CN101733109B - 一种铜基催化剂的制备方法 - Google Patents
一种铜基催化剂的制备方法 Download PDFInfo
- Publication number
- CN101733109B CN101733109B CN200810195138A CN200810195138A CN101733109B CN 101733109 B CN101733109 B CN 101733109B CN 200810195138 A CN200810195138 A CN 200810195138A CN 200810195138 A CN200810195138 A CN 200810195138A CN 101733109 B CN101733109 B CN 101733109B
- Authority
- CN
- China
- Prior art keywords
- catalyst
- preparation
- copper
- auxiliary agent
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
样品编号 | 比表面积(m2/g) | 孔容(ml/g) | 平均孔径(nm) | <3nm(%) | 3nm~10nm(%) | >10nm(%) |
1-1 | 87 | 0.24 | 5.4 | 9.6 | 71.7 | 18.7 |
1-2 | 97 | 0.32 | 6.7 | 7.6 | 81.4 | 11 |
2-1 | 116 | 0.31 | 5.3 | 11 | 83.9 | 5.1 |
2-2 | 115 | 0.31 | 5.4 | 12 | 81.6 | 6.4 |
3 | 99 | 0.28 | 6.3 | 10.5 | 79.8 | 9.7 |
4 | 88 | 0.26 | 6.0 | 8.1 | 80.1 | 11.8 |
5-1 | 114 | 0.33 | 5.8 | 7.1 | 81 | 11.9 |
5-2 | 105 | 0.28 | 5.3 | 15.1 | 75.1 | 9.8 |
Claims (1)