BR112015021149A2 - chapa de aço laminada a quente e seu método de produção - Google Patents
chapa de aço laminada a quente e seu método de produçãoInfo
- Publication number
- BR112015021149A2 BR112015021149A2 BR112015021149A BR112015021149A BR112015021149A2 BR 112015021149 A2 BR112015021149 A2 BR 112015021149A2 BR 112015021149 A BR112015021149 A BR 112015021149A BR 112015021149 A BR112015021149 A BR 112015021149A BR 112015021149 A2 BR112015021149 A2 BR 112015021149A2
- Authority
- BR
- Brazil
- Prior art keywords
- less
- production method
- rolled steel
- steel sheet
- hot rolled
- Prior art date
Abstract
resumo patente de invenção: "chapa de aço laminada a quente e seu método de produção". uma chapa de aço em uma composição contendo, em % em massa: c: 0,01 a 0,2?; si: 2,5? ou menos; mn: 4,0? ou menos; p: 0,10? ou menos; s: 0,03? ou menos; al: 0,001 a 2,0?; n: 0,01? ou menos; e o: 0,01? ou menos, e um elemento ou um total de dois elementos entre ti e nb em 0,01 a 0,30?. o diâmetro médio efetivo do grão de cristal e 1/4 da espessura da chapa é 10 ?m ou menos, e o diâmetro médio efetivo do grão de cristal em uma parte na faixa de 50 ?m a partir da superfície é 6 ?m ou menos. a estrutura da chapa de aço é martensita temperada ou bainita inferior, e sua fraca de volume é 90% ou mais como total.
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2013107324 | 2013-05-21 | ||
JP2013-107324 | 2013-05-21 | ||
PCT/JP2014/063026 WO2014188966A1 (ja) | 2013-05-21 | 2014-05-16 | 熱延鋼板及びその製造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
BR112015021149A2 true BR112015021149A2 (pt) | 2017-07-18 |
BR112015021149B1 BR112015021149B1 (pt) | 2020-03-10 |
Family
ID=51933523
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112015021149-6A BR112015021149B1 (pt) | 2013-05-21 | 2014-05-16 | Chapa de aço laminada a quente e seu método de produção |
Country Status (11)
Country | Link |
---|---|
US (1) | US10023929B2 (pt) |
EP (1) | EP3000905B1 (pt) |
JP (1) | JP6048580B2 (pt) |
KR (1) | KR101766567B1 (pt) |
CN (1) | CN105143488B (pt) |
BR (1) | BR112015021149B1 (pt) |
ES (1) | ES2759051T3 (pt) |
MX (1) | MX2015011027A (pt) |
PL (1) | PL3000905T3 (pt) |
TW (1) | TWI510649B (pt) |
WO (1) | WO2014188966A1 (pt) |
Families Citing this family (39)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104520463B (zh) * | 2013-08-13 | 2016-03-30 | 新日铁住金株式会社 | 钢板 |
JP6417252B2 (ja) * | 2014-09-17 | 2018-11-07 | 新日鐵住金ステンレス株式会社 | ブレーキディスク用マルテンサイト系ステンレス鋼とその製造方法 |
JP6524716B2 (ja) * | 2015-03-03 | 2019-06-05 | 日本製鉄株式会社 | 加工性に優れた熱延鋼板の製造方法 |
CN105002425B (zh) * | 2015-06-18 | 2017-12-22 | 宝山钢铁股份有限公司 | 超高强度超高韧性石油套管用钢、石油套管及其制造方法 |
KR102119333B1 (ko) * | 2016-02-10 | 2020-06-04 | 제이에프이 스틸 가부시키가이샤 | 고강도 강판 및 그 제조 방법 |
CN109154044B (zh) | 2016-07-15 | 2020-09-04 | 日本制铁株式会社 | 热浸镀锌钢板 |
TWI615484B (zh) * | 2016-07-18 | 2018-02-21 | Nippon Steel & Sumitomo Metal Corp | 熔融鍍鋅鋼板 |
RU2681094C2 (ru) * | 2016-12-23 | 2019-03-04 | Российская Федерация, от имени которой выступает Министерство промышленности и торговли Российской Федерации (Минпромторг России) | Хладостойкая свариваемая arc-сталь повышенной прочности |
MX2019009803A (es) * | 2017-02-17 | 2019-11-11 | Jfe Steel Corp | Lamina de acero laminada en caliente de alta resistencia y metodo para producir la misma. |
BR112019026926A2 (pt) * | 2017-08-09 | 2020-07-07 | Nippon Steel Corporation | chapa de aço laminada a quente e método para produção da mesma |
KR102075216B1 (ko) * | 2017-12-24 | 2020-02-07 | 주식회사 포스코 | 고 항복비형 고 강도 강판 및 그 제조방법 |
WO2019186906A1 (ja) * | 2018-03-29 | 2019-10-03 | 日本製鉄株式会社 | オーステナイト系耐摩耗鋼板 |
RU2679679C1 (ru) * | 2018-05-31 | 2019-02-12 | Акционерное общество "Научно-производственное объединение "Центральный научно-исследовательский институт технологии машиностроения", АО "НПО "ЦНИИТМАШ" | Литая хладостойкая сталь |
CN112534077B (zh) | 2018-07-31 | 2022-06-14 | 杰富意钢铁株式会社 | 高强度热轧钢板及其制造方法 |
US20220056543A1 (en) * | 2018-09-20 | 2022-02-24 | Arcelormittal | Hot rolled steel sheet with high hole expansion ratio and manufacturing process thereof |
CN112805395B (zh) * | 2018-10-19 | 2023-03-28 | 日本制铁株式会社 | 热轧钢板及其制造方法 |
KR102528161B1 (ko) * | 2018-10-19 | 2023-05-03 | 닛폰세이테츠 가부시키가이샤 | 열연 강판 및 그 제조 방법 |
WO2020080554A1 (ja) * | 2018-10-19 | 2020-04-23 | 日本製鉄株式会社 | 熱延鋼板 |
PL3653736T3 (pl) * | 2018-11-14 | 2021-05-17 | Ssab Technology Ab | Taśma stalowa walcowana na gorąco i sposób wytwarzania |
CN113366136B (zh) * | 2019-01-30 | 2023-10-31 | 杰富意钢铁株式会社 | 高碳热轧钢板和其制造方法 |
KR102618288B1 (ko) * | 2019-02-18 | 2023-12-29 | 닛폰세이테츠 가부시키가이샤 | 열연 강판 및 그 제조 방법 |
JP6835294B2 (ja) * | 2019-03-07 | 2021-02-24 | 日本製鉄株式会社 | 熱延鋼板およびその製造方法 |
MX2021010462A (es) | 2019-03-22 | 2021-09-21 | Nippon Steel Corp | Lamina de acero de alta resistencia y metodo para fabricar la misma. |
KR102208165B1 (ko) | 2019-05-21 | 2021-01-27 | 주식회사 삼원강재 | 뜨임 공정을 생략하기 위한 스프링용 강재 |
KR102131137B1 (ko) | 2019-05-21 | 2020-07-07 | 대원강업주식회사 | 뜨임 공정 생략을 통해 제조된 스프링 |
KR102119207B1 (ko) | 2019-05-21 | 2020-06-05 | 주식회사 삼원강재 | 자동차 현가장치용 판스프링 |
KR20200136068A (ko) | 2019-05-27 | 2020-12-07 | 주식회사 삼원강재 | 지연파괴 저항성이 향상된 구조 체결용 강재 및 이를 이용한 구조 체결재 제조 방법 |
JP6819840B1 (ja) | 2019-06-14 | 2021-01-27 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
US20220396856A1 (en) * | 2019-11-20 | 2022-12-15 | Jfe Steel Corporation | Hot-rolled steel sheet for electric resistance welded steel pipe and method for manufacturing the same, electric resistance welded steel pipe and method for manufacturing the same, line pipe, and building structure |
WO2021141100A1 (ja) * | 2020-01-09 | 2021-07-15 | 日本製鉄株式会社 | ホットスタンプ成形体 |
US20230087014A1 (en) * | 2020-03-16 | 2023-03-23 | Nippon Steel Corporation | Steel sheet |
KR20210131724A (ko) | 2020-04-24 | 2021-11-03 | 주식회사 삼원강재 | 뜨임 공정 생략을 위한 로터리 칼날용 강재 및 이를 이용한 로터리 칼날 제조 방법 |
CN115244202B (zh) * | 2020-05-08 | 2023-06-13 | 日本制铁株式会社 | 热轧钢板及其制造方法 |
KR20220132625A (ko) * | 2020-05-08 | 2022-09-30 | 닛폰세이테츠 가부시키가이샤 | 열연 강판 및 그 제조 방법 |
JPWO2022044492A1 (pt) * | 2020-08-27 | 2022-03-03 | ||
EP4223892A4 (en) * | 2020-09-30 | 2024-03-13 | Nippon Steel Corporation | STEEL SHEET AND METHOD FOR MANUFACTURING STEEL SHEET |
KR102498155B1 (ko) * | 2020-12-18 | 2023-02-08 | 주식회사 포스코 | 저온 충격인성이 우수한 고경도 방탄강 및 이의 제조방법 |
WO2022209838A1 (ja) | 2021-03-31 | 2022-10-06 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
WO2024111525A1 (ja) * | 2022-11-22 | 2024-05-30 | Jfeスチール株式会社 | 高強度熱延鋼板及びその製造方法 |
Family Cites Families (27)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59219473A (ja) | 1983-05-26 | 1984-12-10 | Nippon Steel Corp | カラ−エツチング液及びエツチング方法 |
CN1146784A (zh) | 1995-01-26 | 1997-04-02 | 新日本制铁株式会社 | 低温韧性优良的可焊性高强度钢 |
JPH092859A (ja) | 1995-06-21 | 1997-01-07 | Nippon Concrete Ind Co Ltd | 防藻および防カビコンクリート |
JP3386726B2 (ja) | 1997-09-11 | 2003-03-17 | 川崎製鉄株式会社 | 超微細粒を有する加工用熱延鋼板及びその製造方法並びに冷延鋼板の製造方法 |
WO1999013123A1 (fr) | 1997-09-11 | 1999-03-18 | Kawasaki Steel Corporation | Plaque d'acier laminee a chaud contenant des particules hyperfines, son procede de fabrication et procede de fabrication de plaques d'acier laminees a froid |
JP3636872B2 (ja) | 1997-09-18 | 2005-04-06 | Jfeスチール株式会社 | 超微細組織を有する高張力熱延鋼板の製造方法 |
JP3539548B2 (ja) * | 1999-09-20 | 2004-07-07 | Jfeスチール株式会社 | 加工用高張力熱延鋼板の製造方法 |
JP4306202B2 (ja) * | 2002-08-02 | 2009-07-29 | 住友金属工業株式会社 | 高張力冷延鋼板及びその製造方法 |
JP4367091B2 (ja) | 2002-12-20 | 2009-11-18 | Jfeスチール株式会社 | 耐疲労特性に優れ、かつ強度−延性バランスに優れた高強度熱延鋼板およびその製造方法 |
JP4272541B2 (ja) | 2004-01-13 | 2009-06-03 | 株式会社神戸製鋼所 | 加工性の良い超高強度熱延鋼板 |
JP4661306B2 (ja) * | 2005-03-29 | 2011-03-30 | Jfeスチール株式会社 | 超高強度熱延鋼板の製造方法 |
JP4502272B2 (ja) | 2005-12-14 | 2010-07-14 | 株式会社神戸製鋼所 | 加工性および疲労特性に優れる熱延鋼板及びその鋳造方法 |
JP5008896B2 (ja) * | 2006-05-17 | 2012-08-22 | 日産自動車株式会社 | 温間プレス成形高強度部材及びその製造方法 |
JP4688782B2 (ja) | 2006-12-11 | 2011-05-25 | 株式会社神戸製鋼所 | 焼付硬化用高強度鋼板およびその製造方法 |
CN101265553B (zh) | 2007-03-15 | 2011-01-19 | 株式会社神户制钢所 | 挤压加工性优异的高强度热轧钢板及其制造方法 |
JP2008248341A (ja) | 2007-03-30 | 2008-10-16 | National Institute For Materials Science | 超高強度鋼板及びこれを用いた自動車用強度部品 |
JP5339765B2 (ja) | 2007-04-17 | 2013-11-13 | 株式会社中山製鋼所 | 高強度熱延鋼板およびその製造方法 |
JP4959471B2 (ja) * | 2007-08-28 | 2012-06-20 | 新日本製鐵株式会社 | 靭性に優れた機械構造用高強度シームレス鋼管及びその製造方法 |
JP5088631B2 (ja) | 2008-09-17 | 2012-12-05 | 新日本製鐵株式会社 | 疲労特性と曲げ成形性に優れた機械構造鋼管とその製造方法 |
KR101091306B1 (ko) | 2008-12-26 | 2011-12-07 | 주식회사 포스코 | 원자로 격납 용기용 고강도 강판 및 그 제조방법 |
JP5453964B2 (ja) | 2009-07-08 | 2014-03-26 | Jfeスチール株式会社 | 高強度熱延鋼板およびその製造方法 |
JP5609383B2 (ja) * | 2009-08-06 | 2014-10-22 | Jfeスチール株式会社 | 低温靭性に優れた高強度熱延鋼板およびその製造方法 |
JP5724267B2 (ja) * | 2010-09-17 | 2015-05-27 | Jfeスチール株式会社 | 打抜き加工性に優れた高強度熱延鋼板およびその製造方法 |
JP5126326B2 (ja) * | 2010-09-17 | 2013-01-23 | Jfeスチール株式会社 | 耐疲労特性に優れた高強度熱延鋼板およびその製造方法 |
JP5029748B2 (ja) | 2010-09-17 | 2012-09-19 | Jfeスチール株式会社 | 靭性に優れた高強度熱延鋼板およびその製造方法 |
JP5598225B2 (ja) * | 2010-09-30 | 2014-10-01 | Jfeスチール株式会社 | 曲げ特性と低温靭性に優れた高強度熱延鋼板およびその製造方法 |
EP2692894B1 (en) | 2011-03-31 | 2018-03-21 | Nippon Steel & Sumitomo Metal Corporation | Bainite-containing-type high-strength hot-rolled steel sheet having excellent isotropic workability and manufacturing method thereof |
-
2014
- 2014-05-16 WO PCT/JP2014/063026 patent/WO2014188966A1/ja active Application Filing
- 2014-05-16 ES ES14801712T patent/ES2759051T3/es active Active
- 2014-05-16 MX MX2015011027A patent/MX2015011027A/es active IP Right Grant
- 2014-05-16 KR KR1020157023646A patent/KR101766567B1/ko active IP Right Grant
- 2014-05-16 PL PL14801712T patent/PL3000905T3/pl unknown
- 2014-05-16 CN CN201480022394.9A patent/CN105143488B/zh active Active
- 2014-05-16 EP EP14801712.2A patent/EP3000905B1/en active Active
- 2014-05-16 JP JP2015518219A patent/JP6048580B2/ja active Active
- 2014-05-16 US US14/767,807 patent/US10023929B2/en active Active
- 2014-05-16 BR BR112015021149-6A patent/BR112015021149B1/pt not_active IP Right Cessation
- 2014-05-20 TW TW103117668A patent/TWI510649B/zh not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
BR112015021149B1 (pt) | 2020-03-10 |
US10023929B2 (en) | 2018-07-17 |
MX2015011027A (es) | 2015-10-22 |
KR20150114540A (ko) | 2015-10-12 |
ES2759051T3 (es) | 2020-05-07 |
PL3000905T3 (pl) | 2020-04-30 |
TWI510649B (zh) | 2015-12-01 |
JPWO2014188966A1 (ja) | 2017-02-23 |
KR101766567B1 (ko) | 2017-08-08 |
EP3000905A4 (en) | 2016-11-02 |
EP3000905B1 (en) | 2019-10-30 |
WO2014188966A1 (ja) | 2014-11-27 |
JP6048580B2 (ja) | 2016-12-21 |
TW201502287A (zh) | 2015-01-16 |
US20150376730A1 (en) | 2015-12-31 |
CN105143488B (zh) | 2017-05-17 |
CN105143488A (zh) | 2015-12-09 |
EP3000905A1 (en) | 2016-03-30 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112015021149A2 (pt) | chapa de aço laminada a quente e seu método de produção | |
BR112015024854A2 (pt) | chapa de aço laminada a quente e método para sua produção | |
BR112013026115A2 (pt) | chapa de aço laminada a quente e método de produção da mesma | |
CR20140327A (es) | Pirimidinas y triazinas fusionadas sustituidas y su uso | |
MX2016001273A (es) | Lamina de acero de alta resistencia que tiene alto modulo de young y metodo para la fabricacion de la misma. | |
BR112015024840A2 (pt) | chapa de aço laminada a quente | |
BR112014031739A2 (pt) | chapa de aço laminada a quente de alta resistência e método de produção da mesma | |
BR112014003519A2 (pt) | chapa de aço com ni adicionado e método de produção da mesma | |
BR112019008329A2 (pt) | chapa de aço para carburação, e método de fabricação da chapa de aço para carburação | |
MX2016001272A (es) | Lamina de acero de alta resistencia que tiene un modulo de young alto y metodo para la fabricacion de la misma. | |
BR112017004711A2 (pt) | chapa de aço laminada a quente | |
BR112015030003A2 (pt) | chapa de aço laminada a frio, chapa de aço laminada a frio galvanizada e método de produção da mesma | |
BR112015026643A2 (pt) | chapa de aço | |
BR112014028230A2 (pt) | chapa de aço grossa de alta resistência para uso estrutural que tenha excelente capacidade de interrupção de fratura frágil, e método para produção da mesma | |
WO2014047551A8 (en) | Flavonoid based antiviral targets | |
TH176570B (th) | แผ่นเหล็กกล้ารีดเย็นบางความแข็งแรงสูง และวิธีการเพื่อการผลิตแผ่นเหล็กกล้านั้น | |
TH163151A (th) | แผ่นเหล็กกล้ารีดร้อนและวิธีการผลิตตัวมัน | |
TH163151B (th) | แผ่นเหล็กกล้ารีดร้อนและวิธีการผลิตตัวมัน | |
TH167491A (th) | แผ่นเหล็กกล้ารีดเย็นความแข็งแรงสูงมีอัตราส่วนการครากสูง และวิธีการผลิต สำหรับแผ่นเหล็กกล้านั้น | |
TH176521B (th) | แผ่นเหล็กกล้าชุบเคลือบสังกะสีความแข็งแรงสูงและวิธีการเพื่อ การผลิตแผ่นเหล็กกล้านั้น | |
TH176967B (th) | แผ่นเหล็กกล้ารีดร้อน | |
TH162324B (th) | แผ่นเหล็กกล้ารีดเย็นแข็งแรงสูงที่มีอัตราส่วนการครากสูง และวิธีการผลิต สำหรับแผ่นเหล็กกล้านั้น | |
TH137826B (th) | แผ่นเหล็กกล้ารีดร้อน และวิธีการสำหรับการผลิตสิ่งเดียวกันนั้น | |
TH170480B (th) | แผ่นเหล็กกล้าสำหรับกระป๋องและวิธีการผลิตของแผ่นเหล็กกล้าสำหรับกระป๋อง | |
TH160511B (th) | แผ่นเหล็กกล้ารีดร้อนความแข็งแรงสูง และวิธีการเพื่อการผลิตแผ่นเหล็กกล้านั้น |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B06F | Objections, documents and/or translations needed after an examination request according [chapter 6.6 patent gazette] | ||
B06A | Patent application procedure suspended [chapter 6.1 patent gazette] | ||
B25D | Requested change of name of applicant approved |
Owner name: NIPPON STEEL CORPORATION (JP) |
|
B09A | Decision: intention to grant [chapter 9.1 patent gazette] | ||
B16A | Patent or certificate of addition of invention granted [chapter 16.1 patent gazette] |
Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 16/05/2014, OBSERVADAS AS CONDICOES LEGAIS. |
|
B21F | Lapse acc. art. 78, item iv - on non-payment of the annual fees in time |
Free format text: REFERENTE A 8A ANUIDADE. |
|
B24J | Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12) |
Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2671 DE 15-03-2022 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013. |