CN105400271A - 一种外墙柔性真石漆及其制备方法 - Google Patents
一种外墙柔性真石漆及其制备方法 Download PDFInfo
- Publication number
- CN105400271A CN105400271A CN201510893447.0A CN201510893447A CN105400271A CN 105400271 A CN105400271 A CN 105400271A CN 201510893447 A CN201510893447 A CN 201510893447A CN 105400271 A CN105400271 A CN 105400271A
- Authority
- CN
- China
- Prior art keywords
- mineral varnish
- true mineral
- wall flexible
- flexible
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种外墙柔性真石漆,由以下组分按照以下重量份数比配制而成:水8-14份、纤维素0.3-0.5份、氨水0.1-0.2份、防腐杀菌剂0.2-0.4份、柔性真石漆乳液15-18份、2-羟基-4-正辛氧基二苯甲酮0.2-0.4份、丙二醇0.2-0.4份、矿物油消泡剂0.2-0.4份、快干剂0.1-0.3份、醇酯十二1.0-1.2份、天然彩砂8-72份。本发明不仅具有一定的柔性,可有效防止开裂,而且还有着优异的耐水性、耐候性、和卓越的附着力。
Description
技术领域
本发明涉及建筑涂料技术领域,尤其涉及一种外墙柔性真石漆及其制备方法。
背景技术
真石漆具有颜色自然,质感逼真,坚硬如石的天然石材般装饰效果,给人以严肃、典雅、奢华的视觉享用,从而得到广泛的应用,尤其使用于别墅、大厦剂旅游景区等建筑物的内外墙装饰。而且随着建筑节能技术的应用,对外墙外保温的饰面材料有了新的要求,目前市场上的普通真石漆,由于漆较强的刚性,在外保温体系有动态变化的情况下极易产生开裂,失去了应有的装饰效果。因此,研究一种既能保持真石漆原有的质感,逼真的天然石材效果,又能同时避免开裂,满足外装饰要求的外墙柔性真石漆有着重要的意义。
发明内容
本发明提供了一种外墙柔性真石漆及其制备方法,本发明制备的外墙柔性真石漆不仅具有一定的柔性,可有效防止开裂,而且还有着优异的耐水性、耐候性和卓越的附着力。
本发明的技术方案如下:
一种外墙柔性真石漆,由以下组分按照以下重量份数比配制而成:
进一步地,所述纤维素为采用速溶型羟丙基甲基纤维素。
进一步地,所述防腐杀菌剂为固含5-10%且ph值为7.5-8.5的纳米银溶液,具有广谱抗菌的作用,且安全无毒。
进一步地,所述柔性真石漆乳液为玻璃化温度为0~15℃且成膜温度为0~10℃的柔性真石漆乳液。所述柔性真石漆乳液为具有更低的玻璃化温度和成膜温度硬度,以及更好的耐水性。
进一步地,所述2-羟基-4-正辛氧基二苯甲酮为一种紫外线吸收剂,具有卓越的高效的耐老化功能,有助于减少色泽,延缓漆膜泛黄,对漆膜有很大的保护作用。
进一步地,所述快干剂为采用乙二醇单丁醚、二丙二醇丁醚或二丙二醇甲醚中的一种或多种任意组合。
进一步地,所述天然彩砂为采用40-80目、80-120目和120-160目天然彩砂的混合物,其之间的比例为1:1:0.1。
一种外墙柔性真石漆的制备方法,它包括如下依序进行的步骤:
将8-14份的水加入分散缸中,调整分散缸的搅拌速率为300-600r/min,接着依次加入0.3-0.5份纤维素和0.1-0.2份氨水,搅拌5-10分钟;
然后,加入0.2-0.4份防腐杀菌剂和15-18份的柔性真石漆乳液,搅拌1-3分钟;
接着,依次加入0.2-0.4份2-羟基-4-正辛氧基二苯甲酮、0.2-0.4份丙二醇、0.2-0.4份矿物油消泡剂、0.1-0.3份快干剂和1.0-1.2份醇酯十二,搅拌2-4分钟,即得基础漆
最后将上述步骤制备好的基础漆加入到68-72份天然彩砂中,搅拌3-6分钟,即得本发明产品。
本发明的有益效果:本发明制备的一种外墙柔性真石漆具有如下优点:采用本发明所述的组分及配比结合制备的一种外墙柔性真石漆不仅具有一定的柔性,可有效防止开裂,而且还有着优异的耐水性、耐候性、和卓越的附着力。
本发明一种外墙柔性真石漆与现有的技术相比具有如下优点:本发明的外墙柔性真石漆选用具有较低的玻璃化温度和成膜温度的柔性真石漆乳液,并配以2-羟基-4-正辛氧基二苯甲酮的耐老化助剂,使本发明的真石漆不仅具有优异的天然石材般装饰效果和耐水性,还同时具有优异的耐候性和柔韧性,可有效保证其在施工中不会因内部的运动导致涂层开裂,并且配方中添加了快干剂,使真石漆易于干燥,进一步提高了真石漆的耐水性,最后与天然彩砂按照一定量的比例混合,赋予了本发明产品卓越的附着力,有效改善真石漆的掉砂率。
具体实施方式
下述组分中所述纤维素优选为山东宸邦生产的10W黏度型羟丙基甲基纤维素。所述柔性真石漆乳液优选为陶氏生产的TX120型柔性真石漆乳液。所述矿物油消泡剂优选为诺普科生产的SN-NXZ型矿物油消泡剂。所述快干剂优选为采用二丙二醇丁醚。所述醇酯十二优选为伊士曼生产的Texnol型醇酯十二。
具体实施案例1
一种外墙柔性真石漆,由以下组分按照以下重量份数比配制而成:
一种外墙柔性真石漆的制备方法,它包括如下依序进行的步骤:
将11份的水加入分散缸中,在300-600r/min速度下依次加入0.4份纤维素和0.15份氨水,搅拌5-10分钟。然后,加入0.3份防腐杀菌剂和16.5份的柔性真石漆乳液,搅拌1-3分钟。接着,依次加入0.3份2-羟基-4-正辛氧基二苯甲酮、0.3份丙二醇、0.3份矿物油消泡剂、0.2份快干剂和1.1份醇酯十二,搅拌2-4分钟,即得本发明产品的基础漆,最后将制备好的基础漆加入到70份天然彩砂中,使用电子搅拌器,搅拌3-6分钟,即得本发明产品。
具体实施案例2
一种外墙柔性真石漆,由以下组分和重量份数比配制而成:
一种外墙柔性真石漆的制备方法,它包括如下依序进行的步骤:
将8份的水加入分散缸中,在300-600r/min速度下依次加入0.3份纤维素和0.1份氨水,搅拌5-10分钟。然后,加入0.2份防腐杀菌剂和18份的柔性真石漆乳液,搅拌1-3分钟。接着,依次加入0.2份2-羟基-4-正辛氧基二苯甲酮、0.2份丙二醇、0.2份矿物油消泡剂、0.1份快干剂和1.2份醇酯十二,搅拌2-4分钟,即得本发明产品的基础漆,最后将制备好的基础漆加入到72份天然彩砂中,使用电子搅拌器,搅拌3-6分钟,即得本发明产品。
具体实施案例3
一种外墙柔性真石漆,由以下组分和重量份数比配制而成:
一种外墙柔性真石漆的制备方法,它包括如下依序进行的步骤:
将14份的水加入分散缸中,在300-600r/min速度下依次加入0.5份纤维素和0.2份氨水,搅拌5-10分钟。然后,加入0.4份防腐杀菌剂和15份的柔性真石漆乳液,搅拌1-3分钟。接着,依次加入0.4份2-羟基-4-正辛氧基二苯甲酮、0.4份丙二醇、0.4份矿物油消泡剂、0.3份快干剂和1.0份醇酯十二,搅拌2-4分钟,即得本发明产品的基础漆,最后将制备好的基础漆加入到68份天然彩砂中,使用电子搅拌器,搅拌3-6分钟,即得本发明产品。
经过对各实施例的测试,本发明外墙柔性真石漆的各实施例依据JG/T24-2000和JG/T172-2014的标准要求测试产品的技术指标,实验数据如下表所示:
由上述实施例测试结果可知:本发明制备的一种外墙柔性真石漆具有一定的柔性,可有效防止开裂,而且还有着优异的耐水性、耐候性、和卓越的附着力。
本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。
Claims (7)
1.一种外墙柔性真石漆,其特征在于,所述的外墙柔性真石漆由以下组分按照以下重量份数比配制而成:
2.根据权利要求1所述的一种外墙柔性真石漆,其特征在于:所述纤维素为速溶型羟丙基甲基纤维素。
3.根据权利要求1所述的一种外墙柔性真石漆,其特征在于:所述防腐杀菌剂为固含5-10%且ph值为7.5-8.5的纳米银溶液。
4.根据权利要求1所述的一种外墙柔性真石漆,其特征在于:所述柔性真石漆乳液为玻璃化温度为0~15℃且成膜温度为0~10℃的柔性真石漆乳液。
5.根据权利要求1所述的一种外墙柔性真石漆,其特征在于:所述快干剂为乙二醇单丁醚、二丙二醇丁醚或二丙二醇甲醚中的一种或多种任意组合。
6.根据权利要求1所述的一种外墙柔性真石漆,其特征在于:所述天然彩砂为40-80目、80-120目和120-160目天然彩砂按照1:1:0.1混合而成的混合彩砂。
7.一种权利要求1-6中任意一项所述的一种外墙柔性真石漆的制备方法,其特征在于:它包括如下依序进行的步骤:
将8-14份的水加入分散缸中,调整分散缸的搅拌速率为300-600r/min,接着依次加入0.3-0.5份纤维素和0.1-0.2份氨水,搅拌5-10分钟;
然后,加入0.2-0.4份防腐杀菌剂和15-18份的柔性真石漆乳液,搅拌1-3分钟;
接着,依次加入0.2-0.4份2-羟基-4-正辛氧基二苯甲酮、0.2-0.4份丙二醇、0.2-0.4份矿物油消泡剂、0.1-0.3份快干剂和1.0-1.2份醇酯十二,搅拌2-4分钟,即得基础漆;
最后将上述步骤制备好的基础漆加入到68-72份天然彩砂中,搅拌3-6分钟,即得本发明产品。