CN101899137A - 酚醛绝缘树脂的生产方法 - Google Patents
酚醛绝缘树脂的生产方法 Download PDFInfo
- Publication number
- CN101899137A CN101899137A CN 201010147244 CN201010147244A CN101899137A CN 101899137 A CN101899137 A CN 101899137A CN 201010147244 CN201010147244 CN 201010147244 CN 201010147244 A CN201010147244 A CN 201010147244A CN 101899137 A CN101899137 A CN 101899137A
- Authority
- CN
- China
- Prior art keywords
- insulating resin
- waste water
- reactor
- wastewater
- ethanol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
针对酚醛绝缘树脂在生产过程中排放含酚废水不易处理、污染环境等缺陷，本发明提供了一种酚醛绝缘树脂的生产方法，所述的生产方法是：原料→入反应釜→升温→静止分层→废水回收→抽真空→残余废水回收→降温→加丙酮→乙醇→绝缘材料成品；将回收的废水、回收的残余废水入反应釜中→原料→升温→反应→降温→加乙醇、丙酮→搅拌→过滤→回收成品。
Description
技术领域
本发明公开了一种酚醛绝缘树脂的生产方法，属化工生产技术领域，尤其是与电气绝缘材料有关。产品主要用于电工环氧酚醛玻纤层压制品、电工酚醛棉布制品、电工模塑料、电工层压木的生产使用。
背景技术
在绝缘材料生产中，酚醛绝缘树脂是大量使用的绝缘树脂，如电工环氧酚醛玻纤层压制品、电工酚醛棉布制品、电工模塑料、电工层压木等产品的生产使用，用量较大，因此每年生产该类产品产生大量的废水。公知的酚醛绝缘树脂生产中产生工艺为：
原料→入反应釜→升温→静止分层→放出废水→抽真空→排出残余废水→升温→加丙酮、乙醇→绝缘材料成品。
从上述生产工艺可以看出，在生产过程中有大量含有酚类的废水排放，排放这些含有分类的废水，会造成环境污染，若对这些废水进行处理，处理工艺复杂，处理难度大，处理费用高，甚至经过复杂处理工艺处理后的废水，仍难达到排放要求，无法杜绝含酚废水排放后污染环境的问题，因此，传统酚醛绝缘树脂的生产方法不能解决环境污染事宜。
发明内容
针对酚醛绝缘树脂在生产过程中排放含酚废水不易处理、污染环境等缺陷，本发明提供了一种酚醛绝缘树脂的生产方法，利用该方法生产酚醛绝缘树脂材料，可以达到废水零排放、不污染环境，且还可以将废水中的酚类及低分子聚合物等再回收利用，既节约了生产用原材料、降低生产成本，又杜绝了废水排放，保护了环境。
为实现本发明的目的采取了如下技术方案：
一种酚醛绝缘树脂的生产方法，所述的生产方法是：
原料→入反应釜→升温→静止分层→废水回收→抽真空→残余废水回收→降温→加丙酮→乙醇→绝缘材料成品；
将回收的废水、回收的残余废水入反应釜中→原料→升温→反应→降温→加乙醇、丙酮→搅拌→过滤→回收成品。
本发明废水回收工艺中的升温温度是60℃-110℃。
本方明第二次加入的原料是多聚甲醛30-80重量份、苯酚90-120重量份，NaOH(10％水溶液)1-5重量份。
本发明的显著优点是生产工艺简单，生产中无三废排放，不污染环境；回收原材料，降低生产成本。
具体实施方案
下面结合实施例进一步详细说明本发明的技术特征：
原料→入反应釜→升温→静止分层→废水回收→抽真空→残余废水回收→降温→加丙酮→乙醇→绝缘材料成品；
将回收的废水、回收的残余废水入反应釜中→原料→升温→反应→降温→加乙醇、丙酮→搅拌→过滤→回收成品。
将原料甲醛80-130重量份、苯酚60-120重量份、草酸0.1-5重量份投入反应釜中，酸值调整到Ph：1-3.8，升温到70℃-90℃，反应2-5hr，静止分层1-2小时，回收放出的下层废水，抽真空到0.03-0.09MPa，回收残余废水，降温到50℃-60℃，加丙酮20-70重量份，乙醇30-80重量份，搅拌均匀、过滤、包装得成品；将回收的酚醛废水约40-70重量份加入反应釜，加入多聚甲醛30-80重量份、苯酚90-120重量份，NaOH(10％水溶液)1-5重量份，加入反应釜，酸值调整到Ph：7.5-10.5，加热到60℃-110℃，反应到3-6hr，降温到50℃-60℃，加丙酮30-60重量份，乙醇40-70重量份，搅 拌均匀、过滤、包装得产品。
实施例1：
取甲醛80kg、苯酚60kg、草酸0.3kg投入反应釜中，酸值调整到Ph：2.7，升温到80℃，反应3hr，静止分层2小时，回收放出的下层废水，抽真空到0.09MPa，回收残余废水，降温到50℃，加丙酮30kg，
乙醇30kg，搅拌均匀、过滤、包装得成品；将回收的酚醛废水约40kg加入反应釜，加入多聚甲醛30kg、苯酚90kg，NaOH(10％水溶液)1.5kg，加入反应釜，酸值调整到Ph：7.5，加热到90℃，反应到5hr，降温到50℃，加丙酮30kg，乙醇40kg，搅拌均匀、过滤、包装得产品。
Claims (3)
1.一种酚醛绝缘树脂的生产方法，其特征在于，所述的生产方法是：
原料→入反应釜→升温→静止分层→废水回收→抽真空→残余废水回收→降温→加丙酮→乙醇→绝缘材料成品；
将回收的废水、回收的残余废水入反应釜中→原料→升温→反应→降温→加乙醇、丙酮→搅拌→过滤→回收成品。
2.按权利要求1所述的酚醛绝缘树脂的生产方法，其特征在于，所述的废水回收工艺中的升温温度是60℃-110℃。
3.按权利要求1所述的酚醛绝缘树脂的生产方法，其特征在于，所述的第二次加入的原料是多聚甲醛30-80重量份、苯酚90-120重量份，NaOH(10％水溶液)1-5重量份。