CN101139746A - 一种聚酰亚胺(pi)无纺布的制备方法 - Google Patents

一种聚酰亚胺(pi)无纺布的制备方法 Download PDF

Info

Publication number
CN101139746A
CN101139746A CNA2006100104839A CN200610010483A CN101139746A CN 101139746 A CN101139746 A CN 101139746A CN A2006100104839 A CNA2006100104839 A CN A2006100104839A CN 200610010483 A CN200610010483 A CN 200610010483A CN 101139746 A CN101139746 A CN 101139746A
Authority
CN
China
Prior art keywords
nonwoven fabric
polyimide
paa
preparation
voltage electrostatic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2006100104839A
Other languages
English (en)
Inventor
张明艳
张玉军
段宏伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Harbin University of Science and Technology
Original Assignee
Harbin University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Harbin University of Science and Technology filed Critical Harbin University of Science and Technology
Priority to CNA2006100104839A priority Critical patent/CN101139746A/zh
Publication of CN101139746A publication Critical patent/CN101139746A/zh
Pending legal-status Critical Current

Abstract

一种聚酰亚胺无纺布的制备方法，它涉及利用高压静电纺丝法制备聚酰亚胺无纺布的制备工艺。本发明以含柔性官能团的4，4’－二氨基二苯醚(ODA)和3，3’，4，4’－二苯醚四甲酸二酐(ODPA)为缩聚单体，合成聚酰胺酸(PAA)溶液，然后利用高压静电纺丝技术制备出PAA无纺布，然后经高温处理使PAA发生缩聚反应生成聚酰亚胺(PI)，即可得到PI无纺布。该发明得到的聚酰亚胺无纺布纤维直径分布在0.5～2μm，热分解温度在500℃以上，横向拉伸强度为18MPa，纵向拉伸强度为16MPa。

Description

一种聚酰亚胺(PI)无纺布的制备方法
技术领域：
本发明涉及利用高压静电纺丝法制备聚酰亚胺无纺布的工艺。
背景技术：
静电纺丝技术工艺简单，操作方便，是制备超细纤维及其无纺布的重要方法。聚合物熔体或溶液在高压静电作用下，利用电场力克服聚合物表面张力形成一股带电的喷射流，之后溶剂挥发固化，纳米级纤维无序地排列在收集板上，形成无纺布纤维膜。因其具有纤维直径小、表面积大、孔隙率高等特点，具有广泛的应用前景。聚酰亚胺(Polyimide，简称PI)是目前已经工业化的工程塑料中耐热性能最好的品种之一，因具有其它材料无法比拟的突出强度、耐磨性以及在极端温度下优异的形状和化学稳定性，而被广泛地应用于航天、航空、原子能、膜分离技术、精密及大型机电产品、液晶显示等高技术领域。同时，由于聚酰亚胺具有突出的耐高温性能、介电性能和优良的抗辐射性能，它作为功能材料在微电子工业及大规模和超大规模集成电路中获得日益广泛的应用。随着我国高新技术产业的发展，对聚酰亚胺的需求量将越来越大，聚酰亚胺是一种很有前途的高分子材料。聚酰亚胺无纺布经树脂漆浸渍或涂覆，再经烘焙、干燥而成的柔软绝缘材料，可广泛应用于电器线圈包扎、衬垫绝缘和配线绝缘等。
发明内容：
本发明的目的是提供一种聚酰亚胺无纺布的制备方法，利用高压静电纺丝法制备得到聚酰亚胺无纺布。本发明以含柔性官能团的4，4’-二氨基二苯醚(ODA)和3，3’，4，4’-二苯醚四甲酸二酐(ODPA)为缩聚单体，合成聚酰胺酸(PAA)溶液，然后利用高压静电纺丝技术制备出PAA无纺布，经高温处理使PAA发生缩聚反应生成聚酰亚胺(PI)，即可得到PI无纺布。该发明得到的聚酰亚胺无纺布纤维直径分布在0.5～2μm，热分解温度在500℃以上，横向拉伸强度为18MPa，纵向拉伸强度为16MPa。
具体实施方式：
1、可溶性PAA的合成
在室温下，将一定量的ODA溶解在DMAC中，不断搅拌，直到ODA完全溶解并成无色透明溶液，将等当量的ODPA分批加入到溶液中，当快达到等当量点时，聚酰胺酸的粘度迅速增大，继续搅拌2h，使其粘度达到稳定。
2、PAA无纺布的制备
将一定浓度PAA的纺丝液抽入计量泵中，然后调节喷丝口与接收屏的间距。把电极的一端接到喷丝口上，随后启动高压电源调节电压使电纺丝过程稳定。在喷丝口上的电极和收集电极之间的高压电场给高分子溶液施加电场力，纺丝溶液在电场力的作用下形成泰勒锥，当电场力达到一定程度足以克服溶液的表面张力时，从毛细管喷嘴喷出，溶液在运动的过程中发生裂分形成无数的细小的纤维，同时溶剂的挥发并形成PAA无纺布，并被收集在收集轮上。
3、PI无纺布的制备
将制得的PAA无纺布放在真空烘箱内分别在80℃下0.5h，120℃下0.25h，200℃下0.25h，250℃下0.25h，300℃下1h，进行阶梯升温，使其PAA发生缩聚反应脱除水分子生成PI，同时高沸点的溶剂被除去，然后缓慢冷却至室温，即可得到PI无纺布。

Claims (7)

1.一种聚酰亚胺(PI)无纺布的制备方法，其特征在于以含柔性官能团的4，4’-二氨基二苯醚(ODA)和3，3’，4，4’-二苯醚四甲酸二酐(ODPA)为缩聚单体，合成聚酰胺酸(PAA)溶液，然后利用高压静电纺丝技术制备出PAA无纺布，然后经高温处理使PAA发生缩聚反应生成聚酰亚胺(PI)，即可制得本发明的聚酰亚胺(PI)无纺布。
2.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的制备方法为高压静电纺丝技术。
3.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的利用高压静电纺丝技术制备出PAA无纺布。
4.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的利用高压静电纺丝技术制备出的PAA无纺布，经高温处理得到PI无纺布。
5.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的聚酰亚胺无纺布纤维直径分布在0.5～2μm。
6.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的聚酰亚胺无纺布的热分解温度在500℃以上。
7.根据权利要求一所述的一种聚酰亚胺无纺布的制备方法，其特征在于所述的聚酰亚胺无纺布的横向拉伸强度为18MPa，纵向拉伸强度为16MPa。
CNA2006100104839A 2006-09-04 2006-09-04 一种聚酰亚胺(pi)无纺布的制备方法 Pending CN101139746A (zh)