CN101104771A - 水性环氧富锌底漆 - Google Patents
水性环氧富锌底漆 Download PDFInfo
- Publication number
- CN101104771A CN101104771A CNA2007101433240A CN200710143324A CN101104771A CN 101104771 A CN101104771 A CN 101104771A CN A2007101433240 A CNA2007101433240 A CN A2007101433240A CN 200710143324 A CN200710143324 A CN 200710143324A CN 101104771 A CN101104771 A CN 101104771A
- Authority
- CN
- China
- Prior art keywords
- water
- zinc
- based epoxy
- rich primer
- primer according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
A组分 | 项目 | 实施例 | ||||||
1# | 2# | 3# | 4# | 5# | 6# | 7# | 8# | |
水性环氧固化剂EPI-KURE 8545-W-52(美国汉森) | 4 | 4 | 4 | 4 | 8 | 8 | 8 | 8 |
400目锌粉 | 78 | 78 | 78 | 78 | 78 | 82 | 82 | 86 |
丙二醇甲醚 | 9 | 9 | 9 | 9 | 5 | 4 | 4 | 5 |
分散剂T-731(罗门哈斯) | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 |
消泡剂NXZ(德国汉高) | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 |
600目云母粉 | 3 | 0 | 0 | 0 | 8 | 0 | 0 | 0 |
600目滑石粉 | 0 | 3 | 0 | 0 | 0 | 0 | 0 | 0 |
600目煅烧高岭土 | 0 | 0 | 3 | 0 | 0 | 0 | 0 | 0 |
600目轻质碳酸钙 | 0 | 0 | 0 | 3 | 0 | 0 | 0 | 0 |
磷酸锌 | 5 | 5 | 0 | 0 | 0 | 5 | 0 | 0 |
三聚磷酸铝 | 0 | 0 | 5 | 5 | 0 | 0 | 5 | 0 |
羟乙基纤维素ER30M(美国陶氏) | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 | 0.2 |
合计 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | |
B组份 | 三乙胺 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
软化水 | 84.5 | 79.5 | 74.5 | 69.5 | 54.5 | 49.5 | 44.5 | 39.5 | |
水性环氧分散体EPIKOTE3520(美国汉森) | 15 | 20 | 25 | 30 | 0 | 0 | 0 | 0 | |
水性环氧乳液EPIKOTE3510-W-60(美国汉森) | 0 | 0 | 0 | 0 | 45 | 50 | 55 | 60 | |
合计 | 100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
项目 | 实施例 | 对比例 | 指标 | ||||||||
1# | 2# | 3# | 4# | 5# | 6# | 7# | 8# | 1# | 2# | ||
开罐状态 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 均匀无沉淀 |
涂层外观 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 合格 | 平整光滑无颗粒 | |
粘度,CPS,≥ | 2.5 | 2.5 | 2.6 | 2.6 | 2.4 | 2.5 | 2.6 | 2.2 | 2.3 | 2.1 | ≥2 | |
固体份,%,≥ | 70 | 70 | 70 | 70 | 70 | 70 | 70 | 70 | 72 | 66 | ≥60 | |
干燥时间 | 表干,min | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 30 | 30 | ≤60 |
实干,h | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | 24 | ≤24 | |
附着力,级 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | |
耐冲击,cm | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | 50 | ≥40 | |
柔韧性,mm | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | ≤2 | |
耐盐雾,h | 通过 | 通过 | 通过 | 通过 | 通过 | 通过 | 通过 | 通过 | 通过 | 通过 | 1000 | |
一道干膜厚,μm | 10-110 | 10-110 | 10-110 | 10-110 | 10-110 | 10-110 | 10-110 | 10-110 | 10-40 | 10-40 | ≥10 |
Claims (13)