CN100428536C - 一种用于锂离子电池的三硒化二锑阳极薄膜材料及其制备方法 - Google Patents

一种用于锂离子电池的三硒化二锑阳极薄膜材料及其制备方法 Download PDF

Info

Publication number
CN100428536C
CN100428536C CNB2007100404927A CN200710040492A CN100428536C CN 100428536 C CN100428536 C CN 100428536C CN B2007100404927 A CNB2007100404927 A CN B2007100404927A CN 200710040492 A CN200710040492 A CN 200710040492A CN 100428536 C CN100428536 C CN 100428536C
Authority
CN
China
Prior art keywords
lithium ion
antimony
film
ion battery
anode material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2007100404927A
Other languages
English (en)
Other versions
CN101051683A (zh
Inventor
薛明喆
傅正文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fudan University
Original Assignee
Fudan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fudan University filed Critical Fudan University
Priority to CNB2007100404927A priority Critical patent/CN100428536C/zh
Publication of CN101051683A publication Critical patent/CN101051683A/zh
Application granted granted Critical
Publication of CN100428536C publication Critical patent/CN100428536C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明属电化学技术领域，具体为一种可以作为锂离子电池阳极材料的三硒化二锑(Sb2Se3)。该材料为薄膜形式，通过反应性脉冲激光沉积法制备获得。该薄膜制成的电极，具有良好的充放电循环可逆性，由三硒化二锑薄膜制成的电极的可逆比容量为605mAh/g左右。电极经100次循环后容量仍有531mAh/g。三硒化二锑电极材料化学稳定性好、比容量高、制备方法简单，适用于锂离子电池。

Description

一种用于锂离子电池的三硒化二锑阳极薄膜材料及其制备方法
技术领域
本发明属电化学技术领域，具体涉及一类用于锂离子电池的阳极材料及其制备方法。
背景技术
锂离子电池是笔记本电脑、照相机、手机以及其它通讯器材的重要电源，而且有可能作为绿色能源用于汽车和其它交通工具。目前市售的锂离子电池主要由碳基阳极材料，有机液体电解质和含锂的过渡金属氧化物阴极材料所组成。为了进一步提高锂离子电池的性能，人们正在研究、寻找比碳基阳极材料性能更好的新型的阳极材料。此外，随着微电子器件的小型化，迫切要求开发与此相匹配的锂离子电池，例如薄膜锂离子电池等。
发明内容
本发明的目的在于提出一种性能良好的锂离子电池阳极材料及其制备方法。
本发明提出的锂离子电池阳极材料，是一种具有正交结构的三硒化二锑(Sb2Se3)材料。经研究表明，此类材料具有良好的电化学性能，可作为高性能锂离子电池的阳极材料。目前为止没有关于三硒化二锑(Sb2Se3)材料用作锂离子电池阳极材料的报道。
本发明提出的作为锂离子电池阳极材料的三硒化二锑(Sb2Se3)为薄膜形式，其薄膜材料的厚度为0.2-1μm。
本发明还提出了前述锂离子电池阳极材料的制备方法，具体介绍如下：
作为锂离子电池阳极材料的三硒化二锑(Sb2Se3)薄膜可采用反应性脉冲激光沉积法制备，具体步骤为：将锑粉和硒粉研磨混合后压片制成脉冲激光沉积所用的靶，其中硒粉的物质的量为锑粉的3-5倍，由掺钕钇铝榴石激光器产生的1064nm基频经三倍频后获得355nm脉冲激光，激光束经透镜聚焦后入射到上述靶上，靶子和基片的距离为25-50mm，在氩气气氛中在基片上沉积得到三硒化二锑(Sb2Se3)薄膜，基片可采用不锈钢片、铂片和镀金单晶硅片，基片温度为200-300℃。薄膜的沉积时间由薄膜厚度要求确定，一般为0.2-1.0小时。薄膜厚度可由扫描电镜测定，薄膜的重量根据电子天平称量实验前后基片重量作差得到。
本发明中，三硒化二锑(Sb2Se3)薄膜的晶体结构由X-射线衍射仪(Bruker D8 Advance)确定。X-射线衍射图谱表明由脉冲激光反应沉积法制得的三硒化二锑(Sb2Se3)薄膜为多晶正交结构。由扫描电镜(Philips XL30)测定表明，由脉冲激光反应沉积法制得的三硒化二锑(Sb2Se3)薄膜表面光滑并伴有一些细小裂痕。
本发明中，三硒化二锑(Sb2Se3)薄膜可直接制成锂离子电池薄膜电极。
本发明中，三硒化二锑(Sb2Se3)薄膜电极的电化学性能测试采用由三电极组成的电池系统，其中，三硒化二锑(Sb2Se3)薄膜用作工作电极，高纯锂片分别用作为对电极和参比电极。电解液为1M LiPF6+EC+DMC(V/V＝1/1)。电池装配在充氩气的干燥箱内进行。电池的充放电实验在蓝电(Land)电池测试系统上进行。
本发明中，由脉冲激光反应性沉积法在不锈钢片等基片上制得的三硒化二锑(Sb2Se3)薄膜电极均具有充放电性能，第一次放电反应的放电平台出现在1.60、1.47和0.87V(相对于Li+/Li)，第二次放电过程与第一次放电过程相比，不可逆放电容量损失为8.4％，在电压范围0.3-2.5V和电流密度5μA/cm2时，三硒化二锑(Sb2Se3)薄膜电极的比容量在前100次循环内保持在531～661mAh/g。
上述性能表明，三硒化二锑(Sb2Se3)是一类新型的阳极材料，可应用于锂离子电池。
附图说明
图1为三硒化锑薄膜的XRD谱图。图中星号表示不锈钢基片的衍射峰，括号内的是衍射峰的晶面指标。
具体实施方式
采用反应性脉冲激光沉积法制备三硒化二锑(Sb2Se3)薄膜，颜色为灰色。制备时，混合靶中，硒粉的物质的量是锑粉的3倍，采用不锈钢片作为基片，基片与靶的距离为40mm，基片温度为250℃，由Nd:YAG激光器产生的基频经三倍频产生355nm脉冲激光，激光束经透镜聚焦后入射到锑粉与硒粉的混合靶上。能量密度为2J·cm-2，沉积时间为0.5小时。
X-射线衍射测定表明沉积的薄膜为多晶立方结构的三硒化二锑(Sb2Se3)(附图1)。由扫描电镜照片测定表明由脉冲激光反应性沉积制得的三硒化二锑(Sb2Se3)薄膜表面光滑并伴有一些细小裂痕。
对不锈钢基片上的三硒化二锑(Sb2Se3)薄膜电极的电化学性能测试结果如下：
三硒化二锑(Sb2Se3)薄膜电极可在5μA/cm2充放电速率下进行充放电循环。在电压范围0.3-2.5V内，第一次放电容量可达661mAh/g，可逆容量为605mAh/g，循环40次后容量趋于稳定，循环100次容量保持在531mAh/g。
因此，在不锈钢片上沉积的三硒化二锑(Sb2Se3)薄膜可用作锂离子电池的阳极材料。

Claims (3)

1、一种锂离子电池阳极材料，其特征在于为一种具有正交结构的三硒化二锑薄膜，薄膜的厚度为0.2-1μm。
2、一种如权利要求1所述的锂离子电池阳极材料的制备方法，其特征在于采用反应性脉冲激光沉积法制备，具体步骤为：将锑粉和硒粉研磨混合后压片制成脉冲激光沉积所用的靶，其中硒粉的物质的量为锑粉的3-5倍，由掺钕钇铝榴石激光器产生的1064nm基频经三倍频后获得355nm脉冲激光，激光束经透镜聚焦后入射到上述靶上，靶子和基片的距离为25-50mm，在氩气气氛中在基片上沉积得到三硒化二锑薄膜，基片可采用不锈钢片、铂片和镀金单晶硅片，基片温度为200-300℃。
3、一种具有正交结构的三硒化锑薄膜作为锂离子电池阳极材料的应用。
CNB2007100404927A 2007-05-10 2007-05-10 一种用于锂离子电池的三硒化二锑阳极薄膜材料及其制备方法 Expired - Fee Related CN100428536C (zh)