ATA12032003A - Korrosionsgeschütztes stahlblechteil mit hoher festigkeit - Google Patents
Korrosionsgeschütztes stahlblechteil mit hoher festigkeitInfo
- Publication number
- ATA12032003A ATA12032003A AT0120303A AT12032003A ATA12032003A AT A12032003 A ATA12032003 A AT A12032003A AT 0120303 A AT0120303 A AT 0120303A AT 12032003 A AT12032003 A AT 12032003A AT A12032003 A ATA12032003 A AT A12032003A
- Authority
- AT
- Austria
- Prior art keywords
- corrosion
- steel plate
- high strength
- proof steel
- proof
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
- C23C2/29—Cooling or quenching
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Thermal Sciences (AREA)
- Physics & Mathematics (AREA)
- Coating With Molten Metal (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
- Heat Treatment Of Sheet Steel (AREA)
Priority Applications (36)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AT0120303A AT412878B (de) | 2003-07-29 | 2003-07-29 | Korrosionsgeschütztes stahlblechteil mit hoher festigkeit |
PCT/EP2004/006250 WO2005021820A1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen eines gehärteten profilbauteils |
CN200480022188.4A CN1829817B (zh) | 2003-07-29 | 2004-06-09 | 制造硬化钢零件的方法 |
DE202004021264U DE202004021264U1 (de) | 2003-07-29 | 2004-06-09 | Korrosionsschicht und gehärtetes Stahlbauteil |
PCT/EP2004/006251 WO2005021822A1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen eines gehärteten stahlbauteils |
US10/566,059 US8021497B2 (en) | 2003-07-29 | 2004-06-09 | Method for producing a hardened steel part |
US10/566,069 US7832242B2 (en) | 2003-07-29 | 2004-06-09 | Method for producing a hardened profile part |
PT47363866T PT1660693E (pt) | 2003-07-29 | 2004-06-09 | Processo de produção de um elemento de perfil temperado |
JP2006521404A JP5054378B2 (ja) | 2003-07-29 | 2004-06-09 | 薄鋼板製造方法 |
BRPI0412599A BRPI0412599B1 (pt) | 2003-07-29 | 2004-06-09 | método para produção de peças estruturais endurecidas feitas de chapa de chapa de aço. |
PL09015813T PL2177641T3 (pl) | 2003-07-29 | 2004-06-09 | Blacha stalowa z ocynkowaną ogniowo warstwą ochrony przeciwkorozyjnej |
EP20040739756 EP1651789B1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen von geharteten bauteilen aus stahlblech |
EP20090015813 EP2177641B1 (de) | 2003-07-29 | 2004-06-09 | Stahlblech mit einer feuerverzinkten Korrosionschutzschicht |
CNA2004800221723A CN1829816A (zh) | 2003-07-29 | 2004-06-09 | 由薄钢板制造硬化零件的方法 |
ES04736386.6T ES2524324T3 (es) | 2003-07-29 | 2004-06-09 | Procedimiento para la producción de un componente perfilado templado |
EP04736386.6A EP1660693B1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen eines gehärteten profilbauteils |
US10/566,219 US8181331B2 (en) | 2003-07-29 | 2004-06-09 | Method for producing hardened parts from sheet steel |
PL04739756T PL1651789T3 (pl) | 2003-07-29 | 2004-06-09 | Sposób wytwarzania hartowanych elementów konstrukcyjnych z blachy stalowej |
BRPI0412601 BRPI0412601B1 (pt) | 2003-07-29 | 2004-06-09 | método para produção de uma peça de aço endurecido |
PCT/EP2004/006252 WO2005021821A1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen von gehärteten bauteilen aus stahlblech |
PT04739756T PT1651789E (pt) | 2003-07-29 | 2004-06-09 | Processo de fabrico de peças temperadas de chapa de aço |
AT04739756T ATE478971T1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen von geharteten bauteilen aus stahlblech |
CA 2533633 CA2533633C (en) | 2003-07-29 | 2004-06-09 | Method for producing hardened parts from sheet steel |
ES04739755.9T ES2525731T3 (es) | 2003-07-29 | 2004-06-09 | Procedimiento para la producción de un componente de acero templado |
EP04739755.9A EP1658390B1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen eines gehärteten stahlbauteils |
JP2006521403A JP5113385B2 (ja) | 2003-07-29 | 2004-06-09 | 焼入れ鋼部品の製造方法 |
KR1020067002212A KR100834555B1 (ko) | 2003-07-29 | 2004-06-09 | 경화 강판 부품의 제조 방법 |
KR1020067002210A KR100825975B1 (ko) | 2003-07-29 | 2004-06-09 | 경화 강판 부품의 제조 방법 |
CN201410444698.6A CN104372278A (zh) | 2003-07-29 | 2004-06-09 | 由薄钢板制造硬化零件的方法 |
ES04739756T ES2350931T3 (es) | 2003-07-29 | 2004-06-09 | Procedimiento para la fabricación de componentes templados de chapa de acero. |
DE200450011583 DE502004011583D1 (de) | 2003-07-29 | 2004-06-09 | Verfahren zum herstellen von geharteten bauteilen aus stahlblech |
MXPA06000825A MXPA06000825A (es) | 2003-07-29 | 2004-06-09 | Metodo para producir una pieza de acero endurecido. |
ES09015813T ES2421182T3 (es) | 2003-07-29 | 2004-06-09 | Componente de chapa de acero con una capa de protección anticorrosiva catódica |
MXPA06000826A MXPA06000826A (es) | 2003-07-29 | 2004-06-09 | Metodo para producir lamina de acero. |
CA 2533327 CA2533327C (en) | 2003-07-29 | 2004-06-09 | Method for producing a hardened steel part |
US12/917,109 US7938949B2 (en) | 2003-07-29 | 2010-11-01 | Method for producing a hardened profiled structural part |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AT0120303A AT412878B (de) | 2003-07-29 | 2003-07-29 | Korrosionsgeschütztes stahlblechteil mit hoher festigkeit |
Publications (2)
Publication Number | Publication Date |
---|---|
ATA12032003A true ATA12032003A (de) | 2005-01-15 |
AT412878B AT412878B (de) | 2005-08-25 |
Family
ID=33569183
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
AT0120303A AT412878B (de) | 2003-07-29 | 2003-07-29 | Korrosionsgeschütztes stahlblechteil mit hoher festigkeit |
Country Status (2)
Country | Link |
---|---|
AT (1) | AT412878B (de) |
DE (1) | DE202004021264U1 (de) |
Families Citing this family (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE202007006168U1 (de) | 2007-04-19 | 2007-07-19 | Rothfuss, Thomas | Gitterdraht, insbesondere für Drahtkörbe |
DE102007038214A1 (de) | 2007-08-13 | 2009-02-19 | Volkswagen Ag | Verfahren zum Korrosionsschutz von Karosserie-, Fahrwerks-, Motorbauteilen oder Abgasanlagen |
DE102007038215A1 (de) | 2007-08-13 | 2009-02-19 | Nano-X Gmbh | Verfahren zur Herstellung einer aktiven Korrosionsschutzbeschichtung auf Bauteilen aus Stahl |
DE102007048504B4 (de) * | 2007-10-10 | 2013-11-07 | Voestalpine Stahl Gmbh | Korrosionsschutzbeschichtung für Stahlbleche und Verfahren zum Konditionieren einer Korrosionsschutzbeschichtung |
DE102007058222A1 (de) * | 2007-12-03 | 2009-06-04 | Salzgitter Flachstahl Gmbh | Stahl für hochfeste Bauteile aus Bändern, Blechen oder Rohren mit ausgezeichneter Umformbarkeit und besonderer Eignung für Hochtemperatur-Beschichtungsverfahren |
DE102008054318A1 (de) * | 2008-11-03 | 2010-05-12 | Bdw Technologies Gmbh | Verfahren und Anlage zur Herstellung eines Gussbauteils |
DE102009015160A1 (de) | 2009-03-26 | 2010-09-30 | Bayerische Motoren Werke Aktiengesellschaft | Verfahren zur Herstellung eines beschicht- und/oder fügbaren Blechformteils mit einer Korrosionsschutzbeschichtung |
DE102009016852A1 (de) | 2009-04-08 | 2010-10-14 | Bayerische Motoren Werke Aktiengesellschaft | Verfahren zur Herstellung wärmebehandelter Blechformteile aus einem Stahlblechmaterial mit einer Korrosionsschutzbeschichtung und derartiges Blechformteil |
DE102009050879B3 (de) * | 2009-10-27 | 2011-09-01 | Itg Induktionsanlagen Gmbh | Verfahren und Vorrichtung zur Erwärmung von Platinen |
DE102009052210B4 (de) * | 2009-11-06 | 2012-08-16 | Voestalpine Automotive Gmbh | Verfahren zum Herstellen von Bauteilen mit Bereichen unterschiedlicher Duktilität |
DE102010037077B4 (de) * | 2010-08-19 | 2014-03-13 | Voestalpine Stahl Gmbh | Verfahren zum Konditionieren der Oberfläche gehärteter korrosionsgeschützter Bauteile aus Stahlblech |
DE102011119562A1 (de) * | 2011-11-26 | 2013-05-29 | GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) | Äußere Wandstruktur für die Karosserie eines Kraftfahrzeuges sowie Fahrzeugkarosserie |
DE102012215512A1 (de) | 2012-08-31 | 2014-05-28 | Bayerische Motoren Werke Aktiengesellschaft | Verfahren und Fertigungsanlage zum Herstellen eines warmumgeformten oder pressgehärteten Blechformteils mit einer metallischen Korrosionsschutzbeschichtung sowie hiermit hergestelltes Blechformteil und Fahrzeugkarosserie mit solchem Blechformteil |
DE102012024616A1 (de) | 2012-12-17 | 2014-06-18 | GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) | Stahlblech und Formteil daraus |
DE102013015032A1 (de) * | 2013-09-02 | 2015-03-05 | Salzgitter Flachstahl Gmbh | Zinkbasierte Korrosionsschutzbeschichtung für Stahlbleche zur Herstellung eines Bauteils bei erhöhter Temperatur durch Presshärten |
DE102014000969A1 (de) | 2014-01-27 | 2015-07-30 | GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) | Kraftfahrzeugbauteil |
DE102014004652A1 (de) * | 2014-03-29 | 2015-10-01 | Daimler Ag | Bauteil, insbesondere Strukturbauteil für einen Kraftwagen, sowie Verfahren zum Herstellen eines solchen Bauteils |
DE102015016656A1 (de) * | 2015-12-19 | 2017-06-22 | GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) | Verfahren zur Herstellung eines beschichteten, durch Warmumformung gehärteten Körpers sowie ein nach dem Verfahren hergestellter Körper |
DE102016102324B4 (de) * | 2016-02-10 | 2020-09-17 | Voestalpine Metal Forming Gmbh | Verfahren und Vorrichtung zum Erzeugen gehärteter Stahlbauteile |
DE102018009745A1 (de) | 2018-12-14 | 2020-06-18 | Salzgitter Flachstahl Gmbh | Blechplatine zur Hertstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils sowie Warmumformverfahren |
DE102020202171A1 (de) | 2020-02-20 | 2021-08-26 | Thyssenkrupp Steel Europe Ag | Verfahren zur Herstellung eines oberflächenveredelten Stahlblechs und oberflächenveredeltes Stahlblech |
DE102021105131A1 (de) | 2021-03-03 | 2022-09-08 | Salzgitter Flachstahl Gmbh | Verfahren zur Herstellung eines warmumgeformten und pressgehärteten Stahlblechbauteils |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
FR2787735B1 (fr) * | 1998-12-24 | 2001-02-02 | Lorraine Laminage | Procede de realisation d'une piece a partir d'une bande de tole d'acier laminee et notamment laminee a chaud |
FR2807447B1 (fr) * | 2000-04-07 | 2002-10-11 | Usinor | Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue |
-
2003
- 2003-07-29 AT AT0120303A patent/AT412878B/de not_active IP Right Cessation
-
2004
- 2004-06-09 DE DE202004021264U patent/DE202004021264U1/de not_active Ceased
Also Published As
Publication number | Publication date |
---|---|
DE202004021264U1 (de) | 2007-05-31 |
AT412878B (de) | 2005-08-25 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ATA12032003A (de) | Korrosionsgeschütztes stahlblechteil mit hoher festigkeit | |
CY2018019I2 (el) | Υποκατεστημενες διυδροκιναζολινες με αντι-ιικες ιδιοτητες | |
DE602005027481D1 (de) | Nichtorientiertes elektrostahlblech mit hervorragendem eisenverlust. | |
DE602005011023D1 (de) | Nichtausgerichtetes elektrisches stahlblech mit hervorragendem kernverlust | |
ATE520841T1 (de) | Verbindungsplatte | |
DE502006004311D1 (de) | Biegesteife verbundplatte | |
DE602005007145D1 (de) | Aufhängungsplatte mit Schaltung | |
DE602004022833D1 (de) | Fahrzeugaufbauplatte mit integraler klammer | |
ATE408608T1 (de) | Benzoylsubstituierte serin-amide | |
DE602005003372D1 (de) | Verbundmikroresonator mit hoher deformation | |
DE602004027859D1 (de) | Entgaser mit Flachmembranen | |
DE602005015508D1 (de) | Aufhängungsplatte mit Schaltung | |
DE602004012421D1 (de) | Mer | |
DE602004018071D1 (de) | Druckverfahren mit Druckplatte | |
ATE455283T1 (de) | Kühlplatte | |
DE602006015078D1 (de) | Kernplatte mit mehreren gliedern | |
ITTO20050068A1 (it) | Rubinetto con base fissa, perfezionato | |
DE602006004566D1 (de) | Substituierte pyrrole, zusammensetzungen, die dieshre verwendung | |
GB0603833D0 (en) | Electrophoresis plate | |
DE602004000611D1 (de) | Einschlussanordnung für Taumelscheibe | |
ITMI20060151U1 (it) | Moble | |
BRPI0402683B1 (pt) | Laminador de chapa | |
DK1723278T3 (da) | Multiaksialt kompleks | |
FI20030136A0 (fi) | Sovitelma ankkurin yhteydessä | |
DE502004011175D1 (de) | Transimpedanzverstärker mit hoher verstärkungsband |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MK07 | Expiry |
Effective date: 20230729 |