CN102443294A - 一种水性无机富锌涂料的生产方法 - Google Patents
一种水性无机富锌涂料的生产方法 Download PDFInfo
- Publication number
- CN102443294A CN102443294A CN2011102745373A CN201110274537A CN102443294A CN 102443294 A CN102443294 A CN 102443294A CN 2011102745373 A CN2011102745373 A CN 2011102745373A CN 201110274537 A CN201110274537 A CN 201110274537A CN 102443294 A CN102443294 A CN 102443294A
- Authority
- CN
- China
- Prior art keywords
- aqueous inorganic
- inorganic zinc
- zinc
- rich coating
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供的一种水性无机富锌涂料的生产方法,原料以重量份数配制,由锌粉30-40份、磷钛粉20-30份、E777T30-35份、弹性乳液1-4份组成;将原料依次置于容器中,在常温、常压下搅拌5-10分钟,搅拌均匀后备用;施工前将喷、涂面经抛丸或喷砂预处理,除锈标准达瑞典Sa2.5级方可施工,或手工和动力工具除锈达St3级方可施工;施工条件:将所配料经80-100目过筛,在外力的作用下边搅拌边施工,其室外的施工温度为5℃以上,空气相对湿度不小于75%,雨天停止施工;施工时采用机械喷涂、滚涂或手工刷涂皆可。
Description
技术领域
本发明涉及底漆涂料,尤其针对防锈底漆,在配加弹性乳液后产生了突出效果,即可以作为单独的防锈蚀漆使用。
背景技术
水性无机富锌底漆是由锌粉、防锈颜料、碱金属硅酸盐、助剂等组成,可用于油罐、油舱、溶剂舱、压载水舱及环境和条件较苛刻的海洋钢铁结构、桥梁、烟囱等,是一种电化学保护涂料,具有阴极保护作用,防锈性能优异,附着力好,耐油、耐水性能优异等特性。
文献检索披露:①上海振华重工(集团)常州油漆有限公司张斌等人进行了水性无机富锌涂料及其改性研究。文中指出:水性无机富锌涂料一般以硅酸钠、硅酸钾、硅酸锂为基料并复配锌粉制成。②中油管道防腐工程有限责任公司研制了一种新型水性无机富锌涂料。其配方组成为:A组分:蒸馏水、硅酸锂、氧基硅烷、硅溶胶;B组分:500目锌粉;使用时按A:B=1:2.5的比例混合即可。③湖南湘江涂料集团有限公司研制了一种由水性无机粘结剂、超细锌粉及助剂组成的水性无机富锌涂料,获得了平整、无光和VOC含量为零的涂膜,涂膜的耐盐雾时间达到1000h,户外曝晒1年无明显锈蚀,在400℃下放置6h漆膜完好。④北京紫禁城漆业有限公司研制生产了一种由水性无机粘结剂、偶联剂、防腐剂、助剂(组份一)、锌粉(组份二)等组成的无机富锌底漆,为双组份水性涂料。⑤中国人民解放军海军后勤技术装备研究所蔡森等人发明了一种水性无机富锌涂料及其制备方法(专利申请号:201010000166)。该涂料将制备好的组分A与组分B以1:1.5~3.5的重量比混合而成。⑥上海门普来新材料实业有限公司林左峰发明了一种混合型硅溶胶水性无机富锌涂料(专利申请号:03129131)。该涂料包括涂料A组份和B组份。
国内现在已有采用乳液改性的水性无机富锌原料,由于配方不采用纯锌粉,易出现闪锈;本发明通过配方优化和调整,加入弹性乳液,实施优化调配,其性能达到预期的指标,为环保型产品,为企业的节能减排提供了保障性措施。
发明内容
本发明的目的在于:提供的水性无机富锌涂料,既可以做底漆也可以做防锈漆;该产品具有优良的防腐蚀作用,以水为溶剂,无火灾危险,能耐400℃高温,耐原油、耐溶剂性能等特点。
本发明目的是这样实现的:一种水性无机富锌涂料的生产方法,原料以重量份数配制,由锌粉30-40份、磷钛粉20-30份、 E777T 30-35份、弹性乳液1-4份组成;将原料依次置于容器中,在常温、常压下搅拌5-10分钟,搅拌均匀后备用;施工前将喷、涂面经抛丸或喷砂预处理,除锈标准达瑞典Sa2.5级方可施工,或手工和动力工具除锈达St3级方可施工;施工条件:将所配料经80-100目过筛,在外力的作用下边搅拌边施工,其室外的施工温度为5℃以上,空气相对湿度不小于75%,雨天停止施工;施工时采用机械喷涂、滚涂或手工刷涂皆可。
所述的生产方法,选用的弹性乳液的规格为48±2%,由巴斯夫生产;锌粉规格为325-500目,由长沙锌威生产;磷钛粉的规格为X-500,由常州众普生产;E777T由武汉现代生产。
本发明产品中添加了锌粉和弹性乳液后更具有回弹性、柔韧性、粘接性、防水性、耐候性、耐积尘性和耐紫外线等性能,等同于纯丙、硅丙、水性聚氨酯等系列产品;弹性乳液本为助剂,无毒无害,不燃不爆,用弹性乳液对原配方实施复合,不仅增加了实用效果,而且更具环保,作为通用型的防锈底漆,也可以作为单独的防锈蚀漆,彰显技术进步。
具体实施方式
本发明对照实施例作进一步说明。
产品配方:以重量份数配制原料,取500目锌粉35份、磷钛粉25份、 E777T 32份、弹性乳液3份组成;将配料置于容器中,在常温、常压下搅拌35分钟,搅拌均匀后即可使用;
施工条件:施工温度5℃以上,空气相对湿度不小于75%,雨天禁止施工;
表面处理:喷、涂面经抛丸或喷砂处理,除锈标准达瑞典Sa2.5级,或手工和动力工具除锈达St3级;
施工方法:施工前将配料用80目的金属筛网过滤,在施工过程中应边施工边搅拌,实施机械喷涂、滚涂或手工刷涂即可。
本产品的性能指标的对比分析:
调整配方前的产品性能见表1。
表1 水性无机富锌底漆物理性能指标
由上表数据得知:主要是气候干燥区湿度小,绝大数时间的情况下小于35%,对于该类产品无法进行正常施工。
新配方的产品性能
实验加入1-5%通用型弹性乳液(建筑涂料用),即达到性能要求,指标见表2。
表2 水性无机富锌底漆物理性能指标
由上表数据得知:柔韧性为1 mm、冲击强度 为50 kg.cm、耐水性(25±1℃)72h不起泡、允许变白;耐盐雾 30d允许轻微变色,无锈无泡;耐热性(400℃)24h允许轻微变色。
Claims (2)
1.一种水性无机富锌涂料的生产方法,其特征在于:原料以重量份数配制,由锌粉30-40份、磷钛粉20-30份、 E777T 30-35份、弹性乳液1-4份组成;将原料依次置于容器中,在常温、常压下搅拌5-10分钟,搅拌均匀后备用;施工前将喷、涂面经抛丸或喷砂预处理,除锈标准达瑞典Sa2.5级方可施工,或手工和动力工具除锈达St3级方可施工;施工条件:将所配料经80-100目过筛,在外力的作用下边搅拌边施工,其室外的施工温度为5℃以上,空气相对湿度不小于75%,雨天停止施工;施工时采用机械喷涂、滚涂或手工刷涂皆可。
2.根据权利要求1所述的生产方法,其特征在于:选用的弹性乳液的规格为48±2%,由巴斯夫生产;锌粉规格为325-500目,由长沙锌威生产;磷钛粉的规格为X-500,由常州众普生产;E777T由武汉现代生产。