CN101892589B - 拒水拒油型浸润剂 - Google Patents

拒水拒油型浸润剂 Download PDF

Info

Publication number
CN101892589B
CN101892589B CN201010215900XA CN201010215900A CN101892589B CN 101892589 B CN101892589 B CN 101892589B CN 201010215900X A CN201010215900X A CN 201010215900XA CN 201010215900 A CN201010215900 A CN 201010215900A CN 101892589 B CN101892589 B CN 101892589B
Authority
CN
China
Prior art keywords
solid content
water
sizing agent
oil repellent
high temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201010215900XA
Other languages
English (en)
Other versions
CN101892589A (zh
Inventor
王玉华
李大福
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Xingguo Xinli Environmental Protection Technology Co.,Ltd.
Original Assignee
Shandong Xinli Filter Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Xinli Filter Material Co Ltd filed Critical Shandong Xinli Filter Material Co Ltd
Priority to CN201010215900XA priority Critical patent/CN101892589B/zh
Publication of CN101892589A publication Critical patent/CN101892589A/zh
Application granted granted Critical
Publication of CN101892589B publication Critical patent/CN101892589B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种高温无纺布用拒水拒油型浸润剂，其特征在于包括如下重量百分组成：固含量为60％的PTFE溶液6~8％、固含量为30％的聚丙烯酸脂10~12％、固含量为12％的聚乙烯醇水溶液12~15％、固含量为30％的甲基苯基硅油2.5~3％、固含量为16％的偶联剂分散液2.5％、固含量为15％的氟碳化合物共聚物5~6％和余量的水。本发明增加了氟碳化合物共聚物一种化工原料，采用这种浸润剂表面涂覆高温无纺布过滤毡，拒水拒油效果好。经过实际检测用这种配方生产的过滤毡防水防油效果达到70％左右，大大提高了产品性能，具有良好的社会效益和经济效益。

Description

拒水拒油型浸润剂
技术领域
本发明涉及一种具有拒水拒油性能的高温无纺布浸润剂配方，特别适合用于高温无纺布过滤毡。
背景技术
目前，公知的高温无纺布过滤毡浸润剂配方中的组分全部采用PTFE溶液、聚丙烯酸酯、聚乙烯醇（PVA-17-88）、甲基苯基硅油、偶联剂分散液等物质。这种浸润剂，拒水拒油的效果差，用这种过滤毡制造的过滤袋，在潮湿多油的公放条件下，有不易清灰、过滤效果差、使用寿命短等缺点。
发明内容
本发明所要解决的技术问题是提供一种具有拒水拒油性能的过滤毡浸润剂，克服现有浸润剂无法提供过滤毡拒水拒油性能的问题。
本发明高温无纺布用拒水拒油型浸润剂，其特征在于包括如下重量百分组成：
固含量为60％的PTFE溶液6~8％、固含量为30％的聚丙烯酸酯10~12％、固含量为12％的聚乙烯醇水溶液12~15％、固含量为30％的甲基苯基硅油2.5~3％、固含量为16％的偶联剂分散液2.5％、固含量为15％的氟碳化合物共聚物5~6％和余量的水。
所述PTFE为PTFE浓缩分散液，可选用中昊晨光化院或东岳集团氟化工厂生产的产品，加水稀释成固含量为60％的PTFE溶液。
所述的固含量为30％的聚丙烯酸酯，为改性乳液，选用型号为LI-3。
所述的固含量为12％的聚乙烯醇水溶液，选用规格为PVA17-88的聚乙烯醇，加水稀释成固含量为12％的聚乙烯醇水溶液。聚乙烯醇（PVA17-88）可选用陕西三维生产的产品。
所述的固含量为30％的甲基苯基硅油，选用型号为285-1。固含量为30％的甲基苯基硅油（285-1）可选用中昊晨光化院或江阴双雄等地生产的产品。
所述的固含量为16％的偶联剂分散液，选用硅烷偶联剂A-151水溶液。硅烷偶联剂A-151水溶液产地为曲阜等地化工厂。
本发明增加了氟碳化合物共聚物一种化工原料，氟碳化合物共聚物多为日本或德国进口，含氟量约为18％。
采用这种浸润剂表面涂覆高温无纺布过滤毡，拒水拒油效果好。经过实际检测用这种配方生产的过滤毡拒水拒油效果达到70％左右，大大提高了产品性能。
本发明的配制工艺为：
1、将32公斤的水倒入夹套式反应釜，并开动搅拌。
2、将按比例称重3.5公斤聚乙烯醇颗粒（PVA17-88）倒入反应釜加热到90度，至原料全部融化两个半小时后倒出备用。
3、将2公斤硅烷偶联剂溶液（A-151）、2公斤酒精和20公斤水配制的溶液，倒入小搅拌分散，制成分散液备用。
4、往搅拌桶加入清水，水量为配方量100公斤的2/3，并开动搅拌。
5、将6-8公斤固含量为60％的PTFE溶液、10-12公斤固含量为30％的聚丙烯酸脂（LI-3）、35公斤固含量为12％的聚乙烯醇水溶液、2.5-3公斤固含量为30％的甲基苯基硅油（285-1）、5公斤固含量为16％的硅烷偶联剂分散液、5-6公斤固含量为15％的氟碳化合物共聚物依次倒入搅拌桶。
6、搅拌30分钟后，加入水稀释至100公斤即成。
本发明的有益效果在于，采用这种浸润剂表面涂覆高温无纺布过滤毡，其各项技术指标经检测都达到国家标准（GB/T18371-2002），并且拒水拒油效果好。经过实际检测用这种配方生产的过滤毡防水防油效果达到70％左右，大大提高了产品性能，具有良好的社会效益和经济效益。
具体实施方式
以下结合实施例说明本发明，但不限制本发明。均以重量百分数计。
其中实施例1和2为本发明的优选方式，实施例3为现有技术。
实施例1：
         PTFE：                                                                          6％
         聚丙烯脂：（改性乳液LI-3）                                         10％
         聚乙烯醇：（PVA17-88）                                             1.25％ 
         甲基苯基硅油：(285-1)                                              2.5％
         偶联剂分散液:( 硅烷偶联剂溶液A-151)                  2.5％
         氟碳化合物共聚物:(含氟量约为18%)                  5％
         水                                                                 余量
实施例2：
         PTFE：                                                                          8％
         聚丙烯脂：（改性乳液LI-3）                                         12％
         聚乙烯醇：（PVA17-88）                                             1.3％ 
         甲基苯基硅油：(285-1)                                              3％
         偶联剂分散液:( 硅烷偶联剂溶液A-151)                  3％
         氟碳化合物共聚物:(含氟量约为18%)                  6％
         水                                                                 余量
实施例3（现有浸润剂配方）：
         PTFE：（浓缩分散液）                                                6％
         聚丙烯脂：（改性乳液LI-3）                                         10％
         聚乙烯醇：（PVA17-88）                                             1.25％ 
         甲基苯基硅油：(285-1)                                               2.5％
         偶联剂分散液:(A-151)                                                2.5％
         水                                                                 余量
以下为检测结果：（均以百分计）
Figure 528280DEST_PATH_IMAGE001
                
由检测结果可以看出：与现有技术相比，使用本发明浸润剂配方后，过滤毡的拒水拒油率大大提高。 

Claims (4)

1.一种高温无纺布用拒水拒油型浸润剂，其特征在于包括如下重量百分组成：固含量为60％的PTFE溶液6～8％、固含量为30％的聚丙烯酸酯10～12％、固含量为12％的聚乙烯醇水溶液12～15％、固含量为30％的甲基苯基硅油2.5～3％、固含量为16％的偶联剂分散液2.5％、固含量为15％的氟碳化合物共聚物5～6％和余量的水；所述氟碳化合物共聚物的含氟量为18％。
2.根据权利要求1所述的浸润剂，其特征在于所述的聚乙烯醇规格为PVA17-88。
3.根据权利要求1所述的浸润剂，其特征在于所述的固含量为30％的甲基苯基硅油型号为285-1。
4.根据权利要求1所述的浸润剂，其特征在于所述的偶联剂分散液选用硅烷偶联剂A-151水溶液。
CN201010215900XA 2010-07-02 2010-07-02 拒水拒油型浸润剂 Active CN101892589B (zh)