CN101157543B - Method for making ceramic tile with metallic luster local interspersing surface - Google Patents
Method for making ceramic tile with metallic luster local interspersing surface Download PDFInfo
- Publication number
- CN101157543B CN101157543B CN2007100305353A CN200710030535A CN101157543B CN 101157543 B CN101157543 B CN 101157543B CN 2007100305353 A CN2007100305353 A CN 2007100305353A CN 200710030535 A CN200710030535 A CN 200710030535A CN 101157543 B CN101157543 B CN 101157543B
- Authority
- CN
- China
- Prior art keywords
- biscuit
- glaze
- ceramic tile
- ceramic
- concaves
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a production method of ceramic tile with metallic luster partial embellishment surface, which includes such working procedures as biscuit formation, spray glazing, silk screen printing and firing process. Ceramic semi-finished materials are pressed by a ceramic pressing machine into biscuit, and the pressing machine mold is distributed with bulges, thereby forming a plurality of concaves with a diameter less than 5mm on the surface of the pressed biscuit. 400 to 700 concaves are distributed per square meter. After the biscuit with concaves is dried, the surface of the biscuit is spurted evenly with metallic glaze by spray glazing equipment. After dryness, the metallic glaze on the surface of the biscuit is abraded by a frosting machine, and only the metallic glaze remains in the concaves, and then the silk screen printing and the rotary printing are done successively. At length, the ceramic tile is produced from firing under the temperature of 1,190 DEG C for 50 to 60 minutes. The method enables the sunken surface of the ceramic tile to have bright metallic luster, while the plane part is the texture in the style of antiquity. The overall vision is gracefuland noble, and the decoration effect is rich.
Description
Technical field
The present invention relates to production, the making method of ceramic tile, the particularly variation of ceramic brick surface decorative effect, innovation.
Background technology
In present Building Ceramics Industry, the ceramic tile product is that the master develops into a plurality of kinds such as polished tile, entire body brick, ornamental brick gradually from single polished tile, and interpenetrating, changing between the product category is also very many.And surface decoration effect also develops to the direction of combination stamp, multiple stamp from single glaze spraying, pouring glaze, screen printing, rotary printing, therefore, the ceramic tile pattern that produces upgrades rapid, various, such as imitative bag reason, simulated leather texture, imitative cloth texture or the like.Along with metal glaze---manifest the appearance of the glaze of metalluster, color and luster after burning till, further enriched the decorative effect of ceramic tile, as the ceramic tile of imitative metallic surface effect.But this series products changes seldom because metal glaze is more bigger in the distribution of brick face, and decorative effect is too single, grave and stern, lacks active style.
Summary of the invention
Purpose of the present invention is exactly the weak point that will overcome conventional art, bond glaze technology, screen printing technology also cooperate forming mould, propose various changeable, the noble elegance of visual effect of a kind of pattern, the method for making ceramic tile with metallic luster local interspersing surface that expressive force is abundant.
The objective of the invention is to be achieved through the following technical solutions: a kind of method for making ceramic tile with metallic luster local interspersing surface, include forming of green body operation, glaze spraying operation, screen printing operation, ablating work procedure, ceramic batch forms biscuit through the ceramic press compacting, be distributed with projection on the press die, make on the biscuit surface of extrusion to be formed with a plurality of pits of diameter less than 5mm, pit be distributed as 400-700/m
2, the band pit biscuit after drying, by glaze spraying equipment even metal glaze on surperficial cloth, after the drying, grind off the metal glaze in the only surplus pit with the metal glaze of skin grinder with the biscuit surface, then carry out screen printing, rotary printing, after burnt till in 1190 ℃ of high temperature 50-60 of roller kiln minutes.Owing to remain with metal glaze in the pit, make that the ceramic brick surface that burns till has metalluster, color and luster is interspersed partly in the surface.Further, the effect that horn of plenty is interspersed, the pit of biscuit surface arrangement, the 48-53% that accounts for that accounts for 25-34%, diameter 3-5mm that accounts for 13-16%, diameter 2-3mm that diameter 2mm is following.For demonstrating fully metalluster, the formulation weight per-cent of metal glaze is: aluminium sesquioxide 18.34%, silicon-dioxide 37.23%, ferric oxide 13.28%, calcium oxide 1.82%, magnesium oxide 0.57%, potassium oxide 4.11%, titanium oxide 5.21%, Vanadium Pentoxide in FLAKES 16.93%, sodium dioxide 0.01%, four oxidations, two manganese 0.04%, aluminum oxide 0.14%, the metal glaze water ratio is 50%.Time more obvious for four boundary layers that make ceramic tile, change abundantlyer, four limits on biscuit surface all are ups and downs irregularity limits.For glaze and the metal shaft that prevents screen printing reacts, influence decorative effect, biscuit is after skin grinder grinds off the surface metal glaze, and the formulation weight per-cent of the first road printing glaze is: Wingdale 8.57%, wollastonite 4.28%, albite 5.71%, potassium felspar sand 11.7%, aluminum oxide powder 10%, burning talcum 8.57%, zirconium silicate 9.14%, frit 5.71%, kaolin 2.56%, ethylene glycol 16%, water 16%.
Technical characterstic of the present invention and advantage:
1, technical process is that biscuit forms pit, metal glaze, frosted, one screen printing, multiple tracks rotary printing, and interspersing with decalcomania, texture of metalluster brought out the best in each other, and expression effect is very abundant;
2, the pit of brick surface distribution and the concavo-convex fluctuating on brick four limits, metal glaze is indistinct, makes decorative effect noble elegant;
3, making method and uncomplicated has integrated various routines, traditional technology, but creates a kind of unique decorative effect.
Embodiment
Embodiment one: the ceramic tile with 300 * 300mm specification is an example, the distribution of biscuit surface crater: 12 of the pits below 23 of the pits of 39 of the pits of 5mm diameter, 3mm, the 2mm, ceramic batch is after the ceramic press compacting forms biscuit, through dry 20 minutes of the dry kiln by 180 ℃-210 ℃, the water content of biscuit dropped to 0.8-1.5% about by 6.3-7%.The biscuit that has a pit uses glaze spraying equipment even metal glaze on cloth on the biscuit after drying.The metal glaze water content is 50%, the metal glaze prescription is: aluminium sesquioxide 18.34%, silicon-dioxide 37.23%, ferric oxide 13.28%, calcium oxide 1.82%, magnesium oxide 0.59%, potassium oxide 4.11%, sodium oxide 5.21%, Vanadium Pentoxide in FLAKES 16.93%, titanium dioxide 0.01%, four oxidations, two manganese 0.04%, aluminum oxide 0.14%, after the glaze spraying drying, use skin grinder, the metal glaze major part on biscuit surface is ground off, remain with metal glaze in only remaining pit or the brick four limit recess, go up the screen printing glaze then one, then go up twice rotary printing glaze, then go up twice screen printing glaze again, fire through roller kiln then, 1190 ℃ of firing temperatures, 50 minutes time.Produce the silvery ceramic tile of local interspersing at last.
Embodiment two
Technology and embodiment one are basic identical, just adopt the ceramic tile of 600 * 600mm specification, and the pit of 5mm has 162, the pit of 3mm to have 75 on the biscuit, and the following pit of 2mm has 53,1190 ℃ of 60 minutes times of firing temperature.
Claims (2)
1. method for making ceramic tile with metallic luster local interspersing surface, include forming of green body operation, glaze spraying operation, screen printing operation, ablating work procedure, it is characterized in that: ceramic batch forms biscuit through the ceramic press compacting, be distributed with projection on the press die, make on the biscuit surface of extrusion to be formed with a plurality of pits of diameter less than 5mm, pit be distributed as 400---700/m
2, the band pit biscuit after drying, by glaze spraying equipment even metal glaze on surperficial cloth, after the drying, grind off the metal glaze in the only surplus pit with the metal glaze of skin grinder with the biscuit surface, then carry out screen printing, rotary printing, after burnt till in 1190 ℃ of high temperature 50---60 of roller kiln minutes.
2. method for making ceramic tile according to claim 1, four limits that it is characterized in that the biscuit surface all are ups and downs irregularity limits.