CN101719406B - 一种添加钆铁合金制备钕铁硼永磁材料的方法 - Google Patents
一种添加钆铁合金制备钕铁硼永磁材料的方法 Download PDFInfo
- Publication number
- CN101719406B CN101719406B CN2009102451917A CN200910245191A CN101719406B CN 101719406 B CN101719406 B CN 101719406B CN 2009102451917 A CN2009102451917 A CN 2009102451917A CN 200910245191 A CN200910245191 A CN 200910245191A CN 101719406 B CN101719406 B CN 101719406B
- Authority
- CN
- China
- Prior art keywords
- gadolinium
- alloy
- permanent magnet
- raw material
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
实施例 | 名义成分 | 失重(mg/cm2) |
1 | Nd12.8Dy0.7Tb0.4Fe余Co1.0Cu0.1Al0.5Zr0.06B5.95 | 1.22 |
2 | Nd12.8Dy0.5Tb0.4Gd0.2Fe余Co1.0Cu0.1Al0.5Zr0.06B5.95 | 1.06 |
3 | Nd12.8Dy0.7Tb0.2Gd0.2Fe余Co1.0Cu0.1Al0.5Zr0.06B5.95 | 1.01 |
4 | Nd12.8Dy0.5Tb0.2Gd0.4Fe余Co1.0Cu0.1Al0.5Zr0.06B5.95 | 0.80 |
Claims (8)