CN1041622C - 湿法毡用玻璃纤维浸润剂 - Google Patents
湿法毡用玻璃纤维浸润剂 Download PDFInfo
- Publication number
- CN1041622C CN1041622C CN92107536A CN92107536A CN1041622C CN 1041622 C CN1041622 C CN 1041622C CN 92107536 A CN92107536 A CN 92107536A CN 92107536 A CN92107536 A CN 92107536A CN 1041622 C CN1041622 C CN 1041622C
- Authority
- CN
- China
- Prior art keywords
- agent
- glass fiber
- treating compound
- accounts
- glass fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明属于玻璃纤维表面处理技术领域,它是由润滑剂,分散剂,保护剂,硅烷偶联剂及保湿剂组成。它采用胺氧化物作分散剂,“乙二醇”生产厂下脚料——“多乙二醇聚合体”作保护剂,适用于直径为6~16μ中碱或无碱玻璃纤维短切丝制成的湿法毡生产需要。本产品对玻璃纤维分散效率高,保护性能好,使玻璃纤维短切丝能保存半年以上,无析碱、发脆现象。本产品可广泛用于制造屋面防水材料的基材,塑料地板墙纸的衬材和蓄电池隔离片等湿法毡产品生产上。
Description
一种湿法毡用玻璃纤维浸润剂,属于玻璃纤维表面处理领域。
湿法毡用玻璃纤维浸润剂,既不同于纺织型玻璃纤维浸润剂也不同于增强型玻璃纤维浸润剂。由于湿法毡工艺的特殊需要,它要求这种浸润剂对玻璃纤维的分散性能要好,也就是经过短切后的玻璃纤维能迅速在水中分散成单根纤维状态,以利成毡工序的需要。
现有的湿法毡用玻璃纤维浸润剂大多采用阳离子季胺盐和非离子表面活性剂这两种物质的混合物作玻璃纤维分散剂,如美国专利US.4457785,US.4536446,US.4536447,欧洲专利EP.1045555A2,但是阳离子季胺盐和非离子表面活性剂的混合物分散效果不够好,而且用量大,两种物质分别占浸润剂重量的0.1~0.5%(wt),这样大量的分散剂进入成毡系统后将影响成毡工序中粘结剂对玻璃纤维的粘结效果。此外在上述专利中均采用多元醇衍生物作保护剂,这种多元醇衍生物目前我国尚不能生产。
本发明的目的,在于针对以上存在的问题,提出用胺氧化物作湿法毡用玻璃纤维浸润剂中的分散剂,它不仅分散性能优良,而且使用量少,只占浸润剂重量的0.001~0.1%(wt)。本发明还选用国产乙二醇的副产品-乙醇残液-含4-5个乙二醇的多乙二醇聚合体作为保护剂,其对玻璃纤维保护性能优良,价格底廉且综合利用工厂下脚料。
本发明的技术解决方案是它是由润滑剂、分散剂、保护剂、硅烷偶联剂及保湿剂组成,它采用分散性能极佳的胺氧化物作为分散剂,根据湿法毡产品的不同要求可任选如下品种之一,①脂肪氨氧化物;②氢化脂肪胺氧化物;③十二烷基胺氧化物;④十六烷基胺氧化物;⑤十八烷基胺氧化物。其用量占浸润剂重量的0.001~0.1%(Wt)。采用国内“乙二醇”生产厂的副产品-乙二醇残液-含有4~5个乙二醇分子的聚合体作保护剂,其用量占浸润剂重量的0.5~5%(wt),其作用是对玻璃纤维单丝起防止磨擦损伤,保护纤维并使玻璃纤维短切丝具备较好的贮量性能:例如在贮藏期内玻璃纤维无析碱、发脆现象,能保存半年以上等。本浸润剂组成如下:(1)润滑剂占浸润剂重量0.05~0.5%(wt);(2)分散剂占浸润剂0.001~0.1%(wt);(3)保护剂占浸润剂重量0.5~5%(wt);(4)硅烷偶联剂占浸润剂重量0.05~0.5%(wt);(5)保湿剂占浸润剂重量0.01~1.0%(wt);(6)其余为蒸馏水或去离子水。本发明所提出的湿法毡用玻璃纤维浸润剂主要适用于直径为6-16μ的无碱或中碱纤维短切丝制成的湿法毡生产,它们可以用于制造屋面防水材料基材、塑料地板、墙纸的衬材及蓄电池隔离片等产品。
采用本发明制造的湿法毡玻璃纤维浸润剂,对玻璃纤维分散效率高,用量少,对成毡工序无不良影响,其保护性能优良,价格低廉,且充分利用了化工厂下脚料,变废为宝。
实施例一:配制10Kg用于直径为9-16μ玻璃纤维短切丝湿法毡生产用浸润剂。
(2)称取分散剂“十八烷基胺氧化物”16.6g(30%浓度),用10倍水稀释;
(3)称取保护剂“乙二醇残液”120g,用50倍稀醋酸溶液稀释;
(4)称取牌号为“KH-550”(化学组成为NH2-(CH2)3-Si(OC2H5)3,辽宁盖县化工厂生产)的硅烷偶联剂10g,用50倍稀醋酸溶液稀释;
(5)称取保湿剂“尿素”(化工原料)20g,用10倍水稀释;
(6)蒸馏水或去离子水:余量。
将(1)(2)(3)(4)(5)(6)混合均匀,用稀醋酸调节最终PH值为6~7。
实施例二:配制10kg用于直径为6-7μ玻璃纤维短切丝湿法毡生产用浸润剂。
(1)称取牌号为“阳离子-X”(产地同实施例一)的润滑剂25g,用50倍稀醋酸溶液稀释;
(2)称取分散剂“十八烷基胺氧化物”16.6g(30%浓度),用10倍水稀释;
(3)称取保护剂“乙二醇残液”200g,用50倍稀醋酸溶液稀释;
(4)称取牌号为“KH-550”(产地同实施例一)的硅烷偶联剂10g,用50倍稀醋酸溶液稀释;
(5)称取保湿剂“尿素”(化工原料)20g,用10倍水稀释;
(6)蒸馏水或去离子水:余量。
将(1)(2)(3)(4)(5)(6)混合均匀,用稀醋酸调节最终PH值为6~7。
Claims (2)
1、一种湿法毡用玻璃纤维浸润剂,它是由润滑剂、分散剂、保护剂、硅烷偶联剂及保湿剂组成,其润滑剂为阳离子-X即四乙烯五胺和硬脂酸反应生成的烷基咪啉唑缩合物,结构为:采用脂肪胺氧化物或氢化脂肪胺氧化物作分散剂,含有4-5个乙二醇分子聚合体作为保护剂,KH-550(化学组成为NH2-(CH2)3-Si(OC2H5)3)为硅烷偶联剂,尿素为保湿剂,本浸润剂组成如下:(1)润滑剂占浸润剂重量0.05~0.5%(wt);(2)分散剂占浸润剂重量0.001~0.1%(wt);(3)保护剂占浸润剂重量0.5~5%(wt);(4)硅烷偶联剂占浸润剂重量0.05~0.5%(wt);(5)保湿剂占浸润剂重量0.01~1.0%(wt);(6)其余为蒸馏水或去离子水。
2、根据权利要求1所述的湿法毡用玻璃纤维浸润剂的用途,其特征在于它主要适用于生产直径为6~16μ的无碱、中碱玻璃纤维短切丝的湿法毡生产。