bacteriostatic, improve the added value of regenerated celulose fibre, using graphene
Regenerated celulose fibre brings unique body temperature by biomass graphene, promotes capillary blood circulation, has certainly
Heating function, energy activating cell tissue, quickening is metabolic, promoting blood circulation and removing obstruction in channels, slows down physical distress, quick clearing damp degerming, keeps
Body is persistently dry and comfortable, adsorbs abnormal smell of body, has the function that feeding body body beautification.Underwear collocation combed cotton natural fiber, in common
The warm sense that clothing doubles is pro-skin, safe and environment-friendly but without bored wet sense, and face weave is that four-way is high-elastic, wears frivolous cultivates one's moral character not
Too fat to move, soft comfortable is unlikely to deform.
The present invention has the following advantages that compared with prior art：
The generation of the faults such as folding line, scratch, color spot can be effectively prevent in product processing, can avoid the folding of fabric, friction,
Squeeze and damage etc..The fibrillation of tencel fiber is easy, dyeing and finishing technology equipment and dyestuff requirement are low.Elasticity disclosed by the invention
Absorbing sweat antibacterial underwear fabric has good wearability, possesses the sense of touch and drapability for exactly liking natural fiber, and sweat-absorbing breathable is protected
It is warm and nice and cool, and strength is high, and wearability and excellent spring have preferable antibacterial effect, are ideal underwear fabrics.
Specific embodiment
Illustrate the present invention with specific embodiment below, but is not limitation of the present invention.
Embodiment 1
A kind of spring sweat absorption antibacterial underwear fabric, again by ultra-fine polyester fiber, bamboo fibre, tencel fiber, chitin and graphene
Raw cellulosic fibre blend is weaved, and wherein the parts by weight of ultra-fine polyester fiber are 65 parts, and the parts by weight of bamboo fibre are
15 parts, the parts by weight of tencel fiber are 20 parts, and the parts by weight of chitin are 10 parts, the weight of graphene regenerated celulose fibre
Measuring number is 10 parts.
A kind of preparation method of spring sweat absorption antibacterial underwear fabric, includes the following steps：The first step, pre-treatment：Using tea
Leaf extract antimicrobial coating inorganic agent respectively regenerates ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and graphene
Cellulose fibre carries out coating treatment；Second step, weaving：Using ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and
The blended silk thread of graphene regenerated celulose fibre is weaved, and Dobby Weave Design uses satin weave, using appropriate
Twisting, is made fabric using water-jet loom；Third step, oils at starching：The fabric of second step preparation is subjected to starching and the place that oils
Reason；4th step, desizing refining：Desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under：PH value 6 ~ 7, refining agent are bathed in desizing：0.5g/L, NaOH：0.5g/L, bath raio：1：10, temperature：65 DEG C, the time：5min；5th
Step, alkali process：After the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions NaOH8g/L, temperature：65 DEG C, the time：
5min；6th step, sizing：It after the completion of Alkali reduction, carries out shaping, temperature：100 DEG C, the time：10s；7th step, rear shaping and drying：
Shaping and drying is handled after carrying out after stamp, is first carried out clear water and is padded, then drying and shaping under the conditions of 130 DEG C.
Further, the graphene regenerated celulose fibre is to carry out biomass graphene and rayon spinning liquid uniformly
Doping mixing, through wet spinning, graphene modification regeneration cellulose fibre obtained.
Embodiment 2
A kind of spring sweat absorption antibacterial underwear fabric, again by ultra-fine polyester fiber, bamboo fibre, tencel fiber, chitin and graphene
Raw cellulosic fibre blend is weaved, and wherein the parts by weight of ultra-fine polyester fiber are 65 parts, and the parts by weight of bamboo fibre are
15 parts, the parts by weight of tencel fiber are 10 parts, and the parts by weight of chitin are 5 parts, the weight of graphene regenerated celulose fibre
Measuring number is 5 parts.
A kind of preparation method of spring sweat absorption antibacterial underwear fabric, includes the following steps：The first step, pre-treatment：Using tea
Leaf extract antimicrobial coating inorganic agent respectively regenerates ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and graphene
Cellulose fibre carries out coating treatment；Second step, weaving：Using ultra-fine polyester fiber, bamboo fibre, tencel fiber and chitin and
The blended silk thread of graphene regenerated celulose fibre is weaved, and Dobby Weave Design uses satin weave, using appropriate
Twisting, is made fabric using water-jet loom；Third step, oils at starching：The fabric of second step preparation is subjected to starching and the place that oils
Reason；4th step, desizing refining：Desizing refining processing is carried out using low bath raio high-pressure injection overflow machine, technology preparation and condition are such as
Under：PH value 7, refining agent are bathed in desizing：0.5g/L, NaOH：1g/L, bath raio：1：12, temperature：70 DEG C, time 5min；5th step, alkali
Processing：After the completion of desizing refining, then alkali decrement treatment is carried out, treatment conditions NaOH9g/L, temperature：65 DEG C, the time：5min；
6th step, sizing：It after the completion of Alkali reduction, carries out shaping, temperature：100 DEG C, the time：10s；7th step, rear shaping and drying：Stamp
Shaping and drying is handled after carrying out afterwards, is first carried out clear water and is padded, then drying and shaping under the conditions of 130 DEG C.
Further, the graphene regenerated celulose fibre is to carry out biomass graphene and rayon spinning liquid uniformly
Doping mixing, through wet spinning, graphene modification regeneration cellulose fibre obtained.
Comparative example 1
This comparative example compared with Example 2, weighs in step in raw material, saves tencel fiber ingredient, method and step in addition to this
It is all the same.
Comparative example 2
This comparative example compared with Example 2, weighs in step in raw material, saves graphene regenerated celulose fibre ingredient, removes this
Outer method and step is all the same.
Comparative example 3
This comparative example compared with Example 2, weighs in step in raw material, saves chitin ingredient, and method and step in addition to this is equal
It is identical.
The performance test 1 of underwear fabric prepared by each embodiment and comparative example of table 1
The performance test 2 of underwear fabric prepared by each embodiment and comparative example of table 2
The draping property of spring sweat absorption antibacterial underwear fabric disclosed by the invention is very good it can be seen from table 1 and 2, it is not easy to
Pilling, hygroscopicity with higher.The intensity of fabric is high, and wrinkle, ironing-free performance, elastic recovery are excellent, washing shrinkage
Lower, dimensional stability is preferable.In addition, fabric also has good bacteria resistance function, it is suitble to the high-grade personal health care underwear of production
Product, added value of product is high, economic benefits.The ventilative and water vapour permeability of fabric is good, has preferable snugness of fit.
In addition, wear-resisting property is good.
Claims (3)
1. a kind of spring sweat absorption antibacterial underwear fabric, which is characterized in that the antibacterial underwear fabric is by ultra-fine polyester fiber, bamboo
Fiber, tencel fiber, chitin and graphene regenerated celulose fibre hybrid woven form, wherein the weight of ultra-fine polyester fiber
Number is 55 ~ 65 parts, and the parts by weight of bamboo fibre are 10 ~ 15 parts, and the parts by weight of tencel fiber are 10 ~ 20 parts, chitin
Parts by weight are 5 ~ 10 parts, and the parts by weight of graphene regenerated celulose fibre are 5 ~ 10 parts.
2. a kind of spring sweat absorption antibacterial underwear fabric according to claim 1, which is characterized in that preparation method, including
Following steps：The first step, pre-treatment：Using tea extract antimicrobial coating inorganic agent respectively to ultra-fine polyester fiber, bamboo fibre,
Tencel fiber, chitin and graphene regenerated celulose fibre carry out coating treatment；Second step, weaving：Using super fine polyester fibre
The blended silk thread of dimension, bamboo fibre, tencel fiber and chitin and graphene regenerated celulose fibre is weaved, and fabric tissue is set
Fabric is made using water-jet loom using twisting appropriate using satin weave in meter；Third step, oils at starching：By second
The fabric of step preparation carries out starching and oiling treatment；4th step, desizing refining：It is moved back using low bath raio high-pressure injection overflow machine
Refining treatment is starched, technology preparation and condition are as follows：PH value 6 ~ 7, refining agent are bathed in desizing：0.3 ~ 1g/L, NaOH：0.3 ~ 1g/L, bath
Than：1：8 ~ 12, temperature：60 ~ 70 DEG C, the time：3~5min；5th step, alkali process：After the completion of desizing refining, then carry out Alkali reduction
Processing, treatment conditions are NaOH5 ~ 10g/L, temperature：60 ~ 75 DEG C, the time：1~5min；6th step, sizing：After the completion of Alkali reduction,
It carries out shaping, temperature：100 ~ 120 DEG C, the time：10~20s；7th step, rear shaping and drying：After being carried out after stamp at shaping and drying
Reason first carries out clear water and pads, then drying and shaping under the conditions of 130 ~ 150 DEG C.
3. a kind of spring sweat absorption antibacterial underwear fabric according to claim 1, which is characterized in that the graphene regeneration is fine
Cellulose fiber is that biomass graphene is carried out Uniform Doped with rayon spinning liquid to mix, through wet spinning, graphene obtained
Modification regeneration cellulose fibre.