CN105219197A - 一种真石漆的生产配方及工艺 - Google Patents

一种真石漆的生产配方及工艺 Download PDF

Info

Publication number
CN105219197A
CN105219197A CN201510737542.1A CN201510737542A CN105219197A CN 105219197 A CN105219197 A CN 105219197A CN 201510737542 A CN201510737542 A CN 201510737542A CN 105219197 A CN105219197 A CN 105219197A
Authority
CN
China
Prior art keywords
technique
color sand
add
stir
mineral varnish
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510737542.1A
Other languages
English (en)
Inventor
赵彬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510737542.1A priority Critical patent/CN105219197A/zh
Publication of CN105219197A publication Critical patent/CN105219197A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种真石漆的生产配方及工艺，其生产工艺为：1)按照配方比例先将水加入搅拌机；2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品，生产出的产品粘结力较强，最低成膜温度较高，从根本上解决了涂层太软等问题，生产工艺简单，成本低，性能优异，不易脱落，不存在安全隐患，装饰性强，适用面广，水性环保，耐污性好，使用寿命长，经济实惠。

Description

一种真石漆的生产配方及工艺
技术领域
本发明涉及建筑用材料技术领域，具体涉及一种真石漆的生产配方及工艺。
背景技术
真石漆主要由高分子聚合物、天然彩石砂及相关助剂制成，干结固化后坚硬如石。真石漆具有防火、防水、耐酸碱、耐污染、无毒、无味、粘结力强、永不退色等优点，能有效阻止外界恶劣环境对建筑物侵蚀，延长建筑物的寿命，由于真石漆具有良好的附着力和耐冻融性能，因此特别适合在寒冷地区使用。但是普通的真石漆干燥时间较长，而且是从表面往里面干燥，外表看是干了可实际里面并没有完全干燥，往往遇上下雨天气就会出现空鼓现象。
发明内容
针对上述现有技术存在的问题，本发明提供了一种新型卡板箱，结构简单、合理、使用方便，卡板箱可以实现360°翻转，实用性较强。
为了实现上述目的，本发明采用的技术方案是：
一种真石漆的生产配方及工艺，生产配方为(重量份数)
膨润土1-2，羟乙基纤维素1-2，乙二醇8-12，成膜助剂6-8，调节剂ANP-951-2，硅丙乳液RC-301140-160，增稠剂1.5-2.5，防腐剂1-2，彩砂700-800，水140-160。
优选的是，所述彩砂包括(重量份数)80-120目颗粒度的彩砂340-360，40-80目颗粒度的彩砂180-220，20-40目颗粒度的彩砂180-220。
上述任一方案优选的是，最佳生产配方为(重量份数)
膨润土1.5，羟乙基纤维素1.5，乙二醇10，成膜助剂7，调节剂ANP-951.5，硅丙乳液RC-301150，增稠剂2.0，防腐剂1.5，彩砂(80-120目)350，彩砂(40-80目)200，彩砂(20-40目)200，水150。
上述任一方案优选的是，所述羟乙基纤维素为3万粘度。
一种真石漆的生产配方及工艺，其生产工艺为：
1)按照配方比例先将水加入搅拌机；
2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；加入羟乙基纤维素和膨润土后需要搅拌机在1200rpm的搅拌速度下搅拌15-30分钟，溶解羟乙基纤维素。
3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；
4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品。
本发明的有益效果是：提供一种真石漆的生产配方及工艺，生产配方为(重量份数)膨润土1-2，羟乙基纤维素1-2，乙二醇8-12，成膜助剂6-8，调节剂ANP-951-2，硅丙乳液RC-301140-160，增稠剂1.5-2.5，防腐剂1-2，彩砂700-800，水140-160，其生产工艺为：1)按照配方比例先将水加入搅拌机；2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品，生产出的产品里外同时干，干燥速度快，不会出现空鼓现象，气温较低时也可以施工使用且不影响涂膜的性能，粘结力较强，最低成膜温度较高，从根本上解决了涂层太软等问题，生产工艺简单，成本低，性能优异，不易脱落，不存在安全隐患，装饰性强，适用面广，水性环保，耐污性好，使用寿命长，经济实惠。
具体实施方式
实施例1
一种真石漆的生产配方及工艺，生产配方为(重量份数)
膨润土1，羟乙基纤维素1，乙二醇8，成膜助剂6，调节剂ANP-951，硅丙乳液RC-301140，增稠剂1.5，防腐剂1，彩砂700，水140。
本发明进一步优化的技术方案，所述彩砂包括(重量份数)80-120目颗粒度的彩砂340，40-80目颗粒度的彩砂180，20-40目颗粒度的彩砂180。
本发明进一步优化的技术方案，所述羟乙基纤维素为3万粘度。
一种真石漆的生产配方及工艺，其生产工艺为：
1)按照上述配方比例先将水加入搅拌机；
2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；
3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；
4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品。
实施例2
一种真石漆的生产配方及工艺，生产配方为(重量份数)
膨润土1.5，羟乙基纤维素1.5，乙二醇10，成膜助剂7，调节剂ANP-951.5，硅丙乳液RC-301150，增稠剂2.0，防腐剂1.5，彩砂(80-120目)350，彩砂(40-80目)200，彩砂(20-40目)200，水150。
上述任一方案优选的是，所述羟乙基纤维素为3万粘度。
一种真石漆的生产配方及工艺，其生产工艺为：
1)按照上述配方比例先将水加入搅拌机；
2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；
3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；
4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品。
实施例3
一种真石漆的生产配方及工艺，生产配方为(重量份数)
膨润土2，羟乙基纤维素2，乙二醇12，成膜助剂8，调节剂ANP-952，硅丙乳液RC-301160，增稠剂12.5，防腐剂2，彩砂800，水1160。
本实施例中，所述彩砂包括(重量份数)80-120目颗粒度的彩砂360，40-80目颗粒度的彩砂220，20-40目颗粒度的彩砂220。
上述任一方案优选的是，所述羟乙基纤维素为3万粘度。
一种真石漆的生产配方及工艺，其生产工艺为：
1)按照上述配方比例先将水加入搅拌机；
2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；
3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；
4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品。
本发明提供一种真石漆的生产配方及工艺，其生产工艺为：1)按照配方比例先将水加入搅拌机；2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品，生产出的产品粘结力较强，最低成膜温度较高，从根本上解决了涂层太软等问题，生产工艺简单，成本低，性能优异，不易脱落，不存在安全隐患，装饰性强，适用面广，水性环保，耐污性好，使用寿命长，经济实惠。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (5)

1.一种真石漆的生产配方及工艺，其特征在于，生产配方为(重量份数)
膨润土1-2，羟乙基纤维素1-2，乙二醇8-12，成膜助剂6-8，调节剂ANP-951-2，硅丙乳液RC-301140-160，增稠剂1.5-2.5，防腐剂1-2，彩砂700-800，水140-160。
2.根据权利要求1所述的一种真石漆的生产配方及工艺，其特征在于，所述彩砂包括(重量份数)80-120目颗粒度的彩砂340-360，40-80目颗粒度的彩砂180-220，20-40目颗粒度的彩砂180-220。
3.根据权利要求2所述的一种真石漆的生产配方及工艺，其特征在于，生产配方为(重量份数)
膨润土1.5，羟乙基纤维素1.5，乙二醇10，成膜助剂7，调节剂ANP-951.5，硅丙乳液RC-301150，增稠剂2.0，防腐剂1.5，80-120目颗粒度的彩砂350，40-80目颗粒度的彩砂200，20-40目颗粒度的彩砂200，水150。
4.根据权利要求2所述的一种真石漆的生产配方及工艺，其特征在于，所述羟乙基纤维素为3万粘度。
5.根据权利要求1所述的一种真石漆的生产配方及工艺，其特征在于，其生产工艺为：
1)按照配方比例先将水加入搅拌机；
2)开动搅拌机，慢慢的把羟乙基纤维素和膨润土加入搅拌机搅拌，再加入调节剂继续搅拌，直到搅拌出白色粘稠状乳液；
3)往白色粘稠状乳液中依次加入硅丙乳液、乙二醇、成膜助剂、防腐剂、彩砂，一边加入一边搅拌；
4)待步骤3)中搅拌均匀后，加入增稠剂搅拌均匀后即为成品。
CN201510737542.1A 2015-11-04 2015-11-04 一种真石漆的生产配方及工艺 Pending CN105219197A (zh)