CN101538466A - 一种稀土离子掺杂的钼酸盐发光粉及其制备方法 - Google Patents
一种稀土离子掺杂的钼酸盐发光粉及其制备方法 Download PDFInfo
- Publication number
- CN101538466A CN101538466A CN200910071915A CN200910071915A CN101538466A CN 101538466 A CN101538466 A CN 101538466A CN 200910071915 A CN200910071915 A CN 200910071915A CN 200910071915 A CN200910071915 A CN 200910071915A CN 101538466 A CN101538466 A CN 101538466A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- earth ion
- luminescent powder
- nitric acid
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供的是一种稀土离子掺杂的钼酸盐发光粉及其制备方法。将Ln2O3(Eu2O3或Tb4O7)在搅拌的条件下溶解在稀硝酸中,蒸发掉过量硝酸得到Ln(NO3)3晶体粉末;再把得到的Ln(NO3)3晶体粉末按一定化学计量比(Ln的摩尔浓度占A(NO3)2中A浓度的5%)在搅拌的条件下添加到乙二醇EG和水的体积比=37/3的混合溶液中;然后将含有与A等摩尔数的(NH4)6Mo7O24·4H2O添加到上面的溶液中;混合液搅拌1小时后转移到密闭的聚四氟乙烯高压反应釜中,反应釜静止在160℃加热反应8小时;待反应釜自然冷却到室温,得到的最终产品通过离心分离用无水乙醇和蒸馏水洗涤数次;最后,获得的产品在80℃真空中干燥24小时,就得化学表达式为AMoO4:Ln的稀土离子掺杂的钼酸盐发光粉。
Description
(一)技术领域
本发明涉及的是一种稀土离子掺杂的钼酸盐发光粉。本发明也涉及一种稀土离子掺杂的钼酸盐发光粉的制备方法。。
(二)背景技术
与金属钼酸盐相关的较大的二价阳离子(AMoO4,离子半径>0.099nm,A=Ca,Ba,Sr)主要存在于白钨矿型四面体结构中,此结构中钼原子采取四面体配位[参考文献1]。具有发光行为和结构特性的金属钼酸盐如SrMoO4、BaMoO4在光电装置、固体激光器、光致发光器件、闪烁体与声光过滤器等方面存在潜在的应用前景,因此已经获得了更多关注[2,3]。各种不同的合成方法也应运而生,如固相法、溶胶-凝胶法、反胶束法和溶剂热法。在所有这些方法中,由表面活性剂辅助的、微乳状液调节的溶剂热过程已经被证明是一种高效的合成无机材料的方法,这种方法合成的无机材料粒子具有令人感兴趣的形态和规则的尺寸。然而,在反胶束和微乳状液过程中,模板或基底的引用通常带来各种各样的杂质,这即增加了产物后续处理的花费又导致难以扩大生产。因此,探寻温和可控且不使用表面活性剂的无机材料合成方法前景广阔。
此外,已经报道的许多稀土离子(Eu3+,Tb3+)掺杂的与白钨矿有关的钼酸盐存在宽阔且强烈的吸收峰,这些吸收峰是在近紫外区由氧到金属的电荷转移(CT)引起的[4,5]。CaMoO4:Eu3+能够被近紫外区发光二极管(LEDs)(380-410nm)有效的激发并发射明亮的红色荧光(5D0-7F2)。因此,稀土离子掺杂的钼酸盐材料将会成为LED的潜在应用材料。
(三)发明内容
本发明的目的在于提供一种稀土离子掺杂的钼酸盐发光粉;本发明的目的还在于提供一种探寻温和可控的制备稀土离子掺杂的钼酸盐发光粉的方法。
本发明的目的是这样实现的:
本发明的稀土离子掺杂的钼酸盐发光粉的化学表达式为:
AMoO4:Ln
其中A为Sr2+或Ba2+;Ln为Eu3+或Tb3+;AMoO4:Ln中Ln的摩尔浓度占A浓度的5%。
本发明的稀土离子掺杂的钼酸盐发光粉是采用这样的方法来制备的:
首先,将Ln2O3、其中Ln为Eu3+或Tb3+,在搅拌的条件下溶解在稀硝酸中,蒸发掉过量硝酸得到Ln(NO3)3晶体粉末;再把得到的Ln(NO3)3晶体粉末和按化学计量比(Ln的摩尔浓度占A(NO3)2中A浓度的5%)在搅拌的条件下添加到乙二醇和水的体积比=37/3的混合溶液中;然后将含有与A等摩尔数的(NH4)6Mo7O24·4H2O的溶液添加到上面的溶液中;混合液搅拌1小时后转移到密闭的聚四氟乙烯高压反应釜中,反应釜静止在160℃加热反应8小时;待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次;最后,获得的产品在80℃真空中干燥24小时,就得到了稀土离子掺杂的钼酸盐发光粉。
金属钼酸盐具有典型的白钨矿结构,属于四方晶系。其中,Mo6+位于四面体中心,形成MoO4 2-阴离子配合物;Ca2+与8个近邻氧配位,形成一个畸变的立方体。受到激发时,MoO4 2-配阴离子中O2-离子2p轨道中的1个电子跃迁到Mo6+离子的4d空轨道,形成Mo5+的4s24p64d1的激发态构型,随后又回到基态,产生跃迁辐射。金属钼酸盐由于其独特的结构与光学性质,已经在发光,微波,白光二极管及激光材料等领域引起广泛的关注。已经报道多种合成方法,如高温固相法、溶胶-凝胶法、反胶束法和溶剂热法等。在所有这些方法中,高温固相法一般需1000℃以上高温,溶胶-凝胶法合成的样品往往具有不规则的表面形貌,而表面活性剂辅助的溶剂热过程虽然可以获得具有规整形貌和尺寸的纳米材料。然而,模板或基底的使有所带来的杂质由于增加了后续处理的花费而导致难以扩大生产。本发明采用一种温和的溶剂热方法来合成稀土离子掺杂的钼酸盐发光粉,此溶剂热法利用乙二醇作为反应介质且不作进一步热处理。这种不使用模版或基底的合成方法,即减少了产物后续处理的花费又利于扩大生产,且产物具有均一的形貌和尺寸。
(四)附图说明
图1是160℃反应8小时制备的SrMoO4:Eu3+(a)、SrMoO4:Tb3+(b)样品和SrMoO4标准数据(JCPDS 08-0482)(c)XRD图。
图2为160℃反应8小时制备的BaMoO4:Eu3+(a)、BaMoO4:Tb3+(b)样品和BaMoO4标准数据(JCPDS 29-0193)(c)XRD图。
图3分别给出了160℃反应8小时制备的SrMoO4:Eu3+和SrMoO4:Tb3+样品的SEM照片(图3(a)和图3(b))和EDS图(图3(c)和图3(d)),以及SrMoO4:Eu3+样品的TEM照片(图3(e))和HRTEM照片(图3(f))。
图4分别给出了160℃反应8小时制备的BaMoO4:Eu3+和BaMoO4:Tb3+样品的SEM照片(图4(a)和图4(b))和EDS图(图4(c)和图4(d)),以及BaMoO4:Eu3+样品的TEM照片(图4(e))和HRTEM照片(图4(f))。
图5给出了在160℃下反应8h制备的SrMoO4:Eu3+和BaMoO4:Eu3+粒子的FT-IR光谱。
图6分别给出了SrMoO4:Eu3+(图6(a)),BaMoO4:Eu3+(图6(b)),SrMoO4:Tb3+(图6(c))和BaMoO4:Tb3+(图6(d))的激发和发射光谱及相应的紫外灯下的照片(254nm激发)。
图7的表1是合成的SrMoO4:Eu3+,SrMoO4:Tb3+,BaMoO4:Eu3+和BaMoO4:Tb3+样品的晶胞参数和偏差值表。
(五)具体实施方式
下面举例对本发明做更详细地描述:
具体实施方式1:SrMoO4:Eu3+发光粉的合成
实验中所用化学试剂皆为分析纯,且没有经过进一步的提纯。在SrMoO4:Eu3+中Eu3+的摩尔浓度占Sr3+浓度的5%。首先,0.0088g(0.025mmol)的Eu2O3在搅拌的条件下溶解在稀硝酸中。蒸发掉过量的硝酸直到溶液的pH值达到2~3。得到的Eu(NO3)3晶体粉末和0.201g(0.95mmol)Sr(NO3)2在搅拌中添加到20毫升EG和水(体积比=37/3)的混合溶液中。然后将另外20毫升含有0.176g(NH4)6Mo7O24·4H2O的溶液加入到上面的溶液中。混合液搅拌1小时后转移到50毫升密闭的聚四氟乙烯高压反应釜中,反应釜静止的在160℃加热反应8h。待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次。最后,获得的样品在80℃真空中干燥24小时,就获得了Eu3+掺杂SrMoO4的最终样品,并被标记为SrMoO4:Eu3+。
具体实施方式2:SrMoO4:Tb3+发光粉的合成
在SrMoO4:Tb3+中Tb3+的摩尔浓度占Sr3+浓度的5%。首先,0.0093g(0.0125mmol)的Tb4O7在搅拌的条件下溶解在稀硝酸中。蒸发掉过量的硝酸直到溶液的pH值达到2~3。得到的Tb(NO3)3晶体粉末和0.201g(0.95mmol)Sr(NO3)2在搅拌中添加到20毫升EG和水(体积比=37/3)的混合溶液中。然后将另外20毫升含有0.176g(NH4)6Mo7O24·4H2O的溶液加入到上面的溶液中。混合液搅拌1小时后转移到50毫升密闭的聚四氟乙烯高压反应釜中,反应釜静止的160℃加热反应8h。待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次。最后,获得的样品在80℃真空中干燥24小时,就获得了Tb3+掺杂SrMoO4的最终样品,并被标记为SrMoO4:Tb3+。
具体实施方式3:BaMoO4:Eu3+发光粉的合成
在BaMoO4:Eu3+中Eu3+的摩尔浓度占Ba3+浓度的5%。首先,0.0088g(0.025mmol)的Eu2O3在搅拌的条件下溶解在稀硝酸中。蒸发掉过量的硝酸直到溶液的pH值达到2~3。得到的Eu(NO3)3晶体粉末和0.248g(0.95mmol)Ba(NO3)2在搅拌中添加到20毫升EG和水(体积比=37/3)的混合溶液中。然后将另外20毫升含有0.176g(NH4)6Mo7O24·4H2O的溶液加入到上面的溶液中。混合液搅拌1小时后转移到50毫升密闭的聚四氟乙烯高压反应釜中,反应釜静止160℃加热反应8h。待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次。最后,获得的样品在80℃真空中干燥24小时,就获得了Eu3+掺杂BaMoO4的最终样品,并被标记为BaMoO4:Eu3+。
具体实施方式4:BaMoO4:Tb3+发光粉的合成
在Ba MoO4:Tb3+中Tb3+的摩尔浓度占Ba3+浓度的5%。首先,0.0093g(0.0125mmol)的Tb4O7在搅拌的条件下溶解在稀硝酸中。蒸发掉过量的硝酸直到溶液的pH值达到2~3。得到的Tb(NO3)3晶体粉末和0.248g(0.95mmol)Ba(NO3)2在搅拌中添加到20毫升EG和水(体积比=37/3)的混合溶液中。然后将另外20毫升含有0.176g(NH4)6Mo7O24·4H2O的溶液加入到上面的溶液中。混合液搅拌1小时后转移到50毫升密闭的聚四氟乙烯高压反应釜中,反应釜静止在160℃加热反应8h。待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次。最后,获得的样品在80℃真空中干燥24小时,就获得了Tb3+掺杂BaMoO4的最终样品,并被标记为BaMoO4:Tb3+。
Claims (2)
1、一种稀土离子掺杂的钼酸盐发光粉,其特征是:其化学表达式为:
AMoO4:Ln
其中A为Sr2+或Ba2+;Ln为Eu3+或Tb3+;AMoO4:Ln中Ln的摩尔浓度占A浓度的5%。
2、一种稀土离子掺杂的钼酸盐发光粉的制备方法,其特征是:
首先,将Ln2O3、其中Ln为Eu3+或Tb3+,在搅拌的条件下溶解在稀硝酸中,蒸发掉过量硝酸得到Ln(NO3)3晶体粉末;再把得到的Ln(NO3)3晶体粉末和按化学计量比、即Ln的摩尔浓度占A(NO3)2中A浓度的5%,在搅拌的条件下添加到乙二醇和水的体积比=37/3的混合溶液中;然后将含有与A等摩尔数的(NH4)6Mo7O24·4H2O添加到上面的溶液中;混合液搅拌1小时后转移到密闭的聚四氟乙烯高压反应釜中,反应釜静止在160℃加热反应8小时;待反应釜自然冷却到室温,得到的最终产品通过离心分离用乙醇和蒸馏水洗涤数次;最后,获得的产品在80℃真空中干燥24小时,就得到了稀土离子掺杂的钼酸盐发光粉。