CN102276181A - 混凝土用阻泥剂及其制备方法 - Google Patents
混凝土用阻泥剂及其制备方法 Download PDFInfo
- Publication number
- CN102276181A CN102276181A CN2011101286356A CN201110128635A CN102276181A CN 102276181 A CN102276181 A CN 102276181A CN 2011101286356 A CN2011101286356 A CN 2011101286356A CN 201110128635 A CN201110128635 A CN 201110128635A CN 102276181 A CN102276181 A CN 102276181A
- Authority
- CN
- China
- Prior art keywords
- mud
- agent
- concrete
- parts
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种混凝土用阻泥剂,其聚合母液的单体组成及质量百分含量为:烯基胺醚50-75%,(甲基)丙烯酸酯5-15%,DA 0.1-1%,烯基磺酸盐0.5-5%,EA 0.1-1%,乙烯基酯5-15%。该阻泥剂引入聚合单体脂类单体,这样在该分子吸附与泥颗粒表面后,会降低泥颗粒的吸水率,从而使得混凝土需水量能够在一个合适的量值。同时该阻泥剂聚合物单体为具有支链结构的分子,该支链能够有效降低泥颗粒彼此靠近聚沉凝胶的可能,从而使得含泥混凝土体系有很好的流动性。
Description
技术领域
本发明涉及建筑材料领域,特别涉及一种混凝土用阻泥剂及其制备方法。
背景技术
随着技术的进步好经济建设的发展,混凝土减水剂在混凝土中成了一不可或缺的第三组分,但在施工过程中,因砂石的泥含量的影响,导致减水剂的适应性有不同程度的下降,给工程的成本控制及施工的方便性带来不同程度的困难。
当前,随着国民经济的发展,大型工程的建设越来越多,但优质砂石料的获得存在较大困难。而使用在使用一般的砂石料使为了提高混凝土的质量,必需对沙石料里泥份进行吸附降黏,而目前尚没有一种专门的产品能对沙石料里泥份进行吸附降黏。
发明内容
针对上述现有技术的不足,本发明要解决的技术问题是提供一种能对混凝土中泥份具有很好吸附降黏作用的阻泥剂。
为解决上述技术问题,本发明采用如下技术方案:
一种混凝土用阻泥剂,其聚合母液的单体组成及质量百分含量为:烯基胺醚50-75%,(甲基)丙烯酸酯5-15%,DA 0.1-1%,烯基磺酸盐0.5-5%,EA 0.1-1%,乙烯基酯5-15%。
优选的,所述聚合单体烯基胺醚分子量为200-600其结构式为
R1N〔(R2O)nH〕2
式中R1表示碳原子数3~6的烯基;(R2O)n为碳原子数2和/或3的两种氧化烯基的聚合物,n表示氧化烯基的平均加成摩尔数。
优选的,所述(甲基)丙烯酸酯为丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸甲酯、甲基丙烯酸乙酯中的一种。
优选的,所述DA的聚合单体含有较强还原性基团的多羟基醇类化合物。
优选的,所述烯基磺酸盐为甲基丙烯磺酸钠、丙烯基磺酸钠、amps中的一种。
优选的,所述EA的聚合单体为一种效率比较高的链转移剂,其含有SH-,OH-活性基团。
优选的,所述乙烯基酯为乙酸乙烯、丙酸乙烯中的一种。
本发明还公开了一种上述混凝土用阻泥剂的制备方法,其包括如下步骤:
1)按重量百分比将50~75份烯基胺醚、5~15份(甲基)丙烯酸酯、0.5~5份烯基磺酸盐、0.1~1份EA、40~60份水,加入到反映容器中,搅拌混合制成溶液;
2)将0.1~1份DA与510分的水配成溶液,装入滴液漏斗备用;
3)将0.01~0.8质量份引发剂与5~10份水配成溶液,装入滴液漏斗备用;
4)将步骤1)配制的溶液加入到反应容器中,搅拌加热,溶成均匀透明溶液,保持温度55-60度,同时滴加2)、3)配置的溶液,3小时滴加完毕,然后保持温度在60-65度之间,继续反应1h,降温至40度以下,加碱中和至Ph值等于6.5-7.5,既得该阻泥剂。
优选的,所述引发剂为过硫酸钾,过硫酸胺、双氧水中的一种或几种。
上述技术方案具有如下有益效果:该阻泥剂引入聚合单体脂类单体,这样在该分子吸附与泥颗粒表面后,会降低泥颗粒的吸水率,从而使得混凝土需水量能够在一个合适的量值。同时该阻泥剂聚合物单体为具有支链结构的分子,该支链能够有效降低泥颗粒彼此靠近聚沉凝胶的可能,从而使得含泥混凝土体系有很好的流动性。
具体实施方式
在下述实施例中,如无特别说明,均为质量份。
实施例一
将60份烯基胺醚、10份丙烯酸甲酯、10份丙烯酸甲酯、10醋酸乙烯、0.5丙烯磺酸钠、0.1分EA、45份去离子水加如到反映容器中,控制在60度以内,加热搅拌,呈现均匀透明溶液备用。
将0.2分DA、6份去离子水配置成均匀溶液,装入恒压滴液漏斗备用。
将0.2份过硫酸铵、6分去离子水配制成均匀溶液,装入恒压滴液漏斗备用。
控制反应温度在55-60度之间,同时滴加引发剂溶液和DA溶液,3小时滴完,保持60-65度,1小时,降温至40度一下,加碱中和至ph值6.5-7.5之间,加水调整固含量值40%的阻泥剂溶液。
实施例二
将60份烯基胺醚、10份丙烯酸甲酯、10份丙烯酸甲酯、10醋酸乙烯、0.5丙烯磺酸钠、0.1分EA、45份去离子水加如到反映容器中,控制在60度以内,加热搅拌,呈现均匀透明溶液备用。
将0.2分DA、6份去离子水配置成均匀溶液,装入恒压滴液漏斗备用。
将0.2份过硫酸钾、6分去离子水配制成均匀溶液,装入恒压滴液漏斗备用。
控制反应温度在55-60度之间,同时滴加引发剂溶液和DA溶液,3小时滴完,保持60-65度,1小时,降温至40度一下,加碱中和至ph值6.5-7.5之间,加水调整固含量值40%的阻泥剂溶液。
实施例三
将60份烯基胺醚、10份丙烯酸甲酯、10份丙烯酸甲酯、10醋酸乙烯、0.5丙烯磺酸钠、0.1分EA、0.15份郭硫酸钾,50份去离子水加如到反映容器中,控制在60度以内,加热搅拌,呈现均匀透明溶液备用。
将0.2份过硫酸钾、6分去离子水配制成均匀溶液,装入恒压滴液漏斗备用。
控制反应温度在55-60度之间,滴加DA溶液,3小时滴完,保持60-65度,1小时,降温至40度一下,加碱中和至ph值6.5-7.5之间,加水调整固含量值40%的阻泥剂溶液。
由实施例一至三所制得的阻泥剂应用基准水泥,测定其砂浆减水率和砂浆流动度及其1小时后的流动度保持性。(掺量折固为水泥的0.2%)。
各实例的混凝土实验,在相同减水剂掺量,相同用水量的前提下,其坍落度情况如下表所示:
实施例 | 1 | 2 | 3 |
坍落度 | 200 | 200 | 195 |
扩展度 | 55 | 75 | 60 |
从表中可以看出,使用该阻泥剂后,混凝土的坍落度值、扩展度值会明 显升高,其中实施例二的效果最好。
该阻泥剂引入聚合单体脂类单体,这样在该分子吸附与泥颗粒表面后,会降低泥颗粒的吸水率,从而使得混凝土需水量能够在一个合适的量值。同时该阻泥剂聚合物单体为具有支链结构的分子,该支链能够有效降低泥颗粒彼此靠近聚沉凝胶的可能,从而使得含泥混凝土体系有很好的流动性。
以上对本发明实施例所提供的一种混凝土用阻泥剂及其制备方法进行了详细介绍,对于本领域的一般技术人员,依据本发明实施例的思想,在具体实施方式及应用范围上均会有改变之处,综上所述,本说明书内容不应理解为对本发明的限制,凡以本发明设计思想所做任何改变,均在本发明的保护范围之内。
Claims (9)
1.一种混凝土用阻泥剂,其特征在于,其聚合母液的单体组成及质量百分含量为:烯基胺醚50-75%,(甲基)丙烯酸酯5-15%,DA 0.1-1%,烯基磺酸盐0.5-5%,EA 0.1-1%,乙烯基酯5-15%。
2.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述聚合单体烯基胺醚分子量为200-600其结构式为
R1N〔(R2O)nH〕2
式中R1表示碳原子数3~6的烯基;(R2O)n为碳原子数2和/或3的两种氧化烯基的聚合物,n表示氧化烯基的平均加成摩尔数。
3.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述(甲基)丙烯酸酯为丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸甲酯、甲基丙烯酸乙酯中的一种。
4.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述DA的聚合单体含有较强还原性基团的多羟基醇类化合物。
5.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述烯基磺酸盐为甲基丙烯磺酸钠、丙烯基磺酸钠、amps中的一种。
6.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述EA的聚合单体为一种效率比较高的链转移剂,其含有SH-,OH-活性基团。
7.根据权利要求1所述的混凝土用阻泥剂,其特征在于:所述乙烯基酯为乙酸乙烯、丙酸乙烯中的一种。
8.一种权利要求1-7所述混凝土用阻泥剂的制备方法,其特征在于,其包括如下步骤:1)按重量百分比将50~75份烯基胺醚、5~15份(甲基)丙烯酸酯、0.5~5份烯基磺酸盐、0.1~1份EA、40~60份水,加入到反映容器中,搅拌混合制成溶液;
2)将0.1~1份DA与510分的水配成溶液,装入滴液漏斗备用;
3)将0.01~0.8质量份引发剂与5~10份水配成溶液,装入滴液漏斗备用;
4)将步骤1)配制的溶液加入到反应容器中,搅拌加热,溶成均匀透明溶液,保持温度55-60度,同时滴加2)、3)配置的溶液,3小时滴加完毕,然后保持温度在60-65度之间,继续反应1h,降温至40度以下,加碱中和至Ph值等于6.5-7.5,既得该阻泥剂。
9.根据权利要求8所述的混凝土用阻泥剂的制备方法,其特征在于:所述引发剂为过硫酸钾,过硫酸胺、双氧水中的一种或几种。