CN102617071A - 高光泽真石漆、仿大理石漆 - Google Patents
高光泽真石漆、仿大理石漆 Download PDFInfo
- Publication number
- CN102617071A CN102617071A CN2012100789653A CN201210078965A CN102617071A CN 102617071 A CN102617071 A CN 102617071A CN 2012100789653 A CN2012100789653 A CN 2012100789653A CN 201210078965 A CN201210078965 A CN 201210078965A CN 102617071 A CN102617071 A CN 102617071A
- Authority
- CN
- China
- Prior art keywords
- lacquer
- mineral varnish
- true mineral
- high gloss
- parian
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高光泽真石漆、仿大理石漆,其特征在于它由以下重量百分比的原料制成:硅丙乳液20.7-25.8%;浓度2.5%的HEC羟乙基纤维素溶液4-6%;成膜助剂醇酯十二0.5-0.7%;乙二醇0.35-0.45%;40-80目彩砂10.4-15.5%;80-120目彩砂15.5-20.6%;120-20目彩砂36.1-41.3%;防霉剂0.008-0.012%;防腐剂0.008-0.012%;杀菌剂0.008-0.012%;保湿亮光剂0.35-0.45%;均染剂0.5-0.74%。加入岩片,即为仿大理石漆。该漆,颜色不再发乌,施工中不再泛花,不再出现急干,可喷、可辊涂、可刷涂,使用方便。
Description
技术领域
本发明属于一种建筑涂料制品,涉及真石漆、仿大理石漆的各种原料配比及生产方法的改进,特别是一种不仅能喷,而且还能涂、能刷、能辊、不泛花、不发乌、方便施工的高光泽真石漆、仿大理石漆。
背景技术
众所周知,天然的花岗岩石材,是一种高档的装饰材料,在市场上很受关注。但是,这种天然的花岗岩石材,储藏量有限,其花纹和色彩具有确定性,而且不能再生,所以,采用天然的花岗岩石材作为建筑装饰材料越来越困难。也正因为如此,真石漆、仿大理石漆的生产便成了建筑装饰领域的热门话题。近几年来,仿真石漆涂料面层在民用建筑外墙、室内装饰、以及园林塑石领域已经得到了广泛的应用,具有庄重、典雅、和谐和具有回归自然的感觉。目前,生产真石漆所采用的原料,有的包括乳液15.5-19.3%、甲基纤维素5.2%、消泡剂0.02%、有机氨0.02%、分散剂0.01%、醇脂十二1.5%、乙二醇0.05%、40-80目彩砂20-26%、80-120目彩砂47-53%;有的包括乳液21-26%、消泡剂适量、醇脂十二为0.5-0.6%、乙二醇0.02-0.06%、彩砂72-78%、增稠剂0.02%、PH调节剂适量、分散剂0.008-0.01%、流平剂0.02%;有的包括乳液400份、彩砂100份、建筑用细沙400份、流平剂10份、对甲磺酸30份、二氧化钛12份、防紫外线吸收剂10份;有的包括乳液15-18%、分散剂0.3-0.4%、乙二醇0.7-0.9%、彩砂66-72%、增稠剂0.2-0.4%、杀菌剂0.03-0.08%、水10-15%。其配比的不同,使用效果有所不同,但以上所使用的真石漆,具有颜色发乌、施工中泛花、易出现急干的不足,同时,施工方法只能喷施,不能刷涂和辊涂,导致了施工不方便。
发明内容
本发明的目的在于提供颜色不发乌、施工中不泛花、干的速度慢,同时,施工方法不仅能喷施,而且能刷涂和辊涂的一种高光泽真石漆、仿大理石漆。
为达到以上目的,本发明所采用的技术方案是:高光泽真石漆、仿大理石漆,其特征在于:它包括以下重量百分比的原料制成:
硅丙乳液20.7-25.8%;浓度为2.5%的HEC羟乙基纤维素溶液4-6%;成膜助剂醇酯十二0.5-0.7%;乙二醇0.35-0.45%;40-80目彩砂10.4-15.5%;80-120目彩砂15.5-20.6%;120-200目彩砂36.1-41.3%;防霉剂0.008-0.012%;防腐剂0.008-0.012%;杀菌剂0.008-0.012%;保湿亮光剂0.35-0.45%;均染剂0.5-0.74%。
作为一种改进:还加入所述原料的重量的2-4%的水。
作为一种改进:还加入所述原料和水的总重量的15-21%的岩片。
该高光泽真石漆、仿大理石漆的制备方法,其特征在于:将硅丙乳液20.7-25.8%、浓度为2.5%的HEC羟乙基纤维素4-6%、成膜助剂醇酯十二0.5-0.7%、乙二醇0.35-0.45%、40-80目彩砂10.4-15.5%、80-120目彩砂15.5-20.6%、120-200目彩砂36.1-41.3%、防霉剂0.008-0.012%、防腐剂0.008-0.012%和杀菌剂0.008-0.012%一同装入一个搅拌釜内,搅拌速度为17转/分钟,搅拌时间为80-100分钟,待HEC羟乙基纤维素粒子完全溶解,使其均匀混合后,再加入均染剂0.5-0.74%,继续搅拌15-25分钟,搅拌速度仍为17转/分钟,再加入保湿亮光剂0.35-0.45%,再继续搅拌15-25分钟,搅拌速度仍为17转/分钟,成为稠真石漆成品;在制成的稠真石漆成品内加入其重量的2-4%的水,边加入边搅拌,进行稀释均匀,即为高光泽真石漆,装入成品桶内;在高光泽真石漆成品内,加入所述高光泽真石漆成品重量的15-21%的岩片,即为仿大理石漆,岩片是在施工时加入。
所述的硅丙乳液是一种市场上常用的外墙涂料,具有耐水性、耐洗刷性、耐沾污性和耐老化性的特点,为ZS-6318硅丙乳液。
所述的浓度为2.5%的HEC羟乙基纤维素溶液为市场上销售的HEC羟乙基纤维素溶液,规格为2.5-4万,是以天然高分子材料纤维素为原料,经一系列化学加工而制取的非离子型水溶性聚合物,可起增稠、粘结、乳化、成膜、分散、稳定、保水等作用,还能提供保护胶体效应,相对密度0.55-0.75,软化温度为134-140℃,分解温度为205-210℃。
所述的成膜助剂醇酯十二为2,2,4-三甲基-1,3-戊二醇单异丁酸酯,具有水解性能好的特点,加入后被吸收在乳液粒子上,并在涂漆时引起更好的融合,可有效的聚合乳液粒子,溶液掺入乳液中,且不影响漆的稳定性,是乳液聚合物的强溶剂,并具有抑制泡沫的作用;产自美国伊斯曼。
所述的乙二醇是一种抗冻剂,规格为涤纶级,加入后可有利于在低温下施工,乙二醇产自北京东方化工厂,其加入量不超过0.45%,克服了目前所使用的真石漆因乙二醇加入过量而带来的干燥速度过慢、成本高、环保性能降低的不足。
所述的均染剂是浓度为50%的钛白粉溶液,加入钛白粉溶液后,由于钛白粉可起漂染作用,所以即可克服了目前所使用的真石漆颜色发乌的问题。
所述的保湿亮光剂是浓度为1%的聚丙烯酰胺溶液,规格为1000万,由于聚丙烯酰胺溶液具有保湿、亮光作用,通过加入浓度为1%的聚丙烯酰胺溶液,即可防止急干,也可克服目前所使用的真石漆在施工中泛花的问题;同时,与钛白粉溶液共同起克服目前所使用的真石漆颜色发乌、泛花的问题。
所述的防霉剂为华科108防霉剂;防腐剂为市场上销售的华科981防腐剂;杀菌剂为杀菌剂HF或杀菌剂KSG-105S。
所述的岩片为黑砂石、灰砂石、白砂石、红砂石中的1种或2-3种的混合砂。购自中国联科。
本发明的的有益效果在于:与目前使用的真石漆、仿大理石漆相比,由于加入了均染剂和保湿亮光剂,并合理的控制了乙二醇和硅丙乳液的加入量,所以,不仅可在低温下施工、更加环保,而且颜色不再发乌,施工中不再泛花,不再出现急干,施工方法不仅可喷,而且可辊涂、可刷涂,使用方便,可提高施工速度及其灵活性。
具体实施方式
实施例1
高光泽真石漆、仿大理石漆,其特征在于:它由以下重量百分比的原料制成:
硅丙乳液23.3%;浓度为2.5%的HEC羟乙基纤维素5.3%;成膜助剂醇酯十二 0.61%;乙二醇0.4%;40-80目彩砂12.76%;80-120目彩砂18%;120-200目彩砂38.6%;华科108防霉剂0.01%;华科981防腐剂0.01%;杀菌剂HF 0.01%;浓度为1%的聚丙烯酰胺溶液0.4%;浓度为50%的钛白粉溶液0.6%;
将硅丙乳液23.3%、浓度为2.5%的HEC羟乙基纤维素5.3%、成膜助剂醇酯十二0.61%、乙二醇0.4%、60目彩砂12.76%、100目彩砂18%、160目彩砂38.6%、华科108防霉剂0.01%、华科981防腐剂0.01%和杀菌剂HF0.01%一同装入一个搅拌釜内,搅拌速度为 17 转/分钟,搅拌时间为90分钟,待HEC羟乙基纤维素粒子完全溶解,使其均匀混合后,再加入浓度为50%的钛白粉溶液0.6%,继续搅拌20分钟,搅拌速度仍为17转/分钟,再加入浓度为1%的聚丙烯酰胺溶液0.4%,再继续搅拌20分钟,搅拌速度仍为17转/分钟,成为稠真石漆成品;在制成的稠真石漆成品内加入其重量的3%的水,边加入边搅拌,进行稀释均匀,即为高光泽真石漆,装入成品桶内;
在高光泽真石漆成品内加入所述高光泽真石漆成品重量的1.8%的黑砂石岩片,即为仿大理石漆,1.8%的黑砂石岩片在施工时加入。
作为本发明的进一步改进:
所述的硅丙乳液是一种市场上常用的外墙涂料,具有耐水性、耐洗刷性、耐沾污性和耐老化性的特点,为ZS-6318硅丙乳液。
所述的浓度为2.5%的HEC羟乙基纤维素为市场上销售的HEC羟乙基纤维素,规格为2.5-4万,是以天然高分子材料纤维素为原料,经一系列化学加工而制取的非离子型水溶性聚合物,可起增稠、粘结、乳化、成膜、分散、稳定、保水等作用,还能提供保护胶体效应,相对密度0.55-0.75,软化温度为134-140℃,分解温度为205-210℃。
所述的成膜助剂醇酯十二为2,2,4-三甲基-1,3-戊二醇单异丁酸酯,具有水解性能好的特点,加入后被吸收在乳液粒子上,并在涂漆时引起更好的融合,可有效的聚合乳液粒子,溶液掺入乳液中,且不影响漆的稳定性,是乳液聚合物的强溶剂,并具有抑制泡沫的作用。产地为美国伊斯曼。
所述的乙二醇是一种抗冻剂,规格为涤纶级,产地为北京东方,其加入量不超过0.45%,克服了目前所使用的真石漆因乙二醇加入过量而带来的干燥速度过慢、成本高、环保性能降低的不足。
实施例2
高光泽真石漆、仿大理石漆,其特征在于:它由以下重量百分比的原料制成:
硅丙乳液22.9%;浓度为2.5%的HEC羟乙基纤维素溶液6%;成膜助剂醇酯十二 0.57%;乙二醇0.45%; 40-80目彩砂12%;80-120目彩砂20%;120-200目彩砂37%;华科108防霉剂 0.008%;华科981防腐剂0.012%;杀菌剂HF 0.01%;浓度为1%的聚丙烯酰胺溶液0.35%;浓度为50%的钛白粉溶液 0.7%;
将硅丙乳液22.9%、浓度为2.5%的HEC羟乙基纤维素溶液6%、成膜助剂醇酯十二0.57%、乙二醇0.45%、60目彩砂12%、100目彩砂20%、160目彩砂37%、华科108防霉剂0.008%、华科981防腐剂0.012%和杀菌剂HF 0.01%一同装入一个搅拌釜内,搅拌速度为17转/分钟,搅拌时间为100分钟,待HEC羟乙基纤维素粒子完全溶解,使其均匀混合后,再加入浓度为50%的钛白粉溶液 0.7%,继续搅拌25分钟,搅拌速度仍为17转/分钟,再加入浓度为1%的聚丙烯酰胺溶液0.35%,再继续搅拌15分钟,搅拌速度仍为 17转/分钟,成为稠真石漆成品;在制成的稠真石漆成品内加入其重量的2%的水,边加入边搅拌,进行稀释均匀,即为高光泽真石漆,装入成品桶内装入成品桶内;
在高光泽真石漆成品内加入所述高光泽真石漆成品重量的15%的灰砂石岩片,即为仿大理石漆,15%的灰砂石岩片在施工时加入。
实施例3
高光泽真石漆、仿大理石漆,其特征在于:它由以下重量百分比的原料制成:
硅丙乳液24%;浓度为2.5%的HEC羟乙基纤维素4%;成膜助剂醇酯十二 0.67%;乙二醇0.35%;40-80目彩砂15%;80-120目彩砂16%;120-200目彩砂39%;华科108防霉剂 0.01%;华科981防腐剂0.008%;杀菌剂KSG-105S 0.012%;浓度为1%的聚丙烯酰胺溶液0.45%;浓度为50%的钛白粉溶液0.5%;
将硅丙乳液24%、浓度为2.5%的HEC羟乙基纤维素溶液4%、成膜助剂醇酯十二0.67%、乙二醇0.35%、60目彩砂15%、100目彩砂16%、160目彩砂39%、华科108防霉剂0.01%、华科981防腐剂0.008%和杀菌剂KSG-105S 0.012%一同装入一个搅拌釜内,搅拌速度为17转/分钟,搅拌时间为80分钟,待HEC羟乙基纤维素粒子完全溶解,使其均匀混合后,再加入浓度为50%的钛白粉溶液0.5%,继续搅拌15分钟,搅拌速度仍为17转/分钟,再加入浓度为1%的聚丙烯酰胺溶液45%,再继续搅拌25分钟,搅拌速度仍为17转/分钟,成为稠真石漆成品;在制成的稠真石漆成品内加入其重量的4%的水,边加入边搅拌,进行稀释均匀,即为高光泽真石漆,装入成品桶内装入成品桶内;
在高光泽真石漆成品内加入所述高光泽真石漆成品重量的21%的黑砂石、白砂石和红砂石的混合岩片,即为仿大理石漆,21%的黑砂石、白砂石和红砂石的混合岩片在施工时加入。
Claims (7)
1.高光泽真石漆、仿大理石漆,其特征在于:它包括以下重量百分比的原料制成:
硅丙乳液20.7-25.8%;浓度为2.5%的HEC羟乙基纤维素溶液4-6%;成膜助剂醇酯十二0.5-0.7%;乙二醇0.35-0.45%;40-80目彩砂10.4-15.5%;80-120目彩砂15.5-20.6%;120-200目彩砂36.1-41.3%;防霉剂0.008-0.012%;防腐剂0.008-0.012%;杀菌剂0.008-0.012%;保湿亮光剂0.35-0.45%;均染剂0.5-0.74%。
2.根据权利要求1所述的高光泽真石漆、仿大理石漆,其特征在于:还加入所述原料的重量的2-4%的水。
3.根据权利要求2所述的高光泽真石漆、仿大理石漆,其特征在于:还加入所述原料和水的总重量的15-21%的岩片。
4.根据权利要求1所述的高光泽真石漆、仿大理石漆,其特征在于:所述的均染剂是浓度为50%的钛白粉溶液。
5.根据权利要求1所述的高光泽真石漆、仿大理石漆,其特征在于:所述的保湿亮光剂是浓度为1%的聚丙烯酰胺溶液。
6.根据权利要求3所述的高光泽真石漆、仿大理石漆,其特征在于:所述的岩片为黑砂石、灰砂石、白砂石、红砂石中的1种或2-3种的混合砂。
7.如权利要求1所述的高光泽真石漆、仿大理石漆的制备方法,其特征在于:将硅丙乳液20.7-25.8%、浓度为2.5%的HEC羟乙基纤维素4-6%、成膜助剂醇酯十二0.5-0.7%、乙二醇0.35-0.45%、40-80目彩砂10.4-15.5%、80-120目彩砂15.5-20.6%、120-200目彩砂36.1-41.3%、防霉剂0.008-0.012%、防腐剂0.008-0.012%和杀菌剂0.008-0.012%一同装入一个搅拌釜内,搅拌速度为17转/分钟,搅拌时间为80-100分钟,待HEC羟乙基纤维素粒子完全溶解,使其均匀混合后,再加入均染剂0.5-0.74%,继续搅拌15-25分钟,搅拌速度仍为17转/分钟,再加入保湿亮光剂0.35-0.45%,再继续搅拌15-25分钟,搅拌速度仍为17转/分钟,成为稠真石漆成品;在制成的稠真石漆成品内加入其重量的2-4%的水,边加入边搅拌,进行稀释均匀,即为高光泽真石漆,装入成品桶内;在高光泽真石漆成品内,加入所述高光泽真石漆成品重量的15-21%的岩片,即为仿大理石漆,岩片是在施工时加入。