CN101708553A - 一种高金属感铝银浆的制造方法 - Google Patents

一种高金属感铝银浆的制造方法 Download PDF

Info

Publication number
CN101708553A
CN101708553A CN200910227182A CN200910227182A CN101708553A CN 101708553 A CN101708553 A CN 101708553A CN 200910227182 A CN200910227182 A CN 200910227182A CN 200910227182 A CN200910227182 A CN 200910227182A CN 101708553 A CN101708553 A CN 101708553A
Authority
CN
China
Prior art keywords
metal
silver paste
sense
aluminum silver
ball mill
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN200910227182A
Other languages
English (en)
Other versions
CN101708553B (zh
Inventor
夏风
曾孟金
周志良
罗林
姜小平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHANGSHA AOTE METALLIC PIGMENT Co Ltd
Original Assignee
CHANGSHA AOTE METALLIC PIGMENT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHANGSHA AOTE METALLIC PIGMENT Co Ltd filed Critical CHANGSHA AOTE METALLIC PIGMENT Co Ltd
Priority to CN2009102271825A priority Critical patent/CN101708553B/zh
Publication of CN101708553A publication Critical patent/CN101708553A/zh
Application granted granted Critical
Publication of CN101708553B publication Critical patent/CN101708553B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高金属感铝银浆的制造方法。采用直径0.4-1.0mm的高碳钢球作为球磨机磨介，将微细球形铝粉按重量比为：d50＜5μm微细球形铝粉∶有机溶剂∶润滑剂＝40∶300∶1混合均匀，置于球磨机内球磨25-50小时后出料，压滤，滤液回到球磨工序循环使用；滤饼进入筛分分级工序，过500目筛的物料进入湿式旋流分级工序，压滤，滤液回到筛分工序循环使用；滤饼进入捏合工序进行表面处理，包装即成为高金属感铝银浆产品。本发明由于采用小钢球长时间对微细球形铝粉进行温和转形作业，球磨用油和筛分用油分离使用，过500目物料湿式分级，使片状铝颜料颗粒的表面平滑光洁，粒度分布窄，确保了铝银浆产品的高金属感。

Description

一种高金属感铝银浆的制造方法
技术领域
本发明涉及一种精细无机化工领域中铝颜料的制备方法；具体地说是一种湿法生产铝银浆的制造方法。
背景技术
铝颜料是用纯铝金属生产的，铝颜料粒子实际上是表面包覆有脂肪酸薄膜的具有颜料特性的片状物，这种形态使其具有优越的耐腐蚀性能和装饰性能，应用非常广泛。现有铝颜料的制造方法主要包括干法生产和湿法生产；现有湿法生产包括(1)将铝粉与有机溶剂、润滑剂等按一定比例混合后置于球磨机中研磨；(2)筛分后压滤制成滤饼，(3)经捏合表面处理成为铝银浆；但是现有湿法生产是用1.5mm以上的大钢球，球磨15-25h将粗铝粉破碎成鳞片状，经筛分，过500目物料后直接压滤，滤液返回球磨工序，滤饼经过捏合表面处理，包装即为铝银浆产品。其产品颗粒形状不规则，表面光滑度差，粒度分布宽，致使金属质感差。
发明内容
本发明的目的在于克服已有湿法生产铝银浆的不足，提供了一种产品颗粒形状规则、表面平滑光洁、粒度分布窄、并具有高金属质感的铝银浆的制备方法。
本发明包括以下步骤：
(1)采用直径0.4-1.0mm的高碳钢球作为球磨机磨介，将微细球形铝粉按以下重量比混合均匀：d50＜5μm微细球形铝粉∶有机溶剂∶润滑剂＝40∶300∶1，置于球磨机内球磨25-50小时后出料，压滤，滤液回到球磨工序循环使用；
(2)滤饼进入筛分分级工序，过500目筛的物料进入湿式旋流分级工序，压滤，滤液回到筛分工序循环使用；
(3)滤饼进入捏合工序进行表面处理，包装即成为高金属感铝银浆产品。
所述微细球形铝粉是氮气雾化微细球形铝粉。
所述润滑剂为油酸，芥酸类不饱和脂肪酸。
所述有机溶剂为200#溶剂油或D50溶剂油或D80溶剂油或S150溶剂油。
所述湿式旋流分级试用小直径水力旋流器。
所述球磨机为卧式球磨机。
本发明由于采用小钢球长时间对微细球形铝粉进行温和转形作业，球磨工序用油和筛分工序用油分离使用，过500目物料湿式分级，使片状铝颜料颗粒的表面平滑光洁，粒度分布窄，确保了铝银浆产品的高金属感。
具体实施方式
实施例1：
在
Figure G2009102271825D0000021
卧式球磨机内装入0.5mm钢球2000kg，加入200#溶剂油300kg，D50为4.6μm的氮气雾化微细球形铝粉40kg，油酸1kg，球磨48h，出料，压滤；滤液返回球磨工序；滤饼稀释，筛分，过500目物料经湿式离心分级，压滤，滤液返回筛分工序；滤饼经过捏合表面处理，包装即为高金属感铝银浆产品。
实施例2：
在
Figure G2009102271825D0000022
卧式球磨机中装入0.8mm钢球2000kg，加入200#溶剂油300kg，D50为4.6μm的氮气雾化微细球形铝粉40kg，油酸1kg，球磨38h，出料，压滤；滤液返回球磨工序；滤饼稀释，筛分，过500目物料经湿式离心分级，压滤，滤液返回筛分工序；滤饼经过捏合表面处理，包装即为高金属感铝银浆产品。
实施例3：
在
Figure G2009102271825D0000023
卧式球磨机中装入1.0mm钢球2000kg，加入200#溶剂油300kg，D50为4.6μm的氮气雾化微细球形铝粉40kg，油酸1kg，球磨28h，出料，压滤；滤液返回球磨工序；滤饼稀释，筛分，过500目物料经湿式离心分级，压滤，滤液返回筛分工序。滤饼经过捏合表面处理，包装即为高金属感铝银浆产品。
实施例4：
在卧式球磨机中装入0.5mm钢球2000kg，加入200#溶剂油300kg，D50为4.6μm的氮气雾化微细球形铝粉40kg，芥酸1kg，球磨48h，出料，压滤；滤液返回球磨工序；滤饼稀释，筛分，过500目物料经湿式离心分级，压滤，滤液返回筛分工序。滤饼经过捏合表面处理，包装即为高金属感铝银浆产品。
对比实施例：
在
Figure G2009102271825D0000031
卧式球磨机中装入1.5mm钢球2000kg，加入200#溶剂油300kg，D50为4.6μm的氮气雾化微细球形铝粉40kg，油酸1kg，球磨24h，出料，筛分，过500目物料压滤，滤液返回球磨工序。滤饼经过捏合表面处理，包装即为铝银浆产品。
实施例和对比实施例产品性能指标的对比：
将实施例和对比实施例所获得的铝银浆产品进行粒度分布测试和显微镜观察，并将铝银浆产品用市售的稀释剂和光油(树脂)按照1∶2∶8配成金属涂料，用湿膜制备器制成对比漆膜样板。性能指标对比如表1所示：
表1  性能指标对比表
  产品粒度分布   显微镜观察   漆膜
实施例1 D102.3；D508.2；D9014.8 形状规则，表面光滑，金属感最强   漆膜平整光滑，遮盖力好，金属感强烈，L值146
  产品粒度分布   显微镜观察   漆膜
实施例2 D101.8；D508.6；D9015.6 形状规则，表面光滑，金属感强   漆膜平整光滑，遮盖力好，金属感强烈，L值138
实施例3 D101.3；D508.1；D9016.8 形状规则，表面光滑，金属感较强   漆膜平整光滑，遮盖力好，金属感强烈，L值136
实施例4 D102.2；D508.3；D9014.9 形状规则，表面光滑，金属感强   漆膜平整光滑，遮盖力好，金属感强烈，L值140
对比实施例   D102.3；D508.2；D9014.8 有大量小碎片，金属感弱   漆膜平整光滑，遮盖力一般，金属感弱，L值98

Claims (6)

1.一种高金属感铝银浆的制造方法，其特征在于，包括以下步骤：
(1)采用直径0.4-1.0mm的高碳钢球作为球磨机磨介，将微细球形铝粉按以下重量比混合均匀：d50＜5μm微细球形铝粉∶有机溶剂∶润滑剂＝40∶300∶1，置于球磨机内球磨25-50小时后出料，压滤，滤液回到球磨工序循环使用；
(2)滤饼进入筛分分级工序，过500目筛的物料进入湿式旋流分级工序，压滤，滤液回到筛分工序循环使用；
(3)滤饼进入捏合工序进行表面处理，包装即成为高金属感铝银浆产品。
2.根据权利要求1所述的高金属感铝银浆的制造方法，其特征在于，所述微细球形铝粉是氮气雾化微细球形铝粉。
3.根据权利要求1所述的高金属感铝银浆的制造方法，其特征在于，所述润滑剂为油酸，芥酸类不饱和脂肪酸。
4.根据权利要求1所述的高金属感铝银浆的制造方法，其特征在于，所述有机溶剂为200#溶剂油或D50溶剂油或D80溶剂油或S150溶剂油。
5.根据权利要求1所述的高金属感铝银浆的制造方法，其特征在于，所述湿式旋流分级试用小直径水力旋流器。
6.根据权利要求1所述的高金属感铝银浆的制造方法，其特征在于，所述球磨机为卧式球磨机。
CN2009102271825A 2009-12-11 2009-12-11 一种高金属感铝银浆的制造方法 Active CN101708553B (zh)