AU2014265262B2 - High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath - Google Patents

High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath Download PDF

Info

Publication number
AU2014265262B2
AU2014265262B2 AU2014265262A AU2014265262A AU2014265262B2 AU 2014265262 B2 AU2014265262 B2 AU 2014265262B2 AU 2014265262 A AU2014265262 A AU 2014265262A AU 2014265262 A AU2014265262 A AU 2014265262A AU 2014265262 B2 AU2014265262 B2 AU 2014265262B2
Authority
AU
Australia
Prior art keywords
temperature
steel sheet
austenite
partitioning
martensite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
AU2014265262A
Other languages
English (en)
Other versions
AU2014265262A1 (en
Inventor
Jose Mauro B. Losz
Grant Aaron Thomas
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Cleveland Cliffs Steel Properties Inc
Original Assignee
AK Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by AK Steel Properties Inc filed Critical AK Steel Properties Inc
Publication of AU2014265262A1 publication Critical patent/AU2014265262A1/en
Application granted granted Critical
Publication of AU2014265262B2 publication Critical patent/AU2014265262B2/en
Ceased legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/78—Combined heat-treatments not provided for above
    • C21D1/785—Thermocycling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
AU2014265262A 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath Ceased AU2014265262B2 (en)

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
US201361824699P 2013-05-17 2013-05-17
US201361824643P 2013-05-17 2013-05-17
US61/824,699 2013-05-17
US61/824,643 2013-05-17
PCT/US2014/038364 WO2014186689A2 (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath

Publications (2)

Publication Number Publication Date
AU2014265262A1 AU2014265262A1 (en) 2015-11-12
AU2014265262B2 true AU2014265262B2 (en) 2016-12-15

Family

ID=50933550

Family Applications (2)

Application Number Title Priority Date Filing Date
AU2014265262A Ceased AU2014265262B2 (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
AU2014265214A Ceased AU2014265214B2 (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath

Family Applications After (1)

Application Number Title Priority Date Filing Date
AU2014265214A Ceased AU2014265214B2 (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath

Country Status (12)

Country Link
US (2) US20140338798A1 (enExample)
EP (2) EP2997172B1 (enExample)
JP (3) JP2016524038A (enExample)
KR (5) KR20190101504A (enExample)
CN (3) CN113151735A (enExample)
AU (2) AU2014265262B2 (enExample)
BR (2) BR112015027901B1 (enExample)
CA (2) CA2908491C (enExample)
MX (2) MX378110B (enExample)
RU (3) RU2632042C2 (enExample)
TW (4) TWI560279B (enExample)
WO (2) WO2014186722A2 (enExample)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA2908491C (en) * 2013-05-17 2019-07-30 Ak Steel Properties, Inc. High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath
WO2016020714A1 (en) 2014-08-07 2016-02-11 Arcelormittal Method for producing a coated steel sheet having improved strength, ductility and formability
CN104532126B (zh) * 2014-12-19 2017-06-06 宝山钢铁股份有限公司 一种低屈强比超高强度热轧q&p钢及其制造方法
US20160201159A1 (en) * 2015-01-14 2016-07-14 Ak Steel Properties, Inc. Dual Phase Steel with Improved Properties
MX2020004592A (es) 2017-11-02 2020-08-24 Ak Steel Properties Inc Acero templado en prensa con propiedades personalizadas.
US20190300995A1 (en) * 2018-03-30 2019-10-03 Ak Steel Properties, Inc. Low alloy third generation advanced high strength steel and process for making
CN109554622B (zh) * 2018-12-03 2020-12-04 东北大学 淬火至贝氏体区获得Q＆P组织的热轧Fe-Mn-Al-C钢及制造方法
CN109554621B (zh) * 2018-12-03 2020-11-27 东北大学 一种低密度Fe-Mn-Al-C热轧Q＆P钢及其制造方法
CN110055465B (zh) * 2019-05-16 2020-10-02 北京科技大学 一种中锰超高强度钢及其制备方法
CN112327970B (zh) * 2020-09-04 2022-04-12 凌云工业股份有限公司 一种热成型变强度工件过渡区强度的控制方法
US20240167130A1 (en) * 2021-04-02 2024-05-23 Baoshan Iron & Steel Co., Ltd. Low-carbon low-alloy q&p steel or hot-dip galvanized q&p steel with tensile strength greater than or equal to 1180 mpa, and manufacturing method therefor
CN114774652B (zh) * 2022-04-29 2024-07-23 重庆长征重工有限责任公司 一种17CrNiMo6材料预备热处理方法
WO2025255081A1 (en) * 2024-06-07 2025-12-11 Cleveland-Cliffs Steel Properties Inc. High strength steel having retained austenite

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100370054C (zh) * 2001-06-15 2008-02-20 新日本制铁株式会社 镀有铝合金体系的高强度钢板以及具有优异的耐热性和喷漆后耐腐蚀性的高强度汽车零件
US20060011274A1 (en) * 2002-09-04 2006-01-19 Colorado School Of Mines Method for producing steel with retained austenite
CN100368580C (zh) * 2003-04-10 2008-02-13 新日本制铁株式会社 高强度熔融镀锌钢板及其制造方法
US20050247382A1 (en) * 2004-05-06 2005-11-10 Sippola Pertti J Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
CA2482100A1 (en) * 2003-09-19 2005-03-19 Pertti J. Sippola Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
BRPI0816738A2 (pt) * 2007-09-10 2015-03-17 Pertti J Sippola Método e equipamento para conformabilidade melhorada de aço galvanizado tendo alta resistência à tração
CN101121955A (zh) * 2007-09-13 2008-02-13 上海交通大学 采用碳分配和回火提高淬火钢件机械性能的热处理方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4712882B2 (ja) * 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5333298B2 (ja) * 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
CN102002558B (zh) * 2010-11-26 2012-07-25 清华大学 含抑制碳化物形成元素钢的分级淬火-分配热处理工艺
ES2535420T3 (es) * 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
CN102758142A (zh) * 2011-04-25 2012-10-31 宝山钢铁股份有限公司 一种抗拉强度大于980MPa的热镀锌钢板及其制造方法
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
EP2524970A1 (de) 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
WO2013051238A1 (ja) * 2011-10-04 2013-04-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN103045950B (zh) * 2012-12-28 2015-04-22 中北大学 一种低合金高强韧性复相钢及其热处理方法
AU2014249192B2 (en) * 2013-03-11 2017-12-21 The Regents Of The University Of Michigan BET bromodomain inhibitors and therapeutic methods using the same
CA2908491C (en) * 2013-05-17 2019-07-30 Ak Steel Properties, Inc. High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
JOHN G. SPEER et al., "Analysis of Microstructure Evolution in Quenching and Partitioning Automotive Sheet Steel" *

Also Published As

Publication number Publication date
CA2908491C (en) 2019-07-30
RU2018133682A (ru) 2020-03-25
JP6843612B2 (ja) 2021-03-17
RU2632042C2 (ru) 2017-10-02
WO2014186689A3 (en) 2015-01-22
CN105392906A (zh) 2016-03-09
KR101776242B1 (ko) 2017-09-07
TWI560279B (en) 2016-12-01
TWI564402B (zh) 2017-01-01
CA2910012C (en) 2020-02-18
RU2669654C2 (ru) 2018-10-12
TW201708562A (zh) 2017-03-01
BR112015027447A2 (pt) 2017-07-25
KR20170104158A (ko) 2017-09-14
RU2015145865A3 (enExample) 2018-03-29
AU2014265214B2 (en) 2016-12-22
KR20170104159A (ko) 2017-09-14
RU2015141563A (ru) 2017-06-22
KR20160007647A (ko) 2016-01-20
AU2014265214A1 (en) 2015-11-05
BR112015027901B1 (pt) 2020-04-22
CN105247090A (zh) 2016-01-13
EP2997172B1 (en) 2020-08-26
WO2014186722A3 (en) 2015-01-08
MX2015015332A (es) 2016-07-15
RU2015145865A (ru) 2017-06-22
RU2018133682A3 (enExample) 2020-03-25
EP2997168B1 (en) 2021-03-03
TW201446974A (zh) 2014-12-16
TWI616538B (zh) 2018-03-01
MX2015015333A (es) 2016-06-23
AU2014265262A1 (en) 2015-11-12
EP2997168A2 (en) 2016-03-23
KR101776241B1 (ko) 2017-09-07
BR112015027901A2 (pt) 2017-07-25
CA2908491A1 (en) 2014-11-20
KR20160007646A (ko) 2016-01-20
BR112015027447B1 (pt) 2020-04-22
TW201502284A (zh) 2015-01-16
CN113151735A (zh) 2021-07-23
JP2016526096A (ja) 2016-09-01
WO2014186722A2 (en) 2014-11-20
KR20190101504A (ko) 2019-08-30
EP2997172A2 (en) 2016-03-23
US20140338798A1 (en) 2014-11-20
JP2018178262A (ja) 2018-11-15
MX378110B (es) 2025-03-10
US20140338797A1 (en) 2014-11-20
TWI627288B (zh) 2018-06-21
JP2016524038A (ja) 2016-08-12
TW201702397A (zh) 2017-01-16
WO2014186689A2 (en) 2014-11-20
CA2910012A1 (en) 2014-11-20

Similar Documents

Publication Publication Date Title
AU2014265262B2 (en) High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
EP3164516B1 (en) Method for producing an ultra high strength coated or not coated steel sheet and obtained sheet
EP3704276B1 (en) Press hardened steel with tailored properties after novel thermal treatment
BR112017000027B1 (pt) método para manufaturar uma chapa de aço de alta resistência e chapa de aço alta resistência
US20210047707A1 (en) Method For Producing an Ultra High Strength Galvannealed Steel Sheet and Obtained Galvannealed Steel Sheet
BR112017000026B1 (pt) método para fabricar uma chapa de aço e chapa de aço
US10907232B2 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet

Legal Events

Date Code Title Description
FGA Letters patent sealed or granted (standard patent)
MK14 Patent ceased section 143(a) (annual fees not paid) or expired