CN101481568A - 一种环保防冻真石漆及其制备方法 - Google Patents

一种环保防冻真石漆及其制备方法 Download PDF

Info

Publication number
CN101481568A
CN101481568A CNA2008100023493A CN200810002349A CN101481568A CN 101481568 A CN101481568 A CN 101481568A CN A2008100023493 A CNA2008100023493 A CN A2008100023493A CN 200810002349 A CN200810002349 A CN 200810002349A CN 101481568 A CN101481568 A CN 101481568A
Authority
CN
China
Prior art keywords
stone
defoamer
paint
environment friendly
orders
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2008100023493A
Other languages
English (en)
Inventor
徐军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jingweihongyuan Industry & Trade Co Ltd Beijing
Original Assignee
Jingweihongyuan Industry & Trade Co Ltd Beijing
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jingweihongyuan Industry & Trade Co Ltd Beijing filed Critical Jingweihongyuan Industry & Trade Co Ltd Beijing
Priority to CNA2008100023493A priority Critical patent/CN101481568A/zh
Publication of CN101481568A publication Critical patent/CN101481568A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种环保防冻真石漆,其包含下列重量份的原料组分:1~4%浓度纤维素水溶液0.1~5、乙二醇0.8~1.2、41~80目彩砂50~70、81~120目彩砂5~25,、KE025丙烯酸乳液17~23、醇酯-12助剂0.6~0.9、消泡剂0.02~0.06、增稠剂0.01-0.1和中和剂0.02~0.06。同时本发明也公开了该真石漆的制备方法。本发明的真石漆具有环保和防冻性能,为适应冬季施工特别是我国北方地区冬季施工的各种苛刻条件,提供有力保障。

Description

一种环保防冻真石漆及其制备方法
技术领域
本发明涉及砂壁状建筑用涂料领域,特别是涉及一种环保防冻真石漆。同时,本发明也涉及该真石漆的制备方法。
背景技术
目前市场上使用的水性真石漆使用时均要求施工条件在0℃以上或者5℃以上,但是在人们的实际生产建设中往往会出现冬季进入装饰工序的现象,普通的水性真石漆在这样的条件下施工容易出现:破乳、粉化、发花、变色甚至来年出现脱落等不良现象。传统的防冻真石漆一般是加入大量乙二醇类助剂,这往往会造成干燥速度太慢的缺点,而且成本高,VOC人为增高,导致环保性能降低。
因此,提供一种既环保又防冻的水性真石漆,一直是业界研究开发的课题。
发明内容
本发明针的目的是提供一种环保防冻真石漆,进一步提高该类功能型涂料所具有的功能性和绿色环保性能,从而使该类真石漆的性价比得到较大改善,继而为适应冬季施工特别是我国北方地区冬季施工的各种苛刻条件,提供有力保障。
为了达到上述目的,本发明提供了下述的技术方案:
一种环保防冻真石漆,其包含下列重量份的原料组分:1~4% 浓度纤维素水溶液0.1~5、乙二醇 0.8~1.2、41~80 目彩砂 50~70、81~120 目彩砂 5~25、KE025丙烯酸乳液 17~23、醇酯-12助剂 0.6~0.9、消泡剂 0.02~0.06、增稠剂 0.01-0.1和中和剂0.02~0.06。
优选地,本发明的环保防冻真石漆,其还包含至多5份重量的20~40目彩砂。
优选地,本发明的环保防冻真石漆,其还包含0.02~0.1份重量的防腐剂。
优选地,本发明的环保防冻真石漆,其中所述的纤维素是市售的HEC羟乙基纤维素、所述消泡剂是市售的SP202消泡剂、所述增稠剂是市售的ASE60增稠剂,所述防腐剂是市售的HY608防腐剂,所述中和剂是市售的HY96中和剂。
本发明还提供了一种制备环保防冻真石漆的方法,该方法包括下列步骤:
a.称取下列重量份的原料组分:1~4% 浓度纤维素水溶液 0.1~5、乙二醇0.8~1.2、20~40 目彩砂 0~5、41~80 目彩砂 50~70、81~120 目彩砂 5~25、KE025丙烯酸乳液 17~23、醇酯-12助剂 0.6~0.9、消泡剂 0.02~0.06、增稠剂 0.01-0.1和中和剂 0.02~0.06;
b.向搅拌机内加入下列组分:乙二醇、一半重量的醇酯-12助剂和消泡剂、KE025丙烯酸乳液、纤维素水溶液,搅拌后,再加入彩砂,搅拌;
c.加入另一半醇酯-12助剂和消泡剂,HY96中和剂,搅拌;
d.加增稠剂调节粘度,搅拌,出料即可。
优选地,本发明的制备环保防冻真石漆的方法,其中在步骤a中还包括向搅拌机内加入0.02~0.1份重量防腐剂的步骤。
优选地,本发明的环保防冻真石漆,其中所述的纤维素是市售的HEC羟乙基纤维素、所述消泡剂是市售的SP202消泡剂、所述增稠剂是市售的ASE60增稠剂,所述防腐剂是市售的HY 608防腐剂,所述中和剂是市售的HY96中和剂。
本发明主要是采用水作为溶剂,与溶剂型漆相比,更环保。同时本发明的真石漆以KE025丙烯酸树脂乳液作为成膜物质,以彩砂等作为产品主要组分,加以各种助剂,并以合适的组分配比,降低了乙二醇的使用量,也就是说降低了VOC的含量,具有成膜快,低温干燥速度快,环保安全的特点。
其中:防腐剂,市面上涂料用防腐剂材料较多,本发明选用HY 608防腐剂。HY 608防腐剂是一种高效、广谱、低毒型防腐杀菌剂,主要由苯井异噻唑啉酮组成,可消除因菌类浸染而引起的产品破乳,发酵,发臭等问题;SP202属于非硅酮矿物油类消泡剂,是一种经济型消泡剂,主要由:酯、醚、有机烃以及表面活性剂等组成,相容性好,消泡抑泡效果优异且具有良好的持久性,一可以降低成本,二施工性能好,漆膜光泽性好;醇酯-12是新一代的成膜助剂,其主要组成为2,2,4-三甲基-1,3-戊二醇-单异丁酸酯,在真石漆中,它能被吸附在乳液粒子上,可以有效的聚结,软化融合乳液粒子,使乳液的成膜温度大大降低,有利于真石漆的施工应用,具有良好的水解稳定性,低的凝固点,适宜挥发速率,高效的聚结效率;HY 96中和剂为一种PH值调节剂,其主要成分为2-氨基-2-甲基-1-丙醇,可有效控制体系PH值,取代用氨水中和,能得到低气味漆,减少对包装桶罐的腐蚀,保持粘度的稳定,同时能比传统功能产品降低VOC含量,提高绿色环保性能;KE025丙烯酸乳液为一种核壳结构丙烯酸酯及醚化物组份制成的一种具有抗冻性乳液,具有低温可成膜,成膜后涂膜在常温下不回粘,低温下可控制含水量,以防结冻,低温快干;本发明用该丙烯酸乳液配制的真石漆可以在-10℃到-25℃下施工,成膜速度快,其性能指标与常温下无异,克服了以往配制防冻真石漆加入大量乙二醇类助剂而造成的干燥速度太慢的缺点;HEC羟乙基纤维素,是非离子型水溶性聚合物,在这里主要起增稠、粘结、乳化、分散、稳定等作用,还能够给体系提供保护胶体效应,这里采用的是ER-30000防酶系列;ASE60增稠剂为一种碱溶胀型增稠剂,配合使用这种增稠剂能够提高体系的存储稳定性,漆膜表观和施工性能。
防冻真石漆的特征:1、低温可成膜,成膜后涂膜在常温下不回粘。2、低温下可控制含水量,以防结冻;3、低温快干;用该真石漆可以在0℃到-25℃下施工,成膜速度快,其性能指标与常温下无异,克服了以往配制防冻真石漆加入大量乙二醇类助剂而造成的干燥速度太慢的缺点。4.绿色环保性强,在整个真石漆配制过程中不加入任何对人体有害组分,特别是功能性物质和以往比降低了VOC含量;5.所采用的成膜物质大大提高了防冻真石漆的耐水、耐候、耐老化等性能。
为了进一步理解本发明,现在结合具体实施例对本发明进行具体说明。
具体实施方式
下述原料均为市售产品。
实施例1
按照下列步骤制备本发明的环保防冻真石漆:
1)先在小容器内加入9.9kg水,在搅拌条件下,向水中加入的100g HEC羟乙基纤维素,搅拌时间为0.5h,待HEC粒子完全溶解后即可停止搅拌,备用;
2)称取下列重量的原料组分:1%浓度HEC羟乙基纤维素水溶液 0.1kg、乙二醇0.8kg、HY608防腐剂 0.02kg、20目彩砂 4kg、41目彩砂 50kg、81目彩砂 5kg、KE025丙烯酸乳液 17kg、醇酯-12助剂 0.6kg、SP202消泡剂 0.02kg、ASE60增稠剂0.01kg和HY96中和剂0.02kg;
3)向搅拌机内加入下列组分:乙二醇、一半重量的醇酯-12助剂和SP202消泡剂、KE025丙烯酸乳液、HEC羟乙基纤维素水溶液,搅拌5min后,再加入彩砂,搅拌10min;
4)加入另一半醇酯-12助剂和SP202消泡剂,HY96中和剂,搅拌5min;
5)加ASE60增稠剂调节粘度,搅拌5min,出料即可得到成品。
实施例2
按照下列步骤制备本发明的环保防冻真石漆:
1)先在小容器内加入9.6kg水,在搅拌条件下,向水中加入的400g HEC羟乙基纤维素,搅拌时间为2h,待HEC粒子完全溶解后即可停止搅拌,备用;
2)称取下列重量的原料组分:4%浓度HEC羟乙基纤维素水溶液 5kg、乙二醇1.2kg、HY608防腐剂 0.1kg、80目彩砂 70kg、120目彩砂 25kg、KE025丙烯酸乳液 23kg、醇酯-12助剂 0.9kg、SP202消泡剂 0.06kg、ASE60增稠剂 0.1kg和HY96中和剂0.06kg;
3)向搅拌机内加入下列组分:乙二醇、一半重量的醇酯-12助剂和SP202消泡剂、KE025丙烯酸乳液、HEC羟乙基纤维素水溶液,搅拌10min后,再加入彩砂,搅拌20min;
4)加入另一半醇酯-12助剂和SP202消泡剂,HY96中和剂,搅拌10min;
5)加ASE60增稠剂调节粘度,搅拌15min,出料即可得到成品。
实施例3
按照下列步骤制备本发明的环保防冻真石漆:
1)在小容器内加入9.8kg水,在搅拌条件下,向水中加入的200g HEC羟乙基纤维
素,搅拌时间为1h,待HEC粒子完全溶解后即可停止搅拌,备用;
2)称取下列重量的原料组分:2%浓度HEC羟乙基纤维素水溶液 3kg、乙二醇 1kg、HY608防腐剂 0.05kg、30目彩砂 3kg、60目彩砂 65kg、100目彩砂 15kg、KE025丙烯酸乳液 20kg、醇酯-12助剂 0.75kg、SP202消泡剂 0.04kg、ASE60增稠剂0.05kg和HY96中和剂0.04kg;
3)向搅拌机内加入下列组分:乙二醇、一半重量的醇酯-12助剂和SP202消泡剂、KE025丙烯酸乳液、HEC羟乙基纤维素水溶液,搅拌10min后,再加入彩砂,搅拌20min;
4)加入另一半醇酯-12助剂和SP202消泡剂,HY96中和剂,搅拌10min;
5)加ASE60增稠剂调节粘度,搅拌15min,出料即可得到成品。
防冻性试验:
将实施例1和3所制得的真石漆和市售普通真石漆比较,进行抗冻性试验,在产品使用96h后的结果如下面表1所示:
表1
Figure A200810002349D00071
同时对本发明所制得的产品与普通真石漆进行各项性能比较,结果如表2所示。
表2
Figure A200810002349D00081

Claims (7)

1、一种环保防冻真石漆,其包含下列重量份的原料组分:
1~4%浓度纤维素水溶液0.1~5、乙二醇0.8~1.2、        41~80目彩砂50~70、
81~120目彩砂5~25、          KE025丙烯酸乳液17~23、 醇酯-12助剂0.6~0.9、
消泡剂0.02~0.06、            增稠剂0.01-0.1、        中和剂0.02~0.06。
2、根据权利要求1所述的环保防冻真石漆,其还包含至多5份重量的20~40目彩砂。
3、根据权利要求1所述的环保防冻真石漆,其还包含0.02~0.1份重量的防腐剂。
4、根据权利要求1、2和3中任一项权利要求所述的环保防冻真石漆,其中所述的纤维素是HEC羟乙基纤维素、所述消泡剂是SP202消泡剂、所述增稠剂是ASE60增稠剂,所述中和剂是HY96中和剂,所述防腐剂是HY608防腐剂。
5、一种环保防冻真石漆的制备方法,该方法包括下列步骤:
a.称取下列重量份的原料组分:1~4%浓度纤维素水溶液0.1~5、乙二醇0.8~1.2、20~40目彩砂0~5、41~80目彩砂50~70、81~120目彩砂5~25,、KE025丙烯酸乳液17~23、醇酯-12助剂0.6~0.9、消泡剂0.02~0.06、增稠剂0.01-0.1和中和剂0.02~0.06;
b.向搅拌机内加入下列组分:乙二醇、一半重量的醇酯-12助剂和消泡剂、KE025丙烯酸乳液、纤维素水溶液,搅拌后,再加入彩砂,搅拌;
c.加入另一半醇酯-12助剂和消泡剂,HY96中和剂,搅拌;
d.加增稠剂调节粘度,搅拌,出料即可。
6、根据权利要求5所述的环保防冻真石漆的制备方法,其中在步骤a中还包括向搅拌机内加入0.02~0.1份重量防腐剂的步骤。
7、根据权利要求5或6所述的环保防冻真石漆的制备方法,其中所述的纤维素是HEC羟乙基纤维素、所述消泡剂是SP202消泡剂、所述增稠剂是ASE60增稠剂,所述防腐剂是HY608防腐剂,所述中和剂是HY96中和剂;所述KE025丙烯酸乳液是一种核壳结构丙烯酸酯及醚化物组份制成的一种具有抗冻性乳液,具有低温可成膜,成膜后涂膜在常温下不回粘,低温下可控制含水量,以防结冻,低温快干;本发明用该丙烯酸乳液配制的真石漆可以在-10℃到-25℃下施工。
CNA2008100023493A 2008-01-08 2008-01-08 一种环保防冻真石漆及其制备方法 Pending CN101481568A (zh)