CN100372911C - 一种x射线激发的硼磷酸钡发光材料的应用 - Google Patents

一种x射线激发的硼磷酸钡发光材料的应用 Download PDF

Info

Publication number
CN100372911C
CN100372911C CNB2004100541259A CN200410054125A CN100372911C CN 100372911 C CN100372911 C CN 100372911C CN B2004100541259 A CNB2004100541259 A CN B2004100541259A CN 200410054125 A CN200410054125 A CN 200410054125A CN 100372911 C CN100372911 C CN 100372911C
Authority
CN
China
Prior art keywords
luminescent material
calcination
rays
hours
barium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2004100541259A
Other languages
English (en)
Other versions
CN1603386A (zh
Inventor
吴雪艳
赵景泰
段成军
杨昕昕
陈昊鸿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanghai Institute of Ceramics of CAS
Original Assignee
Shanghai Institute of Ceramics of CAS
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Institute of Ceramics of CAS filed Critical Shanghai Institute of Ceramics of CAS
Priority to CNB2004100541259A priority Critical patent/CN100372911C/zh
Publication of CN1603386A publication Critical patent/CN1603386A/zh
Application granted granted Critical
Publication of CN100372911C publication Critical patent/CN100372911C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明涉及一种X射线激发的Ba3BPO7发光材料的应用，属于闪烁发光材料领域。本发明选取含有钡源、硼源、磷源的原材料进行混合，按化学组成式配比原料后，采用灼烧温度为800—1300℃，灼烧时间为2—15小时的一步烧成或300—500℃灼烧1—4小时再以800—1300℃灼烧2—15小时的两步烧成法完成。最后经研磨粉碎后即得所需高效发光材料，该发光材料可应用于闪烁发光材料领域。

Description

一种X射线激发的硼磷酸钡发光材料的应用
技术领域
本发明涉及一种X射线激发的硼磷酸钡发光材料的应用，属于闪烁发光材料领域。
背景技术
无机闪烁材料是一类价值高、经济效益大的发光材料，由于核物理，磁共振成像，正电子发射层析摄影术(PET)，X射线计算机断层扫描图(即CT)等高技术发展和要求，新型无机闪烁材料在上世纪80年代末获得显著进展，开辟了另一个新的应用市场，预期其在21世纪将有更大发展。近年来，闪烁材料也还在安全检查(集装箱快速检查系统)和工业检测(如油井核探测、火箭、导弹、飞行器等重要部件的无损探伤等)中崭露头角，它将催生出一个数百亿美元产值的高新技术产业。目前所使用的闪烁材料主要是NaI∶T1、PbWO4、Bi4Ge3O12等，但它们还存在着某些缺点，或者稳定性差，或者余晖长，或者效率低。到目前为止还未见成功采用较安全、简便的方法制备出新型X射线激发的高效闪烁发光材料的报导。
发明内容：
本发明的目的是提出一种X射线激发的硼磷酸钡发光材料的应用。
本发明提出的X射线激发的高效发光材料为硼磷酸钡，其化学组成式为：Ba3BPO7。
本发明采用的钡源、硼源、铵源三种原料，其中钡源为碳酸钡，硼源为硼酸，铵源为磷酸氢二铵或磷酸二氢铵。
按化学组成式配比原料后，本发明可采用一步烧成或两步烧成法完成。
一步烧成法：钡源、硼源、铵源原料经过程序升温后，反应在高温空气气氛中进行，灼烧温度为800-1300℃，灼烧时间为2-15小时，冷却取出，经过研磨粉碎后即得所需高效发光材料。
两步烧成法：钡源、硼源、铵源中的两种或三种原料经过程序升温后，反应在高温空气气氛中进行，灼烧温度为300-500℃，灼烧时间为1-4小时，灼烧后所得的块体材料研磨成粉末。再加入钡源、硼源、铵源中的第三种原料再次灼烧或直接再次灼烧，灼烧温度为800-1300℃，灼烧时间为2-15小时，冷却取出，经过研磨粉碎后即得所需高效发光材料。
本发明制备工艺简单，易于操作，制备出的发光材料在X射线激发下有很强分发光。
附图说明
图1是Ba3BPO7的X射线衍射图。
图2是Ba3BPO7在X射线激发下的发光光谱。
具体实施方式：
实施例1
称取碳酸钡1.184克，硼酸0.124克，磷酸二氢铵0.230克，在玛瑙研钵中充分研磨混合，放入氧化铝坩锅内，盖好坩锅盖，放入高温炉中，升温至400℃，灼烧2小时，自然冷却后取出，在玛瑙研钵中研磨重新放入氧化铝坩锅中，盖好坩锅盖，放入高温炉中，升温至1100℃，灼烧11小时，自然冷却后取出，研磨后得到白色粉末，经X射线衍射鉴定结构(见图1)，即得所需的高效X射线激发发光材料，在X射线激发下其发射光谱在300-600nm有强发射带，峰值波长为425nm。
实施例2
称取碳酸钡1.184克，硼酸0.124克，磷酸二氢铵0.230克，在玛瑙研钵中充分研磨混合，放入氧化铝坩锅内，盖好坩锅盖，放入高温炉中，升温至1100℃，灼烧11小时，自然冷却后取出，研磨后得到白色粉末，经X射线衍射鉴定结构(见图1)，即得所需的高效X射线激发发光材料，在X射线激发下其发射光谱在300-600nm有强发射带，峰值波长为409nm。与实施例1相比，其峰值强度为实施例1强度的2倍。
实施例3
称取碳酸钡1.184克，硼酸0.124克，磷酸氢二铵0.264克，在玛瑙研钵中充分研磨混合，放入氧化铝坩锅内，盖好坩锅盖，放入高温炉中，升温至400℃，灼烧2小时，自然冷却后取出，在玛瑙研钵中研磨重新放入氧化铝坩锅中，盖好坩锅盖，放入高温炉中，升温至1100℃，灼烧11小时，自然冷却后取出，研磨后得到白色粉末，经X射线衍射鉴定结构(见图1)，即得所需的高效X射线激发发光材料，在X射线激发下其发射光谱在300-600nm有强发射带，峰值波长为416nm。与实施例1相比，其峰值强度为实施例1强度的2倍。
实施例4
称取碳酸钡1.184克，硼酸0.124克，磷酸氢二铵0.264克，在玛瑙研钵中充分研磨混合，放入氧化铝坩锅内，盖好坩锅盖，放入高温炉中，升温至1100℃，灼烧11小时，自然冷却后取出，研磨后得到白色粉末，经X射线衍射鉴定结构(见图1)，即得所需的高效X射线激发发光材料，在X射线激发下其发射光谱在300-600nm有强发射带，峰值波长为415nm。与实施例1相比，其峰值强度为实施例1强度的2.2倍。
实施例5
称取硼酸0.124克，磷酸二氢铵0.230克，在玛瑙研钵中充分研磨混合，放入氧化铝坩锅内，盖好坩锅盖，放入高温炉中，升温至400℃，灼烧2小时，自然冷却后取出，研磨成粉末，与1.184克碳酸钡充分混合后，将混合物放入氧化铝坩锅中，盖好坩锅盖，放入高温炉中，升温至1000℃，灼烧11小时，自然冷却后取出，研磨后得到白色粉末，经X射线衍射鉴定结构(见图1)，即得所需的高效X射线激发发光材料，在X射线激发下其发射光谱在300-600nm有强发射带，峰值波长为406nm(见附图2)。与实施例1相比，其峰值强度为实施例1强度的1.7倍。

Claims (1)

1.一种X射线激发的Ba3BPO7发光材料用作闪烁发光材料。
CNB2004100541259A 2004-08-30 2004-08-30 一种x射线激发的硼磷酸钡发光材料的应用 Expired - Fee Related CN100372911C (zh)