CN102533051A - 一种船用环氧敷料 - Google Patents
一种船用环氧敷料 Download PDFInfo
- Publication number
- CN102533051A CN102533051A CN2011104448884A CN201110444888A CN102533051A CN 102533051 A CN102533051 A CN 102533051A CN 2011104448884 A CN2011104448884 A CN 2011104448884A CN 201110444888 A CN201110444888 A CN 201110444888A CN 102533051 A CN102533051 A CN 102533051A
- Authority
- CN
- China
- Prior art keywords
- ylene
- weight percent
- components
- propyl carbinol
- product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种船用环氧敷料，基础甲板敷料表面上敷设下部涂层，下部涂层上敷设彩砂层，彩砂层上敷设上部涂层；下部涂层是A料和B料按3:1的重量比混合搅拌而成的产物；彩砂层是A料、B料以及彩砂按3:1:1的重量比混合搅拌而成的产物；上部涂层也是A料和B料按3:1的重量比混合搅拌而成的产物。本发明具有耐磨及耐化学性能强，施工方便，节约施工成本等优点。
Description
技术领域
本发明涉及一种船用敷料，尤其涉及一种船用环氧敷料。
背景技术
目前，对于船舶的防水材料主要是乳胶甲板敷料，现有的乳胶甲板敷料虽然起到防水的效果，但是在实际应用中，为外表美观，便于清洁，基础甲板敷料的上部还是要铺设一层瓷砖，而瓷砖的防水性能较差，另外，使用瓷砖务必加大施工程度，延长作业时间，而且不能达到色彩华丽的效果，尤其对于船舶内的实验室、机械室以及冷藏库等需要耐化学腐蚀的区域，瓷砖的效果不是很理想。
发明内容
本发明的目的在于提供一种不仅具有良好的防水性和华丽美观的色彩，而且耐磨及耐化学性能强，施工方便，节约施工成本的船用环氧敷料。
一种船用环氧敷料，技术方案如下：本发明是由三层即下部涂层、彩砂层以及上部涂层组成的，其中下部涂层是A料和B料按3:1的重量比混合搅拌而成的产物，所述A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物，其中优选的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土；所述B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物，其中优选的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。
彩砂层是A料、B料以及彩砂按3:1:1的重量比混合搅拌而成的产物，其中A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物，其中优选的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土；所述彩砂为公知的染色彩砂；所述B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物，其中优选的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。
上部涂层也是A料和B料按3:1的重量比混合搅拌而成的产物，所述A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物，其中优选的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土；所述B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物，其中优选的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。
本发明的适用范围是在船舶的地板、实验室、机械室、需要耐化学性处理的地板、冷藏室等。
本发明的制备及施工方法：
施工前，要保证基础甲板敷料已经敷设15天以上，敷设本发明之前，要清理基础甲板敷料上污物、油、水分等物质，先在基础甲板敷料表面上敷设本发明的下部涂层，即按3:1的重量比混合A料和B料，然后将A料和B料的混合物利用搅拌机搅拌均匀，搅拌后将混合物均匀涂抹在基础甲板敷料的表面；待下部涂层充分干燥后，在下部涂层上敷设彩砂层，即将A料、B料以及彩砂按3:1:1的重量比混合，然后将混合物利用搅拌机搅拌均匀，搅拌后将混合物均匀涂抹在下部涂层的表面；待彩砂层充分干燥后，在彩砂层上敷设上部涂层，即将A料和B料按3:1的重量比混合，然后将混合物利用搅拌机搅拌均匀，搅拌后将混合物均匀涂抹在彩砂层的表面。
本发明与现有技术相比具有如下优点：
1、色彩好，外表华丽美观，易清洁；
2、具有良好的防水性、耐磨性以及耐化学性；
3、施工简便，作业效率高，维护方便；
4、成本低，经济耐用。
附图说明
本发明无附图。
具体实施方式
实施例1
一种船用环氧敷料，由三层即下部涂层、彩砂层以及上部涂层组成，下部涂层是A料和B料按3:1的重量比混合搅拌而成的产物， A料是重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土混合搅拌而成的产物；B料是重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇混合搅拌而成的产物。
彩砂层是A料、B料以及彩砂按3:1:1的重量比混合搅拌而成的产物， A料是重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土混合而成的产物；彩砂为染色彩砂；B料是重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇混合而成的产物。
上部涂层也是A料和B料按3:1的重量比混合搅拌而成的产物，A料是重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土混合搅拌而成的产物；B料是重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇混合搅拌而成的产物。
Claims (7)
1.一种船用环氧敷料，其特征是：由三层即下部涂层、彩砂层以及上部涂层组成，其中下部涂层是A料和B料按3:1的重量比混合搅拌而成的产物，所述A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物；所述B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物；彩砂层是A料、B料以及彩砂按3:1:1的重量比混合搅拌而成的产物，A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物；彩砂为染色彩砂； B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物；上部涂层也是A料和B料按3:1的重量比混合搅拌而成的产物，A料是重量组分为40%～60%环氧树脂、5%～10%二甲苯、1%～5%正丁醇、1%～5%醋酸丁醇、1%～5%分散剂、1%～5%消泡剂、5%～10%流平剂、1%～5%氧化铁红、1%～5%硫酸钡、5%～10%滑石粉、10%～20%石英砂以及1%～5%有机膨润土混合搅拌而成的产物；B料是由重量组分为50%～60%聚酰胺树脂、30%～40%二甲苯以及5%～10%正丁醇混合搅拌而成的产物。
2.根据权利要求1所述的船用环氧敷料，其特征是：下部涂层中的A料的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土。
3.根据权利要求1或2所述的船用环氧敷料，其特征是：下部涂层中的B料的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。
4.根据权利要求3所述的船用环氧敷料，其特征是：彩砂层中的A料的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土。
5.根据权利要求4所述的船用环氧敷料，其特征是：彩砂层中的B料的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。
6.根据权利要求5所述的船用环氧敷料，其特征是：上部涂层中的A料的重量组分为45%环氧树脂、8%二甲苯、2%正丁醇、3%醋酸丁醇、5%分散剂、2%消泡剂、5%流平剂、3%氧化铁红、2%硫酸钡、7%滑石粉、15%石英砂以及3%有机膨润土。
7.根据权利要求6所述的船用环氧敷料，其特征是：上部涂层中的B料的重量组分为60%聚酰胺树脂、32%二甲苯以及8%正丁醇。