CN102134102B - 一种氧化铁纳米棒的制备方法 - Google Patents

一种氧化铁纳米棒的制备方法 Download PDF

Info

Publication number
CN102134102B
CN102134102B CN 201110037640 CN201110037640A CN102134102B CN 102134102 B CN102134102 B CN 102134102B CN 201110037640 CN201110037640 CN 201110037640 CN 201110037640 A CN201110037640 A CN 201110037640A CN 102134102 B CN102134102 B CN 102134102B
Authority
CN
China
Prior art keywords
water
preparation
iron oxide
ferric oxide
oxide nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 201110037640
Other languages
English (en)
Other versions
CN102134102A (zh
Inventor
宋浩杰
沈湘黔
袁新华
盛维琛
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu University
Original Assignee
Jiangsu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu University filed Critical Jiangsu University
Priority to CN 201110037640 priority Critical patent/CN102134102B/zh
Publication of CN102134102A publication Critical patent/CN102134102A/zh
Application granted granted Critical
Publication of CN102134102B publication Critical patent/CN102134102B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属于纳米材料制备技术领域，具体涉及氧化铁纳米棒的制备方法，具体为：其特征在于包括以下步骤：常压下，将水溶性三价铁盐溶解在水和乙醇的混合溶剂中混合均匀，水溶性三价铁盐的摩尔浓度为0.01-0.1mol/L，在90-150℃反应10-60小时，离心、洗涤、干燥即可得到氧化铁纳米棒。本发明绿色环保无污染，操作简单，成本低，产率高，容易工业化生产。制备的氧化铁纳米棒形貌均一，在水中分散性良好。

Description

一种氧化铁纳米棒的制备方法
技术领域
本发明属于纳米材料制备技术领域。具体涉及氧化铁纳米棒的制备方法。
背景技术
纳米氧化铁除了具有普通氧化铁的耐腐蚀、无毒等特点外，还具有分散性高、色泽鲜艳、对紫外线具有良好吸收和屏蔽效应等特点，可广泛应用于闪光涂料、油墨、塑料、皮革、汽车面漆、气敏材料、催化剂、电子、光学抛光剂、生物医学工程等行业中；通常，较具实用价值的有α-Fe2O3、γ-Fe2O3、α-FeOOH、Fe3O4等，由于纳米氧化铁具有如此多的优点及其广泛的应用前景，近年来，国内外研究者对其制备和应用投入了大量的研究工作。
一维纳米材料是一种以纳米为尺度的棒状、线状、管状等不同形貌的一维结构体系的材料，这种材料具有良好的光电特性、热传导性、磁学性能、力学性能及催化性能等，它们可用作新一代纳米光电子、电化学、电动机械的器件的构筑单元，因此该材料的制备与应用研究是近些年来材料研究的热点之一，目前制备一维纳米材料的方法主要有：反相胶束法、溶剂热法、分子束外延法、模板法、激光或电弧蒸发法、催化热解法等等。尽管采用这些工艺能制备尺寸均一的一维纳米材料，但是这些工艺往往工艺复杂、污染环境、成本较高，不能实现大规模工业生产。
发明内容
本发明针对现有技术的不足，提供一种绿色无污染、操作简单、产率高的制备氧化铁纳米棒的方法。
一种制备氧化铁纳米棒的方法，其特征在于包括以下步骤：常压下，将水溶性三价铁盐溶解在水和乙醇的混合溶剂中混合均匀，水溶性三价铁盐的摩尔浓度为0.01-0.1 mol/L，在90-150℃反应10-60小时，离心、洗涤、干燥即可得到氧化铁纳米棒。
上述制备方法中，水溶性三价铁盐指三氯化铁，硝酸铁或硫酸铁。
上述制备方法中，水和乙醇的体积比为1-5：1。
    本发明采用简单的醇水混合体系控制三价铁粒子成核速度，在反应温度超过乙醇的沸点时（78℃），有利于氧化铁核沿（001）面生长，使氧化铁形成一维纳米棒结构。
附图说明
图1为本发明施例1中所制备氧化铁纳米棒的透射电镜照片和EDS图；
图2为本发明施例2中所制备氧化铁纳米棒的透射电镜照片和EDS图；
从图1的透射电镜照片可以看出，氧化铁纳米棒尺寸均一，长度约为30 nm, 直径约为5 nm；
从图2的透射电镜照片可以看出，氧化铁纳米棒尺寸均一，长度约为200 nm, 直径约为30 nm。
具体实施方式
实例1：
将0.005 M的FeCl3·6H2O 溶于100 ml 水和乙醇的混合溶液中（水和乙醇的体积比例3：2），室温下超声30分钟后，将混合溶液在100 ℃静置回流12小时，离心、洗涤、干燥即可得到氧化铁纳米棒。
实例2：
将0.01 M的FeCl3·6H2O 溶于100 ml 水和乙醇的混合溶液中（水和乙醇的体积比例1：1），室温下超声30分钟后，将混合溶液在95 ℃静置回流60小时，离心、洗涤、干燥即可得到氧化铁纳米棒。
实例3：
将0.003 M的Fe（NO3）3·9H2O 溶于100 ml 水和乙醇的混合溶液中（水和乙醇的体积比例5：1），室温下超声30分钟后，将混合溶液在120 ℃静置回流36小时，离心、洗涤、干燥即可得到氧化铁纳米棒。
实例4：
将0.001 M的Fe2（SO4）3溶于100 ml 水和乙醇的混合溶液中（水和乙醇的体积比例3：1），室温下超声30分钟后，将混合溶液在150 ℃静置回流10小时，离心、洗涤、干燥即可得到氧化铁纳米棒。 

Claims (3)

1.一种制备氧化铁纳米棒的方法，其特征在于包括以下步骤：常压下，将水溶性三价铁盐溶解在水和乙醇的混合溶剂中混合均匀，水溶性三价铁盐的摩尔浓度为0.01-0.1 mol/L，在90-150℃静置回流反应10-60小时，离心、洗涤、干燥即可得到氧化铁纳米棒。
2.如权利要求1所述的一种制备氧化铁纳米棒的方法，其特征在于：水溶性三价铁盐指三氯化铁，硝酸铁或硫酸铁。
3.如权利要求1所述的一种制备氧化铁纳米棒的方法，其特征在于：所述水和乙醇的体积比为1-5：1。
CN 201110037640 2011-02-15 2011-02-15 一种氧化铁纳米棒的制备方法 Expired - Fee Related CN102134102B (zh)