CH338680A - Niedrigschmelzendes Hartlot - Google Patents

Niedrigschmelzendes Hartlot

Info

Publication number
CH338680A
CH338680A CH338680DA CH338680A CH 338680 A CH338680 A CH 338680A CH 338680D A CH338680D A CH 338680DA CH 338680 A CH338680 A CH 338680A
Authority
CH
Switzerland
Prior art keywords
sep
brazing alloy
aluminum
melting point
low melting
Prior art date
Application number
Other languages
English (en)
Inventor
Banscher Carl
Original Assignee
Kellenberger Arnold
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kellenberger Arnold filed Critical Kellenberger Arnold
Publication of CH338680A publication Critical patent/CH338680A/de

Description


  Niedrigschmelzendes Hartlot    In der Hauptpatentschrift wird ein niedrig  schmelzendes Hartlot beansprucht, welches auf Alu  minium bzw. Aluminiumlegierungen eine korro  sionsbeständige, eloxierbare Lötstelle ergibt und  ausser Al folgende Bestandteile enthält:  
EMI0001.0000     
  
    0,2 <SEP> bis <SEP> 20/o <SEP> Kupfer
<tb>  0,1 <SEP> bis <SEP> 3 <SEP> 11/o <SEP> Silber
<tb>  4 <SEP> bis <SEP> 27 <SEP> 11/o <SEP> Zinn
<tb>  0,5 <SEP> bis <SEP> 80/o <SEP> Zink
<tb>  0,4 <SEP> bis <SEP> 3,75% <SEP> Kadmium       Es wurde nun gefunden, dass man in gewissen  Fällen ebenfalls ein befriedigendes     niedrigschmelzen-          des    Hartlot erhalten kann, wenn man auf einen Teil  der gemäss Hauptpatent dem Aluminium beigege  benen Legierungszusätze verzichtet.  



  Das Hartlot der vorliegenden     Erfindung    ist somit  dadurch gekennzeichnet, dass es ausser 55 bis     95"/o     Aluminium mindestens eines, . jedoch gleichzeitig  höchstens vier der Elemente Kupfer, Silber, Zinn,  Zink und Kadmium in einer Totalmenge von  höchstens 450/o enthält. Ausserdem kann das erfin  dungsgemässe Hartlot noch mindestens eines der  Elemente Magnesium, Silizium, Mangan, Nickel,  Kobalt, Antimon, Blei und     Wismuth    in einer     Ge-;     Samtmenge von höchstens 150/o enthalten.  



  Die genaue     Zusammensetzung    des Lotes wird  vorzugsweise den jeweiligen Bedürfnissen, das heisst  den Arbeitsbedingungen und den zu verlötenden  Materialien angepasst.  



  So kann das Hartlot 55-950/o Aluminium und  wahlweise     5-451/o    eines der Elemente Silber,  Kupfer, Zinn, Zink und Kadmium enthalten. Es  kann indessen auch zwei oder mehrere, jedoch ins  gesamt höchstens vier der vorgenannten Elemente in  einer Minimalmenge von     511ü    und in einer Höchst  menge von 450/o aufweisen.    Nachstehend seien einige beispielsweise Zusam  mensetzungen von erfindungsgemässen Loten wieder  gegeben, wobei die oben und nachstehend angege  benen Mengenbemessungen der     einzelnen    Bestand  teile in Gewichtsprozenten zu verstehen sind.

    
EMI0001.0011     
  
    <I>Beispiel <SEP> 1</I>
<tb>  0,1 <SEP> bis <SEP> 100/o <SEP> Blei
<tb>  0,2 <SEP> bis <SEP> 3 <SEP> 11/o <SEP> Silber
<tb>  1 <SEP> bis <SEP> 120/o <SEP> Zinn
<tb>  0,5 <SEP> bis <SEP> 8 <SEP> 11/o <SEP> Zink
<tb>  0,4 <SEP> bis <SEP> 50/o <SEP> Kadmium
<tb>  Rest <SEP> Aluminium
<tb>  <I>Beispiel <SEP> 2</I>
<tb>  1 <SEP> bis <SEP> 100/o <SEP> Kadmium
<tb>  0,2 <SEP> bis <SEP> 10/o <SEP> Blei
<tb>  0,2 <SEP> bis <SEP> 20/o <SEP> Wismuth
<tb>  0,2 <SEP> bis <SEP> 20/o <SEP> Zink
<tb>  Rest <SEP> Aluminium
<tb>  <I>Beispiel <SEP> 3</I>
<tb>  0,1 <SEP> bis <SEP> 8 <SEP> 11/o <SEP> Silizium
<tb>  0,1 <SEP> bis <SEP> 20/o <SEP> Mangan
<tb>  0,1 <SEP> bis <SEP> 10/o <SEP> Nickel
<tb>  0,1 <SEP> bis <SEP> 0,811/o <SEP> Magnesium
<tb>  0,

  1 <SEP> bis <SEP> 411/o <SEP> Silber
<tb>  1 <SEP> bis <SEP> 100/o <SEP> Zinn
<tb>  2 <SEP> bis <SEP> 3 <SEP> 11/o <SEP> Blei
<tb>  Rest <SEP> Aluminium
<tb>  <I>Beispiel <SEP> 4</I>
<tb>  0,2 <SEP> bis <SEP> 70/o <SEP> Kadmium
<tb>  0,2 <SEP> bis <SEP> 40/o <SEP> Blei
<tb>  0,5 <SEP> bis <SEP> 111/o <SEP> Wismuth
<tb>  0,1 <SEP> bis <SEP> 511/o <SEP> Zink
<tb>  1 <SEP> bis <SEP> 80/o <SEP> Silber
<tb>  4 <SEP> bis <SEP> 130/o <SEP> Zinn
<tb>  Rest <SEP> Aluminium       
EMI0002.0000     
  
    <I>Beispiel <SEP> S</I>
<tb>  0,1 <SEP> bis <SEP> 7 <SEP> 0/o <SEP> Zinn
<tb>  0,1 <SEP> bis <SEP> 0,9 <SEP> 0/o <SEP> Nickel
<tb>  0,05 <SEP> bis <SEP> 0,10/o <SEP> Kobalt
<tb>  0,1 <SEP> bis <SEP> 10/o <SEP> Antimon
<tb>  0,

  1 <SEP> bis <SEP> 10/o <SEP> Silizium
<tb>  Rest <SEP> Aluminium     
EMI0002.0001     
  
    <I>Beispiel <SEP> 6</I>
<tb>  1 <SEP> bis <SEP> 9 <SEP> 0/o <SEP> Kadmium
<tb>  0,05 <SEP> bis <SEP> 0,2 <SEP> 0/o <SEP> Silber
<tb>  0,5 <SEP> bis <SEP> 3'0/o <SEP> Silizium
<tb>  0,1 <SEP> bis <SEP> 10/o <SEP> Mangan
<tb>  0,1 <SEP> bis <SEP> 4'0/o <SEP> Kobalt
<tb>  0,05 <SEP> bis <SEP> 0,3 <SEP> 0/o <SEP> Wismuth
<tb>  1 <SEP> bis <SEP> 6% <SEP> Blei
<tb>  Rest <SEP> Aluminium       Im übrigen gelten für die erfindungsgemässen  Lote die in der Hauptpatentschrift gemachten Aus  führungen auch in bezug auf das vorliegende Lot.

Claims (1)

  1. PATENTANSPRUCH Niedrigschmelzendes Hartlot, dadurch gekenn zeichnet, dass es ausser 55 bis 95 0/o Aluminium min destens eines, jedoch gleichzeitig höchstens vier der Elemente Kupfer, Silber, Zinn, Zink und Kadmium in einer Totalmenge von höchstens 45% enthält. UNTERANSPRUCH Niedrigschmelzendes Hartlot nach Patentan spruch, dadurch gekennzeichnet, dass es noch min destens eines der Elemente Magnesium, Silizium, Mangan, Nickel, Kobalt, Antimon, Blei und Wismuth in einer Gesamtmenge von höchstens 15% enthält.
CH338680D 1954-06-04 1954-08-12 Niedrigschmelzendes Hartlot CH338680A (de)