CN104671822A - 一种发泡镁水泥eps粒a级不燃板及其制备方法 - Google Patents

一种发泡镁水泥eps粒a级不燃板及其制备方法 Download PDF

Info

Publication number
CN104671822A
CN104671822A CN201410707755.5A CN201410707755A CN104671822A CN 104671822 A CN104671822 A CN 104671822A CN 201410707755 A CN201410707755 A CN 201410707755A CN 104671822 A CN104671822 A CN 104671822A
Authority
CN
China
Prior art keywords
magnesium
eps
foaming
cement
stalk fibre
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410707755.5A
Other languages
English (en)
Inventor
张自喜
张竞
水保军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Xing Yintong Building Materials Science And Technology Ltd In Nanyang
Original Assignee
Xing Yintong Building Materials Science And Technology Ltd In Nanyang
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Xing Yintong Building Materials Science And Technology Ltd In Nanyang filed Critical Xing Yintong Building Materials Science And Technology Ltd In Nanyang
Priority to CN201410707755.5A priority Critical patent/CN104671822A/zh
Publication of CN104671822A publication Critical patent/CN104671822A/zh
Pending legal-status Critical Current

Abstract

本发明公开了发泡镁水泥EPS粒A级不燃板,其特征在于由下述重量份原料制备而成:氧化镁80Kg、7水硫酸镁5Kg、拉开粉500g、硬质酸钙500g、硅化秸秆纤维10Kg、羟基矿纤维20Kg、EPS颗粒18Kg、硼砂500g、纳米纤维石膏10Kg、海泡石粉20Kg、氯化镁20Kg;其中,硅化秸秆纤维由硅酸钠和氯化钠混合乳液喷涂敷于秸秆纤维表层,浸透后形成硅化秸秆纤维。其制备方法是将原料先加水搅拌,再将拉开粉加入搅拌发泡,最后加入EPS颗粒搅拌,注入模具成型,25℃常温养护。由上述原料制备的发泡镁水泥EPS粒A级不燃板,防火隔热、达到防火A2级。保温性能好,抗压强度高、粘结力强。

Description

-种发泡读水泥EPS粒A级不燃板及其制备方法
技术领域
[0001] 本发明属于建筑材料技术领域,具体设及一种新型发泡儀水泥EPS粒A级不燃板。
背景技术
[0002] 发泡水泥属于闭孔蜂窝状无机隔热材料,它突出的特点是在水泥内部形成大量封 闭泡孔,使水泥材料轻质化、保温隔热化,同时该种蜂窝状结构又使其还具备一定强度。由 于研发的不断深入,利用最新的水泥发泡技术已经可W生产出更低密度的发泡水泥产品, 如我公司普通娃酸盐水泥发泡保温板,最低密度已达到15化g/立方米,导热系数《0. 06w/ (m • K)。可见,相较于加气混凝±,发泡水泥拥有密度更低更轻质、导热系数更小使之保温 隔热性能更好,它可广泛应用于各种新建民用及公用建筑外墙、屋面及地下室顶等部位的 保温,也可用于既有建筑的节能改造工程。在材料选择上,物理法水泥发泡技术多选择氯氧 儀水泥、硫侣酸盐水泥,化学法水泥发泡技术则多选择硫侣酸盐水泥、铁侣酸盐水泥和普通 娃酸盐水泥等。水泥发泡保温板在建筑领域有非常广泛频繁的应用,水泥发泡发泡板作为 现在一种新型防火保温材料,近几年在我国被大量使用。
[0003] 发泡水泥保温板W普通娃酸盐水泥、粉煤灰、发泡剂、外加剂等为材料,经复合、揽 拌、发泡、切割等工艺制成的轻质气泡状绝热材料,其突出特征是在混凝±内部形成直径 l-3mm封闭的泡沫孔,使混凝±轻质化和具有保温隔热性能。
[0004] 1.防火隔热;发泡水泥保温板是A1级不燃无机材料,耐火极限3小时W上,具有 很好的隔热性能。
[000引 2.保温性能好;产品容积轻,体积干密度为180-25化g /m3 ;导热系数低,小于 0. 06w/m. k ;吸水率低,小于8% ;是理想的保温、隔热材料。
[0006] 3.抗压强度高、粘结力强;发泡水泥保温板抗压强度高,大于0. 5Mpa ;系统材料具 有良好的相容性,与墙体粘结强度高。
[0007] 4.隔音性能好;泡沫水泥属多密闭孔材料,因此它也是一种良好的隔音材料,能起 到良好的隔音效果,减少噪声影响,改善居住环境。
[000引 5.与建筑物同寿命;系统稳定性好,抗碳化、老化和抗冻性能高,耐候性优良,与 建筑物同寿命。目前建筑物设计寿命为50-100年,有机类材料的使用寿命大多为20-25 年,二次施工成本大,环境污染大,且给人们生产生活带来不便。
[0009] 6.施工简便、周期短;专用砂浆直接粘结,易于操作,同步施工,大大缩短施工周 期。
[0010] 7.节能、环保、利废:W水泥和粉煤灰为主要原材料,高温下不会燃烧和产生有毒 气体,无放射性,属于安全环保产品;生产、施工及使用中无有害气体排放,无矿物棉类材料 飞尘对人体的伤害,作为利废产品符合国家节能减排产业政策。但上述材料具有返面、耐水 性差、翅曲变形、硬化体胀裂和泛霜起白的现象,使其使用受到限制。
发明内容
[0011] 本发明的目的在于提供一种发泡儀水泥EPS粒A级不燃板,具有防火隔热、达到防 火A2级,抗压强度高、粘结力强。
[0012] 本发明提供一种发泡儀水泥EPS粒A级不燃板的制备方法。
[0013] 为实现上述发明目的,本发明采用的技术方案是;该发泡儀水泥EPS粒A级不燃 板,其特征在于由下述重量份原料制备而成: 氧化儀80Kg、7水硫酸儀5Kg、拉开粉500g、硬质酸巧500g、娃化枯杆纤维lOKg、哲基矿 纤维20Kg、EPS颗粒18Kg、棚砂500g、纳米纤维石膏lOKg、海泡石粉20Kg、氯化儀20Kg ; 其中,娃化枯杆纤维由娃酸钢、氯化钢、水质量百分比按2 ;1 ;50混合揽拌制成混合乳 液,喷涂敷于枯杆纤维表层,浸透后形成娃化枯杆纤维。
[0014] 该发泡儀水泥EPS粒A级不燃板的制备方法,按下述步骤制备: 1、 先把氧化儀、7水硫酸儀、硬质酸巧、娃化枯杆纤维、哲基矿纤维、棚砂、纳米纤维石 膏、海泡石粉、氯化儀加入35Kg水,揽拌5分钟混匀; 2、 再把拉开粉加入30Kg水在乳化发泡机内混合乳化发泡5分钟; 3、 将步骤2中制备的乳化发泡剂注入步骤1中,揽拌机内揽拌5分钟W上,加入EPS颗 粒,继续揽拌5分钟W上; 4、 注入模具成型,25 °C常温养护。
[0015] 采用上述技术方案的有益效果;该发泡儀水泥EI^S粒A级不燃板中,氧化儀为胶结 剂和防火剂,7水硫酸儀具有调节电子价、分子结构表面电子价作用,拉开粉为阴离子表面 活性剂,硬质酸巧憎水剂,娃化枯杆纤维、哲基矿纤维具有增加抗拉增初的作用,EPS颗粒减 小导热系数。棚砂憎水增强剂,纳米纤维石膏增强、减少导热系数。氯化儀为氧化儀结晶的 固化剂。海泡石粉利于娃巧化,形成娃巧儀分子团,增加抗压抗折强度,降低导热系数,抗泛 霜。由上述原料制备的发泡儀水泥EPS粒A级不燃板,防火隔热、达到防火A2级。保温性 能好,抗压强度高、粘结力强。可达技术指标如下:
Figure CN104671822AD00041
具体实施方式
[0016] 该发泡儀水泥EPS粒A级不燃板,其特征在于由下述重量份原料制备而成: 氧化儀80Kg、7水硫酸儀5Kg、拉开粉500g、硬质酸巧500g、娃化枯杆纤维lOKg、哲基矿 纤维20Kg、EPS颗粒18Kg、棚砂500g、纳米纤维石膏lOKg、海泡石粉20Kg、氯化儀20Kg ;
Figure CN104671822AD00042
其中,娃化枯杆纤维由娃酸钢、氯化钢、水质量百分比按2 ;1 ;50混合揽拌制成混合乳 液,喷涂敷于枯杆纤维表层,浸透后形成娃化枯杆纤维。
[0017] 该发泡儀水泥EPS粒A级不燃板的制备方法,按下述步骤制备: 1、 先把氧化儀、7水硫酸儀、硬质酸巧、娃化枯杆纤维、哲基矿纤维、棚砂、纳米纤维石 膏、海泡石粉、氯化儀加入35Kg水,揽拌5分钟混匀; 2、 再把拉开粉加入30Kg水在乳化发泡机内混合乳化发泡5分钟; 3、 将步骤2中制备的乳化发泡剂注入步骤1中,揽拌机内揽拌5分钟W上,加入EPS颗 粒,继续揽拌5分钟W上; 4、 注入模具成型,25 °C常温养护。
[001引由上述原料制备的发泡儀水泥EPS粒A级不燃板,防火隔热、达到防火A2级。保 温性能好,抗压强度高、粘结力强。

Claims (2)

1. 一种发泡镁水泥EPS粒A级不燃板,其特征在于由下述重量份原料制备而成: 氧化镁80Kg、7水硫酸镁5Kg、拉开粉500g、硬质酸钙500g、硅化秸杆纤维lOKg、羟基矿 纤维20Kg、EPS颗粒18Kg、硼砂500g、纳米纤维石膏10Kg、海泡石粉20Kg、氯化镁20Kg ;其 中,硅化秸杆纤维由硅酸钠、氯化钠、水质量百分比按2 :1 :50混合搅拌制成混合乳液,喷涂 敷于秸杆纤维表层,浸透后形成硅化秸杆纤维。
2. 如权利要求1所述的发泡镁水泥EPS粒A级不燃板的制备方法,其特征在于按下述 步骤制备: (1) 、先把氧化镁、7水硫酸镁、硬质酸钙、硅化秸杆纤维、羟基矿纤维、硼砂、纳米纤维石 膏、海泡石粉、氯化镁加入35Kg水,搅拌5分钟混匀; (2) 、再把拉开粉加入30Kg水在乳化发泡机内混合乳化发泡5分钟; (3) 、将步骤2中制备的乳化发泡剂注入步骤1中,搅拌机内搅拌5分钟以上,加入EPS 颗粒,继续搅拌5分钟以上; (4 )、注入模具成型,25 °C常温养护。
CN201410707755.5A 2014-12-01 2014-12-01 一种发泡镁水泥eps粒a级不燃板及其制备方法 Pending CN104671822A (zh)