CN101632154B - 利用一步金属有机化学气相沉积工艺制备ⅰ-ⅲ-ⅵ2化合物薄膜的方法 - Google Patents

利用一步金属有机化学气相沉积工艺制备ⅰ-ⅲ-ⅵ2化合物薄膜的方法 Download PDF

Info

Publication number
CN101632154B
CN101632154B CN2008800076821A CN200880007682A CN101632154B CN 101632154 B CN101632154 B CN 101632154B CN 2008800076821 A CN2008800076821 A CN 2008800076821A CN 200880007682 A CN200880007682 A CN 200880007682A CN 101632154 B CN101632154 B CN 101632154B
Authority
CN
China
Prior art keywords
group
iii
elements
precursor
precursor containing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008800076821A
Other languages
English (en)
Chinese (zh)
Other versions
CN101632154A (zh
Inventor
崔寅焕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
In-Solar Tech Co Ltd
Original Assignee
In-Solar Tech Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by In-Solar Tech Co Ltd filed Critical In-Solar Tech Co Ltd
Publication of CN101632154A publication Critical patent/CN101632154A/zh
Application granted granted Critical
Publication of CN101632154B publication Critical patent/CN101632154B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B29/00—Single crystals or homogeneous polycrystalline material with defined structure characterised by the material or by their shape
    • C30B29/10—Inorganic compounds or compositions
    • C30B29/46—Sulfur-, selenium- or tellurium-containing compounds
    • C—CHEMISTRY; METALLURGY
    • C30—CRYSTAL GROWTH
    • C30B—SINGLE-CRYSTAL GROWTH; UNIDIRECTIONAL SOLIDIFICATION OF EUTECTIC MATERIAL OR UNIDIRECTIONAL DEMIXING OF EUTECTOID MATERIAL; REFINING BY ZONE-MELTING OF MATERIAL; PRODUCTION OF A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; SINGLE CRYSTALS OR HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; AFTER-TREATMENT OF SINGLE CRYSTALS OR A HOMOGENEOUS POLYCRYSTALLINE MATERIAL WITH DEFINED STRUCTURE; APPARATUS THEREFOR
    • C30B25/00—Single-crystal growth by chemical reaction of reactive gases, e.g. chemical vapour-deposition growth
    • C30B25/02—Epitaxial-layer growth
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
    • H10F77/00—Constructional details of devices covered by this subclass
    • H10F77/10—Semiconductor bodies
    • H10F77/12—Active materials
    • H10F77/126—Active materials comprising only Group I-III-VI chalcopyrite materials, e.g. CuInSe2, CuGaSe2 or CuInGaSe2 [CIGS]
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
    • H10K99/00—Subject matter not provided for in other groups of this subclass
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/24—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials using chemical vapour deposition [CVD]
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/29—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials characterised by the substrates
    • H10P14/2901—Materials
    • H10P14/2922—Materials being non-crystalline insulating materials, e.g. glass or polymers
    • H—ELECTRICITY
    • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
    • H10P14/00—Formation of materials, e.g. in the shape of layers or pillars
    • H10P14/20—Formation of materials, e.g. in the shape of layers or pillars of semiconductor materials
    • H10P14/34—Deposited materials, e.g. layers
    • H10P14/3402—Deposited materials, e.g. layers characterised by the chemical composition
    • H10P14/3436—Deposited materials, e.g. layers characterised by the chemical composition being chalcogenide semiconductor materials not being oxides, e.g. ternary compounds
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E10/00—Energy generation through renewable energy sources
    • Y02E10/50—Photovoltaic [PV] energy
    • Y02E10/541—CuInSe2 material PV cells
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Photovoltaic Devices (AREA)
  • Chemical Vapour Deposition (AREA)
CN2008800076821A 2007-03-13 2008-02-22 利用一步金属有机化学气相沉积工艺制备ⅰ-ⅲ-ⅵ2化合物薄膜的方法 Expired - Fee Related CN101632154B (zh)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
KR10-2007-0024682 2007-03-13
KR1020070024682 2007-03-13
KR1020070024682A KR100857227B1 (ko) 2007-03-13 2007-03-13 단일 유기금속 화학기상 증착 공정에 의한 ⅰ-ⅲ-ⅵ2화합물 박막의 제조방법
PCT/KR2008/001041 WO2008111738A1 (en) 2007-03-13 2008-02-22 Method for fabricating 1-3-6 2 compound thin film using single metal-organic chemical vapor deposition process

Publications (2)

Publication Number Publication Date
CN101632154A CN101632154A (zh) 2010-01-20
CN101632154B true CN101632154B (zh) 2011-11-02

Family

ID=39759657

Family Applications (1)

Application Number Title Priority Date Filing Date
CN2008800076821A Expired - Fee Related CN101632154B (zh) 2007-03-13 2008-02-22 利用一步金属有机化学气相沉积工艺制备ⅰ-ⅲ-ⅵ2化合物薄膜的方法

Country Status (6)

Country Link
US (1) US20100098856A1 (https=)
EP (1) EP2126964A1 (https=)
JP (1) JP2010530474A (https=)
KR (1) KR100857227B1 (https=)
CN (1) CN101632154B (https=)
WO (1) WO2008111738A1 (https=)

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR100982475B1 (ko) * 2008-09-29 2010-09-15 주식회사 쎄믹스 광 흡수용 화합물 박막 제조방법
TWI373851B (en) * 2008-11-25 2012-10-01 Nexpower Technology Corp Stacked-layered thin film solar cell and manufacturing method thereof
KR101071545B1 (ko) * 2008-12-30 2011-10-11 주식회사 메카로닉스 Ｃｉｇｓ 박막 제조방법
US20120319244A1 (en) * 2010-01-29 2012-12-20 Kyocera Corporation Method for manufacturing semiconductor layer, method for manufacturing photoelectric conversion device, and semiconductor layer forming solution
CN102634776B (zh) * 2012-05-03 2014-03-12 徐明生 一种连续制备二维纳米薄膜的化学气相沉积设备
CN108541349B (zh) * 2016-01-13 2021-06-22 马卡罗能源有限公司 包括cigs光吸收层的太阳能电池及其制造方法
JP6842035B2 (ja) * 2016-12-19 2021-03-17 富士通株式会社 層状カルコゲナイド膜の形成方法及び半導体装置の製造方法
JP7070826B2 (ja) * 2017-02-28 2022-05-18 国立大学法人東海国立大学機構 半導体ナノ粒子およびその製造方法ならびに発光デバイス
WO2018159699A1 (ja) * 2017-02-28 2018-09-07 国立大学法人名古屋大学 半導体ナノ粒子およびその製造方法ならびに発光デバイス
US20200082995A1 (en) * 2018-09-06 2020-03-12 Ascent Solar Technologies, Inc. Chalcopyrite-perovskite pn-junction thin-film photovoltaic device

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6992202B1 (en) * 2002-10-31 2006-01-31 Ohio Aerospace Institute Single-source precursors for ternary chalcopyrite materials, and methods of making and using the same
CN1826697A (zh) * 2003-07-26 2006-08-30 银太阳科技发展公司 太阳能电池吸收层的制造方法
EP1836733A1 (en) * 2005-01-12 2007-09-26 In-Solar-Tech Co., Ltd. Optical absorber layers for solar cell and method of manufacturing the same

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2000144014A (ja) * 1998-11-06 2000-05-26 Asahi Chem Ind Co Ltd 化合物半導体薄膜の形成方法
EP1649520A4 (en) * 2003-07-26 2009-03-11 In Solar Tech Co Ltd PROCESS FOR PREPARING ABSORBENT LAYERS FOR A SOLAR CELL
KR100810730B1 (ko) * 2006-06-19 2008-03-07 (주)인솔라텍 태양전지용 광흡수층의 제조방법

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6992202B1 (en) * 2002-10-31 2006-01-31 Ohio Aerospace Institute Single-source precursors for ternary chalcopyrite materials, and methods of making and using the same
CN1826697A (zh) * 2003-07-26 2006-08-30 银太阳科技发展公司 太阳能电池吸收层的制造方法
EP1836733A1 (en) * 2005-01-12 2007-09-26 In-Solar-Tech Co., Ltd. Optical absorber layers for solar cell and method of manufacturing the same

Also Published As

Publication number Publication date
EP2126964A1 (en) 2009-12-02
CN101632154A (zh) 2010-01-20
WO2008111738A1 (en) 2008-09-18
KR100857227B1 (ko) 2008-09-05
JP2010530474A (ja) 2010-09-09
US20100098856A1 (en) 2010-04-22

Similar Documents

Publication Publication Date Title
CN101632154B (zh) 利用一步金属有机化学气相沉积工艺制备ⅰ-ⅲ-ⅵ2化合物薄膜的方法
US7811633B2 (en) Optical absorber layers for solar cell and method of manufacturing the same
CN101473449B (zh) 用于制备用作太阳能电池光吸收层的方法
US8894826B2 (en) Copper indium gallium selenide (CIGS) thin films with composition controlled by co-sputtering
CN102893371B (zh) 基于硫属化物的材料及制备这种材料的改进方法
KR101094326B1 (ko) 태양전지용 Ｃｕ－Ｉｎ－Ｚｎ－Ｓｎ－（Ｓｅ，Ｓ）계 박막 및 이의 제조방법
US20100248417A1 (en) Method for producing chalcopyrite-type solar cell
KR20130016528A (ko) 태양전지용 ＣＺＴ(Ｓ,Ｓｅ)계 박막의 제조방법 및 그 방법에 의해 제조된 ＣＺＴ(Ｓ,Ｓｅ)계 박막
CN108401469B (zh) 太阳能电池及其制造方法
CN102473747A (zh) 化合物薄膜太阳能电池
Regmi et al. Tailoring selenization for superior thin film and photovoltaic performance in Sb₂Se₃ solar cells
US8846438B2 (en) Method for indium sputtering and for forming chalcopyrite-based solar cell absorber layers
WO2013099180A1 (en) Photovoltaic conversion device and method of manufacturing photovoltaic conversion material
US8632851B1 (en) Method of forming an I-II-VI2 compound semiconductor thin film of chalcopyrite structure
KR101388458B1 (ko) 급속 열처리 공정을 사용한 ｃｉｇｓ 박막의 제조방법
KR101761565B1 (ko) 태양 전지 및 이의 제조 방법
Lee et al. Effects of Cu/In compositional ratio on the characteristics of CuInS2 absorber layers prepared by sulfurization of metallic precursors
US20150263210A1 (en) Cis/cgs/cigs thin-film manufacturing method and solar cell manufactured by using the same
US9437761B2 (en) Method of forming chalcopyrite light-absorbing layer
KR101463327B1 (ko) 스프레이법을 이용한 화합물 태양전지용 ＣｕＩｎＳｅ₂박막의 제조방법
Yamaguchi et al. NaF Addition to Cu2ZnSnSe4 Thin films prepared by sequential evaporation from compound
Martin et al. Characterization of chalcopyrite Cu (In, Al) Se2 thin films grown by selenization of evaporated precursors.
Miyazaki et al. Growth of high‐quality CuGaSe2 thin films using ionized Ga precursor
KR20110030870A (ko) 태양 전지용 광흡수층의 제조 방법

Legal Events

Date Code Title Description
C06 Publication
PB01 Publication
C10 Entry into substantive examination
SE01 Entry into force of request for substantive examination
C14 Grant of patent or utility model
GR01 Patent grant
C17 Cessation of patent right
CF01 Termination of patent right due to non-payment of annual fee

Granted publication date: 20111102

Termination date: 20130222