CN104497763A - 一种抗酸抗碱超耐候仿砖涂料的研制 - Google Patents
一种抗酸抗碱超耐候仿砖涂料的研制 Download PDFInfo
- Publication number
- CN104497763A CN104497763A CN201410779039.8A CN201410779039A CN104497763A CN 104497763 A CN104497763 A CN 104497763A CN 201410779039 A CN201410779039 A CN 201410779039A CN 104497763 A CN104497763 A CN 104497763A
- Authority
- CN
- China
- Prior art keywords
- coating
- resistant
- parts
- agent
- weather
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明的一种抗酸抗碱超耐候仿砖涂料的研制按重量百分比计算为:纯丙乳液15-20份,成膜助剂7-9份,消泡剂0.5-1份,多功能助剂0.2-0.5份,乙二醇5-7份,湿润剂0.3-0.6份,防腐剂1-1.3份,石英砂55-60份,聚氨酯增稠剂2-3份,水8.5-14份,纤维素2-5份,流平剂0.3-0.5份。本发明的目的是储存稳定性好施工性能优良的厚质砂岩涂料,达到与人造面砖一样的表面效果,逼真性非常强,并且施工过程不容易飞沙,涂层施工完毕后漆膜效果较好,不容易泛白发花,漆膜自洁性较好,具有优异的耐水耐候性。
Description
技术领域 本发明涉及一种涂料,特别涉及一种超耐候仿砖,属于外墙装饰涂料技术领域。
背景技术 由于现在市面上的彩砖储存稳定性不好,储存过程中容易浮水,分层变稠等质量问题,并且施工过程中容易飞沙脱落等现象,增加了施工难度,工程施工后容易出现涂层变白发花及涂层容易污染变脏等现象,急需解决。
发明内容 本发明的目的是储存稳定性好施工性能优良的厚质砂岩涂料,达到与人造面砖一样的表面效果,逼真性非常强,并且施工过程不容易飞沙,涂层施工完毕后漆膜效果较好,不容易泛白发花,漆膜自洁性较好,具有优异的耐水耐候性。
本发明的一种抗酸抗碱超耐候仿砖涂料的研制按重量百分比计算为:
纯丙乳液15-20份,成膜助剂7-9份,消泡剂0.5-1份,多功能助剂0.2-0.5份,乙二醇5-7份,湿润剂0.3-0.6份,防腐剂1-1.3份,石英砂55-60份,聚氨酯增稠剂2-3份,水8.5-14份,纤维素2-5份,流平剂0.3-0.5份。
本发明优选的,所述成膜助剂为醇脂-12;所述的消泡剂为有机硅消泡剂;所述的PH调节剂为2-甲基-2-羟基-1-丙醇;所述的湿润剂为烷基聚氧乙烯醚;所述的防腐剂为1,2-苯并异噻唑啉-3-酮;。
该涂料是由天然彩砂作为骨料,改性丙烯酸聚合物为基料,配合各种进口助剂精制而成的一种质感涂料。无毒环保,无公害。具有极高的稳定性和保色性。耐水、耐碱性能优良。附着力极强,硬度高,耐刻划、耐擦洗、耐沾污,滚涂施工,施工方便快捷。可以配合建筑物不同的造型需求,在平面、圆柱、线板或雕刻板上,创造出桔皮状的质感。
具体实施方式 下面是本发明的一个实施例。
本发明的一种抗酸抗碱超耐候仿砖涂料的研制具体组份如下:
先低速以每分钟200~400转依次加入8.5份的水、0.2份的多功能助剂、0.3份的润湿剂、1份的消泡剂,待10分钟搅拌均匀后,再依次加入15份的纯丙乳液、55份的石英砂、5份的乙二醇后,进行高速每分钟1000转运转30分钟,再低速依次加入3份的聚氨酯增稠剂、2份纤维素、1份的防腐剂、0.3%的流平剂、8.7份的成膜助剂、适量的PH值调节剂,之后以每分钟600-800转进行搅拌40分钟,最后经过检验、过滤、称重包装。
适用于批荡平整后的内外砖墙、混凝土及水泥墙等表面涂装的砖墙面。胶合板,水泥砂浆面、砂石面。广泛适用于商业建筑,公用设施、办公大楼、工厂、院、公寓、住宅楼及别墅等内外墙面。
Claims (2)
1.本发明的一种抗酸抗碱超耐候仿砖涂料的研制按重量百分比计算为:
纯丙乳液15-20份,成膜助剂7-9份,消泡剂0.5-1份,多功能助剂0.2-0.5份,乙二醇5-7份,湿润剂0.3-0.6份,防腐剂1-1.3份,石英砂55-60份,聚氨酯增稠剂2-3份,水8.5-14份,纤维素2-5份,流平剂0.3-0.5份。
2.根据权利要求1所述的一种抗酸抗碱超耐候仿砖涂料,其特征是该涂料是由天然彩砂作为骨料,改性丙烯酸聚合物为基料,配合各种进口助剂精制而成的一种质感涂料。无毒环保,无公害。具有极高的稳定性和保色性。耐水、耐碱性能优良。附着力极强,硬度高,耐刻划、耐擦洗、耐沾污,滚涂施工,施工方便快捷。