CN101395002A - 内部用片材纸及其制备方法 - Google Patents
内部用片材纸及其制备方法 Download PDFInfo
- Publication number
- CN101395002A CN101395002A CNA2006800525709A CN200680052570A CN101395002A CN 101395002 A CN101395002 A CN 101395002A CN A2006800525709 A CNA2006800525709 A CN A2006800525709A CN 200680052570 A CN200680052570 A CN 200680052570A CN 101395002 A CN101395002 A CN 101395002A
- Authority
- CN
- China
- Prior art keywords
- resin
- moisture
- mixture
- powder
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种由或者棉纤维或者天然材料组成的环境友好型内部片材及其生产方法。这种内部片材包括或者只用棉纤维制成的纤维,或者所述纤维和沉积在上面的生物可降解的天然材料,于是,这种片材具有天然的质地和立体感。并且,不同于用由有机化学材料制成的纱线生产出来的现有片材,这里所公开的片材在被焚化或者埋在填埋场中时,不会造成环境污染。
Description
技术领域
本发明涉及一种内部片材及其生产方法,并且涉及一种环境友好型内部片材,其包括或者只用棉纤维制成的织物,或者所述织物和沉积在其上面的生物可降解的天然材料,并因此具有天然质地和立体感,而且这种片材被焚化或者埋在填埋场时,不会造成环境污染。本发明还涉及这种片材的生产方法。
背景技术
一般来说,例如无纺织物等片材是用聚乙烯(PE)树脂、聚丙烯(PP)树脂、聚对苯二甲酸乙二醇酯(PET)等有机化学材料制成的纱线生产出来的,或者是通过按特定比例将有机化学纱线和草纤维(grass wool)、蕉麻纤维或者大麻纱混合起来生产出来的。另外,通过使用造纸法将有机化学纱线与纸浆纤维混合起来,然后向里面添加蕉麻纤维或者大麻纱,也生产出上述片材。这样生产出来的片材可用于各种场合,包括民用工程场合、工业场合、汽车的饰面材料以及建筑物的内部饰面材料。
然而,因为以前的片材是基于有机化学纱线,所以,这些片材的问题在于不能再利用,而且在焚化时会释放出对人体有害的二恶英(dioxin)等环境激素。还有,当这些片材被埋在填埋场中时,不会生物降解,因此造成环境污染。
发明内容
相应的,提出了本发明来解决上述现有技术中存在的问题,因此,本发明的目的是提供一种环境友好型内部片材,其包括或者只用棉纤维制成的织物,或者所述织物和沉积在其上面的生物可降解的天然材料,并因此具有天然质地和立体感,而且这种片材被焚化或者埋在填埋场时,不会造成环境污染,本发明还提供了一种生产这种片材的方法。
为了实现上述目的,根据本发明的一个方面,提供了一种内部片材,其包括:多层织物,所述多层织物由多个堆叠的梳理后的棉纤维薄层构成;以及树脂层,所述树脂层施加在所述织物的一个表面上并由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成。
在根据本发明的所述内部片材中,优选地,在所述织物和所述树脂层之间按5~150g/m2的量进一步形成天然材料层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成。
另外,优选地,在所述树脂层和所述天然材料层之间进一步插置有具有与所述织物相同材料的织物。
根据本发明的另一方面,提供了一种内部片材,其包括:底片材,所述底片材包括由多个梳理后的棉纤维薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物一个表面上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;第一涂层,所述第一涂层施加在所述底片材的一个表面上并用第一涂覆材料制成,所述第一涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石、石英斑岩和陶瓷粉末、以及发射阴离子的硒中的任何一种,以及11.5~14wt%的选自甲醇和含水乙醇中的任何一种;印刷层,所述印刷层形成在所述底片材的另一表面上,与所述第一涂层相对;以及第一顶部涂层,所述第一顶部涂层施加在所述印刷层上并用第一顶部涂覆材料制成,所述第一顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的石蜡、聚乙烯蜡、硅酮基防水剂和氟基防水剂,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
根据本发明的所述内部片材,优选地,进一步包括在所述第一顶部涂层上形成的用第一含水泡沫复合材料制成的第一含水泡沫复合材料层,所述第一含水泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者混合物,5~10wt%的水,32.5~35wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~8wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(一乙烯乙二醇),1~10wt%的浆粉(pulp powder),0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,0.3~0.5wt%的非离子分散剂和阴离子分散剂中任何一种,以及1~2wt%的碱性墨水和酸性墨水以及盐基染料和碱性染料中的任何一种。
根据本发明的又一方面,提供了一种内部片材,其包括:第一底片材,所述第一底片材包括由多个梳理后的棉纤维的薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物一个表面上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母粉末、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;第二涂层,所述第二涂层施加在所述底片材的一个表面上并用第一涂覆材料制成,所述第一涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石、石英斑岩和陶瓷粉末、以及发射阴离子的硒中的任何一种,以及11.5~14wt%的选自甲醇和含水乙醇中的任何一种;粘结剂复合材料层,所述粘结剂复合材料层施加在所述底片材的另一表面上,与所述第二涂层相对,所述粘结剂复合材料层用粘结剂复合材料制成,所述粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,36~45wt%的选自碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,1~5wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的消泡剂;第二底片材,所述第二底片材施加在所述粘结剂复合材料层上并具有与所述第一底片材的复合材料相同的复合材料;印刷层,所述印刷层形成在层叠于所述粘结剂复合材料层上面的底片材的表面上;以及第二顶部涂层,所述第二顶部涂层施加在所述印刷层上并用第二顶部涂覆材料制成,所述第二顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的石蜡、聚乙烯蜡、硅酮基防水剂和氟基防水剂,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
优选地,所述粘结剂复合材料层由下面的材料构成:95~97wt%的所述粘结剂复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
根据本发明的再一方面,提供了一种内部片材,其包括:第一底片材,所述第一底片材包括由多个梳理后的棉纤维的薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物一个表面上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母粉末、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;第一阻燃涂层,所述第一阻燃涂层施加在所述底片材的一个表面上并用第一阻燃涂覆材料制成,所述第一阻燃涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水生物可降解EVA树脂中的任何一种,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,22~40wt%的氢氧化铝和氢氧化镁的混合物,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,以及9.5~14wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种;阻燃粘结剂复合材料层,所述阻燃粘结剂复合材料层施加在所述底片材的另一表面上,与所述第一阻燃涂层相对,所述阻燃粘结剂复合材料层用阻燃粘结剂复合材料制成,所述阻燃粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,36~45wt%的氢氧化铝和氢氧化镁的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,1~5wt%的异丁烷基含水发泡剂和异戊烷基含水发泡剂,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的选自阴离子消泡剂和非离子消泡剂中的任何一种;第二底片材,所述第二底片材层叠在所述阻燃复合材料层上并用与所述第一底片材的材料相同的材料制成;印刷层,所述印刷层形成在层叠于所述阻燃粘结剂复合材料层上面的所述第二底片材的表面上;以及第二顶部涂层,所述第二顶部涂层施加在所述印刷层上并用第二顶部涂覆复合材料制成,所述第二顶部涂覆复合材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水甲醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡和硅酮蜡、以及氟基防水剂中任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
优选地,所述阻燃粘结剂复合材料层由下面的材料构成:95~97wt%的所述阻燃粘结剂复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
根据本发明的再一方面,提供了一种内部片材,其包括:多层织物,所述多层织物由多个梳理后的棉纤维的薄堆叠层构成;第三涂层,所述第三涂层施加在所述织物的一个表面上并用第三涂覆材料制成,所述第三涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种,以及11.4~14wt%的选自甲醇和含水甲醇中的任何一种;第二含水泡沫复合材料层,所述第二含水泡沫复合材料层施加在所述织物的另一表面上,与所述第三涂层相对,所述第二含水泡沫复合材料层用第二含水泡沫复合材料制成,所述第二含水泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者混合物,5~10wt%的水,33.5~40wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,以及0.3~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种;印刷层,所述印刷层形成在所述第二含水发泡复合材料层上;以及第三顶部涂层,所述第三顶部涂层施加在所述印刷层上并用第三顶部涂覆材料制成,所述第三顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯基水溶性蜡、硅酮基水溶性蜡和巴西棕榈基水溶性蜡中的任何一种或者两种或更多种的混合物,5~10wt%的选自珠光体和片状云母粉末中的一种或者混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡、硅酮基防水剂以及氟基防水剂中任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
优选地,所述第二含水泡沫复合材料层由下面的材料构成:95~97wt%的所述含水泡沫复合材料,和3~5wt%的发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒。
根据本发明的再一方面,提供了一种内部片材,其包括:多层织物,所述多层织物由多个梳理后的棉纤维的薄堆叠层构成;第二阻燃涂层,所述第二阻燃涂层施加在所述织物的一个表面上并用第二阻燃涂覆材料制成,所述第二阻燃涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水生物可降解EVA树脂中的任何一种,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,22~40wt%的氢氧化铝和氢氧化镁的混合物,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种,以及9.5~14wt%的选自甲醇和含水乙醇中的任何一种;含水阻燃泡沫复合材料层,所述含水阻燃泡沫复合材料层施加在所述织物的另一表面上,与所述第二阻燃涂层相对,所述含水阻燃泡沫复合材料层用含水阻燃泡沫复合材料制成,所述含水阻燃泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者两种或更多种的混合物,5~10wt%的水,33.5~40wt%的无机填充物、氢氧化铝和氢氧化镁的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者两种或更多种的混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的选自非离子乳化剂、阴离子乳化剂和两性乳化剂中任何一种,以及0.3~0.5wt%的非离子分散剂和阴离子分散剂;印刷层,所述印刷层形成在所述含水阻燃发泡复合材料层上;以及第三顶部涂层,所述第三顶部涂层施加在所述印刷层上并用第三顶部涂覆材料制成,所述第三顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯基水溶性蜡、硅酮基水溶性蜡和巴西棕榈基水溶性蜡中的任何一种或者两种或更多种的混合物,5~10wt%的选自珠光体和片状云母粉末中的任何一种或者混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡、硅酮基防水剂以及氟基防水剂中任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
优选地,所述含水阻燃泡沫复合材料层由下面的材料构成:95~97wt%的所述含水泡沫复合材料,和3~5wt%的发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒。
根据本发明的再一方面,提供了一种生产内部片材的方法,所述方法包括步骤:制备或者用棉纤维制成的多层底片材,或者包括按顺序沉积在用棉纤维制成的多层织物的一个表面上的天然材料和树脂材料的底片材;在所述底片材的一个表面上施加阻燃或者非阻燃涂覆材料,以形成涂层;在所述底片材的与所述涂层相对的另一表面上施加阻燃或者非阻燃粘结剂复合材料或者含水泡沫复合材料,以形成复合材料层;在所述复合材料层的表面上形成具有多种图案的印刷层;在所述印刷层上施加形成透明膜的顶部涂覆材料,以获得上面形成有顶部涂层的叠层;使所述叠层发泡以形成泡沫化材料;以及用经雕刻的压花辊对所述泡沫化材料进行压花,所述压花辊具有利用内置加热装置达到的50~200℃的表面温度。
附图说明
图1是示出根据本发明用于生产片材的工艺的流程图。
图2是示出使用图1所示工艺生产的片材的剖视图。
图3是示出用根据本发明的片材处理的墙壁覆盖物的剖视图。
图4是示出两层根据本发明的片材的叠层的剖视图,该叠层用作墙壁覆盖物、汽车内层和建筑物饰面材料。
图5是示出用根据本发明的片材处理的墙壁覆盖物的剖视图。
具体实施方式
下面,将参照附图详细地描述本发明的优选实施例。
图1是示出用于生产根据本发明片材的工艺的流程图。图2是示出使用图1所示工艺生产的片材的剖视图。
如图所示,为了生产根据本发明的片材1,将棉纤维存储在第一原材料储料器10。存储在第一原材料储料器10中的棉纤维在梳棉机11中被梳理。在梳棉机中被梳理后的棉纤维被传送到第一梳棉机12,在第一梳棉机12中,棉纤维被展开成薄片的形式。这里,第一梳棉机12在其将棉纤维从梳棉机11堆叠成多层的同时反复地左右移动而形成多层织物3。这时,织物3优选地形成为厚度是大约0.2~0.6mm(大约30~120g/m2),并且值得注意的是,织物3本身就能够用作墙壁覆盖物的底片材。
然后,选自生物可降解天然材料、木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母粉末、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的材料,被沉积在棉纤维的一个表面上以形成天然材料层5。这里,这种天然材料被从第二原材料储料器经过输送器1414传送到振动筛15,振动筛15接着将这种天然材料按优选为5~150g/cm2的要求数量喷撒在棉纤维的一个表面上,以形成沉积在织物3上的天然材料层5。
然后,由选自合成树脂、丙烯酸树脂、EVE树脂和生物可降解EVE树脂种的任何一种树脂制成的树脂层7,被形成在织物3的一个表面上或者天然材料层5的一个表面上。这里,树脂用水稀释为树脂固体含量为15~30wt%(重量百分比),并稀释后的树脂经过喷洒器被喷洒在天然材料层18上面并经过浸渍系统18渗进该层18中。另外的方式是,通过喷射空气形成气泡将树脂施加在天然材料层5上,然后用施压辊(没有示出)对施加的树脂施压,以达到树脂固体含量为8~25wt%,于是形成树脂层7。
在另一实施例中,使用第二梳棉机16能将织物9先沉积在天然材料层5上达到0.05~0.1mm的厚度,然后按照上述相同的方式能将合成树脂层7施加到织物9上。
然后,所得到的结构按顺序通过筒型干燥器19a和隧道型干燥器19b,因此生产出根据本发明的片材1。这样生产出的具有创造性的片材1具有展现天然材料的质地和功能的优点,于是,当片材厚度小于0.3mm时,可以用作墙壁覆盖物的衬纸或者PVC地板的基纸。
还有,这样生产出的具有创造性的片材1经过下面的步骤能用作墙壁覆盖物、汽车内层或者建筑物内部饰面材料。
图3是示出用片材1加工成的墙壁覆盖物30的剖视图。首先,经过上述的步骤制备厚度大于0.4mm的第一片材1a。在第一片材1a的的一个表面上,即面对建筑物墙壁的表面上,使用照相凹版印刷法按照20~50g/m2的量施加第一涂覆材料,然后,使施加的涂覆材料干燥而形成第一涂层31。涂覆第一涂层31的第一涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石、石英斑岩和陶瓷粉末、以及发射阴离子的硒中的任何一种,以及11.5~14wt%的选自甲醇和含水乙醇中的任何一种。
在第一片材1a的与第一涂层31相对的另一表面上,使用照相凹版印刷工艺形成了具有各种图案的印刷层32。在印刷层32上,使用回转筛工艺、照相凹版印刷工艺或者擦拭工艺(一种渗透工艺)按照大约20~100g/m2的量施加形成透明膜的第一顶部涂覆材料,并使施加的顶部涂覆材料干燥而形成第一顶部涂层33。形成第一顶部涂覆层33的第一顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯基水溶性蜡、硅酮基水溶性蜡和巴西棕榈基水溶性蜡中的任何一种或者两种或更多种的混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子型和阴离子型分散剂中的任何一种,10~15wt%的石蜡、聚乙烯蜡、硅酮基防水剂和氟基防水剂,0.5~1wt%的选自碱性和酸性的墨水和碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
当在印刷层32上形成第一顶部涂覆层33时,从第一片材1a生产墙壁覆盖物30就完成了。进一步,表示为虚线的第一含水泡沫复合材料(foamcomposite)层34也可以形成在第一顶部涂层33上,由此完成从第一片材1a生产墙壁覆盖物1a。通过使用回转筛工艺或者照相凹版印刷工艺按大约20~100g/m2的量(基于固体)在第一顶部涂层33上施加第一含水泡沫复合材料然后干燥所施加的涂层,形成了第一含水泡沫复合材料层34。形成第一含水泡沫复合材料层34的第一含水泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者两种或更多种的混合物,5~10wt%的水,32.5~35wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~8wt%的选自异丁烷基(isobutane-based)含水发泡剂和异戊烷基(isopentane-based)含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(monoethylene glycol,一乙烯乙二醇),1~10wt%的浆粉,0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,0.3~0.5wt%的非离子分散剂和阴离子分散剂,以及1~2wt%的选自碱性和酸性的墨水和盐基染料和碱性染料中的任何一种。
同时,图4是示出每层厚度为0.15~0.4mm的两层片材1的叠层40的剖视图,该叠层用作墙壁覆盖物、汽车内片材和建筑物内片材。首先,制备第二片材1b。在第二片材1b的一个表面上,即面对建筑物等墙壁的表面上,使用照相凹版印刷工艺按大约20~50g/m2的量(基于固体),施加具有与第一涂覆材料层31的第一涂覆材料的复合材料相同的复合材料的第二涂覆材料,并使施加的涂覆材料干燥而形成第二涂层41a。第二涂层41a起到的作用是减小产品的产品热量引起的横向弹性,并且减少在片材用作墙壁覆盖物和建筑物饰面材料时用来将片材贴在墙面上的胶水和粘结剂中的水引起的片材收缩。
在另一实施例中,为了使片材阻燃,可以形成第一阻燃涂层41b取代第二涂层41。作为阻燃剂,使用氧化铝或者氢氧化镁。通过按照与第二涂覆材料相同的方式将第一阻燃材料施加在第二片材1b的一个表面上并干燥该施加的材料,形成第一阻燃涂层41b。形成第一阻燃涂层41b的第一阻燃涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水生物可降解EVA树脂中的任何一种,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,22~40wt%的氢氧化铝和氢氧化镁的混合物,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,以及9.5~14wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种。
在第二片材1b的与第二涂层41a或者阻燃涂层41b相对的另一表面上,使用间隔涂布机(comma coater)工艺或者回转筛工艺,按大约50~150g/m2的量(基于固体)施加能够最大化粘结功能和压花形成效果的粘结剂复合材料(adhesive composite),并使施加的合成物干燥而形成粘结剂复合材料层42a。形成粘结剂复合材料层42a的粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,36~45wt%的选自碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,1~5wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的消泡剂。粘结剂复合材料层用下面的材料制成:95~97wt%的粘结剂复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
在又一种实施例中,为了赋予产品阻燃性能,可以取代粘结剂复合材料层42a形成阻燃粘结剂复合材料层42b。作为阻燃剂,使用氢氧化铝或者氢氧化镁,并通过按照与粘结剂复合材料相同的方式在第二片材1b的另一表面上施加阻燃粘结剂复合材料并干燥施加的复合材料来形成阻燃粘结剂复合材料层42b。形成阻燃粘结剂复合材料层42b的阻燃粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,36~45wt%的氢氧化铝和氢氧化镁的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,1~5wt%的异丁烷基含水发泡剂和异戊烷基含水发泡剂,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的选自阴离子消泡剂和非离子消泡剂中的任何一种。阻燃粘结剂复合材料层用下面的材料制成:95~97wt%的复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
然后,第二片材1c层叠在粘结剂复合材料层42a或者阻燃粘结剂复合材料层42b上。在第二片材1c上,形成印刷层43,而在印刷层43上施加具有与形成第一顶部涂层33的第一顶部涂覆复合材料相同的复合材料的第二顶部涂覆复合材料并进行干燥而形成第二顶部涂层44。两个片材1被层叠在一起,而生产出用作墙壁覆盖物、汽车内片材和建筑物饰面材料的叠层40。这里,第二片材1c被铺在粘结剂复合材料层42上,并在180~250℃的温度下在干燥炉中干燥20~40秒,这样第二片材1c牢固地层叠在下面的片材上。第二涂层44是通过使用回转筛工艺、照相凹版印刷工艺和渗透工艺按大约20~100g/m2的量施加第二顶部涂覆复合材料并干燥施加的复合材料形成的。
对粘结剂复合材料层42的压花可以在形成第二顶部涂层44之前或之后进行。为了最大化压花效果,优选地在利用放在雕刻辊中的热水、传热介质油或者电加热辊使雕刻的压花辊温度达到50~200℃的状态下,进行压花操作。
图5是表示由片材1的织物3加工成的墙壁覆盖物50的剖视图。首先,制备只用棉纤维制成的织物3。制备的织物3具有0.3mm的厚度(50~150g/m2)。在织物3的面对建筑物墙壁的一个表面上,使用照相凹版印刷法按大约20~50g/m2的量(基于固体)施加具有与第一涂层31的第一涂覆材料相同的复合材料的第三涂覆材料,并干燥施加的复合材料而形成第三涂层51a。
在织物3的与第三涂层51a相对的另一表面上,使用间隔涂布机工艺或者回转筛工艺施加第二含水泡沫复合材料,达到0.2~0.5mm的厚度(基于固体的100~300g/m2),于是形成第二含水泡沫复合材料层52a。第二含水泡沫复合材料施加在织物3的另一表面上,在180~250℃的温度下在干燥炉中进行凝胶化20~40秒(这里,含水发泡复合材料的内部泡沫状态变成大约50~70%的半泡沫状态),然后冷却,于是形成第二含水泡沫复合材料层52a。形成第二含水泡沫复合材料层52a的第二含水泡沫复合材料由下面的材料构成:10~50wt%的选自丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者混合物,5~10wt%的水,33.5~40wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,以及0.3~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种。第二含水泡沫复合材料材料层用下面的材料制成:95~97wt%的复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
然后,在第二含水泡沫复合材料层52a上形成印刷层53。然后,使用照相凹版印刷工艺按大约20~50g/m2的量(基于固体)在印刷层53上施加具有与形成第一顶部涂层33的第一顶部涂覆材料相同的复合材料的第一顶部涂覆材料,并进行干燥以形成第三顶部涂层54。然后进行第三顶部涂层54的压花,于是完成从织物3生产墙壁覆盖物50。
为了赋予墙壁覆盖物50以阻燃性,可以取代第三涂层51a形成具有与形成第一阻燃涂层41b的第一阻燃涂覆材料相同的复合材料的第二阻燃涂覆材料51b,以形成第二阻燃涂层。或者,可以取代第二含水泡沫复合材料层52a施加含水阻燃泡沫复合材料,以形成含水阻燃泡沫复合材料层52b,于是赋予墙壁覆盖物50以阻燃性。形成含水阻燃泡沫复合材料层52b的含水阻燃泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者两种或更多种的混合物,5~10wt%的水,33.5~40wt%的无机填充物、氢氧化铝和氢氧化镁的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者两种或更多种的混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的选自非离子乳化剂、阴离子乳化剂和两性乳化剂中的任何一种,以及0.3~0.5wt%的非离子分散剂和阴离子分散剂。含水阻燃泡沫复合材料由下面的材料制成:95~97wt%的复合材料,以及3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
工业实用性
如上所述,本发明提供了一种环境友好型内部片材,这种片材包括或者只用棉纤维制成的纤维,或者所述纤维和沉积在上面的生物可降解的天然材料,于是,这种片材具有天然的质地和立体感。还有,不同于用由有机化学材料制成的纱线生产出来的现有片材,根据本发明的片材在被焚化或者埋在填埋场中时,不会造成环境污染。
Claims (14)
1.一种内部片材,包括:
多层织物,所述多层织物由多个堆叠的梳理后的棉纤维薄层构成;以及
树脂层,所述树脂层施加在所述织物的一个表面上并由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成。
2.如权利要求1所述的内部片材,其中,在所述织物和所述树脂层之间按5~150g/m2的量进一步形成天然材料层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成。
3.如权利要求1所述的内部片材,其中,在所述树脂层和所述天然材料层之间进一步插置有具有与所述织物的材料相同的材料的织物。
4.一种内部片材,包括:
底片材,所述底片材包括由多个梳理后的棉纤维薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物一个表面上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;
第一涂层,所述第一涂层施加在所述底片材的一个表面上并用第一涂覆材料制成,所述第一涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石、石英斑岩和陶瓷粉末、以及发射阴离子的硒中的任何一种,以及11.5~14wt%的选自甲醇和含水乙醇中的任何一种;
印刷层,所述印刷层形成在所述底片材的另一表面上,与所述第一涂层相对;以及
第一顶部涂层,所述第一顶部涂层施加在所述印刷层上并用第一顶部涂覆材料制成,所述第一顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的石蜡、聚乙烯蜡、硅酮基防水剂和氟基防水剂,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
5.如权利要求4所述的内部片材,其中,进一步包括在所述第一顶部涂层上形成的用第一含水泡沫复合材料制成的第一含水泡沫复合材料层,所述第一含水泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者混合物,5~10wt%的水,32.5~35wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~8wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(一乙烯乙二醇),1~10wt%的浆粉,0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,0.3~0.5wt%的非离子分散剂和阴离子分散剂中任何一种,以及1~2wt%的碱性墨水和酸性墨水以及盐基染料和碱性染料中的任何一种。
6.一种内部片材,包括:
第一底片材,所述第一底片材包括由多个梳理后的棉纤维的薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母粉末、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;
第二涂层,所述第二涂层施加在所述底片材的一个表面上并用第一涂覆材料制成,所述第一涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石、石英斑岩和陶瓷粉末、以及发射阴离子的硒中的任何一种,以及11.5~14wt%的选自甲醇和含水乙醇中的任何一种;
粘结剂复合材料层,所述粘结剂复合材料层施加在所述底片材的另一表面上,与所述第二涂层相对,所述粘结剂复合材料层用粘结剂复合材料制成,所述粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,36~45wt%的选自碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,1~5wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的消泡剂;
第二底片材,所述第二底片材施加在所述粘结剂复合材料层上并具有与所述第一底片材的复合材料相同的复合材料;
印刷层,所述印刷层形成在层叠于所述粘结剂复合材料层上面的底片材的表面上;以及
第二顶部涂层,所述第二顶部涂层施加在所述印刷层上并用第二顶部涂覆材料制成,所述第二顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的石蜡、聚乙烯蜡、硅酮基防水剂和氟基防水剂,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
7.如权利要求6所述的内部片材,其中,所述粘结剂复合材料层由下面的材料构成:95~97wt%的所述粘结剂复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
8.一种内部片材,包括:
第一底片材,所述第一底片材包括由多个梳理后的棉纤维的薄堆叠层构成的多层织物、按5~150g/m2的量施加在所述织物一个表面上的天然材料层和由选自丙烯酸树脂、EVE树脂和生物可降解EVE树脂中的任何一种构成的树脂层,所述天然材料层由选自木粉、谷壳粉末、绿茶粉末、艾蒿粉末、木炭粉末、多年生植物的经压缩和干燥的茎、叶、花叶、落叶和落叶粉末、阔叶树或者针叶树的叶、多年生干草、经热膨胀的蛭石、片状云母粉末、切成一定长度的蕉麻纤维、椰子纤维以及大麻纱中的任何一种或者两种或更多种的混合物构成;
第一阻燃涂层,所述第一阻燃涂层施加在所述底片材的一个表面上并用第一阻燃涂覆材料制成,所述第一阻燃涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水生物可降解EVA树脂中的任何一种,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,22~40wt%的氢氧化铝和氢氧化镁的混合物,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,以及9.5~14wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种;
阻燃粘结剂复合材料层,所述阻燃粘结剂复合材料层施加在所述底片材的另一表面上,与所述第一阻燃涂层相对,所述阻燃粘结剂复合材料层用阻燃粘结剂复合材料制成,所述阻燃粘结剂复合材料由下面的材料构成:20~50wt%的选自含水丙烯酸树脂、EVA树脂、生物可降解EVA树脂、含水聚乙烯树脂和水溶性松香树脂中的任何一种或者两种或更多种的混合物,4~10wt%的水,0.2~0.5wt%的选自阴离子分散剂和非离子分散剂中的任何一种,36~45wt%的氢氧化铝和氢氧化镁的混合物,3~5wt%的二氧化硅粉末,2~5wt%的浆粉,2~5wt%的选自轻质微细胞材料和微囊式轻质材料中的任何一种或者混合物,1~5wt%的异丁烷基含水发泡剂和异戊烷基含水发泡剂,1.5~4wt%的MEG(一乙烯乙二醇),以及0.3~0.5wt%的选自阴离子消泡剂和非离子消泡剂中的任何一种;
第二底片材,所述第二底片材层叠在所述阻燃复合材料层上并用与所述第一底片材的材料相同的材料制成;
印刷层,所述印刷层形成在层叠于所述阻燃粘结剂复合材料层上面的所述第二底片材的表面上;以及
第二顶部涂层,所述第二顶部涂层施加在所述印刷层上并用第二顶部涂覆复合材料制成,所述第二顶部涂覆复合材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水甲醇中的任何一种,5~10wt%的选自聚乙烯蜡、硅酮蜡和巴西棕榈蜡中的任何一种或者混合物,5~10wt%的珠光体和/或片状云母粉末,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡和硅酮蜡、以及氟基防水剂中的任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
9.如权利要求8所述的内部片材,其中,所述阻燃粘结剂复合材料层由下面的材料构成:95~97wt%的所述阻燃粘结剂复合材料,和3~5wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒中的任何一种。
10.一种内部片材,包括:
多层织物,所述多层织物由多个梳理后的棉纤维的薄堆叠层构成;
第三涂层,所述第三涂层施加在所述织物的一个表面上并用第三涂覆材料制成,所述第三涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂、含水氨基甲酸乙酯树脂、含水生物可降解EVA树脂中的任何一种或者两种或更多种的混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,20~40wt%的碳酸钙以及/或者滑石,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种,以及11.4~14wt%的选自甲醇和含水甲醇中的任何一种;
第二含水泡沫复合材料层,所述第二含水泡沫复合材料层施加在所述织物的另一表面上,与所述第三涂层相对,所述第二含水泡沫复合材料层用第二含水泡沫复合材料制成,所述第二含水泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者混合物,5~10wt%的水,33.5~40wt%的选自无机填充物、碳酸钙、滑石和二氧化钛中的两种或更多种的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的非离子乳化剂、阴离子乳化剂和两性乳化剂,以及0.3~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种;
印刷层,所述印刷层形成在所述第二含水发泡复合材料层上;以及
第三顶部涂层,所述第三顶部涂层施加在所述印刷层上并用第三顶部涂覆材料制成,所述第三顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯基水溶性蜡、硅酮基水溶性蜡和巴西棕榈基水溶性蜡中的任何一种或者两种或更多种的混合物,5~10wt%的选自珠光体和片状云母粉末中的任何一种或者混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡、硅酮基防水剂以及氟基防水剂中的任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
11.如权利要求10所述的内部片材,其中,所述第二含水泡沫复合材料层由下面的材料构成:95~97wt%的所述含水泡沫复合材料,和3~5wt%的发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒。
12.一种内部片材,包括:
多层织物,所述多层织物由多个梳理后的棉纤维的薄堆叠层构成;
第二阻燃涂层,所述第二阻燃涂层施加在所述织物的一个表面上并用第二阻燃涂覆材料制成,所述第二阻燃涂覆材料由下面的材料构成:15~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水生物可降解EVA树脂中的任何一种,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,15~20wt%的水,22~40wt%的氢氧化铝和氢氧化镁的混合物,0.3~0.5wt%的选自硅酮基消泡剂和非硅酮基消泡剂中的任何一种,3~10wt%的选自发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩、以及发射阴离子的硒中的任何一种,以及9.5~14wt%的选自甲醇和含水乙醇中的任何一种;
含水阻燃泡沫复合材料层,所述含水阻燃泡沫复合材料层施加在所述织物的另一表面上,与所述第二阻燃涂层相对,所述含水阻燃泡沫复合材料层用含水阻燃泡沫复合材料制成,所述含水阻燃泡沫复合材料由下面的材料构成:10~50wt%的选自含水丙烯酸树脂、含水EVA树脂和含水氨基甲酸乙酯树脂中的任何一种或者两种或多种的混合物,5~10wt%的水,33.5~40wt%的无机填充物、氢氧化铝和氢氧化镁的混合物,5~14wt%的二氧化硅粉末,2~10wt%的选自异丁烷基含水发泡剂和异戊烷基含水发泡剂中的任何一种或者两种或更多种的混合物,3~10wt%的MEG(一乙烯乙二醇),1~5wt%的浆粉,0.2~0.5wt%的选自非离子乳化剂、阴离子乳化剂和两性乳化剂中任何一种,以及0.3~0.5wt%的非离子分散剂和阴离子分散剂;
印刷层,所述印刷层形成在所述含水阻燃发泡复合材料层上;以及
第三顶部涂层,所述第三顶部涂层施加在所述印刷层上并用第三顶部涂覆材料制成,所述第三顶部涂覆材料由下面的材料构成:40~70wt%的选自含水丙烯酸树脂、含水氨基甲酸乙酯树脂、含水三聚氰胺树脂中的任何一种或者两种或更多种的混合物,3~5wt%的二氧化硅粉末,6~18wt%的选自甲醇和含水乙醇中的任何一种,5~10wt%的选自聚乙烯基水溶性蜡、硅酮基水溶性蜡和巴西棕榈基水溶性蜡中的任何一种或者两种或更多种的混合物,5~10wt%的选自珠光体和片状云母粉末中的任何一种或者混合物,0.2~0.5wt%的选自非离子分散剂和阴离子分散剂中的任何一种,10~15wt%的选自石蜡、聚乙烯蜡、硅酮基防水剂以及氟基防水剂中任何一种,0.5~1wt%的选自碱性墨水和酸性墨水以及碱性染料中的任何一种,以及0.3~0.5wt%的消泡剂。
13.如权利要求12所述的内部片材,其中,所述含水阻燃泡沫复合材料层由下面的材料构成:95~97wt%的所述含水泡沫复合材料,和3~5wt%的发射远红外线的材料、玉、硬木木炭、黄土、锗、伊利石和石英斑岩以及发射阴离子的硒。
14.一种生产内部片材的方法,所述方法包括步骤:
制备或者用棉纤维制成的多层底片材,或者包括按顺序沉积在用棉纤维制成的多层织物的一个表面上的天然材料和树脂材料的底片材;
在所述底片材的一个表面上施加阻燃或者非阻燃涂覆材料,以形成涂层;
在所述底片材的与所述涂层相对的另一表面上施加阻燃或者非阻燃粘结剂复合材料或者含水泡沫复合材料,以形成复合材料层;
在所述复合材料层的表面上形成具有多种图案的印刷层;
在所述印刷层上施加形成透明膜的顶部涂覆材料,以获得上面形成有顶部涂层的叠层;
使所述叠层发泡以形成泡沫化材料;以及
用经雕刻的压花辊对所述泡沫化材料进行压花,所述压花辊具有利用内置加热装置达到的50~200℃的表面温度。