CN101781113B - 无机发泡耐火门芯板填充材料 - Google Patents

无机发泡耐火门芯板填充材料 Download PDF

Info

Publication number
CN101781113B
CN101781113B CN2009102171244A CN200910217124A CN101781113B CN 101781113 B CN101781113 B CN 101781113B CN 2009102171244 A CN2009102171244 A CN 2009102171244A CN 200910217124 A CN200910217124 A CN 200910217124A CN 101781113 B CN101781113 B CN 101781113B
Authority
CN
China
Prior art keywords
parts
fire
foaming
foaming agent
filling material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2009102171244A
Other languages
English (en)
Other versions
CN101781113A (zh
Inventor
李同生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHOUSHAN SHENGMU THERMAL PRESERVATION BUILDING MATERIAL RESEARCH AND DEVELOPMENT CO., LTD.
Original Assignee
李同生
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 李同生 filed Critical 李同生
Priority to CN2009102171244A priority Critical patent/CN101781113B/zh
Publication of CN101781113A publication Critical patent/CN101781113A/zh
Application granted granted Critical
Publication of CN101781113B publication Critical patent/CN101781113B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种无机发泡耐火门芯板填充材料，主要由料浆经发泡剂发泡而成，所述料浆的成份及各成份的质量分数为：无水氯化镁15-25份，硫酸镁5-15份，碳纤维0.5-0.8份，防火竹签0.2-0.3份，高岭土5-10份，煤灰3-6份，轻质氧化镁45-55份，闭孔珍珠岩1.5-2.5份、水25-35份；所述发泡剂的原料及各成份的质量分数为：动物蛋白发泡剂1.5-2.5份、K12发泡剂1-2份、水25-30份。本发明的发泡材料中的骨架材料均匀分布，发泡效果高，发泡结构稳定、孔密、隔音效果好，发泡材料的防火等级高，防火能力强，无毒、无副作用，使用安全，值得推广使用。

Description

无机发泡耐火门芯板填充材料
技术领域
本发明涉及一种防火材料，具体说是一种无机发泡耐火门芯板填充材料。
背景技术
目前，国内外生产的金属防盗门一般在门芯板内填充发泡材料，以达到防火效果。现有相关技术为：将氧化镁、氢氧化镁、硫酸镁、珍珠岩等防火材料配料、搅拌后，经发泡剂发泡后填充发泡成型，不仅具有防火、防蛀、防腐、高强、质轻等优点，且生产周期短、成本低廉，已被普遍使用于各种防火领域。
如专利号为200710070830.1公开的发泡耐火填充材料，该材料制备方法是：将一定比例的氧化美、高铝酸盐耐火水泥、硫酸镁等混合加水稀释成稠状基料浆，将动物蛋白型高效泡沫发泡剂注入基料浆中，搅拌发泡成型，所有配料、发泡剂都为粉剂，一次性制备成料浆，发泡后缺少骨架支撑，导致发泡后结构稳定性差，变形损坏。
另有一种技术：将多种防火材料经松香等黏合剂混合或在高温下压制成类似防火材料。如专利号为200710191888.1公开的氧化镁生态防火板，采用松香黏合防火材料和玻璃纤维后浇注成型，其玻璃纤维起到一定稳定作用，但玻璃纤维遇火后，易产生有毒气体烟雾，对人体危害严重；采用防火材料混合后在高温下热压而成，其生产工艺复杂，成本高，质量重，不适合作为防火门芯的填充使用。
发明内容
为了解决现有技术中防火发泡材料结构不稳定、孔疏、防火等级低、隔音效果差，且使用玻璃骨架纤维易产生有毒气体，存在安全隐患等不足，本发明的目的是提供一种结构稳定、孔密、防火等级高、隔音效果好，且无毒、无副作用，使用安全的无机发泡耐火门芯板填充材料。
本发明采用的技术方案是：一种无机发泡耐火门芯板填充材料，该填充材料主要由料浆经发泡剂发泡而成，所述料浆的成份及各成份的质量分数为：无水氯化镁15-25份，硫酸镁5-15份，碳纤维0.5-0.8份，防火竹签0.2-0.3份，高岭土5-10份，煤灰3-6份，轻质氧化镁45-55份，闭孔珍珠岩1.5-2.5份、水25-35份；所述发泡剂的成份及各成份的质量分数为：动物蛋白发泡剂1.5-2.5份、K12发泡剂1-2份、水25-30份。
与采用以上技术方案，本发明的有益效果是：
1、以无水氯化镁、硫酸镁、碳纤维、防火竹签、高岭土、煤灰、轻质氧化镁、闭孔珍珠岩等防火材料制备稠状料浆，提高了发泡材料强度，碳纤维、防火竹签作为发泡材料骨架均匀分布于制得的填充材料中，提高发泡材料结构的稳定性，不易变形，发泡后强度高，且无毒、无副作用，使用安全，且防火竹签经防火油浸制，提高防火性能；
2、使用动物蛋白发泡剂、K12发泡剂组成混合发泡剂，能较好地发泡，发泡后孔密、防火等级高、隔音效果显著，防火效果好；
3、采用无水氯化镁，含镁量高达99％，不返潮，稳定性高，避免腐蚀门板内芯；采用轻质氧化镁、闭孔珍珠岩作为防火材料，能进一步提高发泡效果，防火能力强，具有较高的防火等级。
本发明采用碳纤维、防火竹签作为发泡骨架，分级制备料浆，将动物蛋白发泡剂和植物发泡剂混合作为发泡剂对料浆进行发泡，骨架混合均匀，发泡效果高，发泡结构稳定、孔密、隔音效果好，配合无水氯化镁、轻质氧化镁、闭孔珍珠岩等材料，发泡材料的防火等级高，防火能力强，使用安全，无毒、副作用，值得推广使用。
具体实施方式
下面结合实施例对本发明作进一步说明。
该无机发泡耐火门芯板填充材料，由无水氯化镁、硫酸镁、碳纤维、防火竹签、高岭土、煤灰、轻质氧化镁、闭孔珍珠岩、水混合成的料浆经动物蛋白发泡剂、K12发泡剂混合发泡剂发泡而成。
实施例一
将15Kg无水氯化镁、5Kg硫酸镁、0.5Kg碳纤维、0.2Kg防火竹签、5Kg高岭土、3Kg煤灰、45Kg轻质氧化镁、1.5Kg闭孔珍珠岩加入25Kg水中搅拌均匀成料浆；将1.5Kg动物蛋白发泡剂、1Kg的K12发泡剂投入25Kg水中搅拌均匀成发泡剂；将上述发泡剂由空气发泡机注入料浆中发泡经模具成型出耐火门芯板的防火填充材料。
实施例二
将20Kg无水氯化镁、10Kg硫酸镁、0.6Kg碳纤维、0.25Kg防火竹签、8Kg高岭土、4Kg煤灰、50Kg轻质氧化镁、2Kg闭孔珍珠岩加入30Kg水中搅拌均匀成料浆；将2Kg动物蛋白发泡剂、1.4Kg的K12发泡剂混合投入27Kg水中搅拌均匀成发泡剂；将上述发泡剂由空气发泡机注入料浆中发泡经模具成型出耐火门芯板的防火填充材料。
实施例三
将25Kg无水氯化镁、15Kg硫酸镁、0.8Kg碳纤维、0.3Kg防火竹签、10Kg高岭土、6Kg煤灰、55Kg轻质氧化镁、2.5Kg闭孔珍珠岩加入35Kg水中搅拌均匀成料浆；将2.5Kg动物蛋白发泡剂、2Kg的K12发泡剂混合投入30Kg水中搅拌均匀成发泡剂；将上述发泡剂由空气发泡机注入料浆中发泡经模具成型出耐火门芯板的防火填充材料。
上述实施例制备的无机发泡耐火门芯板填充材料孔密、防火等级高、隔音效果好，碳纤维、防火竹签骨架均匀分布使材料整体结构稳定，适合各种规格门芯板填充使用。如采用等量的蛭石代替本发明中闭孔珍珠岩作为防火材料，可达到更高的防火等级，防火性能更好。

Claims (1)

1.一种无机发泡耐火门芯板填充材料，该填充材料主要由料浆经发泡剂发泡而成，所述料浆的成份及各成份的质量分数为：无水氯化镁15-25份，硫酸镁5-15份，碳纤维0.5-0.8份，经防火油浸制的防火竹签0.2-0.3份，高岭土5-10份，煤灰3-6份，轻质氧化镁45-55份，闭孔珍珠岩1.5-2.5份、水25-35份；
所述发泡剂的成份及各成份的质量分数为：动物蛋白发泡剂1.5-2.5份、K12发泡剂1-2份、水25-30份。
CN2009102171244A 2009-12-31 2009-12-31 无机发泡耐火门芯板填充材料 Expired - Fee Related CN101781113B (zh)