CN104844054A - 一种混凝土阻泥剂 - Google Patents

一种混凝土阻泥剂 Download PDF

Info

Publication number
CN104844054A
CN104844054A CN201510198113.1A CN201510198113A CN104844054A CN 104844054 A CN104844054 A CN 104844054A CN 201510198113 A CN201510198113 A CN 201510198113A CN 104844054 A CN104844054 A CN 104844054A
Authority
CN
China
Prior art keywords
parts
weight
concrete
water
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510198113.1A
Other languages
English (en)
Other versions
CN104844054B (zh
Inventor
高建明
张太龙
祁兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Southeast University
Original Assignee
Southeast University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Southeast University filed Critical Southeast University
Priority to CN201510198113.1A priority Critical patent/CN104844054B/zh
Publication of CN104844054A publication Critical patent/CN104844054A/zh
Application granted granted Critical
Publication of CN104844054B publication Critical patent/CN104844054B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种混凝土阻泥剂，以重量计，包括水性聚合物50-80％，没食子酸5-20％和二乙二醇10-30％。所述的水性聚合物生产工艺包括：以重量计：1)取4-7份双氧水与8份水溶解完全，标记溶液Ⅰ；2)取2-4份吊白块与8份水溶解完全，标记溶液Ⅱ；3)在反应釜中加入35-40份水，然后分别加入7份丙烯酰胺、9份马来酸酐和21份烯丙基醚，开动搅拌；4)加入0.5-2份链转移剂，5)升温至40度，同时滴加溶液Ⅰ、溶液Ⅱ，控制反应温度在40-50度，滴加时间为2-4小时；反应完全后，降温至30度，出料为所述水性聚合物，其中固含量38-42％。本发明能减少混凝土减水剂在泥土颗粒上的吸附，提高高含泥量混凝土体系的流动度，显著提高混凝土减水剂的保坍性。

Description

一种混凝土阻泥剂
技术领域
本发明涉及一种混凝土外加剂，特别是涉及混凝土集料中含泥量较高时使用的混凝土阻泥剂。
背景技术
随着混凝土技术的发展，混凝土减水剂已经成为混凝土体系中不可或缺的组份之一。特别是第三代聚羧酸减水剂的出现，由于其更高的减水率，从而赋予混凝土更好的施工性能，同时显著改善了混凝土凝结时间、强度、耐久性等各项性能指标。混凝土减水剂在水泥水化体系中，吸附在水泥水化产物表面并在水溶液和水化产物表面达到平衡。然后在施工过程中，由于集料中高含泥量的影响，导致混凝土减水剂优先被泥土吸附，混凝土减水剂的减水效果大打折扣，给混凝土施工和混凝土质量控制控制带来非常大的困难。
本发明与混凝土减水剂一同使用时，在高含泥量混凝土体系中，混凝土阻泥剂会优先吸附在泥土颗粒表面，在很小掺量的状况下，显著提高混凝土的流动性和保坍性。
发明内容
技术问题：为了克服现有技术的不足，本发明提供了一种混凝土阻泥剂，与市场常用混凝土减水剂有很好的相容性，可以复配使用，该发明成本低、无污染，同等条件下，混凝土体系具有更好的流动性和保坍性。
技术方案:本发明所采用的混凝土阻泥剂以重量计包括：
水性聚合物50-80％，
没食子酸5-20％，
二乙二醇10-30％。
所述的水性聚合物生产工艺包括：以重量计：
1)取4-7份双氧水与8份水溶解完全，标记溶液Ⅰ；
2)取2-4份吊白块与8份水溶解完全，标记溶液Ⅱ；
3)在反应釜中加入35-40份水，然后分别加入7份丙烯酰胺、9份马来酸酐和21份烯丙基醚，开动搅拌；
4)加入0.5-2份链转移剂， 
5)升温至40度，同时滴加溶液Ⅰ、溶液Ⅱ，控制反应温度在40-50度，滴加时间为2-4小时；反应完全后，降温至30度，出料为所述水性聚合物，其中固含量38-42％。
所述的烯丙基醚化学结构为CH2＝CHCH2O(CH2CH2O)nH，其中n为小于10的自然数。
所述的链转移剂是：异丙醇、巯基乙酸或巯基丙酸的一种。
有益效果：与现有技术相比，本发明具有下列优点：
1：本发明为一种新型液体混凝土阻泥剂，与市场常用混凝土减水剂有很好的相容性，可以复配使用，该发明成本低、无污染，同等条件下，混凝土体系具有更好的流动性和保坍性。
2：本发明没食子酸作为活性组分，延缓了水泥的水化速率，混凝土具有更好的保坍性。
3：本发明中使用的二乙二醇在混凝土体系中具有一定程度的引起作用，显著改善混凝土的施工性能。
具体实施方式
实例1：一种混凝土阻泥剂，各组分配比如下：(按重量份)
水性聚合物：70
没食子酸：10
二乙二醇：20
水性聚合物中：
链转移剂为巯基乙酸
烯丙基醚的聚合物为8
实例2：一种混凝土阻泥剂，各组分配比如下：(按重量份)
水性聚合物：80
没食子酸：10
二乙二醇：10
水性聚合物中：
链转移剂为巯基乙酸
烯丙基醚的聚合物为6
实例3：一种混凝土阻泥剂，各组分配比如下：(按重量份)
水性聚合物：75
没食子酸：5
二乙二醇：20
水性聚合物中：
链转移剂为巯基丙酸
烯丙基醚的聚合物为6。
混凝土阻泥剂的效果如下表所示：
注：(1)表中聚羧酸减水剂产量为聚羧酸减水剂与水泥用量的重量比，(2)混凝土阻泥剂掺量为混凝土阻泥剂与水泥用量的重量比。

Claims (4)

1.一种混凝土阻泥剂，其特征在于，该混凝土阻泥剂以重量计包括：
水性聚合物 50-80％，
没食子酸 5-20％，
二乙二醇 10-30％。
2.根据权利要求1所述的混凝土阻泥剂，其特征在于，所述的水性聚合物生产工艺包括：以重量计：
1)取4-7份双氧水与8份水溶解完全，标记溶液Ⅰ；
2)取2-4份吊白块与8份水溶解完全，标记溶液Ⅱ；
3)在反应釜中加入35-40份水，然后分别加入7份丙烯酰胺、9份马来酸酐和21份烯丙基醚，开动搅拌；
4)加入0.5-2份链转移剂，
5)升温至40度，同时滴加溶液Ⅰ、溶液Ⅱ，控制反应温度在40-50度，滴加时间为2-4小时；反应完全后，降温至30度，出料为所述水性聚合物，其中固含量38-42％。
3.根据权利要求2所述的混凝土阻泥剂，其特征在于，所述的烯丙基醚化学结构为CH2＝CHCH2O(CH2CH2O)nH，其中n为小于10的自然数。
4.根据权利要求2所述的混凝土阻泥剂，其特征在于，所述的链转移剂是：异丙醇、巯基乙酸或巯基丙酸的一种。
CN201510198113.1A 2015-04-23 2015-04-23 一种混凝土阻泥剂 Expired - Fee Related CN104844054B (zh)