TWI560279B - High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath - Google Patents

High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath

Info

Publication number
TWI560279B
TWI560279B TW103117426A TW103117426A TWI560279B TW I560279 B TWI560279 B TW I560279B TW 103117426 A TW103117426 A TW 103117426A TW 103117426 A TW103117426 A TW 103117426A TW I560279 B TWI560279 B TW I560279B
Authority
TW
Taiwan
Prior art keywords
heat treatment
high strength
strength steel
molten zinc
exhibiting good
Prior art date
Application number
TW103117426A
Other languages
English (en)
Chinese (zh)
Other versions
TW201446974A (zh
Inventor
Grant Aaron Thomas
Jose Mauro B Losz
Original Assignee
Ak Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ak Steel Properties Inc filed Critical Ak Steel Properties Inc
Publication of TW201446974A publication Critical patent/TW201446974A/zh
Application granted granted Critical
Publication of TWI560279B publication Critical patent/TWI560279B/zh

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/78—Combined heat-treatments not provided for above
    • C21D1/785—Thermocycling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
TW103117426A 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath TWI560279B (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201361824643P 2013-05-17 2013-05-17
US201361824699P 2013-05-17 2013-05-17

Publications (2)

Publication Number Publication Date
TW201446974A TW201446974A (zh) 2014-12-16
TWI560279B true TWI560279B (en) 2016-12-01

Family

ID=50933550

Family Applications (4)

Application Number Title Priority Date Filing Date
TW105135812A TWI616538B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法
TW105132762A TWI627288B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由熔融鋅浴槽的下游在線熱處理之製造方法
TW103117426A TWI560279B (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
TW103117430A TWI564402B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法

Family Applications Before (2)

Application Number Title Priority Date Filing Date
TW105135812A TWI616538B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法
TW105132762A TWI627288B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由熔融鋅浴槽的下游在線熱處理之製造方法

Family Applications After (1)

Application Number Title Priority Date Filing Date
TW103117430A TWI564402B (zh) 2013-05-17 2014-05-16 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法

Country Status (12)

Country Link
US (2) US20140338798A1 (enExample)
EP (2) EP2997168B1 (enExample)
JP (3) JP6843612B2 (enExample)
KR (5) KR20170104158A (enExample)
CN (3) CN113151735A (enExample)
AU (2) AU2014265214B2 (enExample)
BR (2) BR112015027901B1 (enExample)
CA (2) CA2908491C (enExample)
MX (2) MX2015015333A (enExample)
RU (3) RU2632042C2 (enExample)
TW (4) TWI616538B (enExample)
WO (2) WO2014186689A2 (enExample)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140338798A1 (en) * 2013-05-17 2014-11-20 Ak Steel Properties, Inc. High Strength Steel Exhibiting Good Ductility and Method of Production via Quenching and Partitioning Treatment by Zinc Bath
WO2016020714A1 (en) * 2014-08-07 2016-02-11 Arcelormittal Method for producing a coated steel sheet having improved strength, ductility and formability
CN104532126B (zh) * 2014-12-19 2017-06-06 宝山钢铁股份有限公司 一种低屈强比超高强度热轧q&p钢及其制造方法
CN110218942A (zh) * 2015-01-14 2019-09-10 Ak钢铁产权公司 具有改善性质的双相钢
CA3076932C (en) 2017-11-02 2023-08-15 Ak Steel Properties, Inc. Press hardened steel with tailored properties
KR102472740B1 (ko) * 2018-03-30 2022-12-01 클리블랜드-클리프스 스틸 프로퍼티즈 인코포레이티드 저합금 3세대 첨단 고강도 강 및 제조방법
CN109554621B (zh) * 2018-12-03 2020-11-27 东北大学 一种低密度Fe-Mn-Al-C热轧Q＆P钢及其制造方法
CN109554622B (zh) * 2018-12-03 2020-12-04 东北大学 淬火至贝氏体区获得Q＆P组织的热轧Fe-Mn-Al-C钢及制造方法
CN110055465B (zh) * 2019-05-16 2020-10-02 北京科技大学 一种中锰超高强度钢及其制备方法
CN112327970B (zh) * 2020-09-04 2022-04-12 凌云工业股份有限公司 一种热成型变强度工件过渡区强度的控制方法
WO2022206911A1 (zh) * 2021-04-02 2022-10-06 宝山钢铁股份有限公司 抗拉强度≥1180MPa的低碳低合金Q＆P钢或热镀锌Q＆P钢及其制造方法
CN114774652B (zh) * 2022-04-29 2024-07-23 重庆长征重工有限责任公司 一种17CrNiMo6材料预备热处理方法
WO2025255081A1 (en) * 2024-06-07 2025-12-11 Cleveland-Cliffs Steel Properties Inc. High strength steel having retained austenite

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101842509A (zh) * 2007-09-10 2010-09-22 帕蒂·J·西珀拉 用于改进具有高抗拉强度的镀锌钢的成形性的方法及设备

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20070087240A (ko) * 2001-06-15 2007-08-27 신닛뽄세이테쯔 카부시키카이샤 고강도 알루미늄계 합금 도금 강판의 열간 프레스 방법
WO2004022794A1 (en) * 2002-09-04 2004-03-18 Colorado School Of Mines Method for producing steel with retained austenite
ATE469991T1 (de) * 2003-04-10 2010-06-15 Nippon Steel Corp Ein herstellungsverfahren für feuerverzinktes stahlblech mit hoher festigkeit
US20050247382A1 (en) * 2004-05-06 2005-11-10 Sippola Pertti J Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
CA2482100A1 (en) * 2003-09-19 2005-03-19 Pertti J. Sippola Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CN101121955A (zh) * 2007-09-13 2008-02-13 上海交通大学 采用碳分配和回火提高淬火钢件机械性能的热处理方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4712882B2 (ja) * 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5333298B2 (ja) * 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
CN102002558B (zh) * 2010-11-26 2012-07-25 清华大学 含抑制碳化物形成元素钢的分级淬火-分配热处理工艺
ES2535420T3 (es) * 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
CN102758142A (zh) * 2011-04-25 2012-10-31 宝山钢铁股份有限公司 一种抗拉强度大于980MPa的热镀锌钢板及其制造方法
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
EP2524970A1 (de) * 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
JP5454745B2 (ja) * 2011-10-04 2014-03-26 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
CN103045950B (zh) * 2012-12-28 2015-04-22 中北大学 一种低合金高强韧性复相钢及其热处理方法
WO2014164596A1 (en) * 2013-03-11 2014-10-09 The Regents Of The University Of Michigan Bet bromodomain inhibitors and therapeutic methods using the same
US20140338798A1 (en) * 2013-05-17 2014-11-20 Ak Steel Properties, Inc. High Strength Steel Exhibiting Good Ductility and Method of Production via Quenching and Partitioning Treatment by Zinc Bath

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101842509A (zh) * 2007-09-10 2010-09-22 帕蒂·J·西珀拉 用于改进具有高抗拉强度的镀锌钢的成形性的方法及设备

Also Published As

Publication number Publication date
RU2018133682A3 (enExample) 2020-03-25
AU2014265262A1 (en) 2015-11-12
KR20160007647A (ko) 2016-01-20
WO2014186689A2 (en) 2014-11-20
BR112015027447A2 (pt) 2017-07-25
KR20160007646A (ko) 2016-01-20
TW201446974A (zh) 2014-12-16
AU2014265214B2 (en) 2016-12-22
US20140338798A1 (en) 2014-11-20
EP2997172A2 (en) 2016-03-23
WO2014186722A3 (en) 2015-01-08
JP2016524038A (ja) 2016-08-12
CN105392906A (zh) 2016-03-09
KR20170104158A (ko) 2017-09-14
AU2014265262B2 (en) 2016-12-15
TW201702397A (zh) 2017-01-16
EP2997172B1 (en) 2020-08-26
CA2910012C (en) 2020-02-18
EP2997168B1 (en) 2021-03-03
CN105247090A (zh) 2016-01-13
BR112015027901B1 (pt) 2020-04-22
TW201502284A (zh) 2015-01-16
WO2014186722A2 (en) 2014-11-20
EP2997168A2 (en) 2016-03-23
MX378110B (es) 2025-03-10
MX2015015332A (es) 2016-07-15
JP2018178262A (ja) 2018-11-15
RU2018133682A (ru) 2020-03-25
KR20170104159A (ko) 2017-09-14
JP6843612B2 (ja) 2021-03-17
RU2015141563A (ru) 2017-06-22
JP2016526096A (ja) 2016-09-01
RU2632042C2 (ru) 2017-10-02
CN113151735A (zh) 2021-07-23
BR112015027901A2 (pt) 2017-07-25
RU2015145865A (ru) 2017-06-22
BR112015027447B1 (pt) 2020-04-22
TWI616538B (zh) 2018-03-01
KR20190101504A (ko) 2019-08-30
TWI627288B (zh) 2018-06-21
TW201708562A (zh) 2017-03-01
CA2908491C (en) 2019-07-30
WO2014186689A3 (en) 2015-01-22
TWI564402B (zh) 2017-01-01
KR101776242B1 (ko) 2017-09-07
CA2908491A1 (en) 2014-11-20
CA2910012A1 (en) 2014-11-20
AU2014265214A1 (en) 2015-11-05
RU2669654C2 (ru) 2018-10-12
MX2015015333A (es) 2016-06-23
US20140338797A1 (en) 2014-11-20
RU2015145865A3 (enExample) 2018-03-29
KR101776241B1 (ko) 2017-09-07

Similar Documents

Publication Publication Date Title
TWI560279B (en) High strength steel exhibiting good ductility and method of production via in-line heat treatment downstream of molten zinc bath
HUE044562T2 (hu) Nagyszilárdságú acél és gyártási eljárása
EP3050989A4 (en) HIGH STRENGTH STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF
GB2500825B (en) Alloy and method of production thereof
SG11201406599RA (en) Copper-nickel alloy electroplating bath and plating method
PL3370900T3 (pl) Sposób wytwarzania elementu konstrukcyjnego odlanego z metalu lekkiego i element konstrukcyjny odlany z metalu lekkiego
EP2943601A4 (en) APPARATUS AND METHOD FOR MAINTAINING THE EFFICIENCY OF TRIVALENT CHROME BATH PLATING
PL2917377T3 (pl) Drut rdzeniowy do obróbki metalurgicznej kąpieli roztopionego metalu i odpowiadający jej sposób
EP3006588A4 (en) COPPER ALLOY MANUFACTURING METHOD AND COPPER ALLOY
IL245593A0 (en) Metallic assemblies and treatment methods
EP2963154A4 (en) METHOD FOR PRODUCING A SURFACE - TREATED METALLIC TITANIUM MATERIAL OR TITANIUM ALLOY MATERIAL AND SURFACE - TREATED MATERIAL
PL2683845T3 (pl) Kąpiel ze stopionych soli do azotowania wyrobów stalowych i sposób jej wytwarzania
SG11201610667VA (en) MOLTEN Al PLATED STEEL WIRE AS WELL AS STRANDED WIRE AND MANUFACTURING METHOD THEREFOR
TWI562965B (en) Processing method of cooling water system and method for producing treatment agent
EP2775004A4 (en) Extremely heat-resistant and high-strength RH-BASED ALLOY AND METHOD OF MANUFACTURING THEREOF
GB2497354B (en) Method of improvement of mechanical properties of products made of metals and alloys
EP3287541A4 (en) Production apparatus and production method for molten metal plated steel strip
EP3078434A4 (en) TREATMENT DEVICE AND TREATMENT METHOD FOR METAL MELTS
PL3015571T3 (pl) Kwasowa kompozycja kąpieli galwanicznej do powlekania cynkiem i stopem cynkowo- niklowym oraz sposób powlekania galwanicznego
EP2949410A4 (en) METHOD FOR THE CONTINUOUS CASTING BLOCK OF TITANIUM OR TITANIUM ALLOY
PL3380650T3 (pl) Kompozycja kąpieli galwanicznej i sposób bezprądowego powlekania palladem
PL3380649T3 (pl) Kompozycja kąpieli galwanicznej i sposób bezprądowego powlekania palladem
GB2539655B (en) Composite bath tub and method of manufacture
EP2940190A4 (en) SURFACE TREATMENT COMPOSITION, PROCESS FOR PREPARING THE SURFACE TREATMENT COMPOSITION, METAL ARTICLES, AND METHOD OF MANUFACTURING THE METAL ARTICLE
HUE039994T2 (hu) Eljárás olvasztott-só fürdõben nitridálási/nitrokarburálási kezelésnek alávetett fém alkatrészek hûtésére, berendezés az eljárás kivitelezésére és a kezelt fém alkatrészek

Legal Events

Date Code Title Description
MM4A Annulment or lapse of patent due to non-payment of fees