CN100497262C - 改善受污损多孔表面外观并加以保持的方法 - Google Patents
改善受污损多孔表面外观并加以保持的方法 Download PDFInfo
- Publication number
- CN100497262C CN100497262C CNB2005800138970A CN200580013897A CN100497262C CN 100497262 C CN100497262 C CN 100497262C CN B2005800138970 A CNB2005800138970 A CN B2005800138970A CN 200580013897 A CN200580013897 A CN 200580013897A CN 100497262 C CN100497262 C CN 100497262C
- Authority
- CN
- China
- Prior art keywords
- floor
- maintaniing
- agent
- agent composition
- cleaning compositions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明与改善受污损多孔表面外观的方法有关。本发明中的方法包括对受污损的多孔表面施用高浓度的碱性清洁组合物。这种高浓度的碱性清洁组合物在表面接受水洗前会在表面上停留一段时间。等表面干燥后，再向表面施用维护剂组合物。维护剂组合物含有孔隙填充组分。该清洁组合物含有碱性物质。可以选择的是，该清洁组合物还可含有溶剂。
Description
发明领域
一般而言，本发明与改善受污损多孔表面的方法相关，尤其与改善受污损混凝土表面的方法相关。更具体而言，本发明与使混凝土表面光洁并保持这一表面光洁的方法有关。
发明背景
混凝土是水泥、水、沙子、粗石料和改性添加剂的硬化混合物。混凝土开始时是浆料状态，干燥后形成坚硬的表面。然而，由于混凝土中含有空气和各种组分，所以混凝土中自然存在微小的气隙和气孔，这些气隙和气孔会造成混凝土表面并不平坦，这一表面是一个多孔表面。此外，这些气孔形成锯齿结构，而不是平滑的结构，这样就使污渍进入到气孔中或使污渍牢牢地嵌入气孔中。因此，混凝土易于吸收或沾染污渍，并且难于清理。这些污渍会使混凝土表面变黑。此外，混凝土表面在一段时间后会被弄脏，并变得很不美观。
许多年来，混凝土由于其成本低廉，耐用性好以及维护要求低而成为仓库和生产没施内地板的理想材料。然而，由于这些设施自身的用途，人们并不关心仓库设施中地板的外观标准。大部分这些设施只在工作人员或设施提供商的视野内，并不会受到普通公众的注意。尤其是这些地板只要没有碎屑并且不致使人滑倒，人们就不会太在意混凝土表面的总体光洁度以及所存在的污渍。
近来，由于其成本低廉以及耐用性好，混凝土及彩色混凝土在零售业设施和其他商业设施变得愈来愈流行。很显然，由于这些设施的零售/商业性质，所以地板表面的外观对于零售企业的整体形象和留给消费者的印象是相当重要的。
在常规的零售业环境或其他设施中，人员往来频繁的混凝土地面部分会变得很黑，地面的孔隙中充满了来自商店内和停车场的碎屑。人们可以容易地看出地板上所形成的“行走路线”，在“行走路线”上，尘土和污渍的浓度很高。混凝土中所含有的污渍包括残余的固化剂、残余的涂料、沙子、陶土和沥青质。此外，在地板表面塑上还可以发现食品所形成的有机污渍、机油、灰尘、碳水化合物、脂肪、质白质类污渍等。
清洁混凝土表面的大多数方法都只限于对相对较小的受污损区域进行清洁，比如对户外车道或停车场表面上的油脂进行清洁。在这些情况下，通常是在污渍上撒上干燥的吸收材料，并来回扫动，从而将污渍吸收。然后将用过的吸收材料收集起来，并以适当的形式处理掉。在5,990,067号美国专利中有这样的吸收材料。在某些这样的系统中，吸收材料被弄湿，从而使清洁材料产生活性。然后用扫帚将这些材料扫除掉。
另外一种方法是在污渍上施用清洁组合物，然后将污渍冲洗掉。5,951,784号美国专利提供了这样一种实例。所有这类系统都只是针对混凝土表面上相对较小区域中的零散污渍。
在需要对整个混凝土表面进行处理时，传统的方法包括使用中性或碱性清洁剂对地板进行清洁，或使用永久性或半永久性封盖剂，或使用其他涂料。但是，常规的清洁剂并不能改善混凝土表面的光洁度，光亮度或光泽度。此外，虽然封盖剂和其他永久或半永久性涂料可以改善混凝土的总体光泽度，但随着时间的推移，这些封盖剂或涂料需要相当大的费用进行清除和更换。
总之，在改善、清洁和维护多孔表面；尤其是混凝土表面的技术中存在着大量的缺陷。在以往的技术中，虽然所用的组合物和方法也能清除掉混凝上的浓渍，但是清理过程需要大量人工和时间，所用的组合物和方法繁杂，对于较大的面积而言，比如对整个地板进行清洁时，清理这些组合物就使人不胜其烦，并且需要耗费大量的时间。此外，在对较大面积进行清洁时，以往的技术也达不到最佳的改善和清洁效果。再者，传统的地板清洁剂和相关的清洁方法也无法满足清洁混凝土多孔表面所需的特殊要求。此外，使用常规的清洁剂只能使光亮度和光泽度得到微小的改善。虽然使用永久性或半永久性涂料可以改善光泽度，但初次使用的费用和难度以及这些涂料日后清理和更换所带来的附加费用使它们不适于用在混凝土表面。
因此，研究人员进行了研究，从而寻找某种改善和维护像混凝土这样多孔表面的方法，这种方法应用简单，并以可以接受的使用方式改善光洁度和光泽度，同时保持多孔表面经改善后的外观。很显然，人们需要更好的方法并以有效的、成本低廉的方式来改善受到污损的多孔表面，并维持这一表面的外观，人们尤其需要一种能够改善和维护多孔表面的更佳方法，这一方法能够克服以往技术中的缺陷。
发明目的
本发明的目的是提供一种改善和维护多孔表面的方法，尤其是提供一种改善和维护混凝土表面的方法，该方法能够克服以往技术的某些问题和缺陷。本发明的另一目的是提供一种改善和维护混凝土表面的更佳方法，该方法能够以有效的方式改善和维护混凝土表面。本发明的另一目的是提供一种改善受污损多孔表面光洁度的方法，本发明的另一目的是提供一种无需使用永久性或半永久性涂料从而在表面形成较高光泽度的方法，本发明的另一目的是提供一种对多孔表面进行日常清洁的方法。本发明的另一目的是提供一种改善和维护多孔表面的方法，该方法并不需要费工、耗资的清除永久性或半永久性涂料，同时还能形成较高的光泽度。通过以下的说明和图示可以清楚地表明本发明的重要目的。
发明概述
本发明与改善和维护受污损多孔表面的方法相关。本发明中的方法包括向受污损的多孔表面施用高浓度的碱性清洁组合物。在用水冲洗之前，这种高浓度碱性清洁组合物会在表面上停留一段时间。在某些实施方案中，在对表面进行冲洗从而清理表面前，可对表面上的清洁组合物进行搅动。在表面干燥后，再向表面施加维护剂组合物。维护剂组合物含有孔隙填充组合。过量的维护剂会通过冲洗方式从表面上清除掉。然后使表面干燥。可以选择的是，可使用常规方法对表面进行抛光或擦拭，从而使表面达到更好的光泽度。由于表面会因为踩踏而再次受到污损，所以可以定期向表面施用维护剂，从而保持表面的良好外观。
本发明方法中所使用的清洁组合物含有碱性物质，可以选择的是，该清洁组合物还可含有溶剂。碱性物质可选自于以下物质：胺类物质、金属氧化物、硅酸盐、磷酸盐或这些物质的混合物。在某一实施方案中，碱性物质是乙醇胺。在另一实施方案中，碱性物质是硅酸盐，该硅酸盐选自于硅酸钠、硅酸钾、偏硅酸钠和这些物质的混合物。碱性物质还可以是磷酸盐，该磷酸盐选自于磷酸钾、焦磷酸钠、焦磷酸钾、三聚磷酸钠、三偏磷酸钠、六偏磷酸钠、三聚磷酸钾和这些物质的混合物。
适用于清洁组合物的溶剂包括乙二醇醚、醇类物质、酯类物质、酮类物质、吡咯烷酮、二甲基亚砜、乳酸乙酯、萜烯类物质、芳烃、氯化溶剂、脂肪族溶剂、二价酸酯和这些物质的混合物。
本发明方法中所用的维护剂组合物含有约0.5-100％的孔隙填充组分、0.001-1％的稀释剂、约0.5-90％的溶剂以及约0.5-50％的表面活性剂。孔隙填充组分选自于增塑剂、表面活性剂、皂质、油性物质、蜡质、树脂类物质、聚合物和这些物质的混合物。适用的增塑剂包括苯甲酸酯、二甘醇二苯甲酸酯、双丙甘醇二苯甲酸酯、苯甲酸异癸酯、邻苯二甲酸二丁酯、邻苯二甲酸丁苄酯、邻苯二甲酸二异庚酯、邻苯二甲酸二异十三酯、邻苯二甲酸十一烷基十二烷基酯、邻苯二甲酸二异十一酯、磷酸三芳基酯、磷酸三丁氧基乙酯和这些物质的混合物。
适合用作为孔隙填充组分的油类物质选自于矿物油、硅油、诸如椰子油、棕榈油、麻子油、柑桔油、柏油或豆油等这样的植物油以及这些油类物质的混合物。孔隙填充组分还可以是皂质，皂质选自于椰油皂质、松浆油皂质、麻子油皂质、棕榈油皂质、橄榄油皂质、牛油树脂、牛油酸钠、硬脂酸钠以及这些物质的混合物。表面活性剂也可用作维护剂组合物中的孔隙填充组分。适用的表面活性剂包括非离子表面活性剂，阴离子表面活性剂、两性表面活性剂、阳离子表面活性剂以及这些表面活性剂的混合物。
适用于维护剂组合物的另一种孔隙填充组分是蜡质材料，这些蜡质材料选自于蜂蜡、聚乙烯蜡、聚丙烯蜡以及这些蜡的混合物。
维护剂组合物还可以包括溶剂、表面活性剂、防腐剂、颜料、二级湿润剂、螯合剂、助溶剂、芳香剂、助洗剂以及螯合作用剂。
在本发明方法的某一实施方案中，该方法包括对受污损的多孔表面施用高浓度的碱性清洁组合物；所述的组合物含有约0.1-50％的碱性物质、0.1-50％的胺类物质以及0.1-90％的溶剂，所述的组合物在表面上停留一段时间，然后用水冲洗表面，清除过量的组合物，然后让表面干燥，并在表面上施用维护剂组合物；所述的维护剂组合物含有孔隙填充组分。在某一实施方案中，清洁组合物还含有约0.01-10％的湿润剂。该清洁组合物还含有约0.01-10％的乳化剂。
在本发明方法的某一实施方案中，该方法包括对受污损的多孔表面施用高浓度的碱性清洁组合物；所述的组合物含有约0.1-20％的碱性物质、0.1-30％的胺类物质以及0.1-90％的溶剂，所述的组合物在表面上停留一段时间，然后用水冲洗表面，清除过量的组合物，然后让表面干燥，并在表面上施用维护剂组合物；所述的维护剂组合物含有孔隙填充组分。在某一实施方案中，清洁组合物还含有约0.01-1％的湿润剂。该清洁组合物还含有约0.01-5.0％的乳化剂。
在另一实施方案中，本发明中改善受污损多孔表面的方法包括向受污损的多孔表面施用高浓度的碱性清洁组合物。该清洁组合物在表面上停留一段时间，然后用水进行冲洗，可以选择的是，可以将水除去并使表面干燥。然后向表面施用维护剂。该维护剂组合物含有孔隙填充组分。在对表面施用维护剂组合物后，多孔表面的滑动摩擦系数至少为0.5.
图示简介
图1是多孔表面的截面图。
图2是受污损表面的截面图。
图3是施用清洁组合物并将清洁组合物清除后多孔表面的截面图。
图4是施用维护剂组合剂后多孔表面的截面图。
优选实施方案的详细说明
本发明与改善受污损的表面有关，换一句话说就是，本发明与改善受污损的多孔混凝土表面外观的方法相关，比如与改善混凝土地板和混凝土墙面的外观相关。正如图1所示，多孔表面2上含有许多不规则形状的孔隙4。如图2所表示，过了一段时间后，灰尖和泥土颗粒6嵌入了多孔表面2的孔隙中。这使表面2呈现出较脏且污浊的外观。当表面2是零售设施中的地板或类似表面时，这种较脏的外观会令人十分关注。本发明中的方法提供一种机制，使用这种机制可以花费最小的努力而使嵌有或覆盖有泥土颗粒6的多孔表面得到清洁和维护。
本发明中的方法通过常规施用方法向受污损的多孔表面2施用高浓度的碱性清洁组合物，例如通过倾倒、拖把和料桶施用、机械施用等方法将高浓度碱性清洁组合物施用到受污损的多孔表面上。该清洁组合物在表面2上停留一段时间，然后用水对表面进行冲洗。正如图3所示，在清洁和冲洗过程中，大多数嵌入的泥土颗粒6被清除出孔隙4，但并非所有的泥土颗粒都被清除了出来。然后向表面2施用维护剂组合物，该维护剂组合物在表面上形成均匀的覆盖膜8，如图4所示。在优选情况下，维护剂组合物含有孔隙填充组分，这些孔隙填充组分会嵌入到孔隙4中，如图4所示。维护剂组合物中的孔隙填充组分可防止泥土颗粒嵌入孔隙4中，从而使多孔表面在较长的时间内保持清洁，并易于日常清理。本发明方法的另一实施方案还包括在冲洗前搅动表面上的清洁组合物。
本发明中的方法还包括定期向表面2上重复施用维护剂组合物。经常使用相同(或可能不同)的维护剂组合物维持地板的外观或对地板进行定期清洁可以使地板保持更佳的外观。一般而言，在经过初次处理后，使用维护剂组合物对地板进行定期清洁，这样可以清除掉表面上的尘土，并使新的维护剂组合物附着在表面上。
其他的步骤包括在施用维护剂组合物后对表面进行抛光或擦拭，从而使表面达到更高的光泽度。在施用维护剂组合物前、后使用抛光盘或擦拭片对地板进行抛光就可以完成地板外观的进一步改善。在一段时间内重复进行这一过程可使地板格外光亮。适合的抛光用擦拭片包括含有碳化硅、氧化铝、长石(碱性硅酸铝盐)、碳化钨、二氧化硅、浮石(无规硅酸铝)、碳化硼、金刚石、氮化硼等物质的擦拭片，但适用的擦拭片并不局限于这些擦拭片。
本发明中方法所用的清洁组合物含有碱性物质，可以选择的是，该清洁组合物还可含有溶剂。该碱性物质包括胺类物质、金属氧化物、硅酸盐、磷酸盐以及这些物质的混合物。在某一实施方案中，碱性物质是乙醇胺。适用的乙醇胺可以从美国德克萨斯州休斯顿市的Equistar化学公司、和美国密执根州的Dow化学公司购买得到。
可用于清洁组合物的金属氧化物包括氢氧化钠、氢氧化钾以及它们的混合物。这些金属氧化物可以从美国德克萨斯州达拉斯市的Occidental化学公司购买得到。硅酸盐选自于硅酸钠、硅酸钾、偏硅酸钠，这些硅酸盐的混合物也可用于清洁组合物中。适用硅酸盐的一个来源是多伦多国家硅酸盐公司。碱性物质还包含有磷酸盐，其中磷酸盐选自于磷酸钠、焦磷酸钠、焦磷酸钾、三聚磷酸钠、三偏磷酸钠、六偏磷酸钠、三聚磷酸钾以及这些物质的混合物。
可用于清洁组合物的溶剂包括乙二醇醚，比如三乙二醇醚、二乙二醇醚；丙二醇甲基醚和(乙酸酯)，三乙二醇甲基醚、三乙二醇乙基醚、三乙二醇丙基醚、三乙二醇丁基醚、三乙二醇己基醚、二乙二醇甲基醚、二乙二醇乙基醚、二乙二醇丙基醚、二乙二醇丁基醚、二乙二醇己基醚和(乙酸酯)，乙二醇苄醚，丙二醇苄醚以及这些物质的混合物。此外，诸如乙醇、异丙醇、苯甲醇、戊醇、正丙醇、2-乙基己醇以及这些醇类物质的混合物也可以用作为溶剂。此外，诸如乙酸正丁酯、乙酸异丁酯、乙酸正丙酯、丙酸正丁酯、丙酸正丙酯、丙酸正戊酯以及这些酯类物质的混合物也可以用作为溶剂。同样，诸如甲基异丁基酮、二异丁基甲酮、双丙酮醇、异佛尔酮以及这些物质的混合物也可以用作为溶剂。诸如n-甲基吡咯烷酮这样的吡咯烷酮、二甲亚砜、乳酸乙酯、诸如外消旋苎烯这样的萜烯类物质、诸如萘、二甲苯、甲苯、苯这样的芳烃类物质、诸如二氯甲烷这样的氯化溶剂、诸如矿物油这样的脂肪类溶剂、碳酸异丙烯酯及类似物质、诸如丁二酸二甲酯、乙二酸二甲酯、戊二酸二甲酯这样的二价酸酯也是适用的溶剂。
典型的清洁组合物含有约0.1-20％重量的碱性物质、约0.9-30％重量的胺类物质以及约0.1-90％重量的溶剂。此外，本发明中的清洁组合物可含有湿润剂、消泡剂、芳香剂、螯合剂、助溶剂、缓冲剂、防腐剂、颜料等。适用的清洁组合物可以从下公司获得：Johnson Diversey公司；品牌为PROSTRIR、Betco公司；品牌为AX-ITPLUS、EXTREMER EXTREME ULTRA、Proctor & Gamble公司；品牌为Proline Floor Finish Stripper；典型的地板剥离剂可以从3M公司获得。本发明中的清洁组合物在使用前可进行稀释。然而，最好是使用高浓度的清洁组合物。
在优选情况下，本发明方法中所用的维护剂组合物含有孔隙填充组分。正如前面所述的，从理论上讲，孔隙填充组分8会暂时填充多孔表面2上的孔隙4，从而防止泥土颗粒8嵌入或沉积到孔隙4中。图2非常清楚地表明了这一情况，图2表明的是多孔表面2的截面图，其中泥土颗粒6嵌入或沉积在多孔表面2的孔隙4中，从而造成该表面受到污损、外观变脏。适用于本发明方法的典型维护剂组合物含有约0.5-100％重量的孔隙填充组分、约0.5-90％重量的溶剂以及约0.05-50％重量的至少一种表面活性剂。此外，这些维护剂组合物还可含有二级湿润剂、螯合剂、芳香剂、颜料、水溶助长剂、助洗剂、螯合作用剂、防腐剂等。在使用前，这些维护剂组合物可以用水进行稀释。维护剂组合物与水的典型稀释比在1:1至1:2000之间。优选的稀释比包括1:100、1:128、1:250、1:256、1:500和1:512。
孔隙填充组分选自于增塑剂、表面活性剂、皂质、油性物质、蜡质、树脂类物质、聚合物和这些物质的混合物。适用的增塑剂选自于苯甲酸酯、二甘醇二苯甲酸酯、双丙甘醇二苯甲酸酯、苯甲酸异癸酯、邻苯二甲酸二丁酯、邻苯二甲酸丁苄酯、邻苯二甲酸二异庚酯、邻苯二甲酸二异癸酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异十三酯、邻苯二甲酸十一烷基十二烷基酯、邻苯二甲酸二异十一酯、磷酸三芳基酯、磷酸三丁氧基乙酯和这些物质的混合物。
适合用作为孔隙填充组分的油类物质选自于矿物油、硅油、诸如椰子油、棕榈油、麻子油、柑桔油、柏油或豆油等这样的植物油以及这些油类物质的混合物。孔隙填充组分还可以是皂质，皂质选自于椰子油皂质、松浆油皂质、麻子油皂质、棕榈油皂质、橄榄油皂质、牛油树脂、牛油酸钠、硬脂酸钠以及这些物质的混合物。诸如非离子表面活性剂、阴离子表面活性剂、两性离子表面活性剂、阳离子表面活性剂以及这些表面活性剂的混合物也适合作为本维护剂组合物中的孔隙填充组分。选自于蜂蜡、聚乙烯蜡、聚丙烯蜡的蜡质材料或这些蜡的混合物也可用作为孔隙填充组分。
适用的维护剂组合物含有JohnsonDiversey公司生产的Revive Plus SC、Betco公司生产的Green Earth Natural APC和Factory Formula Super HP以及3M公司生产的3NI Floor CleanerConcentrate。
在对表面进行处理后，尤其是对地板进行处理后，使用本发明的方法可使多孔表面的滑动摩擦系数至少为0.5。该滑动摩擦系数是使用ASTM方法D2047进行测量的，静态摩擦系数使用James机械进行测量。
正如本领域技术人员所理解的，在任何情况下，尤其是在提供文字说明时，本文所给出的所有范围同时也涵盖所有可能的子范围以及这些子范围的组合。所列出的任何范围均被认为可以分成至少相同的二份、三份、四份、五份、十份等。作为非限定性实例，本文所给出的每个范围可分解成下三分之一部分，中三分之一部上和上三分之一部分等。正如本技术领域内技术人员所理解的，所有诸如“高达”、“至少”、“大于”、“少于”这些词语以及类似的词语均包括所引述的范围，并意味着这些范围可被分解为前面所述的子范围。
实例
以下非限制性实例的目的在于对本发明的优点进行进一步的说明。
实例1
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 37.42
乙醇胺 14
乙二醇一丁醚 34
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
磷酸三丁氧基乙酯 10
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL15-S-9表面活性剂 16
去离子水 47.868
乙二胺四乙酸钠，40％ 0.8
BBA884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例2
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 37.42
乙醇胺 24
乙二醇一丁醚 24
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
磷酸三丁氧基乙酯 2
COCAMIDE DEA和二乙醇胺 4
TERGITOL15-S-9表面活性剂 6
去离子水 69.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例3
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 27.42
乙醇胺 24
乙二醇一丁醚 34
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
磷酸三丁氧基乙酯 2
椰子油皂质 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 62.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例4
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 57.42
乙醇胺 14
乙二醇一丁醚 14
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 0
磷酸三丁氧基乙酯 5.2
椰子油皂质 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 87.068
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例5
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 57.42
乙醇胺 4
乙二醇一丁醚 24
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
E-43蜡质乳液 5.2
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 62.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例6
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 67.42
乙醇胺 4
乙二醇一丁醚 14
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
E-43蜡质乳液 15
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 52.868
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例7
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 47.42
乙醇胺 4
乙二醇一丁醚 34
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
E-43蜡质乳液 10
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL 15-S-9表面活性剂 16
去离子水 47.868
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例8
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 47.42
乙醇胺 24
乙二醇一丁醚 14
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 4
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
磷酸三丁氧基乙酯 2
COCAMIDE DEA和二乙醇胺 4
TERGITOL 15-S-9表面活性剂 6
去离子水 69.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例9
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 57.42
乙醇胺 14
乙二醇一丁醚 14
技术级苯甲醇 4
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 0
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
磷酸三丁氧基乙酯 5.2
椰子油皂质 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 62.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例10
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 53.42
乙醇胺 14
乙二醇一丁醚 14
技术级苯甲醇 8
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 0
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 0
磷酸三丁氧基乙酯 5.2
椰子油皂质 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 87.068
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例11
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 39.42
乙醇胺 14
乙二醇一丁醚 24
技术级苯甲醇 12
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 0
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
E-43蜡质乳液 5.2
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 62.668
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
实例12
在不稀释的情况下向地板泼洒清洁剂组合物，从而对受污损的多孔混凝土地板进行深度清洁，混凝土地板的孔隙中嵌有泥土污物。清洁剂组合物的组成如下：
清洁剂组合物
组分 重量％
去离子水 16.42
乙醇胺 14
乙二醇一丁醚 34
技术级苯甲醇 25
二甲苯磺酸钠，40％ 4
乙二胺四乙酸钠，40％ 1.2
氢氧化钠50％ 4.5
Zonyl FSJ 0.08
Antara LP-700 0.8
乙二醇苄醚 0
该清洁剂组合物对地板浸泡10分钟，然后用自动洗涤机进行洗涤。然后用水冲洗地板，并用真空干燥器进行干燥。经过处理后的地板具有醒目的亮光。在地板干燥后使用维护剂组合物。所用的维护剂组合物组成如下：
维护剂组合物
组分 重量％
二甘醇单乙醚 17.4
E-43蜡质乳液 15
COCAMIDE DEA和二乙醇胺 7.8
TERGITOL 15-S-9表面活性剂 6
去离子水 52.868
乙二胺四乙酸钠，40％ 0.8
BBA 884679芳香剂 0.12
酸红388液体 0.012
在使用前，维护剂组合物按1:128的稀释比在洗涤器的料罐中被水稀释。然后用自动洗涤机将稀释的维护剂组合物施用到地板上，并让维护剂组合物浸泡地板10分钟。洗涤机所带的常规湿式真空器将地板上过量的组合物除去。在此处理后，地板的外观出现了明显的整体改善。
在初次处理后，在进行此后的每日维护时，维护剂组合物的稀释比变为1:256。经过3星期的每天维护后，地板上人们经常行走的区域仍然和初次处理完时一样光亮。地板看上去有光泽，并且很均匀。相比之下，旁边使用过清洁组合物但没使用维护剂组合物处理过的地板在同样被踩踏过3个星期后变得像以前一样污浊。
经常使用相同(或可能不同)的维护剂组合物维护地板的外观或对地板进行定期清洁可以使地板保持更佳的外观。一般而言，在经过初次处理后，使用维护剂组合物对地板进行定期清洁，这样可以清除掉表面上的尘土，并使新的维护剂组合物附着在表面上。
其他的步骤包括在施用维护剂组合物前、后使用抛光盘或擦拭片对地板进行抛光就可以完成地板外观的进一步改善。在一段时间内重复进行这一过程可使地板格外光亮。适合的抛光用擦拭片包括含有碳化硅、氧化铝、长石(碱性硅酸铝盐)、碳化钨、二氧化硅、浮石(无规硅酸铝)、碳化硼、金刚石、氮化硼等物质的擦拭片，但适用的擦拭片并不局限于这些擦拭片。
这些实施方案只代表本发明中改善受污损多孔表面方法以及本发明方法中所用清洁剂组合物和维护剂组合物的几种可能情况。
虽然本发明的原则是结合这些实施方案进行说明的，但应该清楚理解的是，这些说明只是通过实例的方式给出的，并不对本发明的范围构成限制。
Claims (21)
1.一种改善受污损多孔混凝土表面外观的方法；该方法包括：
向受污损的多孔混凝土表面施用高浓度的碱性清洁组合物；
使该清洁组合物在表面上停留一段时间；
用水冲洗表面；
向表面施用维护剂组合物，所述的维护剂组合物含有孔隙填充组分，所述孔隙填充组分选自增塑剂、油及其结合物，在对表面使用维护剂之前，用水按维护剂与水的比例为1:100到1:512的比例稀释所述维护剂；
允许维护剂在表面上保留一段时间；和
除去表面上没有填入孔中的那部分维护剂组合物。
2.权利要求1中的方法还包括定期对表面重复施用维护剂组合物，从而除去表面污损物。
3.如权利要求1中的方法，其中清洁组合物含有碱性物质和溶剂。
4.如权利要求1中的方法，其中的碱性物质选自于胺类物质、金属氧化物、硅酸盐、磷酸盐以及这些物质的混合物。
5.如权利要求4中的方法，其中的碱性物质是乙醇胺。
6.如权利要求4中的方法，其中的碱性物质是金属氢氧化物；该金属氢氧化物选自于氢氧化钠、氢氧化钾、氢氧化钙、氢氧化镁、氢氧化锂以及这些物质的混合物。
7.如权利要求4中的方法，其中碱性物质是硅酸盐；该硅酸盐选自于硅酸钠、硅酸钾、偏硅酸钠以及这些物质的混合物。
8.如权利要求4中的方法，其中碱性物质是磷酸盐，该磷酸盐选自于磷酸钾、焦磷酸钠、焦磷酸钾、三聚磷酸钠、三偏磷酸钠、六偏磷酸钠、三聚磷酸钾以及这些物质的混合物。
9.权利要求1中的方法还包括在用水冲洗前对表面上的清洁组合物进行搅动。
10.权利要求1中的方法还包括在除去未填入孔中的维护剂部分后对表面进行抛光。
11.权利要求1中的方法还包括在施用维护剂组合物前对表面进行抛光。
12.如权利要求1中的方法，其中的孔隙填充组分是增塑剂；该增塑剂选自于苯甲酸酯、二甘醇二苯甲酸酯、双丙甘醇二苯甲酸酯、苯甲酸异癸酯、邻苯二甲酸二丁酯、邻苯二甲酸丁苄酯、邻苯二甲酸二异庚酯、邻苯二甲酸二异癸酯、邻苯二甲酸二异壬酯、邻苯二甲酸二异十三酯、邻苯二甲酸十一烷基十二烷基酯、邻苯二甲酸二异十一酯、磷酸三芳基酯、磷酸三丁氧基乙酯和这些物质的混合物。
13.如权利要求1中的方法，其中的孔隙填充组分是油类物质；这些油类物质选自于矿物油、硅油、植物油以及这些油类物质的混合物。
14.如权利要求1所述的方法；该方法包括：
向受污损的多孔混凝土表面施用高浓度的、含有溶剂的碱性清洁组合物；所述的组合物含有约0.1-50％的碱性物质、0.1-50％的胺类物质和0.1-90％的溶剂；其中，所述胺类物质与碱性物质不同；
使该清洁组合物在表面上停留一段时间；
用水冲洗表面；
向表面施用维护剂组合物，所述的维护剂组合物含有孔隙填充组分，所述孔隙填充组分选自增塑剂、油及其结合物，在对表面使用维护剂之前，用水按维护剂与水的比例为1:100到1:512的比例稀释所述维护剂；
允许维护剂在表面上保留一段时间；和
除去表面上没有填入孔中的那部分维护剂组合物。
15.如权利要求14中的方法，其中的清洁组合物还含有0.01-10.0％的湿润剂。
16.如权利要求14中的方法，其中的清洁组合物还含有0.01-10.0％的乳化剂。
17.如权利要求14中的方法，其中的维护剂组合物还含有至少另外一种组分，该组分选自于二级湿润剂、螯合剂、芳香剂、颜料、助溶剂、助洗剂以及螯合作用剂。
18.如权利要求14中的方法，其中的清洁组合物含有0.1-20％的碱性物质、0.1-30.0％的胺类物质以及0.1-90.0％的溶剂；其中，所述胺类物质与碱性物质不同。
19.如权利要求18中的方法，其中的清洁组合物还含有0.01-10.0％的湿润剂。
20.如权利要求18中的方法，其中的清洁组合物还含有0.01-10.0％的乳化剂。
21.根据权利要求13中的方法，所述植物油是椰子油、棕榈油、麻子油、柑桔油、柏油或豆油。