CN101794877A - 一种用于锂离子电池的氟化铜-硒纳米复合负极材料及其制备方法 - Google Patents

一种用于锂离子电池的氟化铜-硒纳米复合负极材料及其制备方法 Download PDF

Info

Publication number
CN101794877A
CN101794877A CN201010132074A CN201010132074A CN101794877A CN 101794877 A CN101794877 A CN 101794877A CN 201010132074 A CN201010132074 A CN 201010132074A CN 201010132074 A CN201010132074 A CN 201010132074A CN 101794877 A CN101794877 A CN 101794877A
Authority
CN
China
Prior art keywords
selenium
copper fluoride
lithium ion
ion battery
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201010132074A
Other languages
English (en)
Inventor
李雯静
周永宁
傅正文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fudan University
Original Assignee
Fudan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fudan University filed Critical Fudan University
Priority to CN201010132074A priority Critical patent/CN101794877A/zh
Publication of CN101794877A publication Critical patent/CN101794877A/zh
Pending legal-status Critical Current

Abstract

本发明属电化学技术领域，具体涉及一种用于锂离子电池的氟化铜-硒(CuF2-Se)纳米复合材料及其制备方法。该材料为薄膜形式，通过激光溅射沉积法制备获得。该薄膜制成的电极，具有良好的充放电循环可逆性，可作为锂离子电池的负极材料。氟化铜-硒(CuF2-Se)纳米复合薄膜电极的可逆比容量约为310mAh/g。氟化铜-硒(CuF2-Se)纳米复合薄膜电极化学稳定性好、比容量高、充放电平台的极化小、制备方法简单，适用于锂离子电池。

Description

一种用于锂离子电池的氟化铜-硒纳米复合负极材料及其制备方法
技术领域
本发明属电化学技术领域，具体涉及一类用于锂离子电池的氟化铜-硒纳米复合负极材料及其制备方法。
背景技术
锂离子电池是笔记本电脑、照相机、手机以及其它通讯器材的重要电源，而且有可能作为绿色能源用于汽车和其它交通工具。目前市售的锂离子电池主要由碳基负极材料，有机液体电解质和含锂的过渡金属氧化物正极材料所组成。为了进一步提高锂离子电池的性能，人们正在研究、寻找比碳基负极材料性能更好的新型的负极材料。此外，随着微电子器件的小型化，迫切要求开发与此相匹配的锂离子薄膜电池。
发明内容
本发明的目的在于提出一类性能良好的用于锂离子电池的氟化铜-硒(CuF2-Se)复合负极材料及其制备方法。
本发明提出的用于锂离子电池的复合负极材料，是一种氟化铜-硒纳米复合的薄膜材料。经研究表明，此类材料具有良好的电化学性能，可作为高性能锂离子电池的负极材料。目前为止没有关于氟化铜-硒(CuF2-Se)纳米复合材料用作锂离子电池负极材料的报道。
本发明提出的作为锂离子电池负极材料的氟化铜-硒(CuF2-Se)纳米复合材料为薄膜形式。
本发明提出用于锂离子电池的氟化铜-硒(CuF2-Se)纳米复合负极材料的制备方法，具体步骤如下：
作为锂离子电池负极材料的氟化铜-硒(CuF2-Se)纳米复合材料薄膜采用激光溅射沉积法制备，具体步骤为：将氟化铜粉末和单质硒粉末混合，研磨后压片制成激光溅射沉积所用的靶。靶和基片距离为3～5cm，溅射腔内真空度为10-1～10-2Pa，沉积时间为0.5～2小时。
本发明中，氟化铜-硒(CuF2-Se)薄膜的晶体结构由X-射线衍射仪(Bruker D8Advance)确定。X-射线衍射图谱表明由激光溅射沉积法制得的氟化铜-硒(CuF2-Se)薄膜为单斜结构。
本发明中，氟化铜-硒(CuF2-Se)纳米复合材料薄膜可直接制成锂离子电池薄膜电极。
本发明中，氟化铜-硒(CuF2-Se)纳米复合材料薄膜电极的电化学性能测试采用由三电极组成的薄膜电池系统。其中，氟化铜-硒纳米复合薄膜用作工作电极，高纯锂片分别用作为对电极和参比电极。电解液为1M LiPF6+EC+DMC(V/V＝1/1)。薄膜电池装配在充氩气的干燥箱内进行。薄膜电池的充放电实验在蓝电(Land)薄膜电池测试系统上进行。
本发明中，由激光溅射沉积法在不锈钢片等基片上制得的氟化铜-硒(CuF2-Se)纳米复合材料薄膜电极具有充放电性能，在电压范围0.01～4.0V和电流密度10μA/cm2时，放电反应的平台出现在1.9和1.12V(相对于Li/Li+)，第二次放电过程与第一次放电过程相比，不可逆放电容量损失较大。第二周以后的循环过程有良好的可逆性，前三十圈平均每次循环容量衰减仅为1.1％。
上述性能表明，氟化铜-硒(CuF2-Se)纳米复合材料可以作为一种新型的负极材料，应用于锂离子电池。
附图说明
图1实施例1氟化铜-硒(CuF2-Se)薄膜的XRD谱图，图中星号表示不锈钢基片的衍射峰，括号内的是衍射峰的晶面指标。
图2实施例1氟化铜-硒(CuF2-Se)薄膜的循环伏安曲线。
具体实施方式
下面通过实施例进一步说明本发明。
实施例：
采用激光溅射沉积法制备氟化铜-硒(CuF2-Se)纳米复合材料薄膜时，将氟化铜粉末和单质硒粉末混合，研磨后压片制成激光溅射沉积所用的靶。靶和基片距离为3～5cm，溅射腔内真空度为10-1～10-2Pa，沉积时间为0.5～2小时。
X-射线衍射测定表明沉积的薄膜为单斜结构的氟化铜-硒(CuF2-Se)(附图1)。
对不锈钢基片上的氟化铜-硒(CuF2-Se)复合材料薄膜电极的电化学性能测试结果如下：
氟化铜-硒(CuF2-Se)纳米复合材料薄膜电极可在10μA/cm2充放电速率下进行充放电循环。在电压范围0.01-4.0V内，可逆容量为310mAh/g左右。氟化铜-硒(CuF2-Se)复合材料薄膜电极的循环伏安曲线见附图2。
因此，在不锈钢片上沉积的氟化铜-硒(CuF2-Se)纳米复合材料薄膜可用作锂离子薄膜电池的负极材料。

Claims (2)

1.一种锂离子电池的复合负极材料，其特征在于为氟化铜-硒：CuF2-Se纳米复合薄膜材料。
2.一种如权利要求1所述的锂离子电池的复合负极材料的制备方法，其特征在于采用激光溅射技术制备，具体步骤为：将氟化铜粉末和单质硒粉末混合，研磨后压片制成激光溅射沉积所用的靶，靶和基片距离为3～5cm，溅射腔内真空度为10-1～10-2Pa，沉积时间为0.5～2小时。
CN201010132074A 2010-03-25 2010-03-25 一种用于锂离子电池的氟化铜-硒纳米复合负极材料及其制备方法 Pending CN101794877A (zh)