CN104973825A - 一种防火保温真石漆及其制备方法 - Google Patents
一种防火保温真石漆及其制备方法 Download PDFInfo
- Publication number
- CN104973825A CN104973825A CN201410144394.8A CN201410144394A CN104973825A CN 104973825 A CN104973825 A CN 104973825A CN 201410144394 A CN201410144394 A CN 201410144394A CN 104973825 A CN104973825 A CN 104973825A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- heat insulating
- revs
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种防火保温真石漆，由预制液、保温隔热树脂粉和烧结彩砂混合而成；所述预制液、保温隔热树脂粉和烧结彩砂的重量比为：255~270:30~40:680~720；所述预制液由以下重量份数的原料混合而成：水310~320份，羟乙基纤维素1.5~3份，助剂1~2份，发泡催化剂180~200份，发泡剂40~55份，成碳剂35~60份，硅丙乳液365~785份，成膜助剂20~27份，BIT杀菌剂4~5.5份。本真石漆既可以防火、隔热，又有良好的保温性能，且具有制备简单、易干省时、施工方便等优点。
Description
技术领域
本发明涉及涂料技术领域，尤其是涉及一种具有防火保温功能的真石漆及其制备方法。
背景技术
真石漆是一种装饰效果酷似大理石、花岗石的涂料，主要由高分子聚合物、天然彩石砂及相关助剂制成，干结固化后坚硬如石，看起来像天然真石一样。真石漆装修后的建筑物，具有天然真实的自然色泽，给人以高雅、和谐、庄重之美感，适合于各类建筑物的室内外装修，特别是在曲面建筑物上装饰，可以收到生动逼真，回归自然的功效。
真石漆具有防水、耐酸碱、耐污染、无毒、无味、粘接力强、永不褪色等特点，能有效地阻止外界恶劣环境对建筑物侵蚀，延长建筑物的寿命，由于真石漆具备良好的附着力和耐冻融性能，因此特别适合在寒冷地区使用。
目前市场对建筑的保温节能要求越来越高，仅仅使用保温墙体对建筑体的保温效果还达不到最佳效果，而在保温墙体外涂覆保温涂料可以极大的提高墙体的隔热保温性能。普通真石漆与保温墙体的配合度不高，容易产生裂纹，目前市场上还没有既可以保温、又具有天然石材效果的真石漆。
发明内容
针对现有技术存在的上述问题，本申请人提供了一种防火保温真石漆及其制备方法。本真石漆既可以防火、隔热，又有良好的保温性能，且具有制备简单、易干省时、施工方便等优点。
本发明的技术方案如下：
一种防火保温真石漆，由预制液、保温隔热树脂粉和烧结彩砂混合而成；所述预制液、保温隔热树脂粉和烧结彩砂的重量比为：255~270:30~40:680~720；
所述预制液由以下重量份数的原料混合而成：
水 310~320份
纤维素 1.5~3份
助剂 1~2份
发泡催化剂 180~200份
发泡剂 40~55份
成碳剂 35~60份
硅丙乳液 365~785份
成膜助剂 20~27份
BIT杀菌剂 4~5.5份。
具体步骤如下：
（1）制备预制液：
在容器中加入水307~312份，然后加入纤维素1.5~3份，1200~1500转/分钟的速度下分散20~30分钟，使混合物均匀混合无颗粒；再加入助剂1~2份，1200~1500转/分钟的速度下分散10~20分钟；
接着分别加入发泡催化剂180~200份、发泡剂40~55份、成碳剂35~60份、硅丙乳液365~785份、成膜助剂20~27份；500~800转/分钟的速度下搅拌5~10分钟；
再加入BIT杀菌剂1~2份、水1~3份，混合后加入BIT杀菌剂3~3.5份、水2~5份，500~800转/分钟的速度下搅拌10~20分钟即可；
（2）将255~270份步骤（1）所得预制液放入混合器中，加入30~40份保温隔热树脂粉，搅拌均匀后再加入680~720烧结彩砂，200~500转/分钟的速度下搅拌30~40分钟混合均匀即可。
述保温隔热树脂粉为热塑性聚合物中空微球的已膨胀湿粉4612-3，所述烧结彩砂为二氧化硅。所述纤维素为羟乙基纤维素，所述助剂为AMP-95多功能助剂，所述发泡催化剂为聚磷酸铵，所述发泡剂为三聚氰胺，所述成碳剂为季戊四醇，所述成膜助剂为醇酯十二。
本发明有益的技术效果在于：
本发明所提供的真石漆具有良好的耐热性，具有优异的隔热性能，可以隔绝热传导和抵抗明火，因此具有防火性。
本真石漆保温性好，且与现有常规的保温墙体有良好的适应性，不会因气候干湿度、雨水、冰雪、日晒等原因出现裂缝和脱落。
此外，本真石漆还具有普通真石漆的装饰性强、防水能力佳、坚硬耐久、水性环保等优点。
具体实施方式
实施例1
本防火保温真石漆按照以下步骤制备：
（1）制备预制液：
在容器中加入水307份，然后加入羟乙基纤维素1.5份，1200转/分钟的速度下分散30分钟，使混合物均匀混合无颗粒；再加入AMP-95多功能助剂1份，1200转/分钟的速度下分散20分钟；
接着分别加入发泡催化剂聚磷酸铵180份、发泡剂三聚氰胺40份、成碳剂季戊四醇35份、硅丙乳液365份、成膜助剂醇酯十二20份；500转/分钟的速度下搅拌10分钟；
再加入BIT杀菌剂1份、水1份，混合后加入BIT杀菌剂3份、水2份，500转/分钟的速度下搅拌20分钟即可。
（2）将255份步骤（1）所得预制液放入混合器中，加入30份保温隔热树脂粉，搅拌均匀后再加入680烧结彩砂，200转/分钟的速度下搅拌40分钟混合均匀即可。述保温隔热树脂粉为热塑性聚合物中空微球的已膨胀湿粉4612-3，所述烧结彩砂为二氧化硅。
实施例2
本防火保温真石漆按照以下步骤制备：
（1）制备预制液：
在容器中加入水312份，然后加入羟乙基纤维素3份，1500转/分钟的速度下分散20分钟，使混合物均匀混合无颗粒；再加入AMP-95多功能助剂2份， 1500转/分钟的速度下分散20分钟；
接着分别加入发泡催化剂聚磷酸铵200份、发泡剂三聚氰胺55份、成碳剂季戊四醇60份、硅丙乳液785份、成膜助剂醇酯十二27份； 800转/分钟的速度下搅拌5分钟；
再加入BIT杀菌剂2份、水3份，混合后加入BIT杀菌剂3.5份、水5份， 800转/分钟的速度下搅拌10分钟即可。
（2）将270份步骤（1）所得预制液放入混合器中，加入40份保温隔热树脂粉，搅拌均匀后再加入720烧结彩砂， 500转/分钟的速度下搅拌30分钟混合均匀即可。述保温隔热树脂粉为热塑性聚合物中空微球的已膨胀湿粉4612-3，所述烧结彩砂为二氧化硅。
实施例3
本防火保温真石漆按照以下步骤制备：
（1）制备预制液：
在容器中加入水310份，然后加入羟乙基纤维素2份，1400转/分钟的速度下分散25分钟，使混合物均匀混合无颗粒；再加入AMP-95多功能助剂1.5份，1300转/分钟的速度下分散15分钟；
接着分别加入发泡催化剂聚磷酸铵190份、发泡剂三聚氰胺50份、成碳剂季戊四醇45份、硅丙乳液500份、成膜助剂醇酯十二25份；600转/分钟的速度下搅拌8分钟；
再加入BIT杀菌剂1.5份、水2份，混合后加入BIT杀菌剂3份、水3份，600转/分钟的速度下搅拌15分钟即可。
（2）将260份步骤（1）所得预制液放入混合器中，加入35份保温隔热树脂粉，搅拌均匀后再加入700烧结彩砂，300转/分钟的速度下搅拌35分钟混合均匀即可。述保温隔热树脂粉为热塑性聚合物中空微球的已膨胀湿粉4612-3，所述烧结彩砂为二氧化硅。
Claims (4)
1.一种防火保温真石漆，其特征在于由预制液、保温隔热树脂粉和烧结彩砂混合而成；所述预制液、保温隔热树脂粉和烧结彩砂的重量比为：255~270:30~40:680~720；
所述预制液由以下重量份数的原料混合而成：
水 310~320份
纤维素 1.5~3份
助剂 1~2份
发泡催化剂 180~200份
发泡剂 40~55份
成碳剂 35~60份
硅丙乳液 365~785份
成膜助剂 20~27份
BIT杀菌剂 4~5.5份。
2.一种权利要求1所述的防火保温真石漆的制备方法，其特征在于具体步骤如下：
（1）制备预制液：
在容器中加入水307~312份，然后加入纤维素1.5~3份，1200~1500转/分钟的速度下分散20~30分钟，使混合物均匀混合无颗粒；再加入助剂1~2份，1200~1500转/分钟的速度下分散10~20分钟；
接着分别加入发泡催化剂180~200份、发泡剂40~55份、成碳剂35~60份、硅丙乳液365~785份、成膜助剂20~27份；500~800转/分钟的速度下搅拌5~10分钟；
再加入BIT杀菌剂1~2份、水1~3份，混合后加入BIT杀菌剂3~3.5份、水2~5份，500~800转/分钟的速度下搅拌10~20分钟即可；
（2）将255~270份步骤（1）所得预制液放入混合器中，加入30~40份保温隔热树脂粉，搅拌均匀后再加入680~720烧结彩砂，200~500转/分钟的速度下搅拌30~40分钟混合均匀即可。
3.根据权利要求1或2所述的防火保温真石漆及其制备方法，其特征在于所述保温隔热树脂粉为热塑性聚合物中空微球的已膨胀湿粉4612-3，所述烧结彩砂为二氧化硅。
4.根据权利要求1或2所述的防火保温真石漆及其制备方法，其特征在于所述纤维素为羟乙基纤维素，所述助剂为AMP-95多功能助剂，所述发泡催化剂为聚磷酸铵，所述发泡剂为三聚氰胺，所述成碳剂为季戊四醇，所述成膜助剂为醇酯十二。